Abstract

The connecting members (2) are mixed with particles, such as balls (3), of a predetermined particle size. These balls are designed to serve as spacer elements between the components being placed together. The balls can be made from a material whose density equals that of the connecting members. The balls can be made of metal or plastics and have a diameter of about 3 mm.

Description

Die Erfindung betrifft ein Verfahren zum Herstellen einer gleichmäßig dicken Verbindungsmittelschicht für aneinanderleg bare Bauelemente, insbesondere für Kalksandsteine.The invention relates to a method for producing a evenly thick layer of fastener for laying together bare components, especially for sand-lime bricks.

Es ist bekannt, bei der Herstellung von Mauerwerk zum Beispiel aus aufeinanderlegbaren Bauelementen auf ein jeweils untenliegendes Bauelement eine Schicht des Verbindungsmittels aufzubringen, in welche ein Bauelement gelegt und angedrückt wird. Dabei ist es wichtig, eine gleichmäßig dicke Verbindungs mittelschicht herzustellen, damit die jeweils aufeinandergeleg ten Bauelemente im Mauerwerk parallel zueinander liegen.It is known to be used in the manufacture of masonry Example of stackable components on each underlying component a layer of the connecting means to apply, in which a component is placed and pressed becomes. It is important to have a uniformly thick connection middle layer, so that the respective superimposed ten components in the masonry are parallel to each other.

Besonders wichtig ist eine durch gleichmäßige Schichtdicke erreichbare gleichmäßige Fuge, wenn Sichtmauerwerk erstellt werden soll, denn Unparallelitäten übereinanderliegender und/oder nebeneinanderliegender Bauelemente sind beim Sichtmau erwerk deutlich zu erkennen.It is particularly important to have a uniform layer thickness Achievable even joint if exposed masonry is created should be, because non-parallelities are superimposed and / or adjacent components are at the exposed wall clearly recognizable.

In bevorzugter Weise werden besonders ausgebildete Kalksand steine, beispielsweise mit einer eingezogenen Lagerfläche (DE-GM 295 02 358), eingesetzt, um ein ästhetisch ansprechendes Fugen bild im Sichtmauerwerk zu bilden. Damit die Dicke dieser durch die Einziehungen künstlich ausgebildeten Fugen der Dicke her kömmlicher Fugen zwischen Mauersteinen entspricht, wird das Sichtmauerwerk nach der Dünnbettechnik geklebt. Die Verbindungs mittelschicht weist dann eine nur geringe Dicke auf, wobei diese trotzdem gleichmäßig ausgebildet sein muß, um nicht das Fugen bild des Sichtmauerwerkes zu beeinträchtigen. Bei der Dünn bettechnik ist eine gleichmäßige, relativ dünne Schicht beson ders wichtig, um feste Verbindungen zwischen den besonders aus gebildeten Kalksandsteinen zu erreichen.Particularly preferred are lime sand stones, for example with a retracted storage area (DE-GM 295 02 358), used to create an aesthetically pleasing joint to form picture in exposed masonry. So that the thickness of this through the retractions of artificially designed joints of thickness corresponds to conventional joints between bricks, it will Visible masonry glued using thin bed technology. The connection middle layer then has only a small thickness, this nevertheless must be evenly formed so as not to grout image of the exposed masonry. At the thin Bet technology is a uniform, relatively thin layer important to make strong connections between the particularly to achieve formed sand-lime bricks.

