CN86100457B - 隔声、阻尼、防辐射材料的制造方法 - Google Patents
隔声、阻尼、防辐射材料的制造方法 Download PDFInfo
- Publication number
- CN86100457B CN86100457B CN86100457A CN86100457A CN86100457B CN 86100457 B CN86100457 B CN 86100457B CN 86100457 A CN86100457 A CN 86100457A CN 86100457 A CN86100457 A CN 86100457A CN 86100457 B CN86100457 B CN 86100457B
- Authority
- CN
- China
- Prior art keywords
- damping
- sound insulation
- lead
- low
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
本发明是隔声、阻尼、防辐射材料的制造方法，这里的辐射主要是指Ｘ射线和低能γ射线。采用树脂、钡盐、铅粉或铅化合物为主要原料，其中钡盐来源丰富，价格低廉，所以用这种方法制成的软质材料成本低、隔声、阻尼、防辐射性能优越，当材料厚度为１ｍｍ时，面密度为３ｋｇ／ｍ2左右，隔声指数可达２２分贝，当其厚度为２．８ｍｍ时，铅当量为０．４９ｍｍＰｂ。该材料加工方便、可粘接、缝合、钉制成各种防护装置。
Description
本发明属于隔声、阻尼、防辐射材料制造方法的范畴。
用树脂与铅共混制造隔声材料技术已有报导，如日本〔特公昭57-18555〕用高分子聚合物与铅纤维混合，挤压成型，制造隔声材料。用这种方法获得的材料隔声效果虽然较好，但由于铅以纤维状态存在，比重又大，所以在制造过程中很难与高分子聚合物混合均匀，而材料对辐射屏蔽作用主要取决于铅层厚度，由于用这种方法制成的材料铅纤维间有空隙，所以该材料用于辐射防护必将造成局部透射。而且其表面的铅纤维容易剥离脱落。
作为隔声材料制造方法，〔特开昭57-158258;GB1420632〕还有介绍，它是采用树脂或橡胶与粉状铅化合物或金属铅微粒混炼，压成一定厚度的隔声材料，产品成本较高，并且得到的是硬质板材，故其应用范围有一定局限性。
寻求价格低廉，原料来源丰富的填料全部或部分代替常用的铅或铅化合物，获得一种同时具有隔声、阻尼、防X射线和低能γ射线多种用途的软质材料，就是本发明的目的。
本发明是将重量组成比例为100的树脂与10-1000的钡盐、1000-10的铅粉或铅化合物、一定量的其他填料和助剂一起混炼，经压延或挤出制成所需厚度的软质材料。
本发明使用的树脂可以是聚乙烯、聚丙烯、聚氯乙烯（PVC）、聚苯乙烯等;钡可以是硫酸钡、硝酸钡、碳酸钡或重晶石粉;铅可以是铅粉、铅的氧化物、铅盐，根据用途可加入适量增塑剂、阻燃剂、着色剂等各种助剂。
按照一定重量比，将树脂、磨细到150-300目的钡盐、铝粉或铅化合物以及其他助剂投入捏合机中，搅拌同时升温，为防止焦化现象产生，蒸气压力控制在2-3kg，捏合时间与投料量及各种原料配比有关，一般为40-60分钟，使各组分充分混合均匀，为防止粉状物质飞散可采取密封操作。将捏合好的物料转入密炼机中进行塑化，控制蒸气压力为5-7kg，时间6-8分钟，再经二辊机加热剪切塑化，然后直接喂入压延机的辊筒之间，经过几个辊筒的热压延，调节辊距，就能得到不同厚度的片材。
用上述压延工艺获得的软质材料，其横切面在电子显微镜下检验，观察到无机填料在树脂中分布比较均匀，作为防辐射材料，材料的均匀度是一个十分重要的指标。
