CN207700519U - A kind of non-ignitable complex shingle panel of A grades for wall decoration - Google Patents
A kind of non-ignitable complex shingle panel of A grades for wall decoration Download PDFInfo
- Publication number
- CN207700519U CN207700519U CN201721930075.5U CN201721930075U CN207700519U CN 207700519 U CN207700519 U CN 207700519U CN 201721930075 U CN201721930075 U CN 201721930075U CN 207700519 U CN207700519 U CN 207700519U
- Authority
- CN
- China
- Prior art keywords
- plate
- resistance
- magnesium
- film
- sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a kind of non-ignitable complex shingle panels of A grades for wall decoration, it includes the black substrate of resistance to plate of magnesium-based, the black thereon of resistance to plate of magnesium-based is compounded with the sheet-metal layers with wear-resisting permanent oil rub resistance function by self-adhesion pulp layer, and the sheet-metal layers outer surface is coated with, the protective layer made of fluorine carbon roller coating weather-resisant paint or polyester paint or PVC film or PP film preparations;Organic polymer infiltration sealing primary coat repairing and polishing layer of paste is provided below in the black substrate of resistance to plate of magnesium-based, and the organic polymer infiltration sealing primary coat repairing and polishing layer of paste is compounded with the anti-oxidation anti-corrosion function, decorative plies made of metal aluminum sheet film or stainless steel plate or PVC film or PP film preparations below by heat molten type irreversible reaction adhesive.
Description
Technical field
The utility model belongs to building wall board apparatus field, and in particular to a kind of A grades for wall decoration are non-ignitable compound
Shingle nail.
Background technology
Traditional decorative board for wall probably has following five type:
(1) Thistle board:First, common Thistle board belongs to non-decorative plank, is by two layers of ox-hide folder
Core gypsum and it is manufactured, two layers of brown paper of surface and bottom surface are all non-watertight bubbles, once brown paper is wet by bubble, paper
Plasterboard will lose the support function of plate, to cause collapsing for wall, secondly, the fire protecting performance of Thistle board and fire resisting
The limit is not high, once wall, by fire, wall will be split by thermal-flame is boiled, wall excessive fire be formed, to cause people
Body injure, finally, Thistle board be mounted to after wall will also pass through batch ash, polishing, mend ash, brush primary coat, brush finish apply (or paste wall
Paper etc.) a variety of complicated processes, construction site airborne dust is serious, pollutes air, and construction personnel is easy to get professional breathing problem.
(2) calcium silicate cement plate:First, this calcium silicate cement plate also belongs to non-decorative plank, produces big when plank
Amount uses the cement of not environment protecting and power-saving as main raw material(s), and to be the high energy consumption to be eliminated on the current earth build cement
The calcium silicate cement plate of material product, many low and middle-ends also added a large amount of asbestos, easily cause the wound to the mankind and to environment
Evil;Secondly, calcium silicate cement plate does not have decorative cover, is also needed after forming wall with it by batch ash, polishing, mends ash, brush
Primary coat, brush finish apply complicated processes such as (or wallpapers etc.), and construction site airborne dust is serious, pollute air, construction personnel must be with mouth
Cover is constructed, the disease in terms of the respiratory tract that is equally easy to get, to cause the actual bodily harm to construction personnel;Finally, calcium silicate cement
Fire protecting performance and the fire endurance of wallboard nor very 800 DEG C high, will high temperature is boiled splits, wall excessive fire is formed, to cause
Injury to human body;
(3) composited aluminum and plastic decking:First, do not have to although aluminium-plastic panel belongs to decorative kind wallboard, when decoration uses using batch ash,
Complicated processes such as ash, brush primary coat, brush finish painting (or wallpaper etc.) are mended in polishing, but sandwich material is that PVC plastic is met among it
A large amount of cigarette poison can be discharged when fire, this is also exactly the main original that plastic-aluminum combined wallboard is gradually eliminated by social building material industry
Cause, the PVC plastic core material among followed by plastic-aluminum combined shingle nail are difficult voluntarily to degrade in the Nature, upper layer and lower layer decorative cover
Aluminium foil is difficult to cut separation again in recycling, is recycled again, which has been unable to meet the standard requirement of green building material, answers
It is classified as obsolete product;
(4) various metal class decorative panels:Metal class shingle nail currently on the market, still from weight either from cost
On cannot all meet world's green, environmental protection, energy-efficient demand for development.Such as the first kind:Al-Zn coated steel;Second class:Galvanized steel
Plate;Third class:General steel plate;4th class:Stainless steel plate etc. causes installation keel excessive, forms high cost all because weight is too heavy
Cost, the power that is impacted is not strong, and dell is formed after shock, sound " absolutely empty to make a sound " after percussion, forms noise.
