DE102016111275B4 - Reinigungstextilie - Google Patents

Reinigungstextilie Download PDF

Info

Publication number
DE102016111275B4
DE102016111275B4 DE102016111275.5A DE102016111275A DE102016111275B4 DE 102016111275 B4 DE102016111275 B4 DE 102016111275B4 DE 102016111275 A DE102016111275 A DE 102016111275A DE 102016111275 B4 DE102016111275 B4 DE 102016111275B4
Authority
DE
Germany
Prior art keywords
cleaning
cleaning textile
layer
textile
nonwoven
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
DE102016111275.5A
Other languages
German (de)
Other versions
DE102016111275A1 (en
Inventor
Oliver Penner
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MASCOT GMBH, DE
Original Assignee
Mascot GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mascot GmbH filed Critical Mascot GmbH
Publication of DE102016111275A1 publication Critical patent/DE102016111275A1/en
Application granted granted Critical
Publication of DE102016111275B4 publication Critical patent/DE102016111275B4/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

Um eine Reinigungstextilie bereitzustellen, die eine sehr gute Reinigungsleistung aufweist und von einem Anwender als angenehm weich empfunden wird, schlägt die vorliegende Erfindung vor, eine vorzugsweise tuchförmige Reinigungstextilie mit einer aus einem ersten synthetischen Material bestehenden ersten Faservliesschicht, die eine Sichtseite der Reinigungstextilie bildet, einer aus einem zweiten, sich hinsichtlich seiner Fasern von dem ersten synthetischen Material unterscheidenden synthetischen Material bestehenden zweiten Faservliesschicht, die eine Rückseite der Reinigungstextilie bildet, und einer die erste mit der zweiten Faservliesschicht verbindenden Polyurethanschaumstoffschicht auszubilden, wobei die erste und die zweite Faservliesschicht Dicken aufweisen, die jeweils von 0,7 mm bis 1,5 mm liegen und die Polyurethanschaumstoffschicht eine Dicke zwischen 1 mm bis 4 mm aufweist, die Reinigungstextilie vernadelt und thermisch verfestigt ist, die Faservliesschichten jeweils eine Flächenmasse von 60 g/m2 bis 250 g/m2 aufweisen und die Reinigungstextilie eine Flächenmasse von 190 g/m2 bis 480 g/m2 aufweist.In order to provide a cleaning fabric which has a very good cleaning performance and is perceived by a user to be pleasantly soft, the present invention proposes a preferably cloth-shaped cleaning textile with a first non-woven fabric layer consisting of a first synthetic material, which forms a visible side of the cleaning textile a second nonwoven fibrous nonwoven layer forming a back side of the cleansing textile and having the first nonwoven fibrous nonwoven layer joined to the first nonwoven fibrous layer, the first and second nonwoven fibrous layers having thicknesses of are each from 0.7 mm to 1.5 mm and the polyurethane foam layer has a thickness between 1 mm to 4 mm, the cleaning fabric is needled and thermally bonded, the nonwoven fabric layers each ei have a basis weight of 60 g / m2 to 250 g / m2 and the cleaning textile has a basis weight of 190 g / m2 to 480 g / m2.

Description

Die vorliegende Erfindung betrifft eine vorzugsweise tuchförmige Reinigungstextilie mit wenigstens einer Faservliesschicht.The present invention relates to a preferably cloth-shaped cleaning textile with at least one fiber fleece layer.

Reinigungstextilien dieser Art sind in großer Vielfalt aus dem Stand der Technik bekannt, wobei man stets versucht, die Reinigungswirkung solcher Reinigungstextilien zu verbessern. Dies kann beispielsweise durch Beschichtung und/oder Strukturierung der Oberfläche des Reinigungstuches erreicht werden.Cleaning textiles of this type are known in great variety from the prior art, always trying to improve the cleaning effect of such cleaning textiles. This can be achieved, for example, by coating and / or structuring the surface of the cleaning cloth.

So ist beispielsweise aus der Druckschrift EP 0 053 201 A1 ein Reinigungstuch bekannt, das aus einem weichelastischen Nadelvlies besteht, auf dessen Vorderseite sich reliefartig von der Oberfläche abhebende Gummileisten aufgedruckt sind, während auf der Rückseite des Nadelvlieses eine kontinuierliche Schicht aus einem offenporigen Latexschaum vorgesehen ist. Die mit den Gummileisten versehene Oberfläche des Reinigungstuches dient dazu, gröberen Schmutz zu entfernen. Durch die kontinuierliche Latexschicht auf der Rückseite soll ein Umkippen der Gummileisten während der Benutzung des Reinigungstuches vermieden werden.For example, from the publication EP 0 053 201 A1 a cleaning cloth is known, which consists of a soft-elastic needle felt, on the front of which relief strips are printed on the surface of contrasting rubber strips, while on the back of the needle felt is provided a continuous layer of an open-cell latex foam. The provided with the rubber strips surface of the cleaning cloth serves to remove coarse dirt. The continuous latex layer on the backside prevents the rubber strips from tipping over while using the cleaning cloth.

