DE19823246A1 - Brick with decorative layer - Google Patents

Brick with decorative layer

Info

Publication number
DE19823246A1
DE19823246A1 DE1998123246 DE19823246A DE19823246A1 DE 19823246 A1 DE19823246 A1 DE 19823246A1 DE 1998123246 DE1998123246 DE 1998123246 DE 19823246 A DE19823246 A DE 19823246A DE 19823246 A1 DE19823246 A1 DE 19823246A1
Authority
DE
Germany
Prior art keywords
base
brick
cover layer
decorative cover
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
DE1998123246
Other languages
German (de)
Inventor
Friedrich Bakels
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kellen BV
Original Assignee
KELLEN BETON BV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by KELLEN BETON BV filed Critical KELLEN BETON BV
Publication of DE19823246A1 publication Critical patent/DE19823246A1/en
Ceased legal-status Critical Current

Abstract

The brick has decorative layer (2) on at least one of its sides. The brick base consists of a light hygroscopic material in the form of rough-grained filling material bonded by means of a binding agent, e.g. cement. It has a degree of hygroscopicity of at least 15 %. The grain size of the filling material is between 0 and 8 mm. The filling material consists of fly ash or BIMS.

Description

Die Erfindung betrifft einen Mauerstein mit einer im wesent­ lichen rechteckigen Basis aus einem Material, das sich gut mauern läßt, wobei mindestens eine Seite der Basis mit einer damit verbundenen Zierdeckschicht versehen ist.The invention relates to a brick with an essential rectangular base made of a material that looks good lets wall, with at least one side of the base with a associated decorative cover layer is provided.

Ein derartiger Verbundmauerstein ist aus der GB-A-2 284 834 bekannt. Die Basis ist hier vollständig aus Beton oder einem anderen zementartigen Material gebildet. Die Zierdeckschicht besteht aus Naturstein und ist auf der Basis festgeklebt oder damit mechanisch verbunden.Such a composite brick is from GB-A-2 284 834 known. The base here is made entirely of concrete or one other cementitious material. The decorative top layer consists of natural stone and is glued to the base or mechanically connected to it.

Nachteilig bei diesem bekannten Verbundmauerstein ist, daß er sich schlecht mauern läßt. Die Mauerbarkeit eines derar­ tigen Verbundmauersteins wird vorwiegend durch die Zusammen­ setzung der Basis bestimmt und hängt stark zusammen mit dem Maß, in dem die Basis Wasser aus dem beim Mauern verwendeten Mörtel aufnehmen kann, der sogenannten Hygroskopizität. Die beton- oder zementartige Basis nach der GB-A-2 284 834 hat eine sehr niedrige Hygroskopizität und läßt sich demnach schlecht mauern. Die wichtigsten Anforderungen, die an einen Mauerstein gestellt werden, sind neben der guten Mauerbar­ keit das Gewicht und die Festigkeit des Mauersteins. Die be­ ton- oder zementartige Basis ist zwar ausreichend fest, aber hat den Nachteil, daß sie den gesamten Verbundmauerstein schwer macht.A disadvantage of this known composite brick is that it is difficult to build walls. The stoneability of a derar bonded masonry brick is mainly through the together The establishment of the basis determines and is closely related to the Dimension in which the base water from that used in the masonry Mortar can absorb, the so-called hygroscopicity. The has a concrete or cement-like base according to GB-A-2 284 834 a very low hygroscopicity and can therefore be bad walling. The most important requirements for one Brick are placed next to the good wall bar the weight and strength of the brick. The be  clay or cement-like base is sufficiently firm, but has the disadvantage that it covers the entire composite brick makes difficult.

Die Aufgabe der vorliegenden Erfindung ist, einen Mauerstein mit einer Zierdeckschicht zu schaffen, der sich gut mauern läßt, ein geringes Gewicht und doch eine ausreichende Fe­ stigkeit hat.The object of the present invention is a brick to create with a decorative top layer that masonry well leaves, a light weight and yet a sufficient Fe has stability.

Nach der Erfindung wird diese Aufgabe dadurch gelöst, daß die Basis aus einem hygroskopischen, leichten Basismaterial besteht, welches im wesentlichen aus einem derart grobkörni­ gen, durch ein Bindemittel gebundenen Füllmaterial besteht, daß die Basis eine Hygroskopizität von mindestens 15% hat. Durch diese Zusammensetzung der Basis entsteht ein gut mau­ erbarer Verbundmauerstein, der außerdem leicht ist und eine ausreichende Festigkeit besitzt.According to the invention, this object is achieved in that the basis of a hygroscopic, light base material consists essentially of such a coarse grain filling material bound by a binder, that the base has a hygroscopicity of at least 15%. This composition of the base creates a good mau attainable composite brick, which is also light and one has sufficient strength.

