CN101693609A - Cement-based decoration material, decoration plate and production method thereof - Google Patents

Cement-based decoration material, decoration plate and production method thereof Download PDF

Info

Publication number
CN101693609A
CN101693609A CN200910070781A CN200910070781A CN101693609A CN 101693609 A CN101693609 A CN 101693609A CN 200910070781 A CN200910070781 A CN 200910070781A CN 200910070781 A CN200910070781 A CN 200910070781A CN 101693609 A CN101693609 A CN 101693609A
Authority
CN
China
Prior art keywords
cement
layer
latex
emulsion
decorative sheet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910070781A
Other languages
Chinese (zh)
Other versions
CN101693609B (en
Inventor
陈友增
Original Assignee
陈友增
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 陈友增 filed Critical 陈友增
Priority to CN2009100707810A priority Critical patent/CN101693609B/en
Publication of CN101693609A publication Critical patent/CN101693609A/en
Application granted granted Critical
Publication of CN101693609B publication Critical patent/CN101693609B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to a cement-based decoration material which comprises cement flour, emulsion and cellulose in following component relations: when the emulsion is liquid emulsion, the ratio of the cement lour to the emulsion is 100: 40-100, and the ratio of the cement to the cellulose is 100:0.1-0.5; and when the emulsion is dispersible emulsion, the ratio of the cement lour to the emulsion is 100:1.5-2.4, and the ratio of the cement to the cellulose is 100:0.1-0.5. The decoration plate provided by the invention can be directly applied to internal and external walls and floors of buildings, also can be used as waterproof materials of roofs, underground structures, washrooms, or kitchens, can realize the protection against water, fire, damp, crack and falling off, and has good aging resistance and weather resistance and same service life with buildings and is a novel poisonless, tasteless, environment-friendly and energy-saving product with convenient use, low production cost and long service life.

