CS248290B1 - Method of seamless rings production with increased elasticity - Google Patents
Method of seamless rings production with increased elasticity Download PDFInfo
- Publication number
- CS248290B1 CS248290B1 CS832468A CS246883A CS248290B1 CS 248290 B1 CS248290 B1 CS 248290B1 CS 832468 A CS832468 A CS 832468A CS 246883 A CS246883 A CS 246883A CS 248290 B1 CS248290 B1 CS 248290B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- temperature
- rings
- exceeding
- deformation
- calibrated
- Prior art date
Description
1
Ha3paHHe Η3θ6ρβΤβΗΗΗ
Cnoco6 H3ΓοτοΒπβΗΗΗ 6ecmoBHbix KOJieu, c yjiymneHHbíMH xapaKTepHCTHKaMH
ýnpyrocTH OÓJiaCTb ΠρΗΜβΗβΗΗΗ Η3θ6ρβΤβΗΗΗ Η3θ6ρβτβΗΗβ KacaeTcs cnocoóa κομ6ηηηροββηηογο npHuaHHH φορΜΜ η Φη3Ηκο-χη-MHUeCKHX KaneCTB 6eCniOBHbÍM KOJIbUaM C nOBbímeHHblMH npefleJlbHblMH flOnyCTHMblMHCTaTHUeeKHMH H UHHaMHWeCKHMH HarpySKaMH, HeOÓXOflHMblM flJIH H3rOTOBJíeHHHKOJihijeBbix npyatHH h flpyrnx 3ΠβΜβΗΤθΒ, npyacnHHbiň 3φφεκτ y κοτορΜΧ peann3yeT-ca sa cneT ynpyroro yBejiHHeHHH hjih yMeHbiueHHH jjnaMeTpa KOJibua.
XapaKTepHCTHKa H3BecTHbix TéxHHuecKHx pemeHHň
CornacHo H3BecTHbiM cnocoSaM SecmoBHbie KOJibua H3roTaBJiMBaioTCH jih6o nyTeMpacKaTbiBaHHH Meacfly uByMH προφιυίΒΗωΜΗ BajiKaMH b o^hh hjih HecKOJibKo 3TanoBnpH TeMnepaType ropaneft oópaÓOTKH uaBJíeHHeM jihÓo nyTeM oÓbeMHoň ιπτβμποβκηc nocjieuyromeň KanHÓpoBKoft npH TeMnepaType ropHHeň πιτ3μποβκη hjih pacKaTKH.flílH flOCTHWeHHH HeOÓXOflHMÓft flJIH npyiKHHHblX 3JieMeHTOB npOHHOCTH 3TH KOJIbUaTepMHHecKH o6pa6aTbiBaioTCH b oTftejibHbix ycTpoňcTBax jih6o HenocpeflCTBeHHo 3a-KanHWTCH pe3KHM oxnaatfleHHeM ot TeMnepaTypw ropimeň oópaÓOTKH uaBJíeHHeM h3aTeM OTnycxaioTCH, npHueM πρκ ρββκοΜ oxjiamfleHHH b xanecTBe MHHHManbHoň τθμ-nepaTypbi TpeÓyeTCH oÓbiUHaa ujih peccopHo-npyjKHHHbix CTaneň TeMnepaTypa 3aKan-kh (cm. BKOHOMHnecKHň πβτβΗΤ C 21 D /141038). IÍ3BecTHo, ητο npH HcnoJib3OBa-hhh BbicoKOTeMnepaTypHoft TepMOMexaHHuecKoň o6pa6oTKH c MapTeHCHTHbíM npeBpa-meHHeM BO3MO3KHQ yjiymneHHe Φη3ηκο-χημηηθοκηχ xawecTB npewue Bcero 3a cqeTCTeneHH ΑβφορΜΒρΗΗ óojiee 20Z Ha nocneuHeM 3Tane HeaHanHTejibHO Bbnne A3. Ta-KHM OÓp33OM H3BeCTHbie ClíOCOÓbl H3rOTOBJIOHHH npyWHHHbIX KOJieu ΗΜΘΙΟΤ HeflOCTaT-kh, 3aKjno3aiomHecH b tom, hto - npH HCnOJIb3OBaHHH