CN209538592U - A kind of cork heating floor - Google Patents
A kind of cork heating floor Download PDFInfo
- Publication number
- CN209538592U CN209538592U CN201920055121.4U CN201920055121U CN209538592U CN 209538592 U CN209538592 U CN 209538592U CN 201920055121 U CN201920055121 U CN 201920055121U CN 209538592 U CN209538592 U CN 209538592U
- Authority
- CN
- China
- Prior art keywords
- layer
- cork
- spc
- substrate layer
- balance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of cork heating floor of the utility model, including wearing layer, decorative layer, balance layer, cork substrate layer, SPC substrate layer, cork balance layer；The wearing layer is tightly disposed in the top of decorative layer；The decorative layer is tightly disposed in the top of balance layer；The balance layer is tightly disposed in the top of cork substrate layer；The cork substrate layer is tightly disposed in the top of SPC substrate layer；The SPC substrate layer is tightly disposed in the top of cork balance layer.The program is combined together using the function of cork and the performance of SPC, reach that fire-proof and water-proof is moisture-proof, stability is high, good heat dissipation effect, mute noise reduction, saves forest, durable etc. meets the applicable characteristic of heating floor, family can not only be widely used in, and it may be also used in kindergarten, hotel, hospital, the public places such as market, theater, library, it is able to achieve Fast Installation simultaneously, improves installation effectiveness.
Description
Technical field:
The utility model relates to technical field of construction and decoration materials, and in particular to a kind of cork heating floor.
Background technique
The relatively other kinds of floor of cork flooring more artistry.Cork flooring can usually arrange in pairs or groups various figures
Case and color are important a ring in home decoration, and especially on those villas or luxurious house, the pattern color on floor is all
It combines together with other ornaments of house, house is allowed to seem more attractive neat in this way.Cork flooring is different according to the purpose used,
Collocation mode be also it is diversified, as the cork flooring on basketball court be because cork flooring it is flexible, safety and beauty
Sight can paint cork flooring miscellaneous pattern;And our general families are usually to fit up using cork flooring
House makes house more attractive comfortable;Cork flooring is also applied relatively more on kitchen floor, because cork flooring is in addition to having
Except the characteristics of elasticity, safety, there are also the functions of anti-skidding, anti-conduction.Cork flooring maintains more convenient, usual cork
Floor only need half a year or 1 year change a wax can, usually cleaning only need to be wiped clean with mop can, but cork finish
Unexpectedly attribute is wooden, is easy rotten, dilatancy etc. after water suction dampness in humidity and more water environments and is easy to happen.
Utility model content
The purpose of the utility model is to provide a kind of cork heating floors, using the function of cork in conjunction with the performance of SPC
Together, it can reach that fire-proof and water-proof is moisture-proof, stability is high, good heat dissipation effect, mute noise reduction, saves forest, is durable etc. full
The applicable characteristic of sufficient heating floor, can not only be widely used in family, and may be also used in kindergarten, hotel, hospital,
The public places such as market, theater, library, while it being able to achieve Fast Installation, improve installation effectiveness.
In order to solve the problems existing in background technology, the utility model uses following technical scheme:
A kind of cork heating floor, including wearing layer, decorative layer, balance layer, cork substrate layer, SPC substrate layer, cork are flat
Weigh layer；
The wearing layer is tightly disposed in the top of decorative layer；
The decorative layer is tightly disposed in the top of balance layer；
The balance layer is tightly disposed in the top of cork substrate layer；
The cork substrate layer is tightly disposed in the top of SPC substrate layer；
The SPC substrate layer is tightly disposed in the top of cork balance layer.
Further, the wearing layer 1 with a thickness of 0.01-2mm.
Further, decorative layer with a thickness of 0.03-5mm.
Further, balance layer with a thickness of 0.5-6mm.
Further, cork substrate layer with a thickness of 0.5-6mm.
Further, SPC substrate layer with a thickness of 1-20mm.
Further, cork balance layer with a thickness of 1-5mm.
Further, the decorative layer using pure solid wood dash board or aluminum oxide dipping decorative layer or PVC coloured silk film or
Scientific and technological wood skin.
Further, the balance layer is using medium and high density fibre panel or aluminium sheet or SPC plate.
Further, the SPC substrate layer is split into bayonet type notch, and two pieces of floors can be realized from the precision of specification
Between Fast Installation, the globality on ground can be enhanced.