(5) common glass magnesium board and other complex class wallboards:First, the white glass magnesium board of generally existing returns halogen phenomenon in the market
Seriously, plank once makes moist and returns halogen, and the disengaging that will form face sheet material decoration falls off, moldy metamorphism, and many in the market
Compound wall covering is all such as honeycomb composite panel made of polyurethane glue cold pressing, suffers from different product qualities
Defect or be that fire-protection rating is A grades inadequate;It is that fire endurance is too low, is no more than 1000 DEG C or more, meets with open fire burning,
Meet with high temperature fission excessive fire, object of hurting sb.'s feelings;It is to meet with open fire burning release cigarette poison, the person is damaged;It is not
Environmentally protective, not energy-efficient emission reduction is unable to cycling and reutilization, and abandonment when not used pollutes the earth, forms a large amount of building rubbish
Rubbish causes environmental injury.
Utility model content
The purpose of this utility model is in view of the above shortcomings of the prior art and provides a kind of A grades for wall decoration not
Fire complex shingle panel.
What the purpose of this utility model was realized in:A kind of non-ignitable complex shingle panel of A grades for wall decoration, it is wrapped
The black substrate of resistance to plate of magnesium-based is included, the black thereon of resistance to plate of magnesium-based is compounded with by self-adhesion pulp layer with wear-resisting permanent oil rub resistance
The sheet-metal layers of function, the sheet-metal layers outer surface are coated with, by fluorine carbon roller coating weather-resisant paint or polyester paint or PVC film or PP
Protective layer made of film preparation;Organic polymer infiltration sealing primary coat repairing and polishing is provided below in the black substrate of resistance to plate of magnesium-based
Layer of paste, the organic polymer infiltration sealing primary coat repairing and polishing layer of paste are compound below by heat molten type irreversible reaction adhesive
There is with the anti-oxidation anti-corrosion function, decorative panel made of metal aluminum sheet film or stainless steel plate or PVC film or PP film preparations
Layer.
The principles of the present invention are:The utility model wall decoration composite plate is for solving on today's society in the market
All kinds of decorative panel fire-protection ratings are low, and most of decorative panels are all B1 grades of flame-proof sheet materials, although and a other A1 grades of decorative panels can reach
It is non-ignitable to A grades, but its weight is very heavy, such as marble, granite, glass, artificial stone, ceramic wafer, calcium silicate board etc., this patent
The basic principle of product seeks to overcome the defect of various planks, and development & production comes out one kind and not only having contained architectural surface but also collected fire prevention
It does not burn, waterproof, the anti-plague of insects, meet with high temperature and burn and do not generate the fire endurance of cigarette poison up to 1 hour or more, refractory temperature is up to 1183
The high fire protecting performance decoration composite plate of degree.The generation of its high fire protecting performance of A1 grades is mainly that our black resistance to plate of inorganic magnesium-based exists
When production other than traditional magnesia, we be added to sulphur in formula with magnesium and mountain flour and flyash and active modifier and
Production, not only image-stone material is the same does not burn for it, but also has more high refractory temperature than stone material, not up to 1183 degree high temperature burnings
It burning and does not split to burn and do not fry.Secondly when the black resistance to plate of magnesium-based is combined into this patented product, and by the black self-adhesion of the resistance to plate slurry of magnesium-based with
Organic type high molecular fire retardant type infiltration wash coats blend, then by the heat molten type irreversible reaction adhesive of flame-retardant nature with
It is cold-pressed to apply on another side again after being bonded again after metal aluminum sheet or stainless steel plate rolling with anti-oxidation anti-corrosion function and load onto
Flame retardant type contains after anticorrosive tension back stretching linging applies and is coated with permanent oil rub resistance fluorine coating aluminium sheet or stainless steel plate on compound,
Finally it is combined into patented product wall decoration complex plate thus.