OCbíHHbIX MeTOUOB TepMOOÓpaÓOTKH He HCHepnblBaiOTCH cymecT-BeHHbie peaepBbi βο3μο»ηογο noBbímeHHH npeuejibHbix uonycTHMbix CTaTHHecKHX h uh-HaMHHecKHX Harpy3OK ujib peccopHO-npyiKHHHbix CTajieň, - npH npHMeHeHHH BbicoKOTeMnepaTypHoň TepMOMexaHHnecKoň o6pa6oTKH TaKuce hnpH KOHenHoň TeMnepaType ,ρθφορΜθρΗΗ, He3HaHHTejibHo npeBbímaioineH As, peRpnc- 248290 2
TajiJiH3anHH b Hcnonb3yeMbix peccopHO-npyacHHHbix CTannx npHBOflHT κ cymecTBeH-HOMy CHmKeHwo MMCJia ΑθΦθκτοΒ penieTKH, Tax μτο thkhm o6pa3OM flocTHraeTCHTonbKo nacTHMHoe ynyqiueHHe Φη3ηκο-χημηηθοκηχ xaqecTB MaTepnana, b qacTHoc-th npeflena TeKyqecTH h ycTanocTHoň προηηοοτη, - 3a caeT KajinfípoBKH πρκ TeMnepaType ropaueň o6pa6oTKH flaBJíeHHeM c κοοφφΗ-Αηθητομ p^opMaijHH HHace 15% HaqHHaeTcn peKpncTajuiH3aijHH, KOTopaa TaKxeorpaHHqnBaeT n3M6HeHHH KaqecTB, flocTHSKHMbie BCJieflCTBHe npHMeneHHH bhcoko-TeMnepaTypHoň TepMOMexaHHqecKOH o6pa6oTKH c MapTeHCHTHbíM npeBpameHHeM, - npH HCriOJIb3OBaHHH flOCTaTOHHO BblCOKHX ΟΤβΠβΗθΗ ΑθΦθΡΜ3ΑΗΗ ΠρΗ ΗΗ3ΚΗΧ KO~HeqHbix TeMnepaTypax ΑθΦθΡΜΗη,ΗΗ c pejibio .boctidkshhh MaKCHManbHo βο3ΜΟ)κηογοynyqiueHHH xaqecTB 3a cqeT conpoTHBJíeHHH αθΦορμηροβηηηιο o6pa6aTbiBaeMbix cTa-jieií BO3HHKaeT BbicoKan Harpy3Ka o6pa6aTbiBaioinHX ManJHH h HHCTpyMeHTa α·πη 06-pačoTKH flaBJíeHHeM.
UeJIb Η3θ6ρεΤΘΗΗΗ
UeJIb Η3θ6ρβΤθΗΗΗ COCTOHT B CO3flaHHH KOMÓHHHpOBaHHOH ΤΘΧΗΟηΟΓΗΗ o6pa6OTKHflaBJíeHHeM h TepMoo6pa6oTKH, KOTopan npH caMbix He3HaqHTenbHbix 3aTpaTax 3Hep-γηη h npn coKpameHHOM qncne 3TanoB npoqecca MoaceT npHMeHHTbcn αλη η3γοτοβ-jieHHH 6ecwoBHbix KOJien α·πη KOJibyeBbix npyxcHH c ynyqmeHHbíMH xapaKTepHCTHKaMHynpyrocTH, bhskocth, ycTanocTHoň npoqHocra, αθμΦηροββηηη h noBbímeHHbíMHnpepejibHbíMH flonycTHMbiMH Harpy3KaMH 6e3 flonojiHHTenbHbix 3aTpaT nerapyiomHX3ΒθΜβΗΤΟΒ. H3Ji03KeHne cyinHoc™ Μ3θ6ρβτθΗΗΗ 3a#aqa H3o6peTeHHH 3aKnioqaeTCH b tom, ητο6μ b pe3yjibTaTe ropHqeň'o6pa6oTKHAaBJíeHHeM aocthbL· He nojiHocTbio peKpncTajinn3HpoBaHHoe cocTOHHHe CTpyxTypbic οτηοοητ&πβηο ycToňqHBoň noflCTpyKTypoň h ynyqmeHHbíMH φΗ3Ηκο-ΧΗΜΗηεοκΗΜΗxaqecTBaMH nocne oxnaacAeHHH 3a cqeT flocraToqHO bhcoko/í CTeneHH ΑθΦορΜβφΐΗHa nocjieflHeM 3Tane b coqeTaHHH c co3flaHneM HeÓnaronpHHTHbix ycnoBHň pexpuc-TajiJiH3au;HH nyTeM Bbi6opa βηγοαηογο TeMnepaTypHo-BpeMeHHoro peatHMa.
