DE10164229B4 - Reibscheiben, Verfahren zu ihrer Herstellung und ihre Verwendung - Google Patents

Reibscheiben, Verfahren zu ihrer Herstellung und ihre Verwendung Download PDF

Info

Publication number
DE10164229B4
DE10164229B4 DE10164229A DE10164229A DE10164229B4 DE 10164229 B4 DE10164229 B4 DE 10164229B4 DE 10164229 A DE10164229 A DE 10164229A DE 10164229 A DE10164229 A DE 10164229A DE 10164229 B4 DE10164229 B4 DE 10164229B4
Authority
DE
Germany
Prior art keywords
friction
fiber fabric
layer
matrix
fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
DE10164229A
Other languages
German (de)
English (en)
Other versions
DE10164229A1 (de
Inventor
Moritz Bauer
Andreas Dr. Kienzle
Ingrid Krätschmer
Mario Krupka
Klaus Dipl.-Ing. Herberg
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SGL Carbon SE
Original Assignee
SGL Carbon SE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SGL Carbon SE filed Critical SGL Carbon SE
Priority to DE10164229A priority Critical patent/DE10164229B4/de
Priority to AT02028771T priority patent/ATE354042T1/de
Priority to DE50209470T priority patent/DE50209470D1/de
Priority to EP02028771A priority patent/EP1323944B1/de
Priority to US10/328,414 priority patent/US6818288B2/en
Priority to JP2003000324A priority patent/JP4535362B2/ja
Publication of DE10164229A1 publication Critical patent/DE10164229A1/de
Application granted granted Critical
Publication of DE10164229B4 publication Critical patent/DE10164229B4/de
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/515—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics
    • C04B35/56—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on carbides or oxycarbides
    • C04B35/565—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on carbides or oxycarbides based on silicon carbide
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B18/00—Layered products essentially comprising ceramics, e.g. refractory products
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/515—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics
    • C04B35/56—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on carbides or oxycarbides
    • C04B35/565—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on carbides or oxycarbides based on silicon carbide
    • C04B35/573—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on carbides or oxycarbides based on silicon carbide obtained by reaction sintering or recrystallisation
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C04B35/63—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B using additives specially adapted for forming the products, e.g.. binder binders
    • C04B35/632—Organic additives
    • C04B35/634—Polymers
    • C04B35/63496—Bituminous materials, e.g. tar, pitch
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/71—Ceramic products containing macroscopic reinforcing agents
    • C04B35/78—Ceramic products containing macroscopic reinforcing agents containing non-metallic materials
    • C04B35/80—Fibres, filaments, whiskers, platelets, or the like
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/71—Ceramic products containing macroscopic reinforcing agents
    • C04B35/78—Ceramic products containing macroscopic reinforcing agents containing non-metallic materials
    • C04B35/80—Fibres, filaments, whiskers, platelets, or the like
    • C04B35/83—Carbon fibres in a carbon matrix
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B37/00—Joining burned ceramic articles with other burned ceramic articles or other articles by heating
    • C04B37/008—Joining burned ceramic articles with other burned ceramic articles or other articles by heating by means of an interlayer consisting of an organic adhesive, e.g. phenol resin or pitch
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16D—COUPLINGS FOR TRANSMITTING ROTATION; CLUTCHES; BRAKES
    • F16D69/00—Friction linings; Attachment thereof; Selection of coacting friction substances or surfaces
    • F16D69/02—Composition of linings ; Methods of manufacturing
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16D—COUPLINGS FOR TRANSMITTING ROTATION; CLUTCHES; BRAKES
    • F16D69/00—Friction linings; Attachment thereof; Selection of coacting friction substances or surfaces
    • F16D69/02—Composition of linings ; Methods of manufacturing
    • F16D69/023—Composite materials containing carbon and carbon fibres or fibres made of carbonizable material
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/40—Metallic constituents or additives not added as binding phase
    • C04B2235/402—Aluminium
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/40—Metallic constituents or additives not added as binding phase
    • C04B2235/404—Refractory metals
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/40—Metallic constituents or additives not added as binding phase
    • C04B2235/405—Iron group metals
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/40—Metallic constituents or additives not added as binding phase
    • C04B2235/407—Copper
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/42—Non metallic elements added as constituents or additives, e.g. sulfur, phosphor, selenium or tellurium