It the advantages of the utility model and has the beneficial effect that:
1. a kind of cork heating floor, including it is wearing layer, decorative layer, balance layer, cork substrate layer, SPC substrate layer, soft
The wooden balance layer；The wearing layer is tightly disposed in the top of decorative layer；The decorative layer is tightly disposed in the top of balance layer；Institute
State the top that balance layer is tightly disposed in cork substrate layer；The cork substrate layer is tightly disposed in the top of SPC substrate layer；Institute
State the top that SPC substrate layer is tightly disposed in cork balance layer.The performance of the function of cork and SPC is incorporated in by the utility model
Together, can be made it is a can reach geothermal heating and be more applicable in, can reach that fire-proof and water-proof is moisture-proof, stability is high, heat dissipation effect
Good, mute noise reduction, saving forest, durable etc. meet the applicable characteristic of heating floor, can not only be widely used and be in
Front yard, and may be also used in kindergarten, hotel, hospital, the public places such as market, theater, library, while being able to achieve quick peace
Dress improves installation effectiveness.
Detailed description of the invention
Fig. 1 is the cork heating floor structural schematic diagram of the utility model.
Specific embodiment
The following will be combined with the drawings in the embodiments of the present invention, carries out the technical scheme in the embodiment of the utility model
Clearly and completely describe, it is clear that the described embodiments are only a part of the embodiments of the utility model, rather than whole
Embodiment.Based on the embodiments of the present invention, those of ordinary skill in the art are without making creative work
Every other embodiment obtained, fall within the protection scope of the utility model.
Embodiment 1 is described in conjunction with attached drawing 1.
A kind of cork heating floor of the utility model, including wearing layer 1, decorative layer 2, balance layer 3, cork substrate layer 4,
SPC substrate layer 5, cork balance layer 6；
The wearing layer 1 is tightly disposed in the top of decorative layer 2；
The decorative layer 2 is tightly disposed in the top of balance layer 3；
The balance layer 3 is tightly disposed in the top of cork substrate layer 4；
The cork substrate layer 4 is tightly disposed in the top of SPC substrate layer 5；
The SPC substrate layer 5 is tightly disposed in the top of cork balance layer 6.
Further, the wearing layer 1 with a thickness of 1mm.
Further, decorative layer with a thickness of 2mm.
Further, balance layer with a thickness of 3mm.
Further, cork substrate layer with a thickness of 2.5mm.
Further, SPC substrate layer with a thickness of 11mm.
Further, cork balance layer with a thickness of 3mm.
Further, the decorative layer using pure solid wood dash board or aluminum oxide dipping decorative layer or PVC coloured silk film or
Scientific and technological wood skin.
Further, the balance layer is using medium and high density fibre panel or aluminium sheet or SPC plate.
Further, the SPC substrate layer is split into bayonet type notch, and two pieces of floors can be realized from the precision of specification
Between Fast Installation, the globality on ground can be enhanced.
Further, the wearing layer 1, cork substrate layer 4, SPC substrate layer 5 have waterproof and dampproof anti abrasive spy
Point.
The decorative layer 2 have wood grain, stone pattern, parquets line decorative effect, can with pure solid wood dash board, three aoxidize two
Aluminium impregnates decorative layer, PVC coloured silk film, can also use scientific and technological wood skin, have the characteristic to economize on resources.
The balance layer 3 has the function of balance strength and sustained release internal stress, can use medium and high density fibre panel, aluminium
Plate, SPC plate and other wood materials；
The SPC substrate layer 5 can otch, bayonet type can be split into, and can realize two from the precision of specification
The globality on ground can be enhanced in Fast Installation between block floor.
The cork balance layer 6 have well balance internal stress, noise reduction, waterproof, anti-skidding, damping, increase feel, no
Characteristic easy to crack, free from environmental pollution.
In conjunction with Fig. 1 describe it is a kind of prepare the utility model the preparation method is as follows:
A kind of preparation method of cork heating floor, comprising the following steps:
S101: cork balance layer heat treatment；
Further,
The cork balance layer heat treatment is specifically: the heat treatment of cork balance layer is using density in the thin of 0.3kg/cm3
Particle cork sheet material, temperature control carries out thermal finalization processing in 100 DEG C of environment Celsius on hot press, play it can either
To the effect of balance internal stress, and enhancing floor comfortable foot feeling can be played, while people can also be reduced and walked and echoed on floor,
Play the role of mute noise reduction.