The utility model has the beneficial effects that:(1) superior performance in terms of fire protecting performance and fire endurance:Due to this patent
The center base substrate of wall surface composite board product is using inorganic A1 grades of the independent research non-ignitable black resistance to plates of magnesium-based of fire prevention
Core layer, very high do not burn up to 1180 DEG C of this core surfaces fire endurance do not crack, actually most prevent fires currently on the market
The high fire resisting fire-proof wall of performance, can protect personal safety well when building suffers from fire, be stayed enough enough to people
More escape times.
(2) function admirable in terms of working procedure:Do not have to use traditional finishing mode again in engineering site:Batch ash,
Polishing mends ash, polishes again, complicated process such as brushing seal coat, brushing finish paint (or wallpaper), simplifies, greatly carries
The high construction efficiency of engineering site, greatly improves construction speed, and kept away the dust pollution of building-site, not in work
Journey scene generates a large amount of construction and decoration rubbish, and effectively energy saving, section resource saves a large amount of human and material resources, financial resources.
(3) advantage protrudes in terms of environmental protection and energy saving cycling and reutilization:Due to the intermediate base core of this wall decoration composite plate
Material is that purely inorganic raw material produce, along with incrustation has the aluminium sheet or stainless steel plate that permanent oil resistant pollutes wear-resisting flower,
For product service life up to 50 years or more, and outside the life cycle of entire product, this patented product can be in the Nature certainly
Row decomposes degradation, and being dismounted for multiple times be recycled for multiple times, it is real to belong to that real green energy conservation is recyclable to recycle building material product.
(4) feature is superior in terms of the poison of resistance to cigarette:Since this patent wall decoration composite plate is kept shortly except decoration performance,
The security performance of the wall decoration composite plate also greatly improved has because it not will produce cigarette poison when meeting with fire disaster
The safety for protecting people of effect.
(5) function admirable in terms of waterproof and dampproof ant prevention:Since the main base material of this patent wall decoration composite plate is to adopt
With the black resistance to board core material of inorganic magnesium-based, and this core material energy bubble has magnesia in 100 days without cracking without dusting, and in main material, pole
Have termite-proof waterproof and dampproof equal excellent performances.
(6) service life with overlength in terms of life of product:This patent wall decoration composite plate is due to main core material
The black resistance to plate of magnesium-based is main material, adds the adhesive used the black tool of resistance to plate of magnesium-based for heat molten type irreversible reaction adhesive again
There is the service life for surpassing 50 years, so the patent wall decoration composite plate produced therefrom similarly uses the longevity with overlength
Life.
(7) advantages in terms of voluntarily decomposing degradation and preserving our planet:Since this patent wall decoration composite plate is by magnesium
Ji Heinai plate main core materials are formed with the irreversible adhesive of environment-friendly hot-melt type and the black slurry compositions of resistance to self-adhesion of magnesium-based, and main material magnesium-based is black
Resistance to plate can voluntarily decompose degradation after the service life by more than 50 years in large nature, can to reduce the injury to the earth
Effective protection earth resource and environment.
Description of the drawings
Fig. 1 is the structural schematic diagram of the utility model.
In figure:1, the black substrate of resistance to plate of magnesium-based;2, self-adhesion pulp layer;3, sheet-metal layers;4, protective layer;5, organic polymer oozes
Saturating sealing primary coat repairing and polishing layer of paste:6, heat molten type irreversible reaction adhesive;7, decorative plies.
Specific implementation mode
The utility model is further described with reference to the accompanying drawings and examples.