In der Druckschrift DE 81 09 783 U1 ist ein Reinigungstuch beschrieben, das beidseitig mit Latex beschichtet ist, wobei eine Latexschicht Aktivruß enthält, um eine Putzschicht mit besserer Scheuerbeständigkeit zur Verfügung stellen zu können.In the publication DE 81 09 783 U1 a cleaning cloth is described, which is coated on both sides with latex, wherein a latex layer contains active carbon black in order to provide a plaster layer with better abrasion resistance can.

Die Druckschrift DE 200 17 627 U1 beinhaltet ein Flächenmaterial für Reinigungszwecke, welches einen mehrschichtigen Aufbau besitzt. Hierbei ist auf einer Basisschicht aus Polyurethanweichschaumstoff ein- oder beidseitig eine Deckschicht aus Faserstoffen aufgebracht. Die Faserstoffe können aus Polyester Multifilamenten/Fasern, Synthesefasern, Naturfasern, Viskose-Fasern/Fäden und/oder Micro-PES-Fasern/Fäden bestehen und durch Benadelung oder Kaschieren auf die Basisschicht aufgebracht sein. Die aufgebrachte Deckschicht kann mit einer Beschichtung aus beispielsweise Latices, Natur- und Synthesedispersionen, Naturlatex, Perbunan-Latex, Polyurethan, Styrol-Butonal, Acrylate, Styrofane oder ähnlichem versehen sein. In einem Beispiel besteht die Deckschicht aus Multifilamentfasern, vorzugsweise aus Viskose, wobei der Anteil der saugenden Fasern mindestens 50% betragen soll. Die Basisschicht kann zum Beispiel eine Dicke von vorzugsweise 5 mm und ein Flächengewicht von ca. 30 g/m2 aufweisen.The publication DE 200 17 627 U1 includes a sheet for cleaning purposes, which has a multilayer structure. Here, on one base layer of flexible polyurethane foam one or both sides a cover layer of fibers applied. The fibrous materials may consist of polyester multifilaments / fibers, synthetic fibers, natural fibers, viscose fibers / threads and / or micro-PES fibers / threads and be applied to the base layer by needling or lamination. The applied cover layer may be provided with a coating of, for example, latices, natural and synthetic dispersions, natural latex, perborane latex, polyurethane, styrene-butonal, acrylates, styrofanes or the like. In one example, the cover layer consists of multifilament fibers, preferably of viscose, wherein the proportion of absorbent fibers should be at least 50%. For example, the base layer may have a thickness of preferably 5 mm and a basis weight of about 30 g / m 2 .

Die Druckschrift DE 699 13 591 T2 offenbart ein Reinigungstuch, welches aus drei Schichten ausgebildet sein kann. Hierbei umfasst das Reinigungstuch zwei erste Schichten mit mehreren Durchtrittslöchern und eine zweite Schicht, die zwischen den zwei ersten Schichten gehalten wird. Die ersten Schichten sind vorzugsweise Vliesgewebe, in welchen die Löcher durch einen Wasserstrahl oder Nadelstich geformt wurden. Dabei sind die zwei ersten Schichten beispielsweise aus einem Vlies mit einer Dicke von 0,3 bis 2,0 mm und einem Basisgewicht von 10 bis 100 g/m2 ausgebildet, wobei das Vlies beispielsweise aus Fasern aus Polyethylen, Polypropylen, Polyester, Nylon, Rayon, Baumwolle ausgebildet sein kann. Hingegen kann die zweite Schicht aus beliebigen Materialien, wie beispielsweise Vlies, einem Kunststofffilm, einem aus Kunstfasern, Schwamm oder Polyurethan, ausgebildet sein. Hierbei weist die zweite Schicht ein Basisgewicht nicht unter 30 g/m2 auf.The publication DE 699 13 591 T2 discloses a cleaning cloth which may be formed of three layers. Here, the cleaning cloth comprises two first layers with a plurality of through holes and a second layer which is held between the two first layers. The first layers are preferably nonwoven fabrics in which the holes have been formed by a jet of water or a pin-prick. The two first layers are formed for example of a nonwoven having a thickness of 0.3 to 2.0 mm and a basis weight of 10 to 100 g / m 2 , wherein the nonwoven, for example, made of fibers of polyethylene, polypropylene, polyester, nylon, Rayon, cotton can be made. On the other hand, the second layer can be formed of any desired materials, such as fleece, a plastic film, one of synthetic fibers, sponge or polyurethane. Here, the second layer has a basis weight not less than 30 g / m 2 .

Die Druckschrift US 3 862 522 A offenbart einen Scheuerschwamm, welcher eine Schaumstoffschicht aufweist, welche auf einer Seite eine Vliesstoffschicht aufweist, die ebenso wie die zweite Seite der Schaumstoffschicht mit einer Harzschicht bedeckt ist.The publication US Pat. No. 3,862,522 A discloses a scouring pad having a foam layer having on one side a nonwoven fabric layer which, like the second side of the foam layer, is covered with a resinous layer.