S102: the fixed thick sanding processing of cork balance；
Further,
Described determines the fixed thick sanding processing of cork balance layer: selection sand paper mesh number is the abrasive band progress sanding of 80 mesh, 180 mesh
Processing 2 times；Last time uses 180 mesh, and thickness error is strict controlled within ± 0.3mm, enables to floor integral thickness
Uniformity；
S103: cork substrate layer heat treatment；
Further,
The cork substrate layer heat treatment: using high density cork sheet of the density between 0.5kg/cm3, in temperature
Control carries out thermal finalization processing in 100 DEG C of environment Celsius.
Floor surface crushing resistance had not only been improved according to national sector standard regulation density, but also the work of balanced structure stress can be played
With；
S104: it forms SPC base blank flat: cork balance layer is successively led to SPC substrate layer, cork substrate layer, balance layer
It is compound to cross the progress of painting water-based glue；
Further,
Cork balance layer+SPC the substrate layer+cork substrate layer+balance layer+painting water-based glue carries out compound: referring to
By cork balance layer successively with SPC substrate layer, cork substrate layer, balance layer, glued with environment-protecting and non-poisonous water-borne polyurethane bond
It is compound to close progress short-cycle hot-pressing；
Double spread processing is carried out to SPC substrate layer, glue-spread control is more when will increase dry in every square metre of 200g
Between, degree of adhesion can be reduced by having lacked；Recombination time, temperature was controlled at 100 DEG C Celsius at 7 minutes, played compound, thermal finalization work
With formation SPC base blank flat；
The fixed thick sanding processing of S105:SPC base blank flat；
Further,
The fixed thick sanding processing of the SPC base blank flat refers to: first using 80 mesh abrasive bands board bottom face over the ground to SPC base blank flat
Carry out fixed thick sanding；
Fixed thick coarse sand is carried out to floor surface with 100 mesh, 180 mesh, 240 mesh abrasive bands respectively again；
Fixed thick washed ore is carried out with 320 mesh, 600 mesh abrasive bands respectively again.
S107: SPC base element plate is formed: SPC base blank flat is compound by applying water-based glue and decorative layer；Further,
Described is compound by applying water-based glue and decorative layer by SPC base blank flat: referring to SPC base blank flat and decoration
Layer, carrying out bonding with environment-protecting and non-poisonous water-borne polyurethane bond, to carry out short-cycle hot-pressing compound, recombination time at 6 minutes, temperature control
System can play the role of compound, thermal finalization at 100 DEG C Celsius, form SPC base element plate.
The fixed thick sanding processing of S108:SPC base element plate；
Further,
The fixed thick sanding processing of the SPC base element plate refers to: to SPC base element plate, first with 80 mesh abrasive bands, board bottom face is carried out over the ground
Fixed thickness sanding；
Fixed thick coarse sand is carried out to floor surface with 100 mesh, 180 mesh, 240 mesh abrasive bands respectively again；
Fixed thick washed ore is carried out with 320 mesh, 600 mesh abrasive bands respectively again.
S109: wear-resistant primer is applied, top coat layer forms cork heating floor.
Further,
The SPC base element plate applies wear-resistant primer top coat layer and refers to: using aqueous priming paint using roller coating or showering mode into
Row coating, will at least coat 3 times, each coated weight will be maintained at 35g/ ㎡ or more, can have the function that wear-resisting bottom；
It reuses aqueous finish paint to be coated using roller coating or showering mode, at least to coat 2 times, each coated weight will be protected
It holds more than 25g/ ㎡, have the function that surface abrasion resistance and improves glossiness.
