DE1521614A1 - Process for single or multi-colored decorative enamelling of cast iron or sheet steel parts using a film - Google Patents
Process for single or multi-colored decorative enamelling of cast iron or sheet steel parts using a filmInfo
- Publication number
- DE1521614A1 DE1521614A1 DE19651521614 DE1521614A DE1521614A1 DE 1521614 A1 DE1521614 A1 DE 1521614A1 DE 19651521614 DE19651521614 DE 19651521614 DE 1521614 A DE1521614 A DE 1521614A DE 1521614 A1 DE1521614 A1 DE 1521614A1
- Authority
- DE
- Germany
- Prior art keywords
- film
- enamel
- enamelling
- sheet steel
- cast iron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
Be/B/PG 2717Be / B / PG 2717
Verfahren zur ein- oder mehrfarbigen Dekoremaillierung von Gui3- oder Stahlblechteilen unter Verwendung einer Folie. (Ausscheidung aus B 72 .ij$8Process for single or multi-colored decorative enamelling of Gui3 or sheet steel parts using a film. (Eliminated from B 72 .ij $ 8
Die Erfindung betrifft ein Verfahren zur Emaillierung von Gu3- oder Stahlblechteilen unter Verwendung einer Folie. Durch das deutsche Patent 1 O89 JJ21 ist es bekannt, ein 0ui3- oder Slahlblecnteil mit J einem Email zu versehen, indem das Emailpulver mit einem Bindemittel aus einer thermoplastischen Masse vermischt und zu einer Folie verarbeitet wird. Diese Folie wird auf das zu emaillierende Teil aufgelegt und einem Brand unterworfen, wobei das Bindemittel verdampft und ein Ernailüburzug entsteht.The invention relates to a method for enamelling Gu3 or sheet steel parts using a foil. From the German patent 1089 JJ21 it is known to use a 0ui3- or Slahlblecnteil with J to provide an enamel by adding the enamel powder with a binder is mixed from a thermoplastic mass and processed into a film. This film is placed on the part to be enamelled and subjected to a fire, wherein the binding agent evaporates and an Ernailüburzug is formed.
Die wesentlichen Eigenschaften des Emails sind von der Schichtstärke abhängig, weshalb man bestrebt ist, die zu emaillierenden Teile mit einer möglicnst dünnen und gleichmäßigen Emailauflage zu versehen. Dies ist aber mit dem bekannten Verfahren nicht möglich. IThe essential properties of the enamel are the layer thickness depending on why one strives to provide the parts to be enamelled with a layer of enamel that is as thin and even as possible. However, this is not possible with the known method. I.
Erfindungsgemäii wird deshalb vorgeschlagen, da;3 nach Aufbringen einer Grundemailsohicht das Deckemail mittels einer bedruckten Kunotharzfolie auf Polyesterbasis aufgebracht wird.According to the invention it is therefore proposed that 3 after application of a Base enamel covers the top enamel using a printed synthetic resin film is applied on a polyester basis.
Das Deckemail kann in sehr dünner und gleichmäßiger Auflage auf die Folie gedruckt und damit entsprechend auf das Grundemail übertragen werden, so daß sich eine wesentliche Verbesserung der Gebrauchstüchtigkeit des Emailüberzuges ergibt. Außerdem wird Email eingespart.The cover enamel can be applied very thinly and evenly to the Foil printed and thus transferred accordingly to the basic enamel, so that there is a significant improvement in usability of the enamel coating results. Email is also saved.
_ 2 _ 9Q9843/0815 _ 2 _ 9Q9843 / 0815
. BAD or. BAD or
15216U.15216U.
Als Deckemaxi kann ein reines Email, d.h. nur ein Glaspulver mit Färb- und Trübungsmitteln benutzt werden. Die 3onst üblichen Zusätze an Ton und Stellmitteln, welche den Emailschlicker in der Schwebe und damit spritzfähig halten, können bei dem Deckemail,A pure enamel, i.e. just a glass powder with coloring and opacifying agents, can be used as the ceiling maxi. The other usual additions of clay and setting agents, which keep the enamel slip in suspension and thus sprayable, can be used with the cover enamel,
oftoften
mit welchem die Folie bedruckt wird, entfallen. Die negativen Einflüsse, welche z.B. auf den Schmelzpunkt oder den Glanz sowiewith which the film is printed are omitted. The negative influences, which e.g. on the melting point or the gloss as well as
und Farbton-'and hue- '
die Glätte, Ooerflnchenspanhung>durch den Mühlenversatz auftreten können, sind somit nicht zu Gefurchten.the smoothness, surface chipping> occur due to the mill misalignment are therefore not to be dreaded.