Zur Ausbildung von Verbindungsmittelschichten in der Dünnbettechnik konnten beispielsweise Zahnspachtel verwendet werden. Mit einem Zahnspachtel kann zwar eine im wesentlichen gleichmäßig dicke Verbindungsmittelschicht hergestellt werden, jedoch wird diese Schicht aufgrund ihrer "gezahnten" Ausbildung durch Auflegen des obenliegenden Kalksandsteins erheblich zu sammengedrückt. Dabei wird die mit dem Zahnspachtel hergestellte Dicke der Schicht minimiert. Die endgültige Dicke der Schicht ist aufgrund jeweils unterschiedlicher Einflüsse, wie der Masse des aufliegenden Kalksandsteines nachteilig nicht vorbestimmbar. Das Überstreichen des auf dem untenliegenden Kalksandstein auf gebrachten Verbindungsmittels mit einem Zahnspachtel ist zudem zeitaufwendig, denn dieser Arbeitsschritt muß nach dem eigentli chen Aufbringen und Verteilen des Verbindungsmittels auf dem Kalksandstein erfolgen.For the formation of bonding agent layers in the Thin bed technology could be used, for example, notched trowels will. With a serrated spatula, one can essentially uniformly thick connection layer are produced, however, this layer becomes due to its "serrated" formation by laying the sand-lime brick on top squeezed. This is done with the notched trowel Layer thickness minimized. The final thickness of the layer is due to different influences such as mass of the overlying lime sandstone disadvantageously cannot be predetermined. The painting on the sand lime stone below brought lanyard with a notched trowel is also time consuming, because this step must be done after the actual Chen application and distribution of the lanyard on the Lime sandstone.

Der Erfindung liegt die Aufgabe zugrunde, ein Verfahren der eingangs genannten Gattung aufzuzeigen, mit dem das Herstellen einer gleichmäßig dicken Verbindungsmittelschicht für aneinan derlegbare Bauelemente optimiert wird.The invention has for its object a method of point to the type mentioned at the beginning, with which the manufacture a uniformly thick connection layer for each other derlegbaren components is optimized.

Diese Aufgabe ist erfindungsgemäß dadurch gelöst, daß dem Verbindungsmittel als Distanzelemente dienende Körner mit vorbe stimmter Korngröße zugefügt werden.This object is achieved in that the Grains serving as connecting elements with passing certain grain size can be added.

Die dem Verbindungsmittel erfindungsgemäß zugefügten Di stanzelemente sind somit vorteilhaft zugleich mit dem Verbin dungsmittel zum Beispiel auf dem untenliegenden Kalksandstein anordbar. Die Zufügung erfolgte vorzugsweise bereits bei der Herstellung des Verbindungsmittels. Durch Verteilen des Verbin dungsmittels auf dem untenliegenden Kalksandstein werden auch die Distanzelemente gleichmäßig auf dem Kalksandstein verteilt. Der obenliegende Kalksandstein wird anschließend auf diese Schicht des Verbindungsmittels aufgelegt, wobei der Kalksand stein auf den Distanzelementen angeordnet wird. Zwischen beiden Kalksandsteinen bildet sich eine Distanz heraus, die durch die vorbestimmte Korngröße der Distanzelemente bestimmt ist. Auf einfache Weise wird eine gleichmäßig dicke Verbindungsmittel schicht zwischen den aufeinandergelegten Kalksandsteinen heraus gebildet, ohne daß der die Auflage der Kalksandsteine ausführende Handwerker auf die Distanz zwischen Kalksandsteinen achten muß. Dadurch wird die Errichtungstätigkeit des Sicht mauerwerkes vorteilhaft nicht unterbrochen.The Di added according to the invention Punching elements are therefore advantageous at the same time as the connection for example on the sand-lime brick below can be arranged. The addition was preferably made at the Manufacture of the lanyard. By distributing the verb also on the underlying sand-lime brick the spacer elements evenly distributed on the sand-lime brick. The lime sandstone on top is then on top of this Layer of the lanyard applied, the lime sand stone is arranged on the spacer elements. Between the two Lime sandstones form a distance through the predetermined grain size of the spacer elements is determined. On simple way is a uniformly thick lanyard layer between the stacked lime sandstones formed without the laying of the sand-lime bricks craftsmen carrying out the distance between sand-lime bricks must pay attention. This is the establishment activity of the view masonry advantageously not interrupted.

