CN209585531U - A kind of Environment-friendlywear-resistant wear-resistant UV terrace - Google Patents
A kind of Environment-friendlywear-resistant wear-resistant UV terrace Download PDFInfo
- Publication number
- CN209585531U CN209585531U CN201920185018.1U CN201920185018U CN209585531U CN 209585531 U CN209585531 U CN 209585531U CN 201920185018 U CN201920185018 U CN 201920185018U CN 209585531 U CN209585531 U CN 209585531U
- Authority
- CN
- China
- Prior art keywords
- aqueous
- resistant
- free
- colored paint
- terrace
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model relates to building coating technical fields, a kind of Environment-friendlywear-resistant wear-resistant UV terrace is specifically disclosed, including concrete substrate layer, in the compound water-base epoxy prime coat of concrete substrate layer surface, in the solvent-free UV floating coat of the water-base epoxy primer coat surface compound one, in the aqueous UV background color layer of the solvent-free UV floating coat surface recombination one, in the aqueous UV colored paint pattern layer of the aqueous UV background color layer surface compound one, in the aqueous UV clear overcoat of the aqueous UV colored paint pattern layer surface compound one.The utility model solves the problems, such as traditional terrace long construction period, and terrace comes into operation immediately after completion, the N-free diet method time, and finished product surface hardness with higher and wear-resisting property, solvent-free and water-based material, low VOC content, safety and environmental protection.
Description
Technical field
The utility model relates to building coating technical fields, specifically, being a kind of Environment-friendlywear-resistant wear-resistant UV terrace.
Background technique
Terrace refer to using certain material and technique to original ground carry out construction processing and show it is certain decorative and
Functional ground.Common terrace type has epoxy self-leveling floor, diamond dust abrasion-proof terrace, epoxy terrazzo terrace, water
Mud base terrazzo, epoxy color sand terrace, epoxy antistatic floor, the anti-skidding terrace of epoxy, polyurea anti-corrosion terrace, silicon PU terrace and mixed
Solidifying soil curing sealing agent terrace etc..Logical terrace often uses room temperature curing type epoxy or polyurethane floor, long construction period, and completes
Also need the reaction time for waiting 5-7 days that could use terrace afterwards, terrace can not come into operation immediately after completion.
Summary of the invention
The purpose of this utility model is to provide a kind of Environment-friendlywear-resistant wear-resistant UV terrace.
To achieve the above object, the technical scheme adopted by the utility model is that:
A kind of Environment-friendlywear-resistant wear-resistant UV terrace, including concrete substrate layer (1), in one water of concrete substrate layer (1) surface recombination
Property epoxy primer layer (2), in the solvent-free UV floating coat (3) of the water-base epoxy prime coat (2) compound one, in the solvent-free UV
The aqueous UV background color layer (4) of floating coat (3) surface recombination one, in the aqueous UV colored paint of aqueous UV background color layer (4) surface recombination one
Pattern layer (5), in the aqueous UV clear overcoat (6) of aqueous UV colored paint pattern layer (5) surface recombination one；The water-base epoxy
Prime coat (2) is water-base epoxy priming paint, with a thickness of 0.5~2mm, dosage 0.1-0.3kg/m2；It is applied in the solvent-free UV
Layer (3) is solvent-free UV coating, with a thickness of 0.3-0.5mm, dosage 0.3-0.6Kg/m2；The aqueous UV background color layer (4)
For aqueous UV colored paint, with a thickness of 15-30 μm, dosage 0.1-0.2Kg/m2；The aqueous UV colored paint pattern layer (5) is aqueous
UV colored paint, by way of Freehandhand-drawing, silk-screen printing or spraying by aqueous UV colored paint material construct in aqueous UV background color layer (4) it
On, form pattern, the aqueous UV colored paint pattern layer (5) with a thickness of 15-40 μm, dosage 0.1-0.3Kg/m2；The water
Property UV clear overcoat (6) be aqueous UV clear dope, 15-30 μm of thickness, dosage 0.1-0.2kg/m2。
In above-mentioned Environment-friendlywear-resistant wear-resistant UV terrace, as a preferred embodiment, the water-base epoxy prime coat (2) with a thickness of
1mm, dosage 0.2kg/m2。
In above-mentioned Environment-friendlywear-resistant wear-resistant UV terrace, as a preferred embodiment, the solvent-free UV floating coat (3) with a thickness of
0.4mm, dosage 0.5Kg/m2；Blade coating is then carried out using hand push uv equipment on the surface of water-base epoxy prime coat (2)
Ultraviolet light solidification.