Further,
The SPC substrate layer applies water-base cement: carrying out double spread processing to SPC substrate layer, glue-spread is controlled every
Within square metre 200g.The bonding force and the feature of environmental protection of different level, the environment-protecting and non-poisonous aqueous poly- ammonia of the utility model can be increased
Ester gum is bonded, and carries out double spread processing to SPC substrate layer, and glue-spread strict control guarantees that drying time will not be too long,
Degree of adhesion will not be reduced simultaneously；
Further, further includes:
S110: fluting slots to SPC base element plate: it is accurate to carry out bayonet type to the composite floor board for being painted with surface layer abrasion-proof paint
Slot treatment can realize Fast Installation between two pieces of floors from the precision of specification, the globality on ground can be enhanced, so as to
It is fast installed in realizing；Since SPC intensity is very big, belt speed when fluting must be controlled in 60m/min, and otherwise floor is easy to appear
Chipping, defect rate can be very high；
S111: test package: certified products inspection is carried out to the floor for ending notch, due to the natural different property on cork surface layer, is increased
Add assembly line hand to touch to examine, improves yield rate；
With carton and heat-sealing plastics package is carried out, since monolithic floor is heavier, every case packing the piece number is preferably not more than 7
Piece will cause personal injury when otherwise can exceed the normal load of people in the handling process；
A kind of generally speaking cork heating floor of the utility model, including wearing layer, decorative layer, balance layer, cork base
Material layer, SPC substrate layer, cork balance layer；The wearing layer is tightly disposed in the top of decorative layer；The decorative layer is closely arranged
In the top of balance layer；The balance layer is tightly disposed in the top of cork substrate layer；The cork substrate layer is tightly disposed in
The top of SPC substrate layer；The SPC substrate layer is tightly disposed in the top of cork balance layer.The utility model is by the function of cork
Can be combined together with the performance of SPC, become it is a can reach geothermal heating more be applicable in, it is moisture-proof, steady that fire-proof and water-proof can be reached
Qualitative height, good heat dissipation effect, mute noise reduction, saving forest, durable etc. meet the applicable characteristic of heating floor, can not only
It is widely used in family, and may be also used in kindergarten, hotel, hospital, the public places such as market, theater, library, together
When be able to achieve Fast Installation, improve installation effectiveness.
Embodiment 2 is described in conjunction with Fig. 1.
A kind of cork heating floor of the utility model, including wearing layer 1, decorative layer 2, balance layer 3, cork substrate layer 4,
SPC substrate layer 5, cork balance layer 6；
The wearing layer 1 is tightly disposed in the top of decorative layer 2；
The decorative layer 2 is tightly disposed in the top of balance layer 3；
The balance layer 3 is tightly disposed in the top of cork substrate layer 4；
The cork substrate layer 4 is tightly disposed in the top of SPC substrate layer 5；
The SPC substrate layer 5 is tightly disposed in the top of cork balance layer 6.
Further, the wearing layer 1 with a thickness of 2mm.
Further, decorative layer with a thickness of 5mm.
Further, balance layer with a thickness of 6mm.
Further, cork substrate layer with a thickness of 6mm.
Further, SPC substrate layer with a thickness of 20mm.
Further, cork balance layer with a thickness of 5mm.
Further, the decorative layer using pure solid wood dash board or aluminum oxide dipping decorative layer or PVC coloured silk film or
Scientific and technological wood skin.
Further, the balance layer is using medium and high density fibre panel or aluminium sheet or SPC plate.
Further, the SPC substrate layer is split into bayonet type notch, and two pieces of floors can be realized from the precision of specification
Between Fast Installation, the globality on ground can be enhanced.
Further, the wearing layer 1, cork substrate layer 4, SPC substrate layer 5 have waterproof and dampproof anti abrasive spy
Point.
The decorative layer 2 have wood grain, stone pattern, parquets line decorative effect, can with pure solid wood dash board, three aoxidize two
Aluminium impregnates decorative layer, PVC coloured silk film, can also use scientific and technological wood skin, have the characteristic to economize on resources.
The balance layer 3 has the function of balance strength and sustained release internal stress, can use medium and high density fibre panel, aluminium
Plate, SPC plate and other wood materials；
The SPC substrate layer 5 can otch, bayonet type can be split into, and can realize two from the precision of specification
The globality on ground can be enhanced in Fast Installation between block floor.
The cork balance layer 6 have well balance internal stress, noise reduction, waterproof, anti-skidding, damping, increase feel, no
Characteristic easy to crack, free from environmental pollution.
In conjunction with Fig. 1 describe it is a kind of prepare the utility model the preparation method is as follows:
A kind of preparation method of cork heating floor, comprising the following steps:
S101: cork balance layer heat treatment；
Further,
The cork balance layer heat treatment is specifically: the heat treatment of cork balance layer is using density between 0.32kg/cm3
Fine grained cork sheet material, on hot press temperature control in 130 DEG C of environment Celsius carry out thermal finalization processing, make it can
Enough play the role of balancing internal stress, and enhancing floor comfortable foot feeling can be played, while people can also be reduced and walked on floor
It echoes, plays the role of mute noise reduction.
S102: the fixed thick sanding processing of cork balance；
Further,
Described determines the fixed thick sanding processing of cork balance layer: selection sand paper mesh number is the abrasive band progress sand of 150 mesh, 180 mesh
Light processing 2 times；Last time uses 180 mesh, and thickness error is strict controlled within ﹢ 0.3mm, enables to floor integral thickness
Uniformity；
S103: cork substrate layer heat treatment；
Further,
The cork substrate layer heat treatment: using high density cork sheet of the density between 0.7kg/cm3, in temperature
Control carries out thermal finalization processing in 130 DEG C of environment Celsius.
