DE102005028465A1 - Material for sound insulation consists of layer of leather fiber material coated on at least one side with layer of water-insoluble polymer material - Google Patents
Material for sound insulation consists of layer of leather fiber material coated on at least one side with layer of water-insoluble polymer material Download PDFInfo
- Publication number
- DE102005028465A1 DE102005028465A1 DE200510028465 DE102005028465A DE102005028465A1 DE 102005028465 A1 DE102005028465 A1 DE 102005028465A1 DE 200510028465 DE200510028465 DE 200510028465 DE 102005028465 A DE102005028465 A DE 102005028465A DE 102005028465 A1 DE102005028465 A1 DE 102005028465A1
- Authority
- DE
- Germany
- Prior art keywords
- leather fiber
- layer
- fiber material
- leather
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
Description
ZusammenfassungSummary
Die vorliegende Erfindung betrifft ein Lederfasermaterial sowie dessen Verwendung als schall- und wärmeisolierendes Trägermaterial im Innenausbau von Bauwerken.The The present invention relates to a leather fiber material and its Use as sound and heat insulating support material in the interior of buildings.
Die Weiterentwicklung der Bauindustrie erfordert in zunehmendem Maße den Einsatz von Bauelementen für die Isolierung und Dämmung von Schall, Wärme und Kälte. Diese Erfordernis begründet sich besonders durch die Notwendigkeit Energie einzusparen, aber auch darin, die Lebensqualität der Bewohner der zu errichtenden Bauwerke zu erhöhen. Bisher sind Bauelemente zur Isolierung bekannt, die aus unterschiedlichsten organischen oder anorganischen Stoffen bestehen und auf verschiedene Weise untereinander gebunden sind. So gibt es beispielsweise zement- oder gipsgebundene isolierende Bauelemente aus Holzfasern, Kunstfasern, Mineralwolle, Kork oder Textilverbundstoffen. Weiterhin sind Schaumkunststoffe und mineralische Schaumstoffe im Einsatz. Diese Bauelemente können beispielsweise als Matten, Platten oder Schüttgüter vorliegen und werden in vielfältiger Weise bereits bei der Errichtung des Bauwerkes mit verbaut.The Further development of the construction industry requires increasing use of building elements for the insulation and insulation of sound, heat and cold. This requirement is justified especially by the need to save energy, but also in it, the quality of life to increase the inhabitant of the buildings to be built. So far, components known for isolation, the most diverse organic or inorganic substances and in different ways with each other are bound. For example, there are cement- or gypsum-bound ones insulating components made of wood fibers, synthetic fibers, mineral wool, Cork or textile composites. Furthermore, foam plastics and mineral foams in use. These components can, for example as mats, plates or bulk materials and become more diverse Way already installed in the construction of the building.
Zusätzlich zu diesen isolierenden Elementen des Rohbaus kann eine Isolierung gegen Wärmeverlust und Lärmbelästigung auch durch Maßnahmen beim Innenausbau erreicht werden. Hierbei sind die Möglichkeiten im Vergleich zu den oben diskutierten Maßnahmen jedoch deutlich eingeschränkt, da die zu isolierenden Räume bereits in ihren Grundmaßen vorhanden sind und durch die zusätzlichen Isolierungen möglichst nicht in ihrem Volumen bzw. den potentiellen Nutzungsmöglichkeiten beschränkt werden sollen.In addition to These insulating elements of the shell can be insulated against heat loss and noise pollution also by measures at Interior work can be achieved. Here are the possibilities compared to the measures discussed above but clearly limited, because the rooms to be insulated already available in their basic dimensions are and by the extra Isolations as possible not in their volume or potential uses limited should be.