    • C04B2235/421—Boron
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/42—Non metallic elements added as constituents or additives, e.g. sulfur, phosphor, selenium or tellurium
    • C04B2235/428—Silicon
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/52—Constituents or additives characterised by their shapes
    • C04B2235/5208—Fibers
    • C04B2235/526—Fibers characterised by the length of the fibers
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/52—Constituents or additives characterised by their shapes
    • C04B2235/5208—Fibers
    • C04B2235/5264—Fibers characterised by the diameter of the fibers
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/52—Constituents or additives characterised by their shapes
    • C04B2235/5208—Fibers
    • C04B2235/5268—Orientation of the fibers
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/52—Constituents or additives characterised by their shapes
    • C04B2235/5208—Fibers
    • C04B2235/5272—Fibers of the same material with different length or diameter
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/72—Products characterised by the absence or the low content of specific components, e.g. alkali metal free alumina ceramics
    • C04B2235/728—Silicon content
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/74—Physical characteristics
    • C04B2235/75—Products with a concentration gradient
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/80—Phases present in the sintered or melt-cast ceramic products other than the main phase
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/36—Non-oxidic
    • C04B2237/365—Silicon carbide
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/38—Fiber or whisker reinforced
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/38—Fiber or whisker reinforced
    • C04B2237/385—Carbon or carbon composite
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/58—Forming a gradient in composition or in properties across the laminate or the joined articles
    • C04B2237/582—Forming a gradient in composition or in properties across the laminate or the joined articles by joining layers or articles of the same composition but having different additives
    • C04B2237/584—Forming a gradient in composition or in properties across the laminate or the joined articles by joining layers or articles of the same composition but having different additives the different additives being fibers or whiskers
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16D—COUPLINGS FOR TRANSMITTING ROTATION; CLUTCHES; BRAKES
    • F16D69/00—Friction linings; Attachment thereof; Selection of coacting friction substances or surfaces
    • F16D2069/009—Linings attached to both sides of a central support element, e.g. a carrier plate
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
    • Y10T428/24802—Discontinuous or differential coating, impregnation or bond [e.g., artwork, printing, retouched photograph, etc.]
    • Y10T428/24926—Discontinuous or differential coating, impregnation or bond [e.g., artwork, printing, retouched photograph, etc.] including ceramic, glass, porcelain or quartz layer
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/249921—Web or sheet containing structurally defined element or component
    • Y10T428/249924—Noninterengaged fiber-containing paper-free web or sheet which is not of specified porosity
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/249921—Web or sheet containing structurally defined element or component
    • Y10T428/249924—Noninterengaged fiber-containing paper-free web or sheet which is not of specified porosity
    • Y10T428/249927—Fiber embedded in a metal matrix
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/249921—Web or sheet containing structurally defined element or component
    • Y10T428/249924—Noninterengaged fiber-containing paper-free web or sheet which is not of specified porosity
    • Y10T428/249928—Fiber embedded in a ceramic, glass, or carbon matrix
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/249921—Web or sheet containing structurally defined element or component
    • Y10T428/249953—Composite having voids in a component [e.g., porous, cellular, etc.]
    • Y10T428/249955—Void-containing component partially impregnated with adjacent component
    • Y10T428/249956—Void-containing component is inorganic
    • Y10T428/249957—Inorganic impregnant
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
    • Y10T428/2913—Rod, strand, filament or fiber
    • Y10T428/2918—Rod, strand, filament or fiber including free carbon or carbide or therewith [not as steel]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
    • Y10T428/2913—Rod, strand, filament or fiber
    • Y10T428/2927—Rod, strand, filament or fiber including structurally defined particulate matter
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
    • Y10T428/2913—Rod, strand, filament or fiber
    • Y10T428/2933—Coated or with bond, impregnation or core
    • Y10T428/2962—Silane, silicone or siloxane in coating