CornacHo H3o6peTeHHto 3Ta 3aflaqa pemaeTCH τβΜ, ητο crarib c coflepacaHHeM yrne-popa 0,40 - 0,70%, κρθμηηη ao 2,00%, MapraHpa flo 1,1% h xpoMa no 1,20% bxaqecTBe οοηοβηβιχ Jierapymupix sneMeHTOB aycTeHH3HpyeTCH npn TeMnepaType Mesc-Ay 1050°C h í200eC η npn TeMnepaTypax csbinie 950°C noABepraeTCH qepHOBoňκοΒκβ ao nonyqeHHfl 33Γοτοβκη c oTBepcraeM no ueHTpy, 3Ta 3aroTOBxa noAsepraeTcn hhctoboh o6pa6oTxe πη6ο nyTeM očbeMHoň mTaMnoB-kh nn6o nyTeM προκβτκΗ 3a oahh hhh HecKonbKO 3TanoB Ha CTaHe, npnqeM TeMne-paTypHO—BpeMeHHoň peacHM npH ropHqeň o6pa6oTxe AasjíerineM Bbi6npaeTcn Tax,qTo6bi KOHennan TeMnepaTypa ΑεφορΜβηπΗ cocTaBnnna He 6onee 850 C. nocne3τογο Konbna 6e3 KanHópoBKH peexo oxnaxcAaiOTCH b TeqeHHe 5-20 c, OTnycxaioT-*ch npn TeMnepaType 400 - 480°C h 3aTeM KanH6pyroTCH co CTeneHbio ΑθΦθΡΜβΑΗΗHe 6onee 5% πρκ TeMnepaType oTnycxa κπη TeMnepaType noMemeHHH. 3axanKa npo-H3BOAHTCH KBK H3BeCTHO B Macne, ΒΟΑθ c AO6aBKaMH ΑΠΗ ΟΚ333ΗΗΗ BnHHHHH HaBpeMH oxnaxAeHHH. B pe3ynbTaTe τβκοή κομ6ηηηροβηηηοη TepMOMexaHnqecKoň o6rpafíoTKH (ropnqan o6pa6oTxa α^βλθηηθμ ycToňqHBoro aycTeHHTa nyTeM oĎbeMHoňπιτ3μποβκη Hnu pacKaTbiBaHun Koneq b coqeTaHHH c o6pa6oTKoň AasneHHH OTnymeH-ηογο aycTeHHTa npn KannópoBKe) -nonyqaeTCH MHKpocTpyxTypa, cymecTBeHHO ynyq-raaioinaH npoqHocTHbie xapaKTepHCTHKH stoh CTann no cpaBHeHHio c ofibnmoň o6pa-6otkoh, T.e., c oahoh cTopoHbí, BcneACTBHe 6onbmeň ynpyroň nnacraqHocTHyBenHqHBaioTCH npeAenbHbie AonycTHMbie Harpy3KH, a, c APyroň CTopoHbí, Bcnen-cTBHe ynyqweHHoň bh3Kocth yMeHbniaeTcn onacHocTb pa3pyraeHHH πρκ cTamec-koh h AHHaMHqecKOH Harpy3Ke h BO3pacTaeT cpox cnyacSbi. 