Isolierendes Material für den Innenausbau sollte daher einerseits ein möglichst geringes Eigenvolumen aufweisen (um die Räume nicht unnötig zu verkleinern) und andererseits hohen Stabilitätsanforderungen genügen (um die Belastungen bei der Nutzung durch die Bewohner zu ertragen). So muss beispielsweise ein Material, das zur Isolierung von Böden verwendet wird (z. B. zur Verbesserung des Trittschallschutzes) hohe Drücke aushalten, da Nutzlasten wie beispielsweise Einrichtungsgegenstände auf dem Material lasten. Diese Ansprüche begrenzen die Verwendung kompressibler organischer Grundstoffe in derartigen Bauteilen. Weitere Ansprüche an ein Material für den Innenausbau werden beispielsweise durch die entsprechenden Brandschutznormen sowie durch die Bedingung gesundheitlicher Verträglichkeit der verwendeten Grundstoffe gestellt.insulating Material for The interior should therefore on the one hand the lowest possible intrinsic volume have (around the rooms not unnecessary on the other hand meet high stability requirements (um to endure the burdens of use by the residents). For example, a material used to insulate floors will withstand high pressures (eg to improve the impact sound insulation), because payloads such as furnishings on the Load material. These claims limit the use of compressible organic raw materials in such components. Further demands on a material for interior work for example, by the appropriate fire safety standards and by the condition of health compatibility of the raw materials used posed.
Es wurde nun gefunden, dass ein neues Material zur Schall- und Wärmeisolierung, welches den obigen Anforderungen an ein geringes Volumen und hohe mechanische Stabilität genügt, erhalten werden kann, wenn als Grundstoff für dieses Material Lederfaserwerkstoffe eingesetzt werden. Aufgrund seiner Eigenschaften kann es insbesondere für den Innenausbau von Bauwerken eingesetzt werden. Im Gegensatz zu gängigen Baumaterialien – wie z.B. Laminatfußbodenmaterialien auf MDF-Basis – bei denen die schall- oder wärmeisolierenden Elemente und Trägermaterialien mit hoher Stabilität zur Erzielung der gewünschten Eigenschaften durch Schichtung der unterschiedlichen Elemente in Verbundstoffen hergestellt werden, vereinigt das gefundene Material alle Eigenschaften direkt in sich.It has now been found that a new material for sound and heat insulation, which meets the above requirements for low volume and high mechanical stability enough, can be obtained if as a base material for this material leather fiber materials be used. In particular, because of its properties for the Interior fittings of buildings are used. In contrast to common building materials - such. Laminate flooring materials on MDF basis - at which the sound or heat insulating Elements and substrates with high stability to achieve the desired Properties by layering the different elements in Composite materials are produced, the found material unites all Properties directly in itself.
Lederreste können zerfasert werden und lassen sich dann zu Lederfaserwerkstoffen (LEFA) verarbeiten. Bei LEFA handelt es sich um in der Regel einschichtige Flächengebilde aus Lederfasern und Bindemitteln. Im folgenden Text werden die Begriffe „Lederfaserwerkstoff" und „Lederfasermaterial" synonym verwendet. Schon seit Ende der dreißiger Jahre werden LEFA-Platten in der Schuhindustrie eingesetzt, beispielsweise zur Herstellung von Hinterkappen, Vorderkappen, Brand- und Zwischensohlen, Laufsohlen, Rahmen und Absätzen. Weiterhin wurden diese Lederfaserstoffe bisher als Ersatzmaterial für das (teurere) Leder beispielsweise in der Auto- und Möbelindustrie eingesetzt. Die vorliegende Erfindung stellt eine Weiterentwicklung dieser Materialien dar und eröffnet diesen ein bisher unbekanntes Anwendungsgebiet.leather scraps can be frayed and can then be converted to leather fiber materials (LEFA) to process. LEFA is usually single-layered sheet made of leather fibers and binders. In the following text, the terms "leather fiber material" and "leather fiber material" are used interchangeably. Already since the end of the thirties Years LEFA panels are used in the shoe industry, for example for the production of rear caps, front caps, fire and midsoles, outsoles, Frames and paragraphs. Furthermore, these leather fibers were previously used as substitute material for the (more expensive) Leather used for example in the car and furniture industry. The present Invention represents a further development of these materials and open this a previously unknown field of application.