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Ceramic Engineering (AREA)
  • Materials Engineering (AREA)
  • Structural Engineering (AREA)
  • Manufacturing & Machinery (AREA)
  • Organic Chemistry (AREA)
  • General Engineering & Computer Science (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Composite Materials (AREA)
  • Mechanical Engineering (AREA)
  • Inorganic Chemistry (AREA)
  • Braking Arrangements (AREA)
  • Mechanical Operated Clutches (AREA)
DE10164229A 2001-12-31 2001-12-31 Reibscheiben, Verfahren zu ihrer Herstellung und ihre Verwendung Expired - Fee Related DE10164229B4 (de)

Priority Applications (6)

Application Number Priority Date Filing Date Title
DE10164229A DE10164229B4 (de) 2001-12-31 2001-12-31 Reibscheiben, Verfahren zu ihrer Herstellung und ihre Verwendung
AT02028771T ATE354042T1 (de) 2001-12-31 2002-12-23 Reibscheiben aus faserverstärkten keramischen verbundswerkstoffen
DE50209470T DE50209470D1 (de) 2001-12-31 2002-12-23 Reibscheiben aus faserverstärkten keramischen Verbundswerkstoffen
EP02028771A EP1323944B1 (de) 2001-12-31 2002-12-23 Reibscheiben aus faserverstärkten keramischen Verbundswerkstoffen
US10/328,414 US6818288B2 (en) 2001-12-31 2002-12-23 Fiber-reinforced ceramic composites
JP2003000324A JP4535362B2 (ja) 2001-12-31 2003-01-06 繊維強化セラミック複合材料

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
DE10164229A DE10164229B4 (de) 2001-12-31 2001-12-31 Reibscheiben, Verfahren zu ihrer Herstellung und ihre Verwendung

Publications (2)

Publication Number Publication Date
DE10164229A1 DE10164229A1 (de) 2003-07-24
DE10164229B4 true DE10164229B4 (de) 2006-03-09

Family

ID=7711030

Family Applications (2)

Application Number Title Priority Date Filing Date
DE10164229A Expired - Fee Related DE10164229B4 (de) 2001-12-31 2001-12-31 Reibscheiben, Verfahren zu ihrer Herstellung und ihre Verwendung
DE50209470T Expired - Lifetime DE50209470D1 (de) 2001-12-31 2002-12-23 Reibscheiben aus faserverstärkten keramischen Verbundswerkstoffen

Family Applications After (1)

Application Number Title Priority Date Filing Date
DE50209470T Expired - Lifetime DE50209470D1 (de) 2001-12-31 2002-12-23 Reibscheiben aus faserverstärkten keramischen Verbundswerkstoffen

Country Status (5)

Country Link
US (1) US6818288B2 (enExample)
EP (1) EP1323944B1 (enExample)
JP (1) JP4535362B2 (enExample)
AT (1) ATE354042T1 (enExample)
DE (2) DE10164229B4 (enExample)

