CN85102535A - A kind of ceramic brick (plate) and manufacture method thereof - Google Patents
A kind of ceramic brick (plate) and manufacture method thereof Download PDFInfo
- Publication number
- CN85102535A CN85102535A CN85102535.8A CN85102535A CN85102535A CN 85102535 A CN85102535 A CN 85102535A CN 85102535 A CN85102535 A CN 85102535A CN 85102535 A CN85102535 A CN 85102535A
- Authority
- CN
- China
- Prior art keywords
- mud
- plate
- decorative pattern
- clay
- manufacture method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
This ceramic brick (plate) is the building surface finishing material of a kind of entire body Chromatic color decorative pattern of being fired into clay.It is with two or more different colours clays refining mud separately respectively, utilizes the character of its plasticity-rheology, with the mud of different chromaticness through mixing gentle drawing, the cutting extruding forms in conjunction with firmly, is of close texture, inside and outside all dapple pug, through cutting extruding once more, make it become flaky mud band or clod, after a little drying, can be made into the base substrate of different shape and size,, make its surfacing smooth through scraped finish processing, decorative pattern is clear, forms through calcination again.
Description
The building and ornament materials ceramic brick (plate) and its manufacture method of a kind of entire body Chromatic color decorative pattern that is fired into the different colours clay.
With the clay is raw material, and the building and ornament materials ornamental brick or the plate of production are known, and extensively adopts.Manufacture method commonly used is with a kind of clay refining mud, shaping, becomes its surperficial decorative pattern or pattern with glaze variable color, colored drawing, subsides impression, drying after calcination form.
In order to enlarge the scope of building and ornament materials, increase new variety, the clay that has proposed with different colours is a raw material, produces new ceramic brick (plate) and its manufacture method.
This new ceramic brick (plate) can be made various shape and size; Inside and outside Chromatic color decorative patterns all, its decorative pattern is except that utilizing the plasticity-properties of flow forms naturally, can also be artificial abundant, as make the decorative pattern or the pattern of various forms such as cloud form, water corrugated, scenery with hills and waters shape and animal.Clear paint can be gone up in the surface, also can not go up any coating, and the basis that all can present nature is color patterned, but the person of coating, its surface is bright more attractive in appearance, the ceramic brick of coating He not coating (plate), the function that all possesses building and ornament materials according to the purposes difference, can be selected arbitrarily.
The manufacture method of this ceramic brick (plate), be to be raw material with two or more different colours or the clay that adds pigment, the ball milling powdered, add water respectively according to its humidity difference, refine mud separately, utilize the plasticity-rheological property of mud, the mud of different chromaticness, mix gentle drawing, it is firm that cutting is squeezed into combination each other, is of close texture, and entire body has this color patterned pug of nature.Through cutting extruding once more, form flaky mud band or clod, after a little drying, with mould or other method, but wet pressing, dry-pressing or extrusion molding, make base substrate, behind base substrate different moisture phase or complete drying, adopt the machinery knives striking or grind its surface (also can after calcination, grind), remove muddy clay seam, make its surfacing smooth, decorative pattern is clear, after calcination form.
This manufacture method also is applicable to the clay goods of the workmanship and other type that are raw material production, as imitative stone carving, jade carving etc.
Ceramic brick (plate) with this method production, all characteristics that not only kept ornamental brick (plate), and it is true to nature naturally to have a decorative pattern, inside and outside the characteristics that all have, what also have ceramic causes thin property and hardness, the class chrysodor is the same, even surface fracture, still have new decorative pattern to occur, can not influence the effect of decoration, also have advantages such as low cost of manufacture simultaneously.
Such as being raw material, produce 20 centimetres of a kind of length of sides, thick 5 centimetres square Tao Yu plate with white high Cen soil and red clay.Its method is with two kinds of clays difference ball milling powdereds.Add water respectively according to its humidity difference, refine mud separately, two kinds of mud are mixed gentle drawing, cutting is squeezed in conjunction with firm pug.Be squeezed into sheet mud band through secondary cut, when treating moisture evaporation to water content 10% left and right sides, make base substrate with wooden model, the oven dry back grinds its surface with general whetstone, removes the clay seam of external haze.Present clear being as the criterion with decorative pattern.Not any coating on the surface.Send in the brickkiln and form through calcination.
Claims (7)
1, the building and ornament materials ceramic brick (plate) that is fired into the different colours clay is characterized in that inside and outside system body all has the chromatic pattern of true qualities.
2, ceramic brick as claimed in claim 1 (plate), the sports lottery ticket that it is characterized in that uniting is color patterned except that forming with the plasticity-rheology, and all right artificial is abundant, as the decorative pattern or the pattern of forms such as the side's of making shape, water corrugated, scenery with hills and waters shape and animals and plants.
3, ceramic brick as claimed in claim 1 or 2 (plate) is characterized in that the surface can coat, but the person of coating, its surface is light more.
4, fire inside and outside all manufacture method of Chromatic color decorative pattern building and ornament materials ceramic bricks (plate) with the different colours clay, it is characterized in that refining mud separately by the clay of two or more different colours or adding pigment, the mud of different chromaticness is mixed into entire body this color patterned pug is arranged, make base substrate, scrape, grind its surface, make its smooth smooth, decorative pattern is clear, form through calcination.
5, manufacture method as claimed in claim 4 is characterized in that utilizing the plasticity-rheological characteristics of mud, with the mud of different chromaticness, gentlely draws, cuts extruding through mixing, and this color patterned pug is all arranged inside and outside the formation.
6, manufacture method as claimed in claim 4 is characterized in that behind base substrate different humidity stage or complete drying, and troubling layer is removed in striking or grind its surface (also can grind) after burning, makes that its surfacing is smooth, decorative pattern is clear.
7, manufacture method as claimed in claim 4 also is applicable to the clay goods of the workmanship and other type that are raw material production.