DE19753243C2 - Method for producing a three-dimensional object coated with a veneer - Google Patents
Method for producing a three-dimensional object coated with a veneerInfo
- Publication number
- DE19753243C2 DE19753243C2 DE1997153243 DE19753243A DE19753243C2 DE 19753243 C2 DE19753243 C2 DE 19753243C2 DE 1997153243 DE1997153243 DE 1997153243 DE 19753243 A DE19753243 A DE 19753243A DE 19753243 C2 DE19753243 C2 DE 19753243C2
- Authority
- DE
- Germany
- Prior art keywords
- veneer
- synthetic resin
- resin coating
- producing
- dimensional object
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
Die Erfindung betrifft ein Verfahren zur Herstellung von einem mit einem Furnier beschichteten dreidimensionalen Gegenstand.The invention relates to a method for producing a three-dimensional coated with a veneer Object.
Es ist bekannt, z. B. Teile eines Kraftfahrzeuginnenraums, insbesondere eines Kraftfahrzeug-Armaturenbretts mit Edel hölzern zu furnieren. Hierbei werden die dreidimensional geformten Werkstücke, welche z. B. aus Formsperrholz, Kunst stoffspritzguß, Aluminiumdruckguß oder Magnesiumdruckguß bestehen, mit dem Edelholzfurnier überzogen. Nach dem Form pressen weisen diese Furniere in der Regel Fehler durch Rissbildungen auf, die anschließend von Hand mit Polyester harz ausgebessert werden müssen. Da das Holzfurnier weicher als das Polyesterharz ist, muss das Werkstück feinfühlig von Hand geschliffen und weiterverarbeitet werden, da eine maschinelle Bearbeitung entweder zu aufwendig oder zu kost spielig ist. Es muss vor allem darauf geachten werden, dass beim Schleifvorgang ein nicht zu großer Holzanteil zwischen den mit Polyesterharz ausgekitteten Rissen ausgeschliffen wird.It is known e.g. B. parts of a motor vehicle interior, especially a motor vehicle dashboard with noble wooden veneer. Here, the three-dimensional shaped workpieces, which, for. B. made of molded plywood, art injection molding, aluminum die casting or magnesium die casting exist, covered with the precious wood veneer. According to the form presses, these veneers usually show defects Cracking, which is then done by hand with polyester resin must be touched up. Because the wood veneer is softer than the polyester resin, the workpiece must be sensitive be sanded by hand and further processed, as a machining either too expensive or too expensive is playful. Above all, care must be taken that a not too large proportion of wood between the grinding process sanded the cracks cemented with polyester resin becomes.
Die DE 35 12 622 A1 offenbart ein rückseitig beschichtetes Echtholzfurnier, welches derart auf Gegenstände auf bringbar sein soll, dass es keinerlei Nacharbeitbarkeit bedarf. Das Echtholzfurnier muß nach dem Aufkleben noch geschliffen und mit einem Decklack versehen werden. Beim Aufkleben muß darauf geachtet werden dass das Furnier nicht zu sehr reisst und beim Schleifen muß darauf geachtet werden, dass das Furnier nicht durchgeschliffen wird.DE 35 12 622 A1 discloses a coated on the back Real wood veneer, which is based on objects should be feasible that there is no reworkability requirement. The real wood veneer still has to be glued on be sanded and provided with a top coat. At the Gluing must take care that the veneer is not tears too much and care must be taken when grinding that the veneer is not sanded through.
Der Erfindung liegt die Aufgabe zugrunde, ein Verfahren bereitzustellen, mit dem auf einfache Weise dreidimensional geformte Gegenstände schneller, einfacher und preiswerter mit Furnieren überzogen werden können.The invention has for its object a method provide with the easy three-dimensional shaped objects faster, easier and cheaper can be covered with veneers.
Diese Aufgabe wird erfindungsgemäß dadurch gelöst, dass das Furnier vor der Applikation auf den dreidimensional geformten Gegenstand auf seiner Sichtfläche mit einem elastischen Kunstharzüberzug versehen wird.This object is achieved in that the Veneer before application to the three-dimensional shaped object on its visible surface with a elastic synthetic resin covering is provided.
Das erfindungsgemäße Verfahren sieht also vor, dass die Sichtfläche des Furniers mit einem elastischen Kunstharz überzogen und getränkt wird, wodurch zwei Effekte erzielt werden. Zum einen wird das Furnier während des Formpressens vom Überzug zusammengehalten, wodurch wesentlich weniger Risse entstehen. Außerdem reisst das Furnier während der Lagerung wesentlich weniger. Ein weiterer Vorteil ist, dass die gesamte Oberfläche des Furniers aus einem Material besteht, welches eine Härte aufweist, die im wesentlichen dem Material entspricht, mit welchem die nach dem Form pressen entstandenen wenigen Risse oder Materialfehler aus gekittet bzw. ausgespachtelt werden. Wird das Furnier bzw. dessen Oberfläche nach dem Ausspachteln geschliffen, kann dies auch maschinell erfolgen, da die Oberfläche keine harten und weichen Bereiche aufweist. Die Oberfläche des Furniers ist im wesentlichen gleichmäßig hart. Die Verar beitung kann daher maschinell erfolgen, was zum einen eine Zeitersparnis, zum anderen eine Kostenersparnis mit sich bringt.The method according to the invention therefore provides that the Visible surface of the veneer with an elastic synthetic resin is coated and soaked, creating two effects become. On the one hand, the veneer is used during compression molding held together by the coating, which means much less Cracks appear. The veneer also tears during the Storage much less. Another advantage is that the entire surface of the veneer from one material exists, which has a hardness that is essentially corresponds to the material with which the shape squeeze out a few cracks or material defects be puttied or filled. If the veneer or the surface of which can be sanded after filling this can also be done mechanically since the surface is none hard and soft areas. The surface of the Veneer is essentially equally hard. The processors Processing can therefore be done mechanically, which on the one hand Time saving, and secondly a cost saving brings.