As shown in Figure 1, the non-ignitable complex shingle panel of A grades for wall decoration of the utility model, it includes that magnesium-based is black resistance to
Plate substrate 1, the black thereon of resistance to plate of magnesium-based are compounded with the gold with wear-resisting permanent oil rub resistance function by self-adhesion pulp layer 2
Belong to plate layer 3,3 outer surface of the sheet-metal layers is coated with, by fluorine carbon roller coating weather-resisant paint or polyester paint or PVC film or PP film preparations
Made of protective layer 4;Organic polymer infiltration sealing primary coat repairing and polishing layer of paste is provided below in the black substrate of resistance to plate of magnesium-based
5, the organic polymer infiltration sealing primary coat repairing and polishing layer of paste is compounded with below by heat molten type irreversible reaction adhesive 6
With the anti-oxidation anti-corrosion function, decorative plies made of metal aluminum sheet film or stainless steel plate or PVC film or PP film preparations
7;Metallic plate used by the sheet-metal layers 3 is metal aluminum foil or stainless steel plate.
Wall decoration composite plate production technology method of the present invention is specifically expressed as follows:(1) first step:By the black resistance to plate of magnesium-based 1
With the black self-adhesion of the resistance to plate slurry of magnesium-based again with the metal aluminum sheet or stainless steel plate primed containing wear-resistant tension back stretching, cold pressing is rolled into
Three-in-one monolithic composite panel body is placed on hydraulic pressure cold press and carries out by the compound plate body of one after then again rolling cold pressing
Sizing cold pressing 6 hours more than so that the black substrate of resistance to plate of magnesium-based, self-adhesion pulp layer, sheet-metal layers is completely combined for three-in-one entirety answer
Plywood body;
(2) second step:The compound plate body of plate will be integral by being completely combined, be placed on full-automatic coating roller
On, compound plate body is transmitted on roller coating roller by conveyer belt, the infiltration sealing primary coat repairing and polishing cream rolling of organic type macromolecule
It is coated onto in composite plate dignity and carries out the reinforcing closing of sealing paint, to improve the sticking strength and peel strength in composite plate body surface face,
Roller coating uniformly carries out three lamp ultraviolet lights again after good organic type macromolecule permeates sealing primary coat repairing and polishing cream in body plate face to be composite
Irradiation solidification is waited for processing in next step after solidification and be used;
(3) third walks:By the compound plate body after the organic type macromolecule infiltration sealing primary coat repairing and polishing cream that is cured, then put
The uniform brushing heat molten type irreversible reaction adhesive on Full automatic doubler is set, waits for processing in next step and use;
(4) will apply has anti-oxidation, antirust in the smooth rolling of compound plate body for brushing heat molten type irreversible reaction adhesive
The metal aluminum sheet film or stainless steel plate or PVC decorative Film or PP decorating films of erosion function, wait for processing in next step and use;
(5) by smooth the metal aluminum sheet film with anti-oxidation anti-corrosion function or stainless steel plate or PVC decorative Film well or
The for use compound plate body of PP decorating films, then be placed on full-automatic roller coating equipment, with weather-proof permanent oil rub resistance in roller coating
PEDF fluorocarbon oils paint or polyester paint or PVC decorative Film or PP decorating films.
(6) the compound plate body being finally composed by 1,2,3,4,5,6,7 is become this after four sides milling machine modifies four sides
Apply for product:Wall decoration composite plate.
Claims (1)
1. a kind of non-ignitable complex shingle panel of A grades for wall decoration, it is characterised in that:It includes the black substrate of resistance to plate of magnesium-based (1),
The black thereon of resistance to plate of magnesium-based is compounded with the sheet-metal layers with wear-resisting permanent oil rub resistance function by self-adhesion pulp layer (2)
(3), sheet-metal layers (3) outer surface be coated with by fluorine carbon roller coating weather-resisant paint or polyester paint or PVC film or PP film preparations and
At protective layer (4);Organic polymer infiltration sealing primary coat repairing and polishing layer of paste is provided below in the black substrate of resistance to plate of magnesium-based
(5), the organic polymer infiltration sealing primary coat repairing and polishing layer of paste is multiple below by heat molten type irreversible reaction adhesive (6)
Conjunction have it is with anti-oxidation anti-corrosion function, decorated made of metal aluminum sheet film or stainless steel plate or PVC film or PP film preparations
Plate layer (7).