248290 3 ΠρΗΜβρ OCymeCTBneHHH Η3θ6ρβΤεΗΗΗ Μ3θ6ρβτβΗΗβ noHCHneTCH Hnáte noypoÓHee Ha npHMepe ero ocymecTBneHHH.3aroTOBKa H3 CTanH MapKH 62SiCr 5, HanpHMep, b BHye στρβ3Κ0Β ynnHHypoBaycTeHH3Hpye.TCH řípu TeMnepaType 1100°C h nepeKOBbiBaeTCH b KpyrJiyio 3aroTOB-Ky c OTBepCTHeM no yeHTpy b HecKonbKO mnoB, πρΗΗβΜ yonacHa BbiyepxHBaTbCHTeMnepaTypa b KOHye kobku He MeHee 950®C. 3βτβΜ πρκ HanajibHoň TeMnepaTypeHe MeHee 900°C Ha CTaHe b «Ba o6»taTHH npoH3BoyHTCH ηηοτοβηη pacnaTKa, npmeMKOHeHHan TeMnepaTypa βεφορΜβμΗΗ He yonxHa npeBbiniaTb 850 C. OnucaHHbiň HHxenpHMep othochtch κ KanH6poBKe npH TeMnepaType OTnycna. ΠρΗ stom Kojibnonocne hhctoboh pacKaTKH c TeMnepaTypoň 850°C 3aKanneTCH b TeneHHe 15 c bMacne h oTnycKaeTcn npn TeMnepaType 470 C. 3βτβΜ cneyyeT KannSpoBKa πρκTeMnepaType OTnycKa nyTeM ββφορΜβίίΗΗ Kontya He 6onee, neM Ha 5% npn TeMne-paType He MeHee 400°C.
CneyyioinHň npHMep othochtch k KannÓpoBKe Koney npH TeMnepaType noMemeHHHnocne OTnycKaHHH. Πρκ stom TepMOMexaHHnecKH o6pa6oTaHHoe, npeTepneBineeMapTeHCHTHoe npeepameHne h OTnymeHHoe πρκ 470°C κοηπηο KanHČpyeTCH nocneoxnaatyeHHH πρκ TeMnepaType noMemeHHH co CTeneHbio ΗβφορΜ3ΗΗΗ He óonee 3%. B το βρθμη KaK no cpaBHeHHio c oóbiHHoň οόρβόοτκοΗ Konbya, H3roTOBneHHbienyTeM BbicoKOTeMnepaTypHoň TepMOMexamrnecKoň oópaóo,TKH, npn oyHHaKOBoň TBep-flocTH xoth η ΗΜειοτ cymecTBeHHO nynmyio nnacTHHHocTb, hto yKa3bffiaeT Ha ynyn-meHHyio bh3kocti> CTann, 3βτο aa cneT πρΗΜβΗβΗΗΗ KOMÓHHHpoBaHHoň TepMOMexa-HHnecKoň o6pa6oTKH πρκ οηηηηκοβοη TBepyocTH h ynynmeHHoň bh3kocth, KpoMetoto, npeyen ynpyrocTH h npeyen TeKynecra CMemaioTCH b CTopoHy ÓonbíHHX Ha-npHxeHHH, TaK hto 3TH Konbya oÓnayaioT ynywnieHHbíMH xapaKTepHCTHKaMH, τβκKaK ohh nonycKaioT BbicoKyio CTeneHb ynpyroft ηεφορΜΒΗΗΗ, MoryT BbiyepacHBaTbBbicoKHe CTaTHHecKHe h yHHaMHHecKHe HarpyaKH h BcneycTBHe ynynmeHHOň BH3KOC-th MoryT KOMneHCHposaTb πρκ bmcokhx MexaHHHecKHx Harpy3Kax MecTHbie KOHyeHT—payHH HanpHHteHHň 3a cnet nnacranecKoň πεφορΜβηΗΗ.