In above-mentioned Environment-friendlywear-resistant wear-resistant UV terrace, as a preferred embodiment, the aqueous UV background color layer (4) with a thickness of 20
μm, dosage 0.2Kg/m2；Roller coating is then carried out using hand push uv equipment purple on the surface of solvent-free UV floating coat (3)
Outer photocuring.
In above-mentioned Environment-friendlywear-resistant wear-resistant UV terrace, as a preferred embodiment, the thickness of the aqueous UV colored paint pattern layer (5)
It is 30 μm, dosage 0.2Kg/m2；After forming pattern, ultraviolet light solidification is carried out using hand push uv equipment.
In above-mentioned Environment-friendlywear-resistant wear-resistant UV terrace, as a preferred embodiment, the thickness of the aqueous UV clear overcoat (6)
It is 20 μm, dosage 0.2kg/m2；Roller coating is carried out purple on aqueous UV colored paint pattern layer (5) using hand push uv equipment
Outer photocuring.
Aiming at the problem that prior art is unable to satisfy terrace rapid construction requirement, the utility model is aqueous by being arranged
Epoxy primer layer, solvent-free UV floating coat, aqueous UV background color layer, aqueous UV colored paint pattern layer, aqueous UV clear overcoat, it is aqueous
Epoxy primer layer can permeate in concrete, sealed porosity, improve concrete strength and improve coating to the attached of concrete simultaneously
Put forth effort；Basal plane flatness and coating entire compression intensity can be improved in solvent-free UV floating coat；Aqueous UV background color layer can increase
Additive color coloured silk improves decorative effect；Aqueous UV colored paint pattern layer can go to form a variety of different patterns, make terrace rich in design, more
Add beauty；Aqueous UV clear overcoat can be improved that terrace is wear-resisting and chemical resistance.The utility model is by being arranged aqueous ring
Oxygen prime coat, solvent-free UV floating coat, aqueous UV background color layer, aqueous UV colored paint pattern layer, aqueous UV clear overcoat effectively solve
Determined traditional terrace long construction period the problem of, terrace comes into operation immediately after completion, the N-free diet method time, and finished product have compared with
High surface hardness and wear-resisting property, solvent-free and water-based material, low VOC content, safety and environmental protection.
Detailed description of the invention
Attached drawing 1 is the utility model Environment-friendlywear-resistant wear-resistant UV floor structure schematic diagram.
Attached drawing 2 is the utility model Environment-friendlywear-resistant wear-resistant UV terrace surface schematic diagram.
Specific embodiment
The following further describes the utility model with specific embodiments.It should be understood that these embodiments are merely to illustrate
The utility model rather than limitation the scope of the utility model.In addition, it should also be understood that, having read in the utility model record
After appearance, those skilled in the art can be made various changes or modifications the utility model, and such equivalent forms equally fall within this
Apply for the appended claims limited range.
Appended drawing reference involved in attached drawing and component part are as follows:
1. the solvent-free UV floating coat of 2. water-base epoxy prime coat of concrete substrate layer 3.
4. the aqueous 5. aqueous UV clear overcoat of aqueous UV colored paint pattern layer 6. of UV background color layer
- Fig. 2 referring to Figure 1.Attached drawing 1 is the utility model Environment-friendlywear-resistant wear-resistant UV floor structure schematic diagram, and attached drawing 2 is that this is practical
The wear-resisting UV terrace surface schematic diagram of novel environment friendly.