Nach einer Weiterbildung der Erfindung ist vorgesehen, daß als Distanzelemente Kugeln verwendet werden. Kugeln weisen wie Würfel, die jeweils mit einer ihrer Flächen auf dem untenliegen den Kalksandstein aufsitzen, unabhängig von ihrer Drehposition immer die gleiche Höhe auf. Kugeln können sich jedoch nicht übereinander "auftürmen", da sie aufgrund ihrer abgerundeten Form voneinander abgleiten. Sämtliche auf dem unteren Kalksand stein aufgebrachten, kugelförmigen Distanzelemente ordnen sich somit vorteilhaft ohne weiteres Zutun nach ihrem Aufbringen ne beneinander an.According to a development of the invention, it is provided that balls are used as spacer elements. Bullets point like Cubes, each with one of their faces on the bottom sit on the sand-lime brick, regardless of its rotational position always the same height. Bullets cannot, however "stack" on top of each other, because they are rounded due to their rounded shape Slip shape from each other. All on the lower lime sand stone-applied, spherical spacers arrange themselves thus advantageous without further action after their application to each other.

Bei der Durchführung des erfindungsgemäßen Verfahrens als Distanzelemente dienende Kugeln zeichnen sich vorzugsweise da durch aus, daß die Kugeln aus einem Werkstoff gefertigt sind, dessen Dichte etwa gleich der Dichte des Verbindungsmittels ist. Diese Ausbildung der Kugeln hat den Vorteil, daß die Kugeln be reits im Herstellungswerk dem Verbindungsmittel zugefügt werden können, da sich die Kugeln aufgrund der gleichen Dichte nicht während der Lagerhaltung des Verbindungsmittels nach unten ab setzen. Aufgrund der gleichen Dichteverhältnisse von Kugeln und Verbindungsmittel bleibt eine gewünschte Gleichverteilung der Kugeln in dem Verbindungsmittel erhalten. Zudem können die Kugeln auch insbesondere dann dem Verbindungsmittel zugefügt werden, wenn dieses in nicht parallel zur Horizontalen, sondern beispielsweise senkrecht ausgerichteten Schichten angeordnet wird. Derart angeordnete Schichten werden zum Beispiel zwischen einander zugeordneten Stoßflächen von in einer Steinreihe neben einanderliegenden Kalksandsteinen ausgebildet.When performing the method according to the invention as Spheres serving as spacer elements are preferred from that the balls are made of one material, whose density is approximately equal to the density of the connecting means. This design of the balls has the advantage that the balls be are already added to the lanyard in the manufacturing plant can, because the balls do not move due to the same density downward during the storage of the connecting means put. Because of the same density ratios of balls and Connection means remains a desired uniform distribution of the Obtained balls in the lanyard. In addition, the Balls also added to the connecting means in particular if this is not parallel to the horizontal, but arranged for example vertically aligned layers becomes. Layers arranged in this way are, for example, between mating faces of one another in a row of stones lime sandstones lying opposite each other.

Gemäß einer weiteren Weiterbildung ist der Werkstoff für die Kugeln ein Kunststoff. Ein Kunststoff kann vorteilhaft eine der Dichte des Verbindungsmittels entsprechende Dichte aufweisen. Dabei kann zugleich gewährleistet sein, daß die Härte der Kugeln der Druckbelastung durch den obenliegenden Kalksandstein bzw. durch mehrere obenliegende Kalksandsteine angepaßt ist. Die Druckbelastung wird dabei bei entsprechend großer Anzahl gleich mäßig zwischen den Kalksandsteinen verteilter Kugeln auf viele Kugeln verteilt und somit für jede einzelne Kugel abgeschwächt. Die Aufnahme der Druckbelastung ist außerdem zeitlich befristet, denn sie dauert nur so lange, wie das Verbindungsmittel abbin det. Nach Abbinden des Verbindungsmittels trägt es die obenlie genden Kalksandsteine.According to a further development, the material for the Balls a plastic. A plastic can advantageously be one of the Density of the connecting means have corresponding density. It can also be guaranteed that the hardness of the balls the pressure load caused by the lime sandstone or is adapted by several overhead sand-lime bricks. The The pressure load becomes the same with a correspondingly large number balls distributed moderately between the sand-lime bricks on many Balls distributed and thus weakened for each individual ball. The absorption of the pressure load is also limited in time, because it only lasts as long as the lanyard sets det. After the lanyard has set, it carries the above lime sandstones.