OopMyna Η3ο6ρβτεΗΗΗ 1. Cnoco6 HsroTOBneHHH óecmoBHhix Koney c ynynineHHbíMH xapaKTepHCTHKaMH ny-TeM ropHHeň o6pa6oTKH yaBneHHeM c nocneyywmeň TepMooópaÓOTKoň c Hcnonb3OBa-HneM Tenna ropHHeň oópaÓOTKH yaBneHHeM, OTHHHaioiHHftcH τθμ, hto Kpýrnan 3a-roTOBKa c oTBepCraeM no yeHTpy H3 CTanH, coyep^ameň 0,40 - 0,70% yrnepoya,yo 1,20% xpoMa, yo 2,0% κρ.βΜΗΗΗ h yo 1,10% MapraHya, KOTopan nocne aycTeHH-3ayHH b flHana3OHe TeMnepaTyp οτ 1050 yo 1200°C H3roTOBneHa nyTeM nepHOBoňkobkh npH TeMnepaTypax CBbune 1000°C, oÓpaÓaTbiBaeTCH yaBneHHeM npy KOHeHHoňTeMnepaType ηεφορΜ3ΐχΗΗ He 6onee 850®C b Konbya, 3βτβΜ 3aKanHBaeTCH b Tene-HHe 5-20 c nyTeM pe3Koro oxnawyeHHH οτ TeMnepaTypbi He 6onee 850 C, OTnyc- íKaeTCH npH TeMnepaTypax οτ 400 yo 480®C c BbiyepxKoň 8-30 μηη, h nocne3Toro KanHčpyeTCH npH TeMnepaType He MeHée 400 C co CTeneHbio ηβφορΜαηΗΗ
He 6onee 5%. 2. Cnocoó no π. 1 ,οτηιϊη3ιοπ(ηηοη τβΜ, hto nonyneHHbie ropaneft oÓpaóoTKoň yaB-neHHeM Konbya nocne aaxanKH h OTnycKa npn TeMnepaType noMemeHHH KanHÓpyioT-ch co CTeneHbio ηεφορΜΗΐχΗΗ MeHee 5%. 3. Cnoco6 no π. 1, OTnnyaiomHňcH TeM, hto nonyneHHbie ropHHeň oÓpaóoTKoňyaBneHHeM nepey 3aKanKoft b TeMnepaTypHOM yHana3OHe Me»yy 700 h 800 C xonb-,ya KanH6pyioTCH h b Teneraie 5 - 20 c 3aKannioTCH, a TaK»e OTnycnaioTCH πρκTeMnepaTypax 400 - 48Ó°C c BbiyepjKKoň οτ 6 yo 30 mhh. 4. Cnocoó no n.l, 2 h 3, OTnHnaiomHňcH τεΜ, hto Kpyrnbie 3ηγοτοβκη c oTBepc- 248290 4 raeM no ueHTpy oópaOaTbiBaKrrca b npyacHHHbie Konbna nyTeM oĎteMHoň ωτβΜποΒ-kh nnn nyTeM προκβτκΜ c KOHenHoň TeMnepaTypoň πεφορΜβρηΗ He Conee 850°C. 5. Cnoco6 no n.l, 2 n 3, oTnnnaioiuHňcň τβΜ, ητο saKamca npoH3BoaHTCa B Mac~ne, Bone Hnu BoflHbix pacTBopax. 6. Cnoco6 no π. 1 , 2 n 3, oTnHnaionmňcH τθμ, ητο KOMGnHHpoBaHHaa TepMOMexa-HHnecKaa oópaóoTKa πρημθηηθτοη y npyaoiHHbix aneMeHTOB wih nnacTHHuaTbix hcnnpant>Hbix npyiKHH.