Die Druckschrift DE 197 10 032 B4 beinhaltet ein textiles Reinigungsmaterial, das aus einem Vlies besteht, auf dem beidseitig zueinander versetzte, erhabene Strukturierungen mit gleichem Aufbau vorgesehen sind, wobei die Strukturierungen aus gebündelten Einzelfasern eines Vlieses oder Garn- oder Zwirnschlingen bestehen und die Reinigungsleistung erhöhen sollen.The publication DE 197 10 032 B4 includes a textile cleaning material, which consists of a nonwoven, on both sides staggered, raised structuring are provided with the same structure, the structuring of bundled individual fibers of a nonwoven or yarn or twisted yarns and should increase the cleaning performance.

Ein anderer Ansatz, die Reinigungswirkung von Reinigungstüchern zu erhöhen, besteht darin, ein entsprechend reinigungsstarkes Material zur Ausbildung der Faservliesschicht zu verwenden. So wird zum Beispiel in der Druckschrift DE 10 2005 038 170 A1 eine Reinigungstextilie auf Basis eines textilen Flächengebildes vorgeschlagen, das zumindest teilweise aus Melaminfasern und/oder Melaminfäden ausgebildet ist, wodurch einerseits eine Beseitigung intensiver Verschmutzung bei andererseits schonender Behandlung der zu reinigenden Flächen möglich ist. Das Flächengebilde kann beispielsweise als Gewebe, Gewirke, Gestrick oder Vliesstoff ausgebildet sein. Die Reinigungstextilie kann jedoch auch aus einem Verbund mit anderen textilen oder nichttextilen Flächengebilden bestehen. So kann die Reinigungstextilie beispielsweise mit einem schwammartigen Flächengebilde verbunden sein, wobei die Verbindung mechanisch oder thermisch nach allgemein bekannten Verfahren erfolgt.Another approach to increase the cleaning effect of cleaning wipes is to use a correspondingly high-cleaning material to form the fiber fleece layer. For example, in the publication DE 10 2005 038 170 A1 proposed a cleaning textile based on a textile fabric, which is at least partially made of melamine fibers and / or melamine fibers, which on the one hand, an elimination of intense pollution on the other hand gentle treatment of the surfaces to be cleaned is possible. The fabric may be formed, for example, as a woven, knitted or knitted fabric or nonwoven fabric. However, the cleaning textile may also consist of a composite with other textile or non-textile fabrics. For example, the cleaning textile can be connected to a sponge-like sheet material, wherein the connection takes place mechanically or thermally according to generally known methods.

Bei wieder anderen Reinigungstextilien wird besonderer Wert auf deren Saug- und Aufnahmefähigkeit gelegt. Hierzu schlägt die Druckschrift DE 10 2007 028 039 A1 einen Reinigungsartikel aus einem weichen entweder bindergebundenen oder Bikomponenten- oder mindestens dreilagigen Sandwich-Vliesstoff mit einer stabilen dreidimensionalen Struktur vor. Der Vliesstoff besitzt ein Flächengewicht von 50 bis 300 g/m2 und eine Dicke von 2 bis 6 mm. Insofern der Vliesstoff als Sandwich-Vliesstoff ausgebildet ist, weist dieser mindestens drei Lagen auf, wobei die innere Lage gleich oder zu mehr als 50 Gew.-% aus Kunststofffasern und die äußeren Lagen zu mehr als 50 Gew.-% aus Baumwoll- und/oder Viskosefasern aufgebaut sind. Der Sandwich-Vliesstoff ist mit einer Latex-Suspension imprägniert.With still other cleaning textiles special emphasis is placed on their suction and absorption capacity. For this purpose, the document proposes DE 10 2007 028 039 A1 a cleansing article of a soft either binder-bound or bicomponent or at least three-ply Sandwich nonwoven fabric with a stable three-dimensional structure in front. The nonwoven fabric has a basis weight of 50 to 300 g / m 2 and a thickness of 2 to 6 mm. Insofar as the nonwoven fabric is formed as a sandwich nonwoven fabric, this has at least three layers, wherein the inner layer is equal to or more than 50 wt .-% of plastic fibers and the outer layers to more than 50 wt .-% of cotton and / or viscose fibers are constructed. The sandwich nonwoven fabric is impregnated with a latex suspension.

All diese Reinigungstücher weisen zwar eine hohe Reinigungswirkung auf, werden aber aufgrund des verwendeten Grundmaterials sowie der Beschichtungen oder Strukturen bei deren Gebrauch häufig als unangenehm rau oder hart empfunden. Dies gilt insbesondere nach mehreren Anwendungen solcher Reinigungstücher, nach denen die Härte der Materialien häufig noch zunimmt.Although these cleaning wipes have a high cleaning effect, but are often perceived as unpleasant rough or hard due to the used base material and the coatings or structures in their use. This is especially true after several applications of such wipes, after which the hardness of the materials often increases.

Es ist daher die Aufgabe der vorliegenden Erfindung eine Reinigungstextilie zur Verfügung zu stellen, die nicht nur eine sehr gute Reinigungsleistung zur Verfügung stellt, sondern darüber hinaus von einem Anwender als angenehm weich empfunden wird.It is therefore an object of the present invention to provide a cleaning fabric available, which not only provides a very good cleaning performance, but is also perceived by a user to be pleasantly soft.