Floor surface crushing resistance had not only been improved according to national sector standard regulation density, but also the work of balanced structure stress can be played
With；
S104: it forms SPC base blank flat: cork balance layer is successively led to SPC substrate layer, cork substrate layer, balance layer
It is compound to cross the progress of painting water-based glue；
Further,
Cork balance layer+SPC the substrate layer+cork substrate layer+balance layer+painting water-based glue carries out compound: referring to
By cork balance layer successively with SPC substrate layer, cork substrate layer, balance layer, glued with environment-protecting and non-poisonous water-borne polyurethane bond
It is compound to close progress short-cycle hot-pressing；
Double spread processing is carried out to SPC substrate layer, glue-spread control is more when will increase dry in every square metre of 220g
Between, degree of adhesion can be reduced by having lacked；Recombination time, temperature was controlled at 130 DEG C Celsius at 8 minutes, played compound, thermal finalization work
With formation SPC base blank flat；
The fixed thick sanding processing of S105:SPC base blank flat；
Further,
The fixed thick sanding processing of the SPC base blank flat refers to: first using 80 mesh abrasive bands board bottom face over the ground to SPC base blank flat
Carry out fixed thick sanding；
Fixed thick coarse sand is carried out to floor surface with 100 mesh, 180 mesh, 240 mesh abrasive bands respectively again；
Fixed thick washed ore is carried out with 320 mesh, 600 mesh abrasive bands respectively again.
S107: SPC base element plate is formed: SPC base blank flat is compound by applying water-based glue and decorative layer；Further,
Described is compound by applying water-based glue and decorative layer by SPC base blank flat: referring to SPC base blank flat and decoration
Layer, carrying out bonding with environment-protecting and non-poisonous water-borne polyurethane bond, to carry out short-cycle hot-pressing compound, recombination time at 8 minutes, temperature control
System can play the role of compound, thermal finalization at 130 DEG C Celsius, form SPC base element plate.
The fixed thick sanding processing of S108:SPC base element plate；
Further,
The fixed thick sanding processing of the SPC base element plate refers to: to SPC base element plate, first with 80 mesh abrasive bands, board bottom face is carried out over the ground
Fixed thickness sanding；
Fixed thick coarse sand is carried out to floor surface with 100 mesh, 180 mesh, 240 mesh abrasive bands respectively again；
Fixed thick washed ore is carried out with 320 mesh, 600 mesh abrasive bands respectively again.
S109: wear-resistant primer is applied, top coat layer forms cork heating floor.
Further,
The SPC base element plate applies wear-resistant primer top coat layer and refers to: using aqueous priming paint using roller coating or showering mode into
Row coating, will at least coat 3 times, each coated weight will be maintained at 35g/ ㎡ or more, can have the function that wear-resisting bottom；
It reuses aqueous finish paint to be coated using roller coating or showering mode, at least to coat 2 times, each coated weight will be protected
It holds more than 25g/ ㎡, have the function that surface abrasion resistance and improves glossiness.
Further,
The SPC substrate layer applies water-base cement: carrying out double spread processing to SPC substrate layer, glue-spread is controlled every
Within square metre 220g.The bonding force and the feature of environmental protection of different level, the environment-protecting and non-poisonous aqueous poly- ammonia of the utility model can be increased
Ester gum is bonded, and carries out double spread processing to SPC substrate layer, and glue-spread strict control guarantees that drying time will not be too long,
Degree of adhesion will not be reduced simultaneously；
Further, further includes:
S110: fluting slots to SPC base element plate: it is accurate to carry out bayonet type to the composite floor board for being painted with surface layer abrasion-proof paint
Slot treatment can realize Fast Installation between two pieces of floors from the precision of specification, the globality on ground can be enhanced, so as to
It is fast installed in realizing；Since SPC intensity is very big, belt speed when fluting must be controlled in 70m/min, and otherwise floor is easy to appear
Chipping, defect rate can be very high；
S111: test package: certified products inspection is carried out to the floor for ending notch, due to the natural different property on cork surface layer, is increased
Add assembly line hand to touch to examine, improves yield rate；
With carton and heat-sealing plastics package is carried out, since monolithic floor is heavier, every case packing the piece number is preferably not more than 7
Piece will cause personal injury when otherwise can exceed the normal load of people in the handling process；
A kind of generally speaking cork heating floor of the utility model, including wearing layer, decorative layer, balance layer, cork base
Material layer, SPC substrate layer, cork balance layer；The wearing layer is tightly disposed in the top of decorative layer；The decorative layer is closely arranged
In the top of balance layer；The balance layer is tightly disposed in the top of cork substrate layer；The cork substrate layer is tightly disposed in
The top of SPC substrate layer；The SPC substrate layer is tightly disposed in the top of cork balance layer.The utility model is by the function of cork
Can be combined together with the performance of SPC, become it is a can reach geothermal heating more be applicable in, it is moisture-proof, steady that fire-proof and water-proof can be reached
Qualitative height, good heat dissipation effect, mute noise reduction, saving forest, durable etc. meet the applicable characteristic of heating floor, can not only
It is widely used in family, and may be also used in kindergarten, hotel, hospital, the public places such as market, theater, library, together
When be able to achieve Fast Installation, improve installation effectiveness.