Insbesondere beträgt die Korngröße des Füllmaterials in der Hauptsache 0-8 mm, wobei die größten Fraktionen bis zu 8 mm groß sind. Das grobkörnige Füllmaterial besteht bevorzugt aus "Aardeliet" (gesinterte Flugasche), Flugasche oder BIMS. Das Bindemittel kann zum Beispiel Zement sein. Eine solche Basis ist preiswert zusammenzustellen und entspricht jeder der wichtigsten Anforderungen.In particular, the grain size of the filling material in the The main thing is 0-8 mm, with the largest fractions up to 8 mm are great. The coarse-grained filler material is preferred from "Aardeliet" (sintered fly ash), fly ash or BIMS. The binder can be, for example, cement. Such The basis is inexpensive to put together and corresponds to everyone of the main requirements.

In einer Ausführungsform besteht die Zierdeckschicht aus in einem härtbaren Material aufgenommenem, gemahlenem Natur­ stein, und sind die Basis und die Zierdeckschicht miteinan­ der verbunden, indem nicht gehärtetes Basismaterial und nicht gehärtetes Zierdeckschichtmaterial unmittelbar mitein­ ander in Kontakt gebracht werden, und man anschließend die­ sen Verbund härten läßt. So erhält man eine preiswerte und starke Verbindung zwischen der Basis und der Zierdeck­ schicht, ohne daß man Kleber oder mechanische Verbindungs­ mittel benutzen muß.In one embodiment, the decorative cover layer consists of a hardened material absorbed, ground nature stone, and are the base and the decorative cover layer together which connected by not hardened base material and  unhardened decorative cover layer material directly with it others are brought into contact, and then the can harden its composite. So you get an inexpensive and strong connection between the base and the decorative deck layer without glue or mechanical connection must use medium.

Die Erfindung wird nachfolgend unter Bezugnahme auf die bei­ liegende Zeichnung näher erläutert, in der:The invention is described below with reference to the lying drawing explained in more detail in which:

Fig. 1 eine perspektivische Ansicht eines Mauersteins nach der Erfindung ist, Fig. 1 is a perspective view of a masonry unit according to the invention,

Fig. 2 eine Ansicht einer besonderen Ausführungsform der Verbindung zwischen der Basis und der Zierdeck­ schicht ist,A view of a particular embodiment of the connection between the base and the trim cover, FIG. 2 layer,

Fig. 3 eine Ansicht einer anderen besonderen Ausfüh­ rungsform der Verbindung zwischen der Basis und der Zierdeckschicht ist und Fig. 3 is a view of another specific exporting approximate shape of the connection between the base and the decorative outer layer and

Fig. 4 eine perspektivische Ansicht eines Mauersteins nach der Erfindung, bei dem zwei benachbarte Seiten mit einer Zierdeckschicht versehen sind. Fig. 4 is a perspective view of a brick according to the invention, in which two adjacent sides are provided with a decorative cover layer.

In der Fig. 1 ist die Basis des Mauersteins mit der Bezugs­ ziffer 1 bezeichnet. Diese Basis 1 besteht in der Hauptsache aus hygroskopischem, leichtem Basismaterial. Das hygroskopi­ sche, leichte Basismaterial wird zum Beispiel aus einem mit Zement gebundenem grobkörnigem Füllmaterial aus gesintertem "Aardeliet", Flugasche oder BIMS gebildet. Die Korngrößever­ teilung des Füllmaterials ist derart, daß 95% der Körner größer als 2 mm sind, und insbesondere die größten Fraktio­ nen der Körner bis zu 8 mm groß sind. Dadurch, daß eine der­ artige Zusammensetzung der Basis gut Wasser aus dem beim Mauern benutzten Mörtel aufnehmen kann, läßt sich ein derar­ tiger Mauerstein gut und schnell mauern. Außerdem ist die Basis 1 leicht im Gewicht, was die Handlichkeit des Mauer­ steins steigert und eventuelle Transportkosten senkt.In Fig. 1, the base of the brick is designated by the reference number 1 . This base 1 consists mainly of hygroscopic, light base material. The hygroscopic, lightweight base material is formed, for example, from a coarse-grained filler material bonded with cement from sintered "aardeliet", fly ash or BIMS. The grain size distribution of the filler is such that 95% of the grains are larger than 2 mm, and in particular the largest fractions of the grains are up to 8 mm in size. The fact that one of the like composition of the base can well absorb water from the mortar used in the masonry, a brick wall of this kind can be built well and quickly. In addition, the base 1 is light in weight, which increases the manageability of the brick and reduces possible transportation costs.

