DE162212C - - Google Patents
Info
- Publication number
- DE162212C DE162212C DENDAT162212D DE162212DA DE162212C DE 162212 C DE162212 C DE 162212C DE NDAT162212 D DENDAT162212 D DE NDAT162212D DE 162212D A DE162212D A DE 162212DA DE 162212 C DE162212 C DE 162212C
- Authority
- DE
- Germany
- Prior art keywords
- iron
- acid
- solution
- alumina
- wood
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
KAISERLICHESIMPERIAL
PATENTAMT.PATENT OFFICE.
l/n.l / n.
Das Feuersichermachen von Holz durch Tränken des Holzes mit einer wässerigen Lösung von schwefelsaurer Tonerde ist bereits bekannt. Es ist auch schon vorgeschlagen worden, diesem Imprägnierungsmittel Säuren, wie Essigsäure, Schwefelsäure, Borsäure, zur Verstärkung der Wirkung hinzuzusetzen. Fire-proofing of wood by soaking the wood with an aqueous one Solution of sulphate of alumina is already known. It has already been suggested Acids, such as acetic acid, sulfuric acid, boric acid, have been added to this impregnating agent to enhance the effect.
Wenn die vorliegende Erfindung an StelleWhen the present invention in place
ίο der früher vorgeschlagenen Säuren einen Zusatz von Oxalsäure benutzt, so geschieht dies zu dem besonderen Zweck und mit der besonderen Wirkung, daß selbst bei Verwendung eiserner Gefäße zum Ansetzen und Aufbewahren der Lösung bezw. zur Vornahme der Imprägnierung jede Fleckenbildung und Mißfärbung der Hölzer — auch bei starkem Gerbstoffgehalt — verhindert wird, während andererseits die Wirksamkeit der Lösung mindestens ebensogroß ist als bei Zusatz anderer Säuren.ίο an additive to the acids proposed earlier If used by oxalic acid, this is done for a special purpose and with a special one Effect that even when using iron vessels to prepare and store the solution BEZW. for making the impregnation any staining and discoloration of the wood - even with strong Tannin content - is prevented, while on the other hand the effectiveness of the solution is at least as large as when other acids are added.
Die Verwendung eiserner Gefäße ist an und für sich der Verwendung säurefester oder säurefest ausgekleideter Gefäße schon der Kostenfrage wegen vorzuziehen. In diesen Gefäßen nimmt aber die sauer reagierende Lösung schwefelsaurer Tonerde durch Angriff der eisernen Wandungen Eisen auf, so daß Ferro- und Ferri-Verbindungen entstehen. Diese verursachen aber beim Imprägnieren — namentlich stark gerbstoffhaltiger Hölzer — Flecke oder eine allgemeine Mißfärbung des Holzes, dessen Wert dadurch wesentlich beeinträchtigt wird.The use of iron vessels is in and of itself more acid-proof than use or acid-proof lined vessels are preferable because of the question of cost. In But the acidic solution of sulphate of clay removes iron from these vessels by attacking the iron walls so that ferrous and ferrous compounds arise. However, these cause the impregnation - especially wood with a high tannin content - stains or a general one Discoloration of the wood, the value of which is significantly impaired as a result.
Aber auch wenn man säurefeste Behälter verwenden wollte, ist zu berücksichtigen, daß die gewöhnliche schwefelsaure Tonerde des Handels, die des Kostenpunktes wegen zu benutzen ist, meist mit Eisen verunreinigt ist.But even if you wanted to use acid-proof containers, you should take into account that the common sulfuric alumina of the trade, which increases because of the cost point use, is mostly contaminated with iron.
Die durch die Eisenspuren verursachte Fleckenbildung und Mißfärbung wird durch den Zusatz der früher vorgeschlagenen Säuren nur verschlimmert und überdies die Holzfaser spröde und brüchig gemacht.The staining and discoloration caused by the traces of iron will be through the addition of the acids suggested earlier only aggravates the wood fiber made brittle and fragile.
Wird dagegen die Lösung schwefelsaurer Tonerde mit Oxalsäure versetzt, so wird einerseits der Einfluß der eisernen Behälter, andererseits der eigene Eisengehalt der unreinen schwefelsauren Tonerde unschädlich gemacht, d. h. jede Fleckenbildung und Mißfärbung verhindert, überdies aber auch der schädliche Einfluß, den die anderen Säuren auf die Haltbarkeit der Holzfaser ausüben, vermieden. Diese der Oxalsäure eigene Wirkung ist damit zu erklären, daß Oxalsäure zwar unreines (oxydiertes) oder feinverteiltes Eisen, nicht sonderlich aber eine reine, geschlossene Eisenoberfläche angreift und die Wirkung hat, das gerbsaure Eisen, aus welchem die Flecken bestehen, bezw. welches die Mißfärbung hervorruft, aufzulösen. Daß eine schädliche Einwirkung der mit Oxalsäure versetzten Lösung auf die eisernen Gefäße nicht zu befürchten ist, hat die Erfahrung bestätigt.If, on the other hand, oxalic acid is added to the solution of alumina sulfur, then on the one hand the influence of the iron containers, on the other hand the iron content of the impure ones sulfuric alumina rendered harmless, d. H. any staining and discoloration prevents, but also the harmful influence that the other acids have on the durability of the wood fiber, avoided. This effect peculiar to oxalic acid can be explained by the fact that oxalic acid impure (oxidized) or finely divided iron, but not particularly one attacks pure, closed iron surface and has the effect of tannic iron, from which the spots consist, respectively. which causes the discoloration to dissolve. There is no need to fear that the solution mixed with oxalic acid will have a harmful effect on the iron vessels the experience confirms.
Beispielsweise wird eine Lösung schwefelsaurer Tonerde, welche auf 4,5 1 Wasser etwa 1260 g gewöhnlicher schwefelsaurerFor example, a solution of alumina sulfuric acid, which is 4.5 l of water about 1260 g of common sulfuric acid
Tonerde enthält, durch einen Zusatz von etwa 57 g trockener Oxalsäure des Handels im Sinne der Erfindung verbessert. Es empfiehlt sich indessen für die Praxis ein stärkerer Säurezusatz — etwa 85 g auf 4,5 1 Lösung —, um den beabsichtigten Erfolg ohne jedesmalige Untersuchung der rohen schwefelsauren Tonerde sicher zu erreichen. Je nach der Beschaffenheit der Handelsware ist nämlich mehr oder weniger Salz erforderlich, um eine Lösung von gewissem spezifischen Gewicht zu ergeben, und die verschiedenen Eigenschaften des Salzes erfordern auch einen verschiedenen Oxalsäurezusatz, wenn dieser genau nach den Eigenschaften des jeweils vorliegenden Salzes bemessen werden soll. Es können aber auch größere Säuremengen als die für die Verbesserung der schwefelsauren Tonerde erforderlichen angewendet werden, ohne daß die Wirkung der Lösung nachweisbar beeinträchtigt würde.Contains clay by adding about 57 g of dry commercial oxalic acid improved within the meaning of the invention. It is recommended, however, for practice stronger acid addition - about 85 g to 4.5 1 Solution - to achieve the intended success without each time studying the raw sulfuric alumina can be reached safely. Depending on the nature of the merchandise namely, more or less salt is required to make a solution of certain specific Weight, and the different properties of the salt also require a different addition of oxalic acid, if this is measured exactly according to the properties of the salt present in each case shall be. But it can also use larger amounts of acid than those used for the improvement the sulphate of alumina required to be applied without affecting the effect the solution would be demonstrably impaired.
Claims (1)