Diese Aufgabe wird durch eine vorzugsweise tuchförmige Reinigungstextilie der eingangs genannten Gattung gelöst, wobei die Reinigungstextilie aus einer aus einem ersten synthetischen Material bestehenden ersten Faservliesschicht, die eine Sichtseite der Reinigungstextilie bildet, einer aus einem zweiten, sich hinsichtlich seiner Fasern von dem ersten synthetischen Material unterscheidenden synthetischen Material bestehenden zweiten Faservliesschicht, die eine Rückseite der Reinigungstextilie bildet, und einer die erste mit der zweiten Faservliesschicht verbindenden Polyurethanschaumstoffschicht ausgebildet ist, wobei die erste und die zweite Faservliesschicht Dicken aufweisen, die jeweils in einem Bereich von 0,7 mm bis 1,5 mm liegen und die Polyurethanschaumstoffschicht eine Dicke in einem Bereich zwischen 1 mm bis 4 mm aufweist, die Reinigungstextilie vernadelt und thermisch verfestigt ist, die Faservliesschichten jeweils eine Flächenmasse in einem Bereich von 60 g/m2 bis 250 g/m2 aufweisen und die Reinigungstextilie eine Flächenmasse in einem Bereich von 190 g/m2 bis 480 g/m2 aufweist.This object is achieved by a preferably cloth-shaped cleaning textile of the aforementioned type, wherein the cleaning textile of a first non-woven fabric layer consisting of a first synthetic material which forms a visible side of the cleaning textile, one of a second, differing with respect to its fibers from the first synthetic material synthetic second material nonwoven layer forming a back side of the cleaning fabric, and a polyurethane foam layer connecting the first nonwoven fabric layer, the first and second nonwoven fabric layers having thicknesses ranging from 0.7 mm to 1.5, respectively mm and the polyurethane foam layer has a thickness in a range of 1 mm to 4 mm, the cleaning fabric is needled and thermally bonded, the nonwoven fabric layers each have a basis weight in a range of 60 g / m 2 to 250 g / m 2 and the cleaning textile has a basis weight in a range of 190 g / m 2 to 480 g / m 2 .

Die erfindungsgemäße Reinigungstextilie zeichnet sich durch beste Reinigungseigenschaften, wie eine insbesondere durch die verwendete Polyurethanschicht bewirkte sehr gute Saugfähigkeit, eine hohe Stabilität durch die verwendete Vernadelung und zusätzliche thermische Verfestigung sowie eine hohe Abriebfestigkeit durch die außen befindlichen Faservliesschichten, aus. Überraschenderweise besitzt die erfindungsgemäße Reinigungstextilie darüber hinaus eine besonders angenehme weiche Haptik, die sich aus der Summe der konstruktiven und Materialeigenschaften der Reinigungstextilie ergibt.The cleaning textile according to the invention is characterized by excellent cleaning properties, such as a very good absorbency, in particular by the polyurethane layer used, high stability by the needling used and additional thermal bonding and a high abrasion resistance by the fiber fleece layers located on the outside. Surprisingly, the cleaning textile according to the invention also has a particularly pleasant soft feel, which results from the sum of the structural and material properties of the cleaning textile.

Vorzugsweise ist auf wenigstens einer der Faservliesschichten eine Acrylbeschichtung vorgesehen. Durch die Acrylbeschichtung ergibt sich eine hohe Haltbarkeit und Fusselfreiheit wenigstens einer Oberfläche der Reinigungstextilie.Preferably, an acrylic coating is provided on at least one of the nonwoven fabric layers. The acrylic coating results in a high durability and lint freedom at least one surface of the cleaning textile.

Eine zusätzliche Verbesserung der Reinigungseigenschaften als auch der Weichheit der Reinigungstextilie lässt sich dann erreichen, wenn in einer Ausführungsform der vorliegenden Erfindung auf der Sichtseite und der Rückseite der Reinigungstextilie zwischen Nadeleinstichbereichen Aufwölbungen ausgebildet sind, wobei die Aufwölbungen auf der Sichtseite der Reinigungstextilie eine geringere Flächenausdehnung als diejenigen auf der Rückseite der Reinigungstextilie aufweisen.An additional improvement of the cleaning properties as well as the softness of the cleaning textile can be achieved if, in one embodiment of the present invention, bulges are formed on the visible side and the back side of the cleaning textile between needle drop areas, the bulges on the visible side of the cleaning textile having a smaller surface area than those on the back of the cleaning textile.

Vor allem die Sichtseite der Reinigungstextilie wird als besonders weich empfunden, wenn in einer speziellen Ausbildung der vorliegenden Erfindung die Aufwölbungen auf der Sichtseite eine um wenigstens 50% geringere Flächenausdehnung als diejenigen auf einer Rückseite der Reinigungstextilie aufweisen.Above all, the visible side of the cleaning textile is perceived as particularly soft if, in a special embodiment of the present invention, the bulges on the visible side have at least 50% smaller surface area than those on a back side of the cleaning textile.