Aufgabe der vorliegenden Erfindung ist es daher, einen modifizierten Lederfaserwerkstoff zur Verfügung zu stellen, der aufgrund seiner Eigenschaften, insbesondere seiner Isolierwirkung für Schall und Wärme und seiner mechanischen Stabilität, zur Herstellung von isolierenden Bauteilen, bevorzugt Platten zur Verkleidung von Wänden, Decken und Böden von Innenräumen, geeignet ist.task Therefore, it is the object of the present invention to provide a modified leather fiber material to disposal to ask, because of its characteristics, in particular its Insulating effect for sound and heat and its mechanical stability, for the production of insulating components, preferably plates for Cladding of walls, Ceilings and floors of interiors, suitable is.
Beschreibung der Erfindungdescription the invention
Die vorliegende Erfindung betrifft ein Material zur Schall- und Wärmeisolierung von Bauwerken, welches dadurch gekennzeichnet ist, dass eine Schicht aus Lederfasermaterial auf einer Seite oder auf beiden Seiten mit einer Schicht aus wasserunlöslichem Polymermaterial beschichtet ist. Die Schicht aus Lederfasermaterial weist bevorzugt eine Dicke von 5 bis 15 Millimetern auf. Besonders bevorzugt ist eine Schichtdicke von 7 bis 15 Millimetern, meistbevorzugt eine Schichtdicke von 9 bis 15 Millimetern.The The present invention relates to a material for sound and heat insulation of buildings, which is characterized in that a layer made of leather fiber material on one side or on both sides with a layer of water-insoluble Polymer material is coated. The layer of leather fiber material preferably has a thickness of 5 to 15 millimeters. Especially preferred is a layer thickness of 7 to 15 millimeters, most preferably a layer thickness of 9 to 15 millimeters.
Bevorzugt besteht dabei die zentrale Schicht aus Lederfasermaterial, welches ein spezifisches Gewicht von ≥ 1,00 g/cm3 aufweist. In einer anderen bevorzugten Ausführungsform besitzt das Lederfasermaterial ein spezifisches Gewicht von ≥ 1,05 g/cm3. Im Vergleich hierzu beträgt das spezifische Gewicht von handelsüblichem Lederfasermaterial – je nach der zur Herstellung verwendeten Lederqualität, Füllstoffen und Bindemitteln – deutlich unter 1,00 g/cm3. Allerdings sind auch Lederfasermaterialien mit spezifischem Gewicht von ca. 1,00 g/cm3, z.B. für Laufsohlenanwendungen, erhältlich. Die angegebenen Werte für das spezifische Gewicht lassen sich nach Stand der Technik im Rahmen der Produktionsprozesse von Lederfaserstoffen erzeugen, die beispielsweise in den internationalen Patentanmeldungen WO 98/50617, WO 00/67937 oder WO 2005/017004 beschrieben werden.Preferably, there is the central layer of leather fiber material having a specific gravity of ≥ 1.00 g / cm 3 . In another preferred embodiment, the leather fiber material has a specific gravity of ≥ 1.05 g / cm 3 . In comparison, the specific gravity of commercially available leather fiber material - depending on the leather quality, fillers and binders used for the production - is well below 1.00 g / cm 3 . However, leather fiber materials with a specific weight of about 1.00 g / cm 3 , eg for outsole applications, are also available. The specified specific gravity values can be produced according to the state of the art in the context of the production processes of leather pulp materials which are described, for example, in international patent applications WO 98/50617, WO 00/67937 or WO 2005/017004.
Die zentrale Schicht kann aus einer einzelnen Schicht des Lederfasermaterials bestehen. Es können jedoch auch zwei oder mehrere Schichten des Lederfasermaterials miteinander verbunden werden, um eine höhere Schichtdicke und damit gesteigerte Isolationswirkung zu erzielen. Die Verbindung der Schichten geschieht bevorzugt durch Verkleben. Geeignete Klebstoffe zur Verbindung der einzelnen Schichten sind z.B. Neopren-Klebstoffe oder PVAC-Klebstoffe.The Central layer may consist of a single layer of the leather fiber material consist. It can but also two or more layers of the leather fiber material be joined together to a higher layer thickness and thus to achieve increased insulation effect. The connection of the layers is preferably done by gluing. Suitable adhesives for the connection of the individual layers are e.g. Neoprene adhesives or PVAC adhesives.