亦可采用挤出工艺生产这种材料。在加工好的软质材料上，可再复合一层带有印刷图案的塑料薄膜，使材料更加美观，并能保护表面。还可以与天然或人造纤维织物复合，对材料进行增强和改性。
本发明具有以下特点：
1、采用的钡盐原料来源丰富，价格低廉，用钡盐代替或部分代替紧缺而价高的铅粉或铅化合物，可使原料成本降低30-50%。
2、该材料比重较高，树脂与填料均匀混合，同时具有优良的隔声、阻尼、防X射线和低能γ射线功能。
3、本发明制得的为软质材料，具有柔软与易剪裁的特性，加工十分方便，粘接、缝合、钉制均可。特别适用于制造各种软质隔声、防X射线和低能γ射线装置。
4、本发明制得的多功能材料，除具有隔声、阻尼、防X射线和低能Y射线外，其他方面性能，如物理力学性能、阻燃性能、老化性能等均能满足使用要求。
该材料可广泛用于工业、交通、民用等领域各种噪声、振动的治理。如机械设备、交通工具的减振降噪，管道隔声和车间、礼堂、剧场、住宅的噪声控制。在防X射线方面，该材料可用来制造各种工业和医用X射线机、雷达、电子束加工设备、现代科学仪器的辐射防护装置。如X线室墙壁、门、窗的屏蔽材料，各种防辐射软帘，防护罩等。
实施例一
原料重量组成比例如表1所示。
表1 原料重量组成比例
| 原料名称 | 重量组成比例 |
| PVC | 100 |
| DOP | 25 |
| DBP | 15 |
| TCP | 10 |
| 氧化铅粉 | 100 |
| 硫酸钡粉 | 250 |
| Al（OH)3 | 40 |
| 821偶联剂 | 5 |
| 石朋 | 0.5 |
根据捏合机的容积，首先称取一定量的树脂，再按表1比例称取事先磨细到200目的固体填料，依次投入捏合机中，最后加入各种液体助剂，搅拌同时升温，蒸气压力控制在2.5kg，时间40-60分钟，将物料转入密炼机中进行塑化，控制蒸气压力为5kg，时间6-10分钟，把密炼好的物料输送到二辊机中混炼，控制蒸气压力6-7kg，时间10-15分钟，成为塑化物料，然后送入压延机中，控制蒸气压力为8kg，根据需要调节辊距，即可得到不同厚度的片材。若压制成厚度为1mm的材料，其各项性能指标如表2所示。
表2 材料各项性能
| 材料性能 | 测量值 | |
| 面密度(kg/m2) | 30 | |
| 抗张强度 (kg/m2) | 纵向 | 100 |
| 横向 | 87 | |
| 伸长率（%） | 纵向 | 180 |
| 横向 | 163 | |
| 铅当量（mmPb） | 0.49（2.8mm厚） | |
| 隔声指数（分贝） | 22 | |
| 耐燃性（氧指数） | 27 | |
实施例二
采用与实施例一相同的工艺，以直径为01-05mm的铅纤维代替表1中的氧化铅粉，可以得到隔声指数为22分贝的隔声、阻尼材料。
Claims (5)
1、隔声、阻尼、防输射材料的制造方法，其特征在于下面的配方：
A、原料中的树脂是聚氯乙烯;钡是硝酸钡、碳酸钡或重晶石粉;铅是铅粉或铅化合物;增塑剂是DOP、DBP;阻燃剂是Al（OH）3、Mg（OH）2、TCP、Sb2O3、氯化石蜡等中的一种或二种。
B、上述材料重量比树脂为100、硝酸钡、碳酸钡或重晶石粉是10-1000、铅或铅化合物是1000-10，其他助剂适量;
2、按照权利要求1所述的隔声、阻尼、防辐射材料的制造方法，其特征在于将原料中不加铅粉或铅化合物，也可制成具有隔声、阻尼、防X射线和低能γ射线的材料。
3、按照权利要求1所述的隔声、阻尼、防辐射材料的制造方法，其特征在于原料中可增加适量的稳定剂、着色剂、润滑剂制成具有隔声、阻尼、防X射线和低能γ射线性能的软质材料。