A kind of Environment-friendlywear-resistant wear-resistant UV terrace, including concrete substrate layer 1, the concrete substrate layer is those skilled in the art
Well known concrete floor base material, usual concrete, which refers to, makees cementitious material, sand, masonry aggregate with cement；One is pressed with water
Certainty ratio cooperation, it is agitated obtained by cement concrete.In 1 surface recombination of concrete substrate layer, one water-base epoxy prime coat 2, institute
The water-base epoxy prime coat 2 stated is water-base epoxy priming paint, specifically, can use Jingde in the embodiments of the present invention
Town Zhan Tian ceramic coating Co., Ltd model ZeitlosTM- 112 water-base epoxy priming paint, it is whole to improve the utility model terrace
Body meets performance, that is, uses Jing Dezhen Zhan Tian ceramic coating Co., Ltd model ZeitlosTM- 112 water-base epoxy priming paint exists
The surface of concrete substrate layer is coated to obtain water-base epoxy prime coat 2.In the present invention, the water-base epoxy priming paint
Layer 2 with a thickness of 0.5~2mm, dosage 0.1-0.3kg/m2；It is preferred that the water-base epoxy prime coat 2 with a thickness of 1mm, use
Amount is 0.2kg/m2；2 roller coating of water-base epoxy prime coat permeates 0.5~2mm of concrete depth on substrate, and sealed porosity improves
Concrete strength improves coating to the adhesive force of concrete simultaneously.In the solvent-free UV of the water-base epoxy prime coat 2 compound one
Coating 3, the solvent-free UV floating coat 3 is solvent-free UV floating coat, can be with specifically, in the embodiments of the present invention
Using Jing Dezhen Zhan Tian ceramic coating Co., Ltd model UcurialTM- 825 solvent-free UV floating coat uses Jing Dezhen
Zhan Tian ceramic coating Co., Ltd model UcurialTM- 825 solvent-free UV floating coat is scratched in water-base epoxy prime coat 2
Then surface carries out ultra-violet curing, exposure energy 800-1000MJ/cm using hand push uv equipment2, obtain in solvent-free UV
Coating 3；The solvent-free UV floating coat 3 with a thickness of 0.3-0.5mm, dosage 0.3-0.6Kg/m2；It is preferred that described solvent-free
UV floating coat 3 with a thickness of 0.4mm, dosage 0.5Kg/m2.Solvent-free UV floating coat 3, which plays, improves basal plane flatness and painting
The effect of layer entire compression intensity.In the aqueous UV background color layer 4 of solvent-free 3 surface recombination of UV floating coat one, the aqueous UV
Background color layer 4 is aqueous UV colored paint, specifically, can use Jing Dezhen Zhan day ceramic coating in the embodiments of the present invention
Co., Ltd model UcurialTMThe aqueous UV colored paint of -831C uses Jing Dezhen Zhan Tian ceramic coating Co., Ltd model
For UcurialTMThe aqueous UV colored paint of -831C is in roller coating in the surface of solvent-free UV floating coat 3, the hand push after moisture volatilizees completely
Uv equipment carries out ultraviolet light solidification, exposure energy 500-900MJ/cm2, obtain aqueous UV background color layer 4；The aqueous bottom UV
Chromatograph 4 with a thickness of 15-30 μm, dosage 0.1-0.2Kg/m2；It is preferred that the aqueous UV background color layer 4 with a thickness of 20 μm, use
Amount is 0.2Kg/m2；Aqueous UV background color layer 4 can increase terrace color and improve decorative effect.In aqueous 4 table of UV background color layer
The aqueous UV colored paint pattern layer 5 in face compound one, the aqueous UV colored paint pattern layer 5 are aqueous UV colored paint, specifically, practical new at this
In the embodiment of type, Jing Dezhen Zhan Tian ceramic coating Co., Ltd model Ucurial can be usedTMThe aqueous UV color of -831C
Paint uses Jing Dezhen Zhan Tian ceramic coating Co., Ltd model UcurialTMThe aqueous UV colored paint of -831C passes through Freehandhand-drawing, silk
The diversified forms such as wire mark brush, spraying construct aqueous UV colored paint material on aqueous UV background color layer 4, form different patterns,
Hand push uv equipment carries out ultraviolet light solidification, exposure energy 500-900MJ/cm after moisture volatilizees completely2, obtain aqueous UV
Colored paint pattern layer 5；The property water UV colored paint pattern layer 5 with a thickness of 15-40 μm, dosage 0.1-0.3Kg/m2；It is preferred that described
Aqueous UV colored paint pattern layer 5 with a thickness of 30 μm, dosage 0.2Kg/m2；Aqueous UV colored paint pattern layer 5 can go to be formed it is various
Different patterns makes terrace rich in design, more beautiful.It is saturating in one aqueous UV of aqueous 5 surface recombination of UV colored paint pattern layer
Bright finishing coat 6；The aqueous UV clear overcoat 6 is the transparent overlay coating of aqueous UV, specifically, in the implementation of the utility model
In example, Jing Dezhen Zhan Tian ceramic coating Co., Ltd model Ucurial can be usedTMThe transparent cover of the aqueous UV of -835T applies
Material uses Jing Dezhen Zhan Tian ceramic coating Co., Ltd model UcurialTMThe transparent overlay coating of aqueous UV of -835T, roller
It is applied on aqueous UV colored paint pattern layer 5, hand push uv equipment carries out ultra-violet curing, exposure energy after moisture volatilizees completely
300-600MJ/cm2, obtain aqueous UV clear overcoat 6；15-30 μm of thickness of the aqueous UV clear overcoat 6, dosage are
0.1-0.2kg/m2；It is preferred that 20 μm of thickness of the aqueous UV clear overcoat 6, dosage 0.2kg/m2.The aqueous transparent cover of UV
Layer 6 plays the role of improving that terrace is wear-resisting and chemical resistance.