Das wasserunlösliche Polymermaterial ist vorzugsweise Melaminharz oder Acrylharz. Es ist jedoch generell jedes wasserunlösliche Polymer verwendbar, welches zur Beschichtung von Möbel- und Bodenelementen eingesetzt werden.The water Polymer material is preferably melamine resin or acrylic resin. It However, any water-insoluble polymer is generally usable, which is used for coating furniture and floor elements are used.
Die Schichtdicke der Beschichtungen aus wasserunlöslichem Polymer beträgt bevorzugt weniger als 1 Millimeter, mehr bevorzugt weniger als 0,7 Millimeter, besonders bevorzugt weniger als 0,5 Millimeter.The Layer thickness of the coatings of water-insoluble polymer is preferred less than 1 millimeter, more preferably less than 0.7 millimeters, more preferably less than 0.5 millimeters.
Generell gibt es keine Beschränkung für das Lederfasermaterial, das als Ausgangsmaterial für die Erfindung eingesetzt werden kann, d.h., jedes im Stand der Technik bekannte Lederfasermaterial ist grundsätzlich geeignet.. Es ist jedoch vorteilhaft, thermoplastische Lederfasermaterialien zu verwenden, wie sie beispielsweise in den internationalen Patentanmeldungen WO 98/50617, WO 00/67937 oder WO 2005/017004 beschrieben werden. Werden diese als Ausgangsmaterialien verwendet, behält das hieraus gewonnene Isolationsmaterial der vorliegenden Erfindung die thermoplastischen Eigenschaften des Ausgangsmaterials. Es ist damit möglich, durch im Stand der Technik bekannte thermoplastische Verarbeitungsverfahren Formteile aus dem Isolationsmaterial herzustellen und damit etwa beim Innenausbau auftretende Probleme durch nicht normierte Raumgestaltungen zu überwinden.As a general rule there is no restriction for the leather fiber material, as starting material for the invention can be used, that is, any in the art known leather fiber material is basically suitable .. It is, however advantageous to use thermoplastic leather fiber materials, as described, for example, in the international patent applications WO 98/50617, WO 00/67937 or WO 2005/017004 are described. If these are used as starting materials, this retains obtained insulation material of the present invention, the thermoplastic Properties of the starting material. It is thus possible through in the Known prior art thermoplastic processing methods To produce moldings from the insulation material and thus about Problems encountered during interior fitting due to non-standardized room designs to overcome.
Es ist weiterhin bevorzugt, dass das Lederfasermaterial aus Rohstoffen hergestellt wird, die den Ansprüchen an die Umwelt- und Gesundheitsverträglichkeit entsprechen. So sollte beispielsweise das Lederfasermaterial nicht aus chromgegerbtem Leder gewonnen worden sein, da Chromverbindungen für den Menschen gesundheitlich bedenklich sind. Weiterhin sollte beispielsweise bei der Herstellung des Ausgangsmaterials ein emissionsarmes Fettungsmittel verwendet werden, um das Raumklima der mit dem erfindungsgemäßen Material isolierten Räume nicht zu belasten. Dasselbe gilt entsprechend für alle weiteren Hilfsstoffe, die bei der Produktion von Lederfasermaterialien zum Einsatz kommen, und die nicht restlos aus dem Material entfernt werden können. Bevorzugt wird, dass das Lederfasermaterial den erhöhten Anforderungen des deutschen SG Zertifikats entspricht.It is further preferred that the leather fiber material from raw materials is manufactured, which the claims to comply with environmental and health compatibility. So should For example, the leather fiber material is not obtained from chrome-tanned leather have been since chromium compounds for humans health are questionable. Furthermore, for example, in the production of the starting material uses a low-emission fatliquoring agent be to the indoor climate with the material of the invention not isolated rooms to charge. The same applies mutatis mutandis to all other auxiliaries, used in the production of leather fiber materials, and that can not be completely removed from the material. Prefers is that the leather fiber material meets the increased requirements of the German SG certificate corresponds.
