CS200006B1 - Process for preparing polydispersion powdered tungsten carbide by thermal decomposition of vapour of tungsten hexacarbonyle - Google Patents
Process for preparing polydispersion powdered tungsten carbide by thermal decomposition of vapour of tungsten hexacarbonyle Download PDFInfo
- Publication number
- CS200006B1 CS200006B1 CS783145A CS314578A CS200006B1 CS 200006 B1 CS200006 B1 CS 200006B1 CS 783145 A CS783145 A CS 783145A CS 314578 A CS314578 A CS 314578A CS 200006 B1 CS200006 B1 CS 200006B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- tungsten
- tungsten carbide
- thermal decomposition
- powdered
- preparing
- Prior art date
Description
SZS POPIS VYNÁLEZU
REPUBLIKA
*’*’ K AUTORSKÉMU OSVEDCENIU
(61) (23) Výstavná priorita(22) Přihlášené 16 05 78(21)PV 3145-78 200 006 (11) (B1) (51)Int.C1.3c 01 B 31/34
ÚŘAD PRO VYNÁLEZY
A OBJEVY (40) Zverejnené 30 11 79(45) Vydané 15 10 82
Autor vynálezu CZAJLIK MIKULÁŠ ing.CSc., JALŮVKA JAROMÍR doc.RNDr.PhDr.CSc.,ĎURIŠIN JOZEF ing. a LENQYBL JURAJ ing., KOŠICE (54) Spdaob přípravy polydisperzného práškového karbidu volfrámu termickým rozkladom pérhexakarbonylu volfrámu 1
Vynález rieSi priamu přípravu vysokodiaperzného práškového karbidu volfrámu termickýmrozkladom hexakyrbonylu volfrámu. V aúSasnoati karbid volfrámu aa připravuje niekolkými apdaobmi:a/ priamou ayntézou uhlíka a práěkovým volfrámom v elektrických peciach,b/ v kúpeli pomocného kovu, c/ ayntézou práSkového volfrámu a kyeličníkom uhoTnatým, priSom fyzikálno-chemickévlaatnoati zlákaného karbidu závieia od přípravy práSkového volfrámu; jemný vol-frámkarbidový práSok vhodný pře katalýzu chemických pochodov aa připravuje: 1. z práSkového volfrámu, zíakaného z bielej, event. žltej modifikácie kyselinyvolfrámovej, 2. z karbonylového volfrámu, zíakaného termickým rozkladom hexakarbonylu volfrámu.Výhody přípravy karbidu volfrámu apdaobmi a/ a b/ apoSívajú predovšetkým v tom, že aa při-praví práSkový karbid volfrámu a přesným atechiometrickým zložením a dobré vyvinutou krys-talickou Struktúrou. Výhody apóaobu cl/ a 02/ apoSívajú v tom, že aa připraví jemný polydisperzný práSkový kar-bid a neatechiometrickým zložením a defektnou krystalickou Struktúrou.
Nevýhodou vSetkýoh uvedených príprav je to, že aú Sašovo zdíhavé a náročné na teplotný re-žim.
Horeuvedepé aedoatatky nemá spdaob přípravy polydisperzného práSkového karbidu volfrámu py- 200 006
Claims (1)
- rolýzou pár hexakarbonylu volfrámu v rozmedzí tepldt 750 až 1050 °C, kterého podstata spo-Sívá v tom, že páry hexakarbonylu volfrámu as rozkladajú v atmosféře kysliSníka uhelnatého. Výhody, ktoré vynález prináča, spoSívajú predovčetkým v odstránenl zdíhavéhp a nároč-ného teplotného režimu a tým doba přípravy karbidu volfrámu sa skráti 30-násobns* Příprava karbidu volfrámu termickým rozkladem hexakarbonylu volfrámu v atmosféře COprebieha v teplotnom intervale 750 až 1050 °C. Při lineárněj rýchlosti prietoku nosného plynu CO 0,75 až 1,5 m/s je třeba zvoliť dížku rozkladnej zóny tak, aby reakSná zmss, tzn. produkty rozkladu W/CO/g a CO sa udrželi na danej teplote priemerne 3 až 5 s. Použitie kysliSníka uhelnatého ako nosného plynu spolahlivo zaručuje výrobu práikovéhopolydisperzného karbidu volfrámu, ktorý má defektnú ítruktdru a nesteehiometrioké zloženie,obsah uhllka v rozmedzí 5,9 až 6,12 %, žiadny volný uhlík a stopové nečistoty pod 0,001 %. Příklad Páry hexakarbonylu volfrámu sa termicky rozkladajú pri teplote 750 °C v atmosféřekysličnlka uhelnatého s prietokom 0,75 m/s, v rozkladnej reakčnej zóně 2,25 m s re-akčnou dobou 3 s. Vzniká polydisperzný práškový karbid volfrámu s defektnou itruktúrou s nestechiometriekým zložením; obsah uhlíka 5,9%, žiadny volný uhlík a stopovénečistoty pod 0,001 %, fialčie výhody vynálezu sú nasledovné: Změnou reakSných podmienok je možné rýchlo a výrazné ovplyvniť fyzikálno-chemické vlasnosti produktu. Celý prooes přípravy VC je možné úplné automatizovať. Připravený karbid volfrámu sa mdže uplatnit v práákovej metalurgii alebo ako katalyzá-tor pri chemických a elektrochemických procesech a v elektrotechnike. PHEDMBT VYNALEZU Spdsob výroby polydisperzného práikového karbidu volfrámu termickým rozkladom pár hexakar-bonylu volfrámu v rozmedzí tepldt 750 až 1050 °C, vyznačujúci sa tým, že rozklad sa prevá-dza v atmosféře kysličníka uhelnatého.