Embodiment 3 is described in conjunction with attached drawing 1.
A kind of cork heating floor of the utility model, including wearing layer 1, decorative layer 2, balance layer 3, cork substrate layer 4,
SPC substrate layer 5, cork balance layer 6；
The wearing layer 1 is tightly disposed in the top of decorative layer 2；
The decorative layer 2 is tightly disposed in the top of balance layer 3；
The balance layer 3 is tightly disposed in the top of cork substrate layer 4；
The cork substrate layer 4 is tightly disposed in the top of SPC substrate layer 5；
The SPC substrate layer 5 is tightly disposed in the top of cork balance layer 6.
Further, the wearing layer 1 with a thickness of 0.01mm.
Further, decorative layer with a thickness of 0.03mm.
Further, balance layer with a thickness of 0.5mm.
Further, cork substrate layer with a thickness of 0.5mm.
Further, SPC substrate layer with a thickness of 1mm.
Further, cork balance layer with a thickness of 1mm.
Further, the decorative layer using pure solid wood dash board or aluminum oxide dipping decorative layer or PVC coloured silk film or
Scientific and technological wood skin.
Further, the balance layer is using medium and high density fibre panel or aluminium sheet or SPC plate.
Further, the SPC substrate layer is split into bayonet type notch, and two pieces of floors can be realized from the precision of specification
Between Fast Installation, the globality on ground can be enhanced.
Further, the wearing layer 1, cork substrate layer 4, SPC substrate layer 5 have waterproof and dampproof anti abrasive spy
Point.
The decorative layer 2 have wood grain, stone pattern, parquets line decorative effect, can with pure solid wood dash board, three aoxidize two
Aluminium impregnates decorative layer, PVC coloured silk film, can also use scientific and technological wood skin, have the characteristic to economize on resources.
The balance layer 3 has the function of balance strength and sustained release internal stress, can use medium and high density fibre panel, aluminium
Plate, SPC plate and other wood materials；
The SPC substrate layer 5 can otch, bayonet type can be split into, and can realize two from the precision of specification
The globality on ground can be enhanced in Fast Installation between block floor.
The cork balance layer 6 have well balance internal stress, noise reduction, waterproof, anti-skidding, damping, increase feel, no
Characteristic easy to crack, free from environmental pollution.
In conjunction with Fig. 1 describe it is a kind of prepare the utility model the preparation method is as follows:
A kind of preparation method of cork heating floor, comprising the following steps:
S101: cork balance layer heat treatment；
Further,
The cork balance layer heat treatment is specifically: the heat treatment of cork balance layer uses density at thin of 0.25cm3
Grain cork sheet material, temperature control carries out thermal finalization processing in 50 DEG C of environment Celsius on hot press, play it can either
The effect of internal stress is balanced, and enhancing floor comfortable foot feeling can be played, while people can also be reduced and walked and echoed on floor, is risen
To the effect of mute noise reduction.
S102: the fixed thick sanding processing of cork balance；
Further,
Described determines the fixed thick sanding processing of cork balance layer: selection sand paper mesh number is the abrasive band progress sand of 110 mesh, 180 mesh
Light processing 2 times；Last time uses 180 mesh, and thickness error is strict controlled within ﹣ 0.3mm, enables to floor integral thickness
Uniformity；
S103: cork substrate layer heat treatment；
Further,
The described cork substrate layer heat treatment: using density 0.45kg/cm3 high density cork sheet, in temperature control
Make the progress thermal finalization processing in 50 DEG C of environment Celsius.