Es ist weiterhin bevorzugt, dass das Isolationsmaterial mit einer flammenhemmenden Ausrüstung versehen ist. Dies kann beispielsweise dadurch geschehen, dass die Oberflächen des als Ausgangsmaterial dienenden Lederfasermaterials einer geeigneten Behandlung unterworfen werden, beispielsweise mit dem handelsüblichen Produkt Flacavon® B 45 der Firma Schill & Seilacher. Alternativ kann bereits bei der Herstellung des Lederfaserstoffs, der als Ausgangsmaterial dient, ein geeigneter flammenhemmender Zusatzstoff mitverarbeitet werden. Werden die Ausgangsmaterialien nach den Verfahren hergestellt, die in den internationalen Patentanmeldungen WO 98/50617, WO 00/67937 oder WO 2005/017004 beschrieben werden (Koagulation), kann beispielsweise der wässrigen Suspension der Lederfasern das Produkt Flacavon® H14-67 der Firma Schill & Seilacher beigefügt werden.It is further preferred that the insulation material is provided with a flame-retardant finish. This can for example take place in that the surfaces of serving as a starting material leather fiber material are subjected to a suitable treatment, for example with the commercial product Flacavon ® B 45 of the company Schill & Seilacher. Alternatively, a suitable flame retardant additive can be co-processed in the production of the leather pulp which serves as starting material. If the starting materials prepared by the methods that are described in the international patent applications WO 98/50617, WO 00/67937 or WO 2005/017004 (coagulation), for example, the aqueous suspension of the leather fibers, the product H14-67 Flacavon ® of the company Schill & Seilacher.
Die Erfindung betrifft weiterhin plattenförmige Bauteile zur Isolierung von Wänden, Decken und Böden, die das genannte Material enthalten bzw. daraus gefertigt werden. So kann beispielsweise eine der Polymerbeschichtungen als Dekorschicht ausgebildet sein, die etwa ein Holzmuster imitiert. Im dieser Ausführungsform eignet sich das erfindungsgemäße Material beispielsweise als schall- und wärmedämmender Ersatz für handelsübliches Fußbodenlaminat oder handelsübliche Wandverkleidungen mit Holzoptik geeignet ist. Alternativ ist es auch möglich, auf ein erfindungsgemäßes Material weitere Schichten nach im Stand der Technik bekannten Verfahren aufzubringen, beispielsweise kunstharzgetränkte Papierschichten. Dadurch wird prinzipiell eine beliebige Oberflächengestaltung des Materials ermöglicht.The The invention further relates to plate-shaped components for insulation of walls, Ceilings and floors, which contain the said material or are produced therefrom. For example, one of the polymer coatings can be used as a decorative layer be formed, which imitates about a wood pattern. In this embodiment the material of the invention is suitable for example, as a sound and heat insulating Replacement for commercial Floor laminate or commercial Wall coverings with wood look is suitable. Alternatively it is also possible, to a material according to the invention further layers by methods known in the art apply, for example, resin-impregnated paper layers. Thereby is basically any surface design of the material allows.
Die Erfindung betrifft weiterhin ein Verfahren zur Herstellung eines Isolationsmaterials wie oben beschrieben, dadurch gekennzeichnet, dass es eine geringe Stärketoleranz (Toleranz in der Dicke des Gesamtmaterials) aufweist. Derartige Anforderungen an die maximale Stärketoleranz bestehen in Abhängigkeit von der vorgesehenen Verwendung. So sind z.B. Stärketoleranzen von +/– 0,01 mm für den Einsatz als Fußbodenelemente üblich. Im Vergleich hierzu beträgt die Stärketoleranz von handelüblichen Lederfaserstoffen von mehreren Millimetern Schichtdicke +/– 0,05 mm oder mehr. Die bevorzugte Stärketoleranz des erfindungsgemäßen Materials beträgt weniger als +/– 0,05 mm. Besonders bevorzugt sind Materialien mit einer Stärketoleranz von weniger als +/– 0,03 mm, noch mehr bevorzugt solche mit einer Stärketoleranz von +/– 0,01 mm.The invention further relates to a method for producing an insulating material as described above, characterized in that it has a low strength tolerance (tolerance in the thickness of the total material). Such requirements to the maximum starch tolerance exist depending on the intended use. For example, thickness tolerances of +/- 0.01 mm are common for use as floor elements. In comparison, the starch tolerance of commercial leather pulp of several millimeters layer thickness +/- 0.05 mm or more. The preferred starch tolerance of the material according to the invention is less than +/- 0.05 mm. Particularly preferred are materials having a starch tolerance of less than +/- 0.03 mm, even more preferably those having a starch tolerance of +/- 0.01 mm.
