CY1122485T1 - Υλικο, χρηση του και μεθοδος παρασκευης του εν λογω υλικου - Google Patents

Υλικο, χρηση του και μεθοδος παρασκευης του εν λογω υλικου

Info

Publication number
CY1122485T1
CY1122485T1 CY20191100939T CY191100939T CY1122485T1 CY 1122485 T1 CY1122485 T1 CY 1122485T1 CY 20191100939 T CY20191100939 T CY 20191100939T CY 191100939 T CY191100939 T CY 191100939T CY 1122485 T1 CY1122485 T1 CY 1122485T1
Authority
CY
Cyprus
Prior art keywords
pores
volume
preparation
hydrophilic
ranging
Prior art date
Application number
CY20191100939T
Other languages
English (en)
Inventor
Patrizio SIGNANINI
Original Assignee
Signa Labs S.R.L.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Signa Labs S.R.L. filed Critical Signa Labs S.R.L.
Publication of CY1122485T1 publication Critical patent/CY1122485T1/el

Abstract

Υλικό, χρήση του και μέθοδος παρασκευής του εν λόγω υλικού· όπου το υλικό είναι πορώδες και έχει: πορώδες που κυμαίνεται από 50% έως 80%, ιδιαίτερα από 60% έως 70%· διασυνδεδεμένους πόρους· τουλάχιστον ένα μέρος κατασκευασμένο από υδρόφιλο υλικό, συγκεκριμένα τουλάχιστον ένα μέρος των εσωτερικών επιφανειών των πόρων είναι κατασκευασμένο από υδρόφιλο υλικό· συντελεστή διαπερατότητας (k) μεγαλύτερο από 10-6 m/δευτ.· και όπου, σε δεδομένο όγκο του υλικού (1), ο συνολικός όγκος των πόρων με διάμετρο που κυμαίνεται από 0,1 μm έως περίπου 0,3 nm είναι τουλάχιστον 15% του συνολικού όγκου των πόρων, ιδιαίτερα κυμαίνεται από 15% έως 36%.
CY20191100939T 2015-09-11 2019-09-06 Υλικο, χρηση του και μεθοδος παρασκευης του εν λογω υλικου CY1122485T1 (el)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
ITUB2015A003550A ITUB20153550A1 (it) 2015-09-11 2015-09-11 Materiale, uso e metodo di realizzazione di tale materiale
PCT/IB2016/055382 WO2017042727A1 (en) 2015-09-11 2016-09-09 Material, use thereof and method to manufacture said material

Publications (1)

Publication Number Publication Date
CY1122485T1 true CY1122485T1 (el) 2021-01-27

Family

ID=55069968

Family Applications (1)

Application Number Title Priority Date Filing Date
CY20191100939T CY1122485T1 (el) 2015-09-11 2019-09-06 Υλικο, χρηση του και μεθοδος παρασκευης του εν λογω υλικου

Country Status (11)

Country Link
US (1) US10730797B2 (el)
EP (1) EP3347325B1 (el)
JP (1) JP6861212B2 (el)
CN (1) CN108025977B (el)
BR (1) BR112018004860B1 (el)
CY (1) CY1122485T1 (el)
DK (1) DK3347325T3 (el)
ES (1) ES2745039T3 (el)
IL (1) IL257985B (el)
IT (1) ITUB20153550A1 (el)
WO (1) WO2017042727A1 (el)

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113277872B (zh) * 2021-05-10 2023-03-24 石家庄华行医疗器械有限公司 一种素陶罐
WO2024033674A1 (en) * 2022-08-08 2024-02-15 Signa Labs S.R.L. Method, heat sink and cooling system