Floor surface crushing resistance had not only been improved according to national sector standard regulation density, but also the work of balanced structure stress can be played
With；
S104: it forms SPC base blank flat: cork balance layer is successively led to SPC substrate layer, cork substrate layer, balance layer
It is compound to cross the progress of painting water-based glue；
Further,
Cork balance layer+SPC the substrate layer+cork substrate layer+balance layer+painting water-based glue carries out compound: referring to
By cork balance layer successively with SPC substrate layer, cork substrate layer, balance layer, glued with environment-protecting and non-poisonous water-borne polyurethane bond
It is compound to close progress short-cycle hot-pressing；
Double spread processing is carried out to SPC substrate layer, glue-spread control is more when will increase dry in every square metre of 180g
Between, degree of adhesion can be reduced by having lacked；Recombination time, temperature was controlled at 50 DEG C Celsius at 5 minutes, played the role of compound, thermal finalization,
Form SPC base blank flat；
The fixed thick sanding processing of S105:SPC base blank flat；
Further,
The fixed thick sanding processing of the SPC base blank flat refers to: first using 80 mesh abrasive bands board bottom face over the ground to SPC base blank flat
Carry out fixed thick sanding；
Fixed thick coarse sand is carried out to floor surface with 100 mesh, 180 mesh, 240 mesh abrasive bands respectively again；
Fixed thick washed ore is carried out with 320 mesh, 600 mesh abrasive bands respectively again.
S107: SPC base element plate is formed: SPC base blank flat is compound by applying water-based glue and decorative layer；Further,
Described is compound by applying water-based glue and decorative layer by SPC base blank flat: referring to SPC base blank flat and decoration
Layer, carrying out bonding with environment-protecting and non-poisonous water-borne polyurethane bond, to carry out short-cycle hot-pressing compound, recombination time at 5 minutes, temperature control
System can play the role of compound, thermal finalization at 50 DEG C Celsius, form SPC base element plate.
The fixed thick sanding processing of S108:SPC base element plate；
Further,
The fixed thick sanding processing of the SPC base element plate refers to: to SPC base element plate, first with 80 mesh abrasive bands, board bottom face is carried out over the ground
Fixed thickness sanding；
Fixed thick coarse sand is carried out to floor surface with 100 mesh, 180 mesh, 240 mesh abrasive bands respectively again；
Fixed thick washed ore is carried out with 320 mesh, 600 mesh abrasive bands respectively again.
S109: wear-resistant primer is applied, top coat layer forms cork heating floor.
Further,
The SPC base element plate applies wear-resistant primer top coat layer and refers to: using aqueous priming paint using roller coating or showering mode into
Row coating, will at least coat 3 times, each coated weight will be maintained at 35g/ ㎡ or more, can have the function that wear-resisting bottom；
It reuses aqueous finish paint to be coated using roller coating or showering mode, at least to coat 2 times, each coated weight will be protected
It holds more than 25g/ ㎡, have the function that surface abrasion resistance and improves glossiness.
Further,
The SPC substrate layer applies water-base cement: carrying out double spread processing to SPC substrate layer, glue-spread is controlled every
Square metre 180g.The bonding force and the feature of environmental protection of different level, the environment-protecting and non-poisonous water-borne polyurethane bond of the utility model can be increased
It is bonded, double spread processing is carried out to SPC substrate layer, glue-spread strict control guarantees that drying time will not be too long, simultaneously
Degree of adhesion will not be reduced；
Further, further includes:
S110: fluting slots to SPC base element plate: it is accurate to carry out bayonet type to the composite floor board for being painted with surface layer abrasion-proof paint
Slot treatment can realize Fast Installation between two pieces of floors from the precision of specification, the globality on ground can be enhanced, so as to
It is fast installed in realizing；Since SPC intensity is very big, belt speed when fluting must be controlled in 50m/min, and otherwise floor is easy to appear
Chipping, defect rate can be very high；
S111: test package: certified products inspection is carried out to the floor for ending notch, due to the natural different property on cork surface layer, is increased
Add assembly line hand to touch to examine, improves yield rate；
With carton and heat-sealing plastics package is carried out, since monolithic floor is heavier, every case packing the piece number is preferably not more than 7
Piece will cause personal injury when otherwise can exceed the normal load of people in the handling process；
A kind of generally speaking cork heating floor of the utility model, including wearing layer, decorative layer, balance layer, cork base
Material layer, SPC substrate layer, cork balance layer；The wearing layer is tightly disposed in the top of decorative layer；The decorative layer is closely arranged
In the top of balance layer；The balance layer is tightly disposed in the top of cork substrate layer；The cork substrate layer is tightly disposed in
The top of SPC substrate layer；The SPC substrate layer is tightly disposed in the top of cork balance layer.The utility model is by the function of cork
Can be combined together with the performance of SPC, become it is a can reach geothermal heating more be applicable in, it is moisture-proof, steady that fire-proof and water-proof can be reached
Qualitative height, good heat dissipation effect, mute noise reduction, saving forest, durable etc. meet the applicable characteristic of heating floor, can not only
It is widely used in family, and may be also used in kindergarten, hotel, hospital, the public places such as market, theater, library, together
When be able to achieve Fast Installation, improve installation effectiveness.