Families Citing this family (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE60010845T3 (de) * 2000-02-09 2011-05-05 Freni Brembo S.P.A., Curno Geformtes Verbundmaterial für Bremsen und Verfahren zu seiner Herstellung
DE10161218B4 (de) * 2001-12-13 2004-06-03 Sgl Carbon Ag Verfahren zum Oxidationsschutz faserverstärkter kohlenstoffhaltiger Verbundwerkstoffe und Verwendung eines nach dem Verfahren hergestellten Verbundwerkstoffes
DE10212486A1 (de) * 2002-03-21 2003-10-16 Sgl Carbon Ag Verbundwerkstoff mit Verstärkungsfasern aus Kohlenstoff
DE10253233A1 (de) 2002-11-15 2004-06-03 Dr.Ing.H.C. F. Porsche Ag Kupplung, vorzugsweise Mehrscheibenkupplung
DE10338199B4 (de) * 2003-08-20 2006-06-08 Audi Ag Kupplungsbeläge aus faserverstärkten keramischen Werkstoffen
DE10338200B4 (de) * 2003-08-20 2006-06-29 Audi Ag Kupplungsbeläge aus faserverstärkten keramischen Werkstoffen
DE10338201C5 (de) * 2003-08-20 2008-11-13 Audi Ag Reibpaarung für Kupplungssysteme
DE10341734A1 (de) * 2003-09-08 2005-04-07 Sgl Carbon Ag Zylinderringförmige Körper aus mit Kurzfasern verstärktem keramischen Verbundmaterial
DE10346499A1 (de) * 2003-10-02 2005-04-28 Sgl Carbon Ag Reibpaarung für Feststellbremsen in Kraftfahrzeugen
DE502004010621D1 (de) * 2004-09-23 2010-02-25 Audi Ag Verfahren zur Herstellung von Carbon-Keramik-Bremsscheiben
DE102006009388B4 (de) * 2006-03-01 2009-02-26 Audi Ag Vorrichtung zur Silicierung von kohlenstoffhaltigen Werkstoffen und darin durchführbares Verfahren
GB0701847D0 (en) * 2007-01-31 2007-03-14 Surface Transforms Plc Improvements in or relating to brake and clutch discs
DE102007010675B4 (de) * 2007-03-02 2009-04-23 Astrium Gmbh Verfahren zur Herstellung eines Bauteils aus einer faserverstärkten Keramik, danach hergestelltes Bauteil und dessen Verwendung als Triebwerkskomponente
CA2630516A1 (en) * 2008-05-05 2009-11-05 C-Bond Technology Inc. Ceramic molded component of sandwich construction with ceramic core, deck layer reinforcement, and ceramic matrix
EP2147776A1 (de) * 2008-07-23 2010-01-27 SGL Carbon SE Verfahren zur Herstellung eines Fasergelege-verstärkten Verbundwerkstoffs, sowie Fasergelege-verstärkte Verbundwerkstoffe und deren Verwendung
US8058191B2 (en) * 2008-09-04 2011-11-15 Siemens Energy, Inc. Multilayered ceramic matrix composite structure having increased structural strength
DE102011084626A1 (de) 2010-10-18 2012-04-19 Sgl Carbon Se Vorformling und Formteil auf Basis von Carbonfaserroving und/oder Siliciumcarbidfaserroving insbesondere zur Verwendung als Kupplungsreibscheibe
US10450235B2 (en) * 2012-04-27 2019-10-22 General Electric Company Method of producing an internal cavity in a ceramic matrix composite and mandrel therefor
US10011043B2 (en) 2012-04-27 2018-07-03 General Electric Company Method of producing an internal cavity in a ceramic matrix composite
EP3004559B1 (en) 2013-05-29 2020-01-15 General Electric Company Method of forming a ceramic matrix composite component with cooling features
JP6824601B2 (ja) * 2015-06-29 2021-02-03 クアーズテック株式会社 強化用繊維材料及びその製造方法、並びに繊維強化セラミックス複合材料
DE102016013523A1 (de) * 2016-11-14 2018-05-17 Sgl Carbon Se Neuartiger Verbundwerkstoff
CN108488284A (zh) * 2018-05-12 2018-09-04 来安县隆华摩擦材料有限公司 一种耐磨离合器片
CN109404450A (zh) * 2018-11-08 2019-03-01 北京天宜上佳高新材料股份有限公司 一种摩擦材料、由其制备的轻量化碳陶盘用有机碳陶刹车片及其制备方法和应用

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE4438456A1 (de) * 1994-10-28 1996-05-02 Deutsche Forsch Luft Raumfahrt Reibeinheit
WO2000041982A1 (de) * 1999-01-14 2000-07-20 Menzolit-Fibron Gmbh Faserverstärkter keramikkörper und verfahren zur herstellung eines solchen
DE19939545A1 (de) * 1999-08-20 2001-02-22 Volkswagen Ag Reibungskupplung, insbesondere für Kraftfahrzeuge
EP1124071A1 (en) * 2000-02-09 2001-08-16 Brembo Engineering S.p.A. Disk-brake disk
EP1124074A1 (en) * 2000-02-09 2001-08-16 Brembo Engineering S.p.A. A shaped composite material for breaking applications and a method for the preparation thereof