The above is only the preferred embodiment of the utility model, it is noted that for the common skill of the art
Art personnel can also make several improvement and supplement without departing from the principle of this utility model, these are improved and supplement
Also it should be regarded as the protection scope of the utility model.
Claims (6)
1. a kind of Environment-friendlywear-resistant wear-resistant UV terrace, including concrete substrate layer (1), which is characterized in that on concrete substrate layer (1) surface
Compound water-base epoxy prime coat (2), in the solvent-free UV floating coat (3) of water-base epoxy prime coat (2) surface recombination one, In
The aqueous UV background color layer (4) of solvent-free UV floating coat (3) surface recombination one, in aqueous UV background color layer (4) surface recombination
One aqueous UV colored paint pattern layer (5), in the aqueous UV clear overcoat (6) of aqueous UV colored paint pattern layer (5) surface recombination one；
The water-base epoxy prime coat (2) is water-base epoxy priming paint, with a thickness of 0.5~2mm, dosage 0.1-0.3kg/m2；It is described
Solvent-free UV floating coat (3) is solvent-free UV coating, with a thickness of 0.3-0.5mm, dosage 0.3-0.6Kg/m2；It is described aqueous
UV background color layer (4) is aqueous UV colored paint, with a thickness of 15-30 μm, dosage 0.1-0.2Kg/m2；The aqueous UV colored paint pattern
Layer (5) is aqueous UV colored paint, and aqueous UV colored paint material is constructed in the aqueous bottom UV by way of Freehandhand-drawing, silk-screen printing or spraying
On chromatograph (4), form pattern, the aqueous UV colored paint pattern layer (5) with a thickness of 15-40 μm, dosage 0.1-0.3Kg/
m2；The aqueous UV clear overcoat (6) be aqueous UV clear dope, 15-30 μm of thickness, dosage 0.1-0.2kg/m2。
2. Environment-friendlywear-resistant wear-resistant UV terrace according to claim 1, which is characterized in that the thickness of the water-base epoxy prime coat (2)
For 1mm, dosage 0.2kg/m2。
3. Environment-friendlywear-resistant wear-resistant UV terrace according to claim 1, which is characterized in that the thickness of the solvent-free UV floating coat (3)
For 0.4mm, dosage 0.5Kg/m2；Blade coating on the surface of water-base epoxy prime coat (2), then using hand push uv equipment into
The solidification of row ultraviolet light.
4. Environment-friendlywear-resistant wear-resistant UV terrace according to claim 1, which is characterized in that the aqueous UV background color layer (4) with a thickness of
20 μm, dosage 0.2Kg/m2；Roller coating is then carried out using hand push uv equipment on the surface of solvent-free UV floating coat (3)
Ultraviolet light solidification.
5. Environment-friendlywear-resistant wear-resistant UV terrace according to claim 1, which is characterized in that the thickness of the aqueous UV colored paint pattern layer (5)
Degree is 30 μm, dosage 0.2Kg/m2；After forming pattern, ultraviolet light solidification is carried out using hand push uv equipment.
6. Environment-friendlywear-resistant wear-resistant UV terrace according to claim 1, which is characterized in that the thickness of the aqueous UV clear overcoat (6)
Degree is 20 μm, dosage 0.2kg/m2；Roller coating is carried out on aqueous UV colored paint pattern layer (5) using hand push uv equipment
Ultraviolet light solidification.