Ein ganz besonders angenehmer Griff wird bei der erfindungsgemäßen Reinigungstextilie erzielt, wenn die Vernadelungsdichte der Vernadelung der Reinigungstextilie auf deren Sichtseite größer als auf deren Rückseite ist.A particularly pleasant handle is achieved in the cleaning textile according to the invention, when the needling density of the needling needle of the cleaning textile on the visible side is greater than on the back.

In bevorzugten Ausführungsformen der vorliegenden Erfindung ist die erste Faservliesschicht aus einer Fasermischung ausgebildet, die insgesamt zu wenigstens 95% aus Viskose und Polypropylen oder insgesamt zu wenigstens 95% aus Viskose, Polypropylen und Polyester besteht, und ist die zweite Faservliesschicht aus einer Fasermischung ausgebildet, die insgesamt zu wenigstens 95% aus Viskose und Polyester besteht. Anstelle von Viskose können hier auch Bambusfasern verwendet werden.In preferred embodiments of the present invention, the first nonwoven fibrous layer is formed from a fiber blend comprising at least 95% viscose and polypropylene or at least 95% total viscose, polypropylene and polyester, and the second nonwoven fibrous layer is formed from a fiber blend total of at least 95% of viscose and polyester. Instead of viscose bamboo fibers can be used here.

Vorzugsweise ist die erfindungsgemäße Reinigungstextilie derart ausgebildet, dass das Wasseraufnahmevermögen der Reinigungstextilie nach DIN 53923 zwischen 400% und 800% liegt.The cleaning textile according to the invention is preferably designed such that the water absorption capacity of the cleaning textile according to DIN 53923 is between 400% and 800%.

In einer bevorzugten Gestaltung der erfindungsgemäßen Reinigungstextilie liegt die Lederweiterreißfestigkeit der Reinigungstextilie nach DIN EN ISO 3377-1 in Längs- und in Querrichtung zwischen 60 N und 70 N (Newton).In a preferred embodiment of the cleaning textile according to the invention, the leather tear resistance of the cleaning textile according to DIN EN ISO 3377-1 in the longitudinal and in the transverse direction is between 60 N and 70 N (Newton).

Eine bevorzugte Ausführungsform der erfindungsgemäßen Reinigungstextilie, deren Aufbau, Funktion und Vorteile werden im Folgenden anhand der 1 und 2 näher erläutert.A preferred embodiment of the cleaning textile according to the invention, its structure, Function and advantages are described below on the basis of 1 and 2 explained in more detail.

Die 1 und 2 zeigen mögliche Ausführungsformen von erfindungsgemäßen Reinigungstextilien 1, 1', jeweils in einer perspektivischen Draufsicht. Die in den 1 und 2 schematisch gezeigten Reinigungstextilien 1, 1' soll nur den Grundaufbau von möglichen Ausführungsformen der erfindungsgemäßen Reinigungstextilie verdeutlichen, wobei zahlreiche Modifikationen möglich sind. In den 1 und 2 sind daher die Reinigungstextilien 1, 1' insbesondere in ihren Dickenabmessungen deutlich vergrößert und nicht maßstabsgetreu dargestellt.The 1 and 2 show possible embodiments of cleaning textiles according to the invention 1 . 1' , each in a perspective plan view. The in the 1 and 2 schematically shown cleaning textiles 1 . 1' is intended to illustrate only the basic structure of possible embodiments of the cleaning fabric according to the invention, with numerous modifications are possible. In the 1 and 2 are therefore the cleaning textiles 1 . 1' especially in their thickness dimensions significantly enlarged and not drawn to scale.

Die Reinigungstextilien 1 sind in den gezeigten Ausführungsbeispielen Reinigungstücher, könnten aber auch andere flächige Reinigungstextilien sein und beispielsweise eine andere Form aufweisen.The cleaning textiles 1 are in the embodiments shown cleaning wipes, but could also be other flat cleaning textiles and, for example, have a different shape.

Die Reinigungstextilien 1, 1' weisen jeweils eine aus einem ersten synthetischen Material bestehende erste Faservliesschicht 2 auf, die eine Sichtseite 5 der Reinigungstextilie 1, 1' bildet. Die erste Faservliesschicht 2 besteht in den gezeigten Ausführungsbeispielen aus einer Fasermischung aus Viskose und Polypropylen, könnte aber in anderen Ausführungsformen der vorliegenden Erfindung auch aus einer aus Viskose, Polypropylen und Polyester bestehen. Die erste Faservliesschicht 2 weist eine Flächenmasse in einem Bereich 60 g/m2 bis 250 g/m2, besonders bevorzugt zwischen 70 g/m2 und 190 g/m2 auf und besitzt eine Dicke d1 in einem Bereich von 0,7 mm bis 1,5 mm.The cleaning textiles 1 . 1' each have a first non-woven fabric layer consisting of a first synthetic material 2 on, the one visible side 5 the cleaning textile 1 . 1' forms. The first nonwoven layer 2 In the embodiments shown, it consists of a fiber blend of viscose and polypropylene, but in other embodiments of the present invention could also consist of one of viscose, polypropylene and polyester. The first nonwoven layer 2 has a basis weight in a range of 60 g / m 2 to 250 g / m 2 , more preferably between 70 g / m 2 and 190 g / m 2 and has a thickness d 1 in a range of 0.7 mm to 1, 5 mm.