ÁHHOTaUHH
Cnocoč HaroTOBneHHH 6ecnioBHbix xonep c ynynmeHHbíMH xapaKTepHCTHxaMH xacaeT-cn nponaBOflCTBa KOJibpeBbix npy»nH ηπη KOJibueBux aneneHTOB H3 CTann, npy»HH-Hbiň οφφεκτ y κοτορωχ peanH3yeTC« 3a cneT ynpyrnx H3MeHeHHň pnaMeTpa κοηβρ.Hejlb Μ3θ6ρβΤβΗΗΒ COCTOHT B C03fl3HHH KOMĎHHHjJOBaHHOň TexHOJlOTOH o6pa6OTKHflaBneHneM h TepMoo6pa6oTKn, KOTopaa npn ποηηικθηημχ 3aTpaTax Ha HaroToene-HHe npnBoflHT κ ynynmeHHio SKcnnyaTauHOHHbix xanecTB npyxHHHbtx Konep. 3aflanaH3o6peTeHHH 3aKntonaeTCH' b tom, mtoÓm nyTeM BbiSopa BbiropHoro pemMa o6pa6oT-xa flaBneHneM - TeMnepaTypa - BpeMH co3flaTb HeCnaronpHHTHbie ycnoBna pnapeKpncTannn3auHn, Tax, ητοβω b coneTaHHH c MapTeHCHTHbíM npeepamenneM nony-nanHCb ynynnieHHbie xapaKTepHCTHKH npyxHH. 3a,n,ana pemaeTcm τβΜ, ητο nyTeM KOM6HHHpoBaHHOň TepMOMexaHHnecKoft o6pa6oT-kh (ropanaa o6pa6oTxa naBnenneM ycToňnHBoro aycTeHHTa h xonopHaa οβρβόοτκβaaBneHHeM OTnymeHHoro aycTeHHTa) pocTHraeTca cocTOHHHe CTpyKTypw peccopHo-npywHHHoň cTann, orannaromeeca noBbnneHHoň ynpyroň aeýopMHpyeMocTbio η ποηη-aceHHoň CKnoHHocTbio κ oGpaaoBaHHto TpenyiH npn CTaTHnecKHX h pHHaMHnecKHX Ha·rpy3Kax. Η3θ6ρετβΗΗΗ μοχθτ HaňTH npHMeHeHHe Ha npeanpHHTHHx MeTannyprHH n' MeTanno-o6pa6aTbiBaromeň npoMbimneHHOCTH npn HaroTOsneHHH npyacHHHbix κοηβρ. IIpnsHaHo H3o6peTeHneM no pesynbTaraM 3KcnepTH3bi, ocynecTBneHHoň BepoMCTBOMno flenaM H3o6peTeHHň η πατεκτοΒ FflP. 248290
Claims (5)
- 248 290 P R B D M fi τ. VYNÁLEZU1. Způsob výroby bezešvých kroužků se zvýšenou pružnostítlakovým tvářením za tepla s následujícím tepelným zpraco-váním, při kterém se využívá teplo tlakového tváření zatepla, vyznačující se tím, že polotovar kruhového tvaru,který má ve středu otvor a je zhotoven z ocele obsahující0,40 až 0,70 % uhlíku, nejvýše 1,20 % chrómu, nejvýše 2,0 %křemíku a nejvýše 1,10 % manganu se vyrobí hrubým kovánímpři teplotách přesahujících 1 000 °C a po austenizaci v roz-mezí teplot od 1 050 do 1 200 °C se zpracovává tlakem přikonečné teplotě deformace nepřesahující 850 °C na kroužky,které se kalí během 5 až 20 sekund rychlým ochlazením z tep-loty nepřesahující 850 °C a potom se popouští při teplotáchod 400 do 480 °C s výdrží od 8 do 50 minut, potom se krouž-ky kalibrují při teplotě nejméně 400 °C se stupněm deformacenepřesahujícím 5
- 2. Způsob podle bodu 1, vyznačující se tím, že se kroužkyzhotovené tlakovým tvářením za tepla po zakalení a popouš-tění kalibrují při normální teplotě místnosti se stupněmdeformace menším než 5 %.
- 5. Způsob podle bodu 1, vyznačující se tím, že se kroužkyzhotovené tlakovým tvářením za tepla kalibrují během 5 až20 sekund kalením v rozmezí teplot od 700 do 800 °C a popouš-těním při teplotách 400 až 480 °C s výdrží od 6 do 50 minut.
- 4. Způsob podle bodů 1, 2 a 5, vyznačující se tím, že se zpolotovaru kruhového tvaru s otvorem ve středu vytvářejípružící kroužky objemovým lisováním 3 konečnou teplotou de-formace nepřesahující 85Ο °C. 248 290
- 5. Způsob podle bodů 1, 2 a 5» vyznačující se tím, že sekalení provádí v oleji, ve vodě anebo ve vodních roztocích.