Wie man sehen kann, ist die Basis 1 an der Vorderseite mit einer Zierdeckschicht 2 versehen. Vorzugsweise besteht die Zierdeckschicht 2 in der Hauptsache aus in einem härtbaren Material auf genommenem, gemahlenem Naturstein und ist frei von Farbstoffen. Dadurch, daß die Zierdeckschicht keinen Farbstoff enthält, tritt sogar nach vielen Jahrzehnten keine Änderung in der Farbe auf. Man könnte hierbei an gemahlenen Marmor oder Granit, das durch ein Gemisch aus Wasser und Ze­ ment gebunden ist, denken. In einer Variante ist der gemah­ lene Naturstein durch Kunststoff gebunden.As can be seen, the base 1 is provided with a decorative cover layer 2 on the front. The decorative cover layer 2 preferably consists mainly of ground natural stone taken up in a hardenable material and is free from dyes. Because the decorative cover layer contains no dye, there is no change in color even after many decades. One could think of ground marble or granite bound by a mixture of water and cement. In a variant, the milled natural stone is bound by plastic.

In der in der Fig. 1 gezeigten Ausführungsform sind die Ba­ sis 1 und die Zierdeckschicht 2 unmittelbar mit einander verbunden. Eine derartige Verbindung kann man insbesondere erhalten, wenn man nicht gehärtetes Basismaterial und nicht gehärtetes Zierdeckschichtmaterial unmittelbar miteinander in Kontakt bringt und den so gebildeten Verbund aushärten läßt. In the embodiment shown in FIG. 1, the base 1 and the decorative cover layer 2 are directly connected to one another. Such a connection can be obtained in particular if the non-hardened base material and the non-hardened decorative cover layer material are brought into direct contact with one another and the composite thus formed is allowed to harden.

In der in Fig. 2 gezeigten Ausführungsform ist eine adhäsi­ ve Zwischenschicht 13, insbesondere ein hierfür geeigneter Kleber, auf entweder die Basis 11 oder die Zierdeckschicht 12 aufgebracht, welche Basis und Zierdeckschicht mit einan­ der verbindet.In the embodiment shown in FIG. 2, an adhesive intermediate layer 13 , in particular a suitable adhesive, is applied to either the base 11 or the decorative cover layer 12 , which connects the base and decorative cover layer to one another.

In Fig. 3 ist wieder eine andere Ausführungsform der Ver­ bindung zwischen der Basis 21 und der Zierdeckschicht 22 ge­ zeigt. Die Verbindung wird hier durch eine Formverbindung 23 gebildet. Diese Formverbindung 23 kann zum Beispiel durch in der Basis 21 angebrachte Rinnen, die mit oben auf die Basis angebrachtem noch nicht ausgehärtetem Zierdeckschichtmate­ rial gefüllt sind, gebildet sein. Nach dem Aushärten wird man so eine formschlüssige Verbindung erhalten. Die Rinnen können natürlich auch in der Zierdeckschicht statt in der Basis ausgebildet werden.In Fig. 3, another embodiment is again the Ver connection between the base 21 and the decorative outer layer 22 shows ge. The connection is formed here by a molded connection 23 . This molded connection 23 can be formed, for example, by grooves in the base 21 , which are filled with material that has not yet hardened on the base and is not cured. After curing, a positive connection will be obtained. The channels can of course also be formed in the decorative cover layer instead of in the base.

Die hier oben beschriebenen Arten von Verbindungen zwischen der Basis und der Zierdeckschicht können auch kombiniert an­ gewendet werden.The types of connections between the base and the decorative cover layer can also be combined be turned.