Ferner weisen die Reinigungstextilien 1, 1' jeweils eine mit der ersten Faservliesschicht 2 verbundene Polyurethanschaumstoffschicht 3 auf. Die Polyurethanschaumstoffschicht 3 besitzt eine Dicke d3, die in einem Bereich von 1 mm bis 4, vorzugsweise zwischen 1,0 mm und 2,5 mm, besonders bevorzugt zwischen 1,5 mm und 2,0 mm liegt.Furthermore, the cleaning textiles 1 . 1' one each with the first nonwoven fabric layer 2 bonded polyurethane foam layer 3 on. The polyurethane foam layer 3 has a thickness d 3 , which is in a range of 1 mm to 4, preferably between 1.0 mm and 2.5 mm, more preferably between 1.5 mm and 2.0 mm.

Die Polyurethanschaumstoffschicht 3 ist jeweils auf der der ersten Faservliesschicht 2 gegenüber befindlichen Seite mit einer zweiten Faservliesschicht 4 verbunden, die aus einem zweiten, sich vom Material der ersten Faservliesschicht 2 unterscheidenden synthetischen Material ausgebildet ist. In den gezeigten Ausführungsbeispielen besteht die zweite Faservliesschicht 4 aus einer Fasermischung aus Viskose und Polyester. Die zweite Faservliesschicht 2 weist eine Flächenmasse in einem Bereich 60 g/m2 bis 250 g/m2, besonders bevorzugt zwischen 70 g/m2 und 190 g/m2 auf und besitzt eine Dicke d2 in einem Bereich von 0,7 mm bis 1,5 mm. Die zweite Faservliesschicht 4 bildet eine Rückseite 6 der Reinigungstextilie 1, 1'.The polyurethane foam layer 3 is respectively on the first nonwoven fabric layer 2 opposite side with a second layer of nonwoven fabric 4 connected, consisting of a second, the material of the first nonwoven fabric layer 2 distinguishing synthetic material is formed. In the illustrated embodiments, the second nonwoven fabric layer 4 from a fiber blend of viscose and polyester. The second nonwoven layer 2 has a basis weight in a range of 60 g / m 2 to 250 g / m 2 , more preferably between 70 g / m 2 and 190 g / m 2 and has a thickness d 2 in a range of 0.7 mm to 1, 5 mm. The second nonwoven layer 4 makes a back 6 the cleaning textile 1 . 1' ,

Auf wenigstens einer der Faservliesschichten 2, 4, in dem Beispiel von 1 auf der Sichtseite 5 der Reinigungstextilie, ist eine Acrylschicht 10 vorgesehen. Die Acrylschicht 10 kann jedoch, wie es anhand der Reinigungstextilie 1' in 2 schematisch gezeigt ist, auch weggelassen werden. Zudem ist in dem Ausführungsbeispiel von 1 auf der ersten Faservliesschicht 2 eine Bedruckung 11 aufgedruckt. Die Reinigungstextilie 1' aus 2 weist keine Bedruckung 11 auf.On at least one of the nonwoven layers 2 . 4 , in the example of 1 on the visible side 5 the cleaning textile, is an acrylic layer 10 intended. The acrylic layer 10 However, as it is based on the cleaning textiles 1' in 2 is shown schematically, also be omitted. In addition, in the embodiment of 1 on the first nonwoven layer 2 a print 11 printed. The cleaning textile 1' out 2 has no printing 11 on.

Die Reinigungstextilien 1, 1' sind jeweils beidseitig vernadelt. Auf der Sichtseite 5 und der Rückseite 6 der Reinigungstextilien 1, 1' sind zwischen Nadeleinstichbereichen 7 Aufwölbungen 8, 9 ausgebildet, wobei die Aufwölbungen 8 auf der Sichtseite 5 der Reinigungstextilie 1, 1' eine geringere Flächenausdehnung als die Aufwölbungen 9 auf der Rückseite 6 der Reinigungstextilie 1, 1' aufweisen. In den in den 1 und 2 gezeigten Ausführungsbeispielen weisen die Aufwölbungen 8 auf der Sichtseite 5 eine um wenigstens 50% geringere Flächenausdehnung als die Aufwölbungen 9 auf einer Rückseite 6 der Reinigungstextilie 1, 1' auf.The cleaning textiles 1 . 1' are each needled on both sides. On the visible side 5 and the back 6 of cleaning textiles 1 . 1' are between needle drop zones 7 bulges 8th . 9 formed, with the bulges 8th on the visible side 5 the cleaning textile 1 . 1' a smaller area than the bulges 9 on the back side 6 the cleaning textile 1 . 1' exhibit. In the in the 1 and 2 embodiments shown have the bulges 8th on the visible side 5 an at least 50% smaller surface area than the bulges 9 on a back 6 the cleaning textile 1 . 1' on.