Der Werkstoff der Kugeln kann auch ein Metall sein, zum Bei spiel Aluminium. Aufgrund der höheren Dichte des Aluminiums wer den Kugeln aus diesem Material dem Verbindungsmittel erst kurz vor dessen Aufbringen auf die Kalksandsteine zugeführt, um ihr Absetzen während der Lagerung des Verbindungsmittels aus zu schließen.The material of the balls can also be a metal, for example play aluminum. Due to the higher density of the aluminum who the balls made of this material only briefly fed to the limestone before it was applied Settling off during storage of the lanyard conclude.

Zur weiteren Ausbildung ist schließlich vorgesehen, daß die Kugeln einen Durchmesser von 2 mm bis 5 mm, vorzugsweise von 3 mm, aufweisen. Mit Kugeln mit einem Durchmesser von 3 mm wird eine gleichmäßig 3 mm dicke Verbindungsmittelschicht für aufein anderlegbare und/oder nebeneinanderlegbare Kalksandsteine ausgebildet. Um zu verhindern, daß in diesem Fall Kugeln mit einem Durchmesser größer als 3 mm dem Verbindungsmittel zugefügt werden, werden Kugeln gleicher Sieblinie verwendet. Ein Vorhan densein von Kugeln mit einem Durchmesser kleiner als 3 mm behin dert die Herstellung der gleichmäßig dicken Verbindungsmittels schicht nicht. Die Druckbelastung des aufliegenden Kalksand steins wird dann von weniger Kugeln, und zwar von den Kugeln mit den größten Durchmessern, aufgenommen.For further training it is finally provided that the Balls with a diameter of 2 mm to 5 mm, preferably of 3 mm. With balls with a diameter of 3 mm a uniform 3 mm thick layer of bonding agent for each other layable and / or layable sand-lime bricks educated. To prevent balls in this case from using a diameter greater than 3 mm added to the connecting means balls of the same sieve line are used. A curtain balls with a diameter smaller than 3 mm changes the production of the uniformly thick lanyard don't shift. The pressure load of the overlying lime sand Stein is then made up of fewer balls, namely from the balls the largest diameters.

Die Zeichnung stellt ein Ausführungsbeispiel aufeinanderlie gender Bauelemente dar, die eine nach dem erfindungsgemäßen Ver fahren hergestellte Verbindungsmittelschicht aufweisen. Es zei gen:The drawing shows an embodiment on top of each other gender components that a according to the invention Ver have produced connection layer. It shows gene:

Fig. 1 eine Seitenansicht zweier aufeinanderliegender Kalk sandsteinreihen und Fig. 1 is a side view of two rows of lime and sandstone rows

Fig. 2 eine maßstäblich vergrößerte Schnittansicht entlang der Linie II-II in Fig. 1. FIG. 2 is a sectional view on a larger scale along the line II-II in FIG. 1.

Zwischen den mit ihren stirnseitigen Stoßflächen aneinander liegenden Kalksandsteinen 1 in Fig. 1 ist eine Schicht eines Verbindungsmittels 2 ausgebildet. Die Verbindungsmittelschicht weist eine gleichmäßige Dicke auf. Die gleichmäßige Dicke wird durch eine Vielzahl kleiner Kugeln 3, die sich in der Schicht 2 befinden und jeweils die gleiche Korngröße aufweisen, herge stellt. Die Korngröße der Kugeln 3 ist hier maßstäblich vergrö ßert dargestellt. Oberhalb und/oder unterhalb beider gezeigter Steinreihen können sich weitere Steinreihen anschließen, die je weils mittels weiterer erfindungsgemäß hergestellten Verbin dungsmittelschichten miteinander verbunden sind.A layer of a connecting means 2 is formed between the sand-lime bricks 1 with their end faces abutting one another in FIG. 1. The bonding agent layer has a uniform thickness. The uniform thickness is produced by a large number of small balls 3 , which are located in the layer 2 and each have the same grain size. The grain size of the balls 3 is shown enlarged to scale here. Above and / or below the two rows of stones shown, further rows of stones can join, each of which is connected to one another by means of additional connecting layers produced according to the invention.