Family Cites Families (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS62172120A (ja) * 1986-01-24 1987-07-29 Asahi Chem Ind Co Ltd 加湿機用エレメント材
GB2199541A (en) * 1986-10-16 1988-07-13 Rig Design Services Production of engineering drawings
DE4411644C1 (de) * 1994-04-02 1995-05-18 Kronauer Gmbh Verfahren und eine Vorrichtung zum Befeuchten und Reinigen von Gasen, insbesondere Luft
JP2971868B1 (ja) * 1998-09-18 1999-11-08 イソライト工業株式会社 無土壌植栽用セラミックブロック及びその使用方法
JP2005067966A (ja) * 2003-08-26 2005-03-17 Makoto Kitamura リン酸カルシウム系セラミックス多孔体及びその製造方法
CN101548615A (zh) * 2009-05-22 2009-10-07 山东省古窖藏酒与酒文化研究发展中心 一种多孔巢砖立体绿化植被技术
WO2012036218A1 (ja) * 2010-09-16 2012-03-22 小松精練株式会社 多孔質セラミックス焼結体
WO2012039127A1 (ja) * 2010-09-21 2012-03-29 パナソニック株式会社 多孔質イオン交換体、水処理装置、給湯装置、及び多孔質イオン交換体の製造方法
CN103917745B (zh) * 2011-06-14 2017-12-26 西格纳化学有限责任公司 使用金属硅化物提高原油采收
CN102410584B (zh) * 2011-10-25 2013-11-20 苏文先 带式滤尘除湿换气机
US9623360B2 (en) * 2013-05-20 2017-04-18 Corning Incorporated Porous ceramic article and method of manufacturing the same
JP6266972B2 (ja) * 2013-12-13 2018-01-24 三井金属鉱業株式会社 焼成治具用多孔質セラミックス、焼成治具用多孔質セラミックスの製造方法および冷却装置
CN105727755B (zh) * 2014-12-09 2018-08-28 中国科学院金属研究所 一种梯度孔隙氮化硅结合碳化硅膜管及其制备方法
CN108751968B (zh) * 2018-06-13 2020-12-22 北京科技大学 一种本征成孔的多孔陶瓷材料制备方法

Also Published As

Publication number Publication date
ES2745039T3 (es) 2020-02-27
IL257985B (en) 2021-01-31
JP2018529621A (ja) 2018-10-11
WO2017042727A1 (en) 2017-03-16
EP3347325B1 (en) 2019-06-19
IL257985A (en) 2018-05-31
EP3347325A1 (en) 2018-07-18
US20180282220A1 (en) 2018-10-04
DK3347325T3 (da) 2019-09-23
CN108025977B (zh) 2022-03-22
BR112018004860B1 (pt) 2022-11-16
BR112018004860A2 (el) 2018-10-02
US10730797B2 (en) 2020-08-04
ITUB20153550A1 (it) 2017-03-11
CN108025977A (zh) 2018-05-11
JP6861212B2 (ja) 2021-04-21

Similar Documents

Publication Publication Date Title
CL2015002927A1 (es) Espuma absorbente de material compuesto.
CL2016001432A1 (es) Nuevos anticuerpos anti-dpep3 y métodos de uso
EA201501082A1 (ru) Пористый зубной имплантат
EP3674354A4 (en) COMPOSITE POROUS MEMBRANE AND PROCESSES FOR PREPARATION AND USE
CR20140529A (es) Anticuerpos e inmunoconjugados contra ly6e y métodos de uso
JP2014098143A5 (el)
CY1122485T1 (el) Υλικο, χρηση του και μεθοδος παρασκευης του εν λογω υλικου
EA201600031A1 (ru) Способ изготовления полимидных мембран
CL2017002101A1 (es) Dispositivo, plataforma y ensayo para evaluación de células
CY1119146T1 (el) Δοχειο υγρων απο υλικο φυσικης πετρας, διαδικασια για την κατασκευη του και τη χρηση του σε μια διαδικασια για την κατασκευη ή την αποθηκευση αλκοολουχων ποτων
TWD190432S (zh) 鼻管
AR106796A1 (es) Apuntalante de peso liviano y métodos para su producción y uso
EP3706948A4 (en) SINTERED POROUS MATERIAL WITH KNOTS AND FIBERS MADE FROM DIFFERENT MATERIALS, WITH DIFFERENT SINTERING POINTS AND ASSOCIATED MANUFACTURING METHODS AND USE
WO2018213218A3 (en) POROUS BODY HAVING ENHANCED CRUSH RESISTANCE
BR112017007728A2 (pt) material sinterizado de cobre poroso, parte compósita de cobre poroso, método de produção de material sinterizado de cobre poroso e método de produção de parte compósita de cobre poroso
CL2015002470A1 (es) Composición para formar una estructura porosa absorbente
CL2018003167A1 (es) Selección de cepas bacterianas útiles en el tratamiento de alergias.
ES2466571A8 (es) Membrana cerámica de filtración
CO2017012883A2 (es) Estructura de capas adhesiva revestida con gel de silicona
JP2017181735A5 (el)
CL2016002380A1 (es) Dispositivo de limpieza para instrumentos médicos y métodos relacionados de utilización.
MX2020003991A (es) Método para diseñar un hormigón autocurable adicionado con un hormigón permeable que contiene materiales biológicos.
BR112016021231A2 (pt) derivados de hexose, preparação e uso destes.
IT201600086161A1 (it) Mezzo filtrante e uso del mezzo filtrante.
WO2015008141A3 (en) Micro-and/or nano-scale patterned porous membranes, methods of making membranes, and methods of using membranes