Family Cites Families (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2547577B1 (fr) * 1983-06-20 1989-12-15 Aerospatiale Matiere refractaire composite renforcee de fibres refractaires et son procede de fabrication
US4613473A (en) * 1984-04-20 1986-09-23 United Technologies Corporation Method for forming composite articles of complex shapes
US4822660A (en) * 1987-06-02 1989-04-18 Corning Glass Works Lightweight ceramic structures and method
US4852347A (en) * 1987-10-16 1989-08-01 The United States Of America As Represented By The Secretary Of The Air Force Advanced composite polar boss
US5198281A (en) * 1989-04-17 1993-03-30 Georgia Tech Research Corporation Non-woven flexible multiply towpreg fabric
JP3383989B2 (ja) * 1992-06-16 2003-03-10 三菱化学株式会社 炭素繊維強化炭素複合材の製造方法
US5654059A (en) * 1994-08-05 1997-08-05 Amoco Corporation Fiber-reinforced carbon and graphite articles and method for the production thereof
DE19710105A1 (de) 1997-03-12 1998-09-17 Sgl Technik Gmbh Mit Graphitkurzfasern verstärkter Siliciumcarbidkörper
DE19711829C1 (de) 1997-03-21 1998-09-03 Daimler Benz Ag Verfahren zur Herstellung einer faserverstärkten Verbundkeramik
US6390304B1 (en) * 1997-06-02 2002-05-21 Hitco Carbon Composites, Inc. High performance filters comprising inorganic fibers having inorganic fiber whiskers grown thereon
US6264045B1 (en) * 1997-06-02 2001-07-24 Hitco Carbon Composites, Inc. High performance filters comprising an inorganic composite substrate and inorganic fiber whiskers
JP3652900B2 (ja) * 1997-12-16 2005-05-25 日本碍子株式会社 繊維複合材料およびその用途
DE19805868C2 (de) * 1998-02-13 2002-09-12 Daimler Chrysler Ag Verfahren zur Herstellung eines Faserverbundwerkstoffs
JPH11292646A (ja) * 1998-04-10 1999-10-26 Nabco Ltd 炭素系摺動部材及びその製造方法
DE19834704C2 (de) * 1998-07-31 2002-08-01 Knorr Bremse Systeme Reibring bzw. Reibelement für eine Reibbremse, insbesondere Scheibenbremse
DE19856721A1 (de) 1998-12-09 2000-06-15 Ecm Ingenieur Unternehmen Fuer Verfahren zur Herstellung eines mittels Kohlenstoffkurzfasern verstärkten Siliciumcarbid-Verbundwerkstoffes
DE10048012A1 (de) 2000-09-26 2002-04-11 Sgl Carbon Ag Reib- oder Gleitkörper aus mit Faserbündeln verstärkten Verbundwerkstoffen mit keramischer Matrix
DE10066044B4 (de) 2000-12-01 2005-08-18 Dr.Ing.H.C. F. Porsche Ag Verfahren zum Herstellen eines Reibkörpers aus siliziumfiltriertem, Kohlenstofffaser verstärktem porösen Kohlenstoff und Verwendung eines solchen Reibkörpers

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE4438456A1 (de) * 1994-10-28 1996-05-02 Deutsche Forsch Luft Raumfahrt Reibeinheit
WO2000041982A1 (de) * 1999-01-14 2000-07-20 Menzolit-Fibron Gmbh Faserverstärkter keramikkörper und verfahren zur herstellung eines solchen
DE19939545A1 (de) * 1999-08-20 2001-02-22 Volkswagen Ag Reibungskupplung, insbesondere für Kraftfahrzeuge
EP1124071A1 (en) * 2000-02-09 2001-08-16 Brembo Engineering S.p.A. Disk-brake disk
EP1124074A1 (en) * 2000-02-09 2001-08-16 Brembo Engineering S.p.A. A shaped composite material for breaking applications and a method for the preparation thereof