Bei dem erfindungsgemäiien Verfahren müssen die Deckschicht und das ™ Grundemail genau aufeinander abgestimmt sein, wenn man größeren Ausschuß vermeiden will. Es nat sich herausgestellt, daJ die Deckschicht eine wesentlich kleinere Oberflächenspannung haben mu:3 als das Grundemail. Außerdem mui3 die Oberflächenspannung des Grundernaiis aroJer sein als die Summe aus Oberflächenspannung der Deckschicht und der Grenzflächenspannung zwischen Deckschicht und Grundemail.In the method according to the invention, the top layer and the ™ Basic enamel must be precisely matched if you have larger Wants to avoid committee. It turned out that the Top layer have a significantly lower surface tension mu: 3 as the basic email. In addition, the surface tension of the The basic surface tension of the area is greater than the sum of the surface tension Top layer and the interfacial tension between top layer and base enamel.
Die Deckkraft des Deckemails ist direkt abhängig von ihrer Schichtstärke. Die kleinste stabile Schichtstärke der Schmelzfarbe hängt davon ab, wie groii der Randwinkel gegenüber dem Grundemail ist. Man mu3 also Deckemails wählen, die einen möglichst kleinen Randwinkel gegenüber dem Grundemail aufweisen, wenn man mit einer möglichst geringen Emailschicht eine einwandfreie Emaillierung erzielen will. Im Idealfalle sollte der Randwinkel 0° betragen. Diese gewünschten Voraussetzungen werden unter den oben angegebenen Bedingungen über die Ooerflächenspannung bzw. Grenzflächenspannung von Grundemail und Deckschicht erreicht.The opacity of the cover enamel is directly dependent on its layer thickness. The smallest stable layer thickness of the enamel color depends on how large the edge angle is compared to the base enamel. Man So you have to choose cover enamels that have the smallest possible edge angle compared to the base enamel, if possible with a want to achieve a flawless enamelling with a small enamel layer. In the ideal case, the edge angle should be 0 °. These desired Under the conditions given above, the prerequisites are the surface tension or interfacial tension of the base enamel and top layer achieved.
909843/0815909843/0815
BAD ORIGINAL BAD ORIGI NAL
" " " 15216H"" "15216H
Die Folie kann zur Erzielung einer dekorativen Wirkung mit einem Deekemail oder Deckemails verschiedener Färbung bedruckt sein. Auch ist es möglich, zusätzliche Schmelzfarben aufzudrucken.The film can be used to achieve a decorative effect with a Deekemail or cover mails of different colors can be printed. It is also possible to print additional enamel colors.
Die additive Berechnung der Oberflächenspannung vun Email ist heute ohne weiteres möglich, da die Faktoren für die einzelnen Bestandteile seit langem bekannt sind.The additive calculation of the surface tension of the enamel is today easily possible, since the factors for the individual components have long been known.
Das erfindungsgemäJe Verfahren lädt sich sowohl für Gu3- als auch Blechteile mit Erfolg anwenden und ist fur öfen, Herde, Kühlschranke, Kochtöpfe und d^l. sowie für Badewannen geeignet.The inventive method loads both for Gu3 and Use sheet metal parts with success and is suitable for ovens, stoves, refrigerators, Saucepans and d ^ l. as well as suitable for bathtubs.
909843/081 5909843/081 5
BAD ORIGINALBATH ORIGINAL
Claims (4)
Deckcmail Mittels einer bedruckten Kunstharr.folie auf Polyesterbasis aufgebracht wird.. ) A method for single or multi-colored decoration of Gu.i- or 3tanlblechteile using a film, characterized in that after applying a base enamel layer
Deckcmail is applied by means of a printed synthetic resin film on a polyester basis.
auf zudrückende Dcckemaii eine Ernailfritte ohne die üclichen
KUhlcnzuGätzc verwendet wird.2.) The method according to claim 1, characterized in that daw T ^ r that
On the dcckemaii to be squeezed, an Ernail frit without the usual ones
KUhlcnzuGätzc is used.
eine Folie -nit eine-n Decketnail oder Deckemails verschiedener
Färbung verwendet wird."i.) Method according to claim 1 or 2, characterized in that it ohnct, da .;
one slide -nit one-n cover thumbnail or cover emails of various types
Coloring is used.
909843/081 5 BATH ORIGINAL
909843/081 5