Fig. 4 zeigt einen Mauerstein, bei dem zwei benachbarte Seiten der Basis 31 mit einer Zierdeckschicht 32 versehen sind. Ein derartiger Mauerstein ist dazu bestimmt, als Eck­ stein zu dienen, der zwei Sichtseiten hat, die dann vorzugs­ weise beide mit einer Zierdeckschicht versehen sind. Eine andere Art zum Mauern von Ecken ist die Anwendung von ge­ gehrten Mauersteinen, wie sie an Hand der Fig. 1-3 be­ schrieben sind. Auch kann man in der Praxis daran denken, die Ecksteine vollständig in Naturstein auszuführen. Fig. 4 shows a brick, in which two adjacent sides of the base 31 are provided with a decorative cover layer 32 . Such a brick is intended to serve as a corner stone, which has two visible sides, which are then preferably both provided with a decorative cover layer. Another way of walling corners is the use of mitered bricks, as described with reference to FIGS . 1-3. In practice, one can also think of making the corner stones entirely from natural stone.

Ein mögliches Verfahren zur Herstellung eines Mauersteins nach der Erfindung, wie er in Fig. 1 gezeigt ist, kann dar­ in bestehen, daß in eine geeignete Form nicht gehärtetes hy­ groskopisches leichtes Basismaterial eingebracht wird, das dann durch Rütteln teilweise verdichtet wird. Dann wird auf die noch nicht ausgehärtete Basis eine Schicht nicht ausge­ härteten Zierdeckschichtmaterials aufgebracht, woraufhin das Ganze völlig verdichtet wird, wonach es aus der Form ent­ fernt und gewaschen werden kann.A possible method for producing a brick according to the invention, as shown in Fig. 1, may consist in that uncured hy grocopopic light base material is introduced into a suitable mold, which is then partially compacted by shaking. Then a layer of uncured decorative cover layer material is applied to the not yet hardened base, whereupon the whole is completely compacted, after which it can be removed from the mold and washed.

So wurde mit der Erfindung ein sehr preiswerter Mauerstein erhalten, der sowohl schön aussieht als auch sich gut mauern läßt und außerdem preiswert und leicht im Gewicht ist.So with the invention a very inexpensive brick that looks and looks good leaves and is also inexpensive and light in weight.

Claims (4)

1. Mauerstein, der eine im wesentlichen rechteckige Basis aus mauerbarem Material umfaßt, wobei mindestens eine Seite der Basis mit einer damit verbundenen Zierdeck­ schicht versehen ist, dadurch gekennzeichnet, daß die Ba­ sis aus einem hygroskopischen leichten Basismaterial be­ steht, welches im wesentlichen aus einem grobkörnigen, durch ein Bindemittel gebundenen Füllmaterial besteht, so daß die Basis eine Hygroskopizität von mindestens 15% hat.1. brick, which comprises a substantially rectangular base made of wallable material, at least one side of the base is provided with an associated decorative deck layer, characterized in that the base consists of a hygroscopic light base material, which consists essentially of a coarse-grained filler material bound by a binder, so that the base has a hygroscopicity of at least 15%. 2. Mauerstein nach Anspruch 1, dadurch gekennzeichnet, daß die Korngröße des Füllmaterials im wesentlichen zwischen 0 und 8 mm liegt, wobei die größten Fraktionen in der Nä­ he von 8 mm liegen.2. brick according to claim 1, characterized in that the grain size of the filling material essentially between 0 and 8 mm, with the largest fractions in the Nä height of 8 mm. 3. Mauerstein nach Anspruch 1 oder 2, dadurch gekennzeich­ net, daß das grobkörnige Füllmaterial aus Flugasche oder BIMS besteht.3. brick according to claim 1 or 2, characterized net that the coarse filling material from fly ash or BIMS exists. 4. Mauerstein nach einem der vorherigen Ansprüche, dadurch gekennzeichnet, daß die Zierdeckschicht aus einem in ei­ nem härtbaren Material aufgenommenen gemahlenen Natur­ stein besteht, und daß die Basis und die Zierdeckschicht des Mauersteins miteinander verbunden sind, indem nicht ausgehärtetes Basismaterial und nicht ausgehärtetes Zier­ deckschichtmaterial unmittelbar in Kontakt miteinander gebracht werden und dann dieser Verbund aushärten gelas­ sen wird.4. Brick according to one of the preceding claims, characterized characterized in that the decorative cover layer from a egg ground material absorbed by a hardenable material  stone exists, and that the base and the decorative cover layer of the brick are connected by not hardened base material and not hardened ornament top layer material in direct contact with each other brought and then let this composite harden will.
DE1998123246 1997-05-27 1998-05-25 Brick with decorative layer Ceased DE19823246A1 (en)