Die in den 1 und 2 schematisch dargestellten Reinigungstextilien 1, 1' weisen jeweils eine Flächenmasse bzw. ein Flächengewicht in einem Bereich von 190 g/m2 bis 450 g/m2, vorzugsweise einem Bereich von 250 g/m2 bis 400 g/m2, beispielsweise von 339 g/m2, auf. Dabei wurde die Flächenmasse bzw. das Flächengewicht der Faservlieslagen 2, 4 und der Reinigungstextilien 1, 1' nach DIN EN 12127 ermittelt, wobei je 5 kreisförmig ausgestanzte Proben mit einem Flächeninhalt von 100 cm2 gewogen und der Mittelwert der Einzelwiegeergebnisse ermittelt wurde.The in the 1 and 2 schematically illustrated cleaning textiles 1 . 1' each have a basis weight or a basis weight in a range of 190 g / m 2 to 450 g / m 2 , preferably in a range of 250 g / m 2 to 400 g / m 2 , for example, of 339 g / m 2 , on. The basis weight or basis weight of the fiber fleece layers was thereby 2 . 4 and the cleaning textiles 1 . 1' according to DIN EN 12127, each weighing 5 circular punched samples with a surface area of 100 cm 2 and determining the mean value of the individual weighing results.

Das Wasseraufnahmevermögen der Reinigungstextilien 1, 1', das nach DIN 53923 ermittelt wurde, liegt zwischen 400% und 800%, vorzugsweise zwischen 500% und 700%, beispielsweise bei 661%.The water absorption capacity of the cleaning textiles 1 . 1' , which was determined according to DIN 53923, is between 400% and 800%, preferably between 500% and 700%, for example at 661%.

Die Lederweiterreißfestigkeit der Reinigungstextilien 1, 1', die nach DIN EN ISO 3377-1 ermittelt wurde, liegt in Längs- und in Querrichtung zwischen 60 N und 70 N, beispielsweise in Längsrichtung bei 68,3 N und in Querrichtung bei 63 N.The leather tear resistance of the cleaning textiles 1 . 1' , which was determined in accordance with DIN EN ISO 3377-1, lies in the longitudinal and in the transverse direction between 60 N and 70 N, for example in the longitudinal direction at 68.3 N and in the transverse direction at 63 N.

Die Reinigungstextilien 1, 1' zeichnen sich durch eine hohe, gemäß DIN EN ISO 12947-1/2 ermittelte Scheuerbeständigkeit aus, wobei die Polyurethanschaumschicht 3 im Test erst nach 8000 Scheuertouren zu erkennen ist.The cleaning textiles 1 . 1' are characterized by a high, according to DIN EN ISO 12947-1 / 2 determined abrasion resistance, wherein the polyurethane foam layer 3 in the test only after 8000 rubbing tours can be recognized.

Darüber hinaus besitzen die erfindungsgemäßen Reinigungstextilien 1, 1' eine hohe, gemäß DIN EN ISO 105-006 ermittelte Waschechtheit, die zwischen 4 (gut) und 5 (sehr gut) liegt.In addition, the cleaning textiles according to the invention have 1 . 1' a high, according to DIN EN ISO 105-006 determined wash fastness, which is between 4 (good) and 5 (very good).

Claims (8)