Aus dem Furnier, welches an sich sehr spröde ist, wird durch das Auftragen des Kunstharzüberzuges ein Verbundstoff hergestellt. Dies hat den wesentlichen Vorteil, dass das Furnier geschmeidiger wird, da der Kunstharzüberzug auch in die Poren, Kapillaren und in die Zellstruktur des Holzes, welches eine sehr geringe Feuchtigkeit aufweist, eindringt. Dieser Verbundwerkstoff lässt sich erheblich leichter verarbeiten als das reine Furnier.The veneer, which is very brittle in itself, becomes by applying the synthetic resin coating a composite manufactured. This has the main advantage that the Veneer becomes more supple because the synthetic resin covering also in the pores, capillaries and into the cell structure of the wood, which has a very low moisture penetrates. This composite material is considerably easier process than the pure veneer.
Vorteilhaft werden für den Kunstharzüberzug Acrylharze oder Polyesterharze verwendet. Diese können als Zusätze Styrol und/oder andere Monomere enthalten, die die Erhärtung oder Verarbeitbarkeit beeinflussen. Dieser Kunstharzüberzug kann eine Grundierung sein bzw. kann als Grundierung verwendet werden, jedoch besteht auch die Möglichkeit, dass der Kunstharzüberzug bereits eine fertige Lackierung ist. In diesem Falle besteht die Möglichkeit, die Teile bereits mit fertiger Oberfläche zu versehen, so dass eventuell eine Nachbehandlung gänzlich entfallen kann.Acrylic resins or are advantageous for the synthetic resin coating Polyester resins used. These can be styrene additives and / or contain other monomers which harden or Affect processability. This resin cover can can be a primer or can be used as a primer , but there is also a possibility that the Resin coating is already a finished paint job. In In this case it is possible to use the parts finished surface, so that possibly a Post-treatment can be completely eliminated.
Bei einem bevorzugten Verfahren wird der Kunstharzüberzug durch Walzenapplikation auf das Furnier aufgebracht. Dieses Verfahren ermöglicht einen Auftrag mit außerordentlicher Ebenheit unabhängig von der Oberflächengüte des Furniers. Weist das Furnier bereits Risse auf, dann werden diese durch den Kunstharzüberzug geschlossen.A preferred method is the resin coating applied to the veneer by roller application. This Process enables an order with extraordinary Flatness regardless of the surface quality of the veneer. If the veneer already shows cracks, they will closed by the synthetic resin coating.
Ein anderes Verfahren sieht vor, dass der Kunstharzüberzug durch Gießapplikation auf das Furnier aufgebracht wird. Dieses Verfahren eignet sich besonders bei relativ dünnflüssigen Materialien, wodurch im wesentlichen die Oberfläche versiegelt wird.Another method provides that the synthetic resin coating is applied to the veneer by pouring. This method is particularly suitable for relative thin materials, which essentially the Surface is sealed.
Ein weiterer Verfahrensschritt sieht vor, dass der Kunstharzüberzug nach dem Aufbringen auf das Furnier getrocknet wird. Dabei muss der Trockenvorgang nicht vollständig abgeschlossen werden, so dass der Kunstharzüberzug nach wie vor elastisch ist. Die vollständige Austrocknung des Kunstharzüberzuges kann in der Formpresse erfolgen. Je nach verwendetem Kunstharzüberzug kann die Trocknung durch ein physikalisches oder mechanisches Verfahren erfolgen. Die Bestrahlung durch Infrarot- oder UV-Licht ist ebenfalls denkbar.A further procedural step provides that the Resin coating after application to the veneer is dried. The drying process does not have to be completed so that the Resin cover is still elastic. The complete drying of the synthetic resin coating can occur the molding press. Depending on the used Resin coating can be done by drying physical or mechanical process. The Irradiation by infrared or UV light is also conceivable.
Um die Elastizität des Kunstharzüberzuges zu erhöhen besteht die Möglichkeit, dass dem Kunstharzüberzug vor dem Aufbringen auf das Furnier ein oder mehrere Elastomere zugesetzt werden. Ein derart beschichtetes Furnier wird optimal zusammengehalten, wobei die Verformbarkeit des Furniers beim Formpressen nicht beeinträchtigt wird.To increase the elasticity of the synthetic resin cover there is a possibility that the synthetic resin coating before Apply one or more elastomers to the veneer be added. Such a veneer is coated optimally held together, while the deformability of the veneer during compression molding is not affected.
Dem Kunstharzüberzug können außerdem Komponenten zur Trocknung, z. B. UV-Iniziatoren o. dgl. beigemischt sein. Diese Komponenten bewirken, dass der Trocknungsprozess des Überzuges erst dann einsetzt, wenn dieser mit UV-Licht bestrahlt wird. Zuvor bleibt der Kunstharzüberzug elastisch, so dass das beschichtete Furnier beliebig verarbeitbar ist.The synthetic resin coating can also have components for Drying, e.g. B. UV initiators or the like can be added. These components cause the drying process of the The coating only starts when it is coated with UV light is irradiated. The synthetic resin covering remains beforehand elastic so that the coated veneer is arbitrary is processable.
Claims (8)