Die Kugeln 3 werden dem Verbindungsmittel 2 vor dessen Auf bringen auf die untengelegenen Kalksandsteine 1 zugefügt. Vor Auflegen der oberen Kalksandsteine 1 wird das Verbindungsmittel 2 mit den Kugeln 3 auf den untengelegenen Kalksandsteinen 1 aufgetragen und verteilt. Sämtliche Kugeln 3 ordnen sich dabei in Gleichverteilung nebeneinander an, wie in Fig. 1 gezeigt. In Fig. 1 ist nur die Verbindungsmittelschicht zwischen den Lager flächen der Kalksandsteine 1 dargestellt. In der gleichen Weise kann auch zwischen den stirnseitigen Stoßflächen der Kalksand steine 1 Verbindungsmittel 2 mit zugefügten Kugeln 3 angeordnet sein, um zwischen den aneinanderliegenden Kalksandsteinen 1 der selben Steinreihe gleichmäßig breite Verbindungsmittelschichten auszubilden.The balls 3 are added to the connecting means 2 before it is brought onto the sand-lime bricks 1 below. Before placing the upper sand-lime bricks 1 , the connecting means 2 with the balls 3 is applied and distributed on the sand-lime bricks 1 below. All balls 3 are arranged next to one another in equal distribution, as shown in FIG. 1. In Fig. 1 only the bonding agent layer between the bearing surfaces of the sand-lime bricks 1 is shown. In the same manner may also between the end-face abutting surfaces of the lime sand stone 1 connecting means 2 may be arranged with added balls 3 to form uniformly wide bonding agent layers between the adjacent sand-lime bricks 1 of the same row of blocks.

Fig. 2 zeigt, daß die Kugeln 3 zwischen den Kalksandsteinen auch über die Breite der Kalksandsteine 1 in der Schicht des Verbindungsmittels 2 gleichverteilt sind. Die jeweils untengele gene Lagerfläche 4 der Kalksandsteine 1 weist Einziehungen 5 auf, mit denen innerhalb eines Sichtmauerwerkes ein Fugenbild erzeugt wird. Die Einziehungen 5 sind als Rundkehlen ausgebil det. Fig. 2 shows that the balls 3 between the sand-lime bricks are evenly distributed over the width of the sand-lime bricks 1 in the layer of the connecting means 2 . The bearing surface 4 of the sand-lime bricks 1 , which is at the bottom in each case, has indentations 5 with which a joint pattern is produced within exposed masonry. The recoveries 5 are ausgebil det as round throats.

Claims

1. A method for producing a uniformly thick connec tion layer for stackable components, in particular for sand-lime bricks, characterized in that the connecting means ( 2 ) serving as spacer elements are added with a predetermined grain size.

2. The method according to claim 1, characterized in that balls ( 3 ) are used as spacer elements.

3. When performing the method according to claim 2 serving as spacer balls, characterized in that the balls ( 3 ) are made of a material whose density is approximately equal to the density of the connecting means ( 2 ).

4. When performing the method according to claim 2 serving as spacer balls according to claim 3, characterized in that the material for the balls ( 3 ) is a plastic.

5. When performing the method according to claim 2 serving as spacer balls, characterized in that the material for the balls ( 3 ) is a metal.

6. When carrying out the method according to claim 2 serving as spacer balls according to one of claims 3 to 5, characterized in that the balls ( 3 ) have a diameter of 2 mm to 5 mm, preferably 3 mm.