Also Published As

Publication number Publication date
JP2003201185A (ja) 2003-07-15
JP4535362B2 (ja) 2010-09-01
US20030129375A1 (en) 2003-07-10
US6818288B2 (en) 2004-11-16
EP1323944A1 (de) 2003-07-02
DE10164229A1 (de) 2003-07-24
DE50209470D1 (de) 2007-03-29
EP1323944B1 (de) 2007-02-14
ATE354042T1 (de) 2007-03-15

Similar Documents

Publication Publication Date Title
DE10164229B4 (de) Reibscheiben, Verfahren zu ihrer Herstellung und ihre Verwendung
EP1314907B1 (de) Reibkörper aus faserverstärkten Keramik-Verbundstoffen
DE10233729B4 (de) Faserverstärkte keramische Bremsbeläge
EP1054765B1 (de) Verfahren zur herstellung eines faserverbundwerkstoffs
DE10131769C5 (de) Bremssystem mit Verbundwerkstoff-Bremsscheibe
DE10157483C2 (de) Formkörper aus faserverstärkten Verbundwerkstoffen mit segmentierter Deckschicht, seine Herstellung und seine Verwendung
EP0968150B1 (de) Faserverstärkte verbundkeramik und verfahren zur herstellung einer solchen
EP1457703B1 (de) Faserverstärkter Keramik-Werkstoff
EP1154970A1 (de) Faserverstärkter keramikkörper und verfahren zur herstellung eines solchen
WO2010010129A1 (de) Verfahren zur herstellung eines fasergelege-verstärkten verbundwerkstoffs, sowie fasergelege-verstärkte verbundwerkstoffe und deren verwendung
EP1323686B1 (de) Verfahren zur Herstellung von Hohlkörpern aus faserverstärkten keramischen Materialien
EP1489331B1 (de) Reibkörper aus metallinfiltriertem, mit Fasern verstärktem porösem Kohlenstoff
EP1342932A2 (de) Keramische Werkstoffe für Reibbeläge
DE10234400B3 (de) Verfahren zur Herstellung von Hohlkörpern aus faserverstärkten keramischen Materialien, Hohlkörper und deren Verwendung
EP1508718B1 (de) Kupplungsbeläge aus faserverstärkten keramischen Werkstoffen
EP2058545B1 (de) Verfahren zur Herstellung von Reibscheiben aus faserverstärkten keramischen Werkstoffen
EP1783395A2 (de) Bremsscheibe mit Zwischenschicht und Verfahren zur Herstellung derselbe
DE10260923B4 (de) Verfahren zur Herstellung von Hohlkörpern aus faserverstärkten keramischen Materialien, dadurch erhältliche Hohlkörper und deren Verwendung
DE19815308C2 (de) Verfahren zur Herstellung von Verstärkungsfasern oder Verstärkungsfaserbündeln, so hergestellte Fasern oder Bündel und deren Verwendung
EP1382879B1 (de) Verwendung von Reibmaterialien für nassreibende Reibpaarungen
DE102009053737A1 (de) Bremsbelag, Verfahren zur Herstellung eines solchen Bremsbelags sowie Bremseinheit umfassend einen solchen Bremsbelag

Legal Events

Date Code Title Description
OP8 Request for examination as to paragraph 44 patent law
8181 Inventor (new situation)

Inventor name: HERBERG, KLAUS, DIPL.-ING., 74336 BRACKENHEIM, DE

Inventor name: KRäTSCHMER, INGRID, 86485 BIBERBACH, DE

Inventor name: KIENZLE, ANDREAS, DR., 86672 THIERHAUPTEN, DE

Inventor name: KRUPKA, MARIO, 86477 ADELSRIED, DE

Inventor name: BAUER, MORITZ, 86153 AUGSBURG, DE

8364 No opposition during term of opposition
8327 Change in the person/name/address of the patent owner

Owner name: SGL CARBON SE, 65203 WIESBADEN, DE

R119 Application deemed withdrawn, or ip right lapsed, due to non-payment of renewal fee