Reinigungstextilie (1, 1') mit wenigstens einer Faservliesschicht, wobei die Reinigungstextilie (1, 1') aus einer aus einem ersten synthetischen Material bestehenden ersten Faservliesschicht (2), die eine Sichtseite (5) der Reinigungstextilie (1, 1') bildet, einer aus einem zweiten, sich hinsichtlich seiner Fasern von dem ersten synthetischen Material unterscheidenden synthetischen Material bestehenden zweiten Faservliesschicht (4), die eine Rückseite (6) der Reinigungstextilie (1, 1') bildet, und einer die erste Faservliesschicht (2) mit der zweiten Faservliesschicht (4) verbindenden Polyurethanschaumstoffschicht (3) ausgebildet ist, wobei die erste Faservliesschicht (2) und die zweite Faservliesschicht (4) Dicken (d1, d2) aufweisen, die jeweils in einem Bereich von 0,7 mm bis 1,5 mm liegen und die Polyurethanschaumstoffschicht (3) eine Dicke (d3) in einem Bereich von 1 mm bis 4 mm aufweist, die Reinigungstextilie (1, 1') vernadelt und thermisch verfestigt ist, die Faservliesschichten (2, 4) jeweils eine Flächenmasse in einem Bereich von 60 g/m2 bis 250 g/m2 aufweisen und die Reinigungstextilie (1, 1') eine Flächenmasse in einem Bereich von 190 g/m2 bis 480 g/m2 aufweist.Cleaning textile ( 1 . 1' ) with at least one fibrous nonwoven layer, wherein the cleaning textile ( 1 . 1' ) of a first non-woven fabric layer consisting of a first synthetic material ( 2 ), which has a visible side ( 5 ) of the cleaning textile ( 1 . 1' ), one of a second, consisting of a second, with respect to its fibers of the first synthetic material different synthetic material second nonwoven layer ( 4 ), which has a back ( 6 ) of the cleaning textile ( 1 . 1' ) and one the first nonwoven layer ( 2 ) with the second nonwoven layer ( 4 ) connecting polyurethane foam layer ( 3 ), wherein the first nonwoven layer ( 2 ) and the second fibrous nonwoven layer ( 4 ) Have thicknesses (d 1 , d 2 ), each in a range of 0.7 mm to 1.5 mm and the polyurethane foam layer ( 3 ) has a thickness (d 3 ) in a range of 1 mm to 4 mm, the cleaning textile ( 1 . 1' ) is needled and thermally bonded, the nonwoven layers ( 2 . 4 ) each have a basis weight in a range of 60 g / m 2 to 250 g / m 2 and the cleaning textile ( 1 . 1' ) has a basis weight in a range of 190 g / m 2 to 480 g / m 2 . Reinigungstextilie nach Anspruch 1, dadurch gekennzeichnet, dass auf wenigstens einer der Faservliesschichten (2, 4) eine Acrylbeschichtung (10) vorgesehen ist.Cleaning textile according to claim 1, characterized in that on at least one of the fiber fleece layers ( 2 . 4 ) an acrylic coating ( 10 ) is provided. Reinigungstextilie nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass auf der Sichtseite (5) und der Rückseite (6) der Reinigungstextilie (1, 1') zwischen Nadeleinstichbereichen (7) Aufwölbungen (8, 9) ausgebildet sind, wobei die Aufwölbungen (8) auf der Sichtseite (5) der Reinigungstextilie (1, 1') eine geringere Flächenausdehnung als die Aufwölbungen (9) auf der Rückseite (6) der Reinigungstextilie (1, 1') aufweisen.Cleaning textile according to claim 1 or 2, characterized in that on the visible side ( 5 ) and the back ( 6 ) of the cleaning textile ( 1 . 1' ) between needle drop areas ( 7 ) Bulges ( 8th . 9 ) are formed, wherein the bulges ( 8th ) on the visible side ( 5 ) of the cleaning textile ( 1 . 1' ) a smaller area than the bulges ( 9 ) on the back side ( 6 ) of the cleaning textile ( 1 . 1' ) exhibit. Reinigungstextilie nach Anspruch 3, dadurch gekennzeichnet, dass die Aufwölbungen (8) auf der Sichtseite (5) eine um wenigstens 50% geringere Flächenausdehnung als die Aufwölbungen (9) auf der Rückseite (6) der Reinigungstextilie (1, 1') aufweisen.Cleaning textile according to claim 3, characterized in that the bulges ( 8th ) on the visible side ( 5 ) an at least 50% smaller surface area than the bulges ( 9 ) on the back side ( 6 ) of the cleaning textile ( 1 . 1' ) exhibit. Reinigungstextilie nach wenigstens einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass die Vernadelungsdichte der Vernadelung der Reinigungstextilie (1, 1') auf deren Sichtseite (5) größer als auf deren Rückseite (6) ist.Cleaning textile according to at least one of the preceding claims, characterized in that the needling density of the needling of the cleaning textile ( 1 . 1' ) on the visible side ( 5 ) larger than on the back side ( 6 ). Reinigungstextilie nach wenigstens einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass die erste Faservliesschicht (2) aus einer Fasermischung ausgebildet ist, die insgesamt zu wenigstens 95% aus Viskose und Polypropylen oder insgesamt zu wenigstens 95% aus Viskose, Polypropylen und Polyester besteht, und die zweite Faservliesschicht (3) aus einer Fasermischung ausgebildet ist, die insgesamt zu wenigstens 95% aus Viskose und Polyester besteht.Cleaning textile according to at least one of the preceding claims, characterized in that the first fibrous nonwoven layer ( 2 ) is formed from a fiber mixture which comprises at least 95% of viscose and polypropylene or altogether at least 95% of viscose, polypropylene and polyester, and the second nonwoven fabric layer (US Pat. 3 ) is formed from a fiber mixture which consists of at least 95% of viscose and polyester. Reinigungstextilie nach wenigstens einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass das Wasseraufnahmevermögen der Reinigungstextilie (1, 1') nach DIN 53923 zwischen 400% und 800% liegt.Cleaning textile according to at least one of the preceding claims, characterized in that the water absorption capacity of the cleaning textile ( 1 . 1' ) according to DIN 53923 between 400% and 800%. Reinigungstextilie nach wenigstens einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass die Lederweiterreißfestigkeit der Reinigungstextilie (1, 1') nach DIN EN ISO 3377-1 in Längs- und in Querrichtung zwischen 60 N und 70 N liegt.Cleaning textile according to at least one of the preceding claims, characterized in that the leather extensibility of the cleaning textile ( 1 . 1' ) according to DIN EN ISO 3377-1 in the longitudinal and transverse direction between 60 N and 70 N.
DE102016111275.5A 2015-07-08 2016-06-20 Reinigungstextilie Active DE102016111275B4 (en)