Um die vorgegebenen Stärketoleranzen zu erzielen und ggf. die exakte Stärke des Materials einzustellen, bestehen prinzipiell mehrere Vorgehensweisen:Around the specified strength tolerances to achieve and adjust the exact thickness of the material if necessary, exist in principle several procedures:
- 1) Ein geeignetes Lederfasermaterial wird durch flächenhaften Druck – zweckmäßig in einer im Stand der Technik bekannten Flachpresse – auf geforderte Stärke mit vorgegebener Stärketoleranz verdichtet und anschließend eine oder beiden Seiten dieses Lederfasermaterials mit einem wasserunlöslichen Polymer beschichtet.1) A suitable leather fiber material is made by planar Pressure - convenient in one in the art known flat press - on demanded strength predetermined starch tolerance compacted and then One or both sides of this leather fiber material with a water-insoluble Polymer coated.
- 2) Ein geeignetes Lederfasermaterial wird auf einer oder beiden Seiten mit einem wasserunlöslichen Polymer beschichtet und anschließend durch flächenhaften Druck – zweckmäßig in einer im Stand der Technik bekannten Flachpresse – auf geforderte Stärke mit vorgegebener Stärketoleranz gebracht.2) A suitable leather fiber material will be on one or both Pages with a water-insoluble Polymer coated and then by areal Pressure - appropriate in a State of the art known flat press - on demanded strength with predetermined starch tolerance brought.
- 3) Ein geeignetes Lederfasermaterial wird auf einer oder beiden Seiten mit einem wasserunlöslichen Polymer beschichtet und während des Laminierprozesses durch flächenhaften Druck – zweckmäßig in einer im Stand der Technik bekannten Flachpresse – auf geforderte Stärke mit vorgegebener Stärketoleranz gebracht.3) A suitable leather fiber material will be on one or both Pages with a water-insoluble Polymer coated and while the lamination process by areal Pressure - convenient in one in the art known flat press - on required strength with predetermined thickness tolerance brought.
Gegebenenfalls umfasst das Verfahren zusätzlich noch den Schritt des Verklebens von zwei oder mehreren Schichten des Lederfasermaterials vor, während oder nach dem Verdichtungsschritt.Possibly includes the method additionally nor the step of gluing two or more layers together of the leather fiber material before or after the compaction step.
Beispielexample
Ein Lederfaserstoff mit einer Dicke von 3,5 +/– 0,1 Millimetern und spezifischem Gewicht von 1,02 g/cm3 wird nach Stand der Technik, beispielsweise nach den in der internationalen Patentanmeldung WO 98/50617 angegebenen Vorschriften, produziert. Anschließend werden zwei Schichten von diesem Material passgenau aufeinander gelegt und unter Verwendung eines Neopren-Klebstoffes verklebt und in einer Flachpresse gleichzeitig auf eine Stärke 6,80 +/– 0,01 mm gebracht.. Nach Aushärtung des Klebstoffes wird das erhaltene Material nach im Stand der Technik bekannten Verfahren auf beiden Seiten mit einer Schicht aus Melaminharz versehen. Das fertige Material fällt in Platten an und kann einfach geschnitten und verarbeitet werden und ist sowohl zur Verwendung als Fußbodenlaminat als auch für Wand- und Deckenpaneele oder Seitenwände mit guter Schall- und Wärmedämmung geeignet.A leather pulp with a thickness of 3.5 +/- 0.1 millimeters and a specific weight of 1.02 g / cm 3 is produced according to the state of the art, for example according to the instructions given in international patent application WO 98/50617. Subsequently, two layers of this material are precisely placed on each other and glued using a neoprene adhesive and simultaneously brought to a thickness of 6.80 +/- 0.01 mm in a flat press. After curing of the adhesive, the material obtained is in the state The technique known on both sides provided with a layer of melamine resin. The finished material accumulates in panels and can be easily cut and processed, and is suitable for use as a floor laminate as well as wall and ceiling panels or sidewalls with good sound and heat insulation.
Claims (11)