In conclusion a kind of cork heating floor and its preparation method of the utility model, SPC substrate primary raw material
It is polyvinyl chloride and mountain flour, polyvinyl chloride is environment-protecting and non-poisonous renewable resource at normal temperature, and 0 formaldehyde of mountain flour is more environmentally friendly, production
Do not have to glue in the process, without harmful substances such as formaldehyde, benzene, will not cause harm to the human body.Can be effectively fire-retardant, fire-protection rating reaches
To B1 grades, fiery self-extinguishment is met, does not generate any toxic gas；Natural not afraid of water, waterproof, anti-mold effect are very good, toilet, kitchen
Room, balcony can use.Wood-based product is solved at all to rotten, expansion easy after water suction dampness in humidity and more water environments
The problem of deformation, can be used in the not applicable environment of classical wood millwork；Cork is to utilize to process cork oak bark again
Made of, physicochemical property is very unique, is made of cork parenchyma cell, is a kind of pure natural high molecular material, in microscope
Under, cork per cubic centimeter contains 40,000,000 cells, is full of air into the cell.With small, environmentally friendly, the light, density of deformation
Low, compressible, flexible, impermeability is strong, moisture-proof anticorrosive, sound insulation, insulating properties are strong, rub resistance, it is nonflammable, not will lead to allergy
A series of excellent physical properties such as reaction.The flooring material made using cork is stablized, is comfortable, environmental protection, energy conservation, meeting the mankind
The life demand of conservation of nature, health environment-friendly.On floor, similar product has excellent composite attribute.By the function of cork with
The performance of SPC substrate is combined together, and is made into B1 grades of fire prevention geothermal heating floors, is had the environmental protection of zero formaldehyde, B1 grades of fire prevention, is surpassed
The features such as strong stability, higher moisture resistance, preferable thermal diffusivity.It is swollen after heated to efficiently solve current wood geothermal floor
Bulging deformation is big, burst size of methanal is big, the deficiency of fire-proof and water-proof performance difference.
Claims (10)
1. a kind of cork heating floor, which is characterized in that including wearing layer, decorative layer, balance layer, cork substrate layer, SPC substrate
Layer, cork balance layer；
The wearing layer is tightly disposed in the top of decorative layer；
The decorative layer is tightly disposed in the top of balance layer；
The balance layer is tightly disposed in the top of cork substrate layer；
The cork substrate layer is tightly disposed in the top of SPC substrate layer；
The SPC substrate layer is tightly disposed in the top of cork balance layer.
2. cork heating floor as described in claim 1, which is characterized in that
The wearing layer with a thickness of 0.01-2mm.
3. cork heating floor as described in claim 1, which is characterized in that
The decorative layer with a thickness of 0.03-5mm.
4. cork heating floor as described in claim 1, which is characterized in that
The balance layer with a thickness of 0.5-6mm.
5. cork heating floor as described in claim 1, which is characterized in that
The cork substrate layer with a thickness of 0.5-6mm.
6. cork heating floor as described in claim 1, which is characterized in that
The SPC substrate layer with a thickness of 1-20mm.
7. cork heating floor as described in claim 1, which is characterized in that
The cork balance layer with a thickness of 1-5mm.
8. cork heating floor as described in claim 1, which is characterized in that
The decorative layer is using pure solid wood dash board or aluminum oxide dipping decorative layer or PVC coloured silk film or wood skin.
9. cork heating floor as described in claim 1, which is characterized in that
The balance layer is using medium and high density fibre panel or aluminium sheet or SPC plate.
10. cork heating floor as described in claim 1, which is characterized in that
The SPC substrate layer is split into the processing of bayonet type notch.