Description

The manufacture method of a kind of cement based finishing material, decorative sheet and this decorative sheet
Technical field
The invention belongs to decorative materials technology, the manufacture method of especially a kind of cement based finishing material, decorative sheet and this decorative sheet.
Background technology
Decorative sheet is the indispensable a kind of material of building construction industry, such as: decorative sheet all can be installed in the exterior wall of building construction, interior wall or ground.When exterior wall is installed, decorative sheet can with the thermal insulation layer formation thermal insulating composite panel that mutually combines, to improve insulation, the heat-proof quality of buildings; When interior wall was installed, the surface of decorative sheet can spray various coating to form distinct colors or decorative pattern; When installing on ground, decorative sheet can be used as the material of alternative carpet, timber floor.The thermal insulating composite panel that the exterior wall of building construction is installed generally is made of the basic unit and the top layer of mutual applying, and basic unit is an adiabator layer, as: polystyrene foam warming plate or hard polyaminoester plate etc., the top layer is a traditional material, as: stone material etc.This top layer is exposed in the physical environment, and the erosion that can be subjected to the irradiation of sunlight and be subjected to rainwater, wind, snow be very easy to damage, and such as common cracking problem, corrodes and can cause coming off of whole decorative plate of outer wall when serious.When interior wall used, the thickness of existing decorative sheet was big, planeness is bad, influence is attractive in appearance, cost is higher, and waterproof, fire prevention, acid and alkali-resistance ability.As seen, easy to crack, the problem that comes off that traditional thermal insulating composite panel exists, and its cost height have increased developer's purchase cost, have also increased the maintenance cost of later stage to buildings.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art, provide with low cost, be easy to use and fire prevention, waterproof, acid and alkali-resistance, a kind of cement based finishing material that ageing resistance is good.
This cement based finishing material comprises cement flour, latex and Mierocrystalline cellulose, and the quality proportion relation of each component is:
When latex is emulsion class latex: cement flour: latex is 100: 40~100, cement flour: Mierocrystalline cellulose is 100: 0.1~0.5;
When latex is redispersable latex powder: cement flour: latex is 100: 1.5~2.4, cement flour: Mierocrystalline cellulose is 100: 0.1~0.5.
And described emulsion class latex is any one or two or more mixing in benzene emulsion, ACRYLIC EMULSION, organosilicon crylic acid latex, elastic emulsion, flexible emulsion, EVA emulsion or the VAE emulsion.
And, also comprising quartz sand or river sand, the ratio of itself and cement flour is 10~150: 100.
And, also comprising polyvinyl alcohol or 107 glue, the ratio of itself and cement flour is 10~30: 100.
And, also comprising softening agent, the ratio of itself and cement flour is 0.1~0.5: 100.
And, also comprising gypsum, the ratio of itself and cement flour is 10~30: 100.
Another object of the present invention provides and comprises the cement based finishing material and can use the outside the building decorative sheet on wall, interior wall or ground.
The structure of this decorative sheet is: comprise nonwoven layer and cement based decorative material layer, nonwoven layer is packed in the bottom surface of cement based decorative material layer, is embedded with the fiberglass gridding cloth layer in the cement based decorative material layer.
And, be fixed with the layer of non-woven fabric layer at the upper surface of cement based decorative material layer.
The structure of this decorative sheet can also be: comprise nonwoven layer and cement based decorative material layer, nonwoven layer is packed in the upper surface and the bottom surface of cement based decorative material layer respectively.
Another object of the present invention provides the composite structure that comprises decorative sheet.
1. the composite structure of thermal insulating composite panel: between two-layer decorative sheet, clamp the insulation laminate.
Decoration composite plate meet structure: clamp inorganic board between two-layer decorative sheet, this inorganic board is any one in calcium-plastic board, plasterboard or the fiber cement board.
Insulation laminate and inorganic board in above-mentioned two kinds of composite structures can be one decks, also can be multilayers, adopt tamanori to fix between each plate.
The insulation laminate can be any one in hard polyurethane foam board, EPS polystyrene board, XEPS polystyrene board or the glass microballon warming plate, and common other organic heat-insulating plate or the inorganic heat preservation plate in market all can use certainly.
Another object of the present invention provides the method for the decorative sheet that a kind of manufacturing is made up of fiberglass gridding cloth layer, nonwoven layer and cement based decorative material layer.
This method may further comprise the steps:
(1) the cement based finishing material is mixed with water;
(2) the fiberglass gridding cloth layer of overlapping placement and bottom layer of non-woven fabrics are advanced forward under the traction of transmission rolling equipment, the material that step (1) is obtained is poured on fiberglass gridding cloth layer and the bottom layer of non-woven fabrics simultaneously, is squeezed into work in-process through upper and lower pressure roller;
(3) work in-process that step (2) is obtained are delivered to oven dry in the baking box;
(4) after the oven dry, cut typing, material is rebuild promptly obtained the decorative sheet finished product then by physical size and shape need.
And the water in the described step (1) and the quality proportion relation of cement based finishing material are:
When latex was emulsion class latex, water: the latex in the cement based finishing material was 4~7: 7~4;
When latex was redispersable latex powder, water: the cement based finishing material was 4~7: 7~4.
Advantage of the present invention and beneficial effect are:
1. the cement in this finishing material can adopt the cement of shades of colour, various labels, its highly versatile, this cement is as the base-material of other material and other material adheres to mutually, uniform mixing, make integral body have anti-aging, fire prevention, waterproof, anticracking, acid and alkali-resistance, high adhesive power and shock proof characteristics, and owing to the plasticity-height of cement, easy levelling, make the decorative sheet of making to adhere to well, to coincide by sand-cement slurry with wall body structure, the installation steelframe need be set on metope, its short construction period has reduced production cost simultaneously.
2. the latex in this finishing material is a kind of or two or more mixing arbitrarily in benzene emulsion, ACRYLIC EMULSION, organosilicon crylic acid latex, elastic emulsion, flexible emulsion, EVA emulsion, VAE emulsion or the redispersable latex powder, after in cement flour, adding latex, can improve whole adhesive power, improved whole water-fast, weathering resistance, make the decorative sheet made not easy to crack, come off.
3. the Mierocrystalline cellulose in this finishing material is lignocellulose, Vltra tears (HPMC), Polyanionic Cellulose (PAC), hydroxyethyl ether cellulose (HEC).After adding Mierocrystalline cellulose, improved the adhesive power between each material, make the decorative sheet of making not easy to crack, come off.
4. polyvinyl alcohol in this finishing material or 107 glue are a kind of water-soluble environment protective type high molecular polymers, and it has the advantage stable, that bonding force is strong, behind the adding cement flour, whole toughness, elasticity are strengthened, and make decorative sheet not easy to crack.
5. after adding quartz sand or river sand in this finishing material, because the two all has not specific shape, as many angled shape etc., because this special shape, form stronger bonding force with cement slurry, strengthen anti-impact force ability, the ultimate compression strength of slurry, further improved physical strength, weathering resistance and the resistance to acids and bases of the decorative sheet of making.
6. after adding softening agent in this finishing material, make other component bonded better, tightr, improved snappiness and plasticity-between each component.
7. the invention provides the manufacture method of a kind of cement based finishing material, decorative sheet and this decorative sheet; decorative sheet can directly use on the inner, external wall or the ground of building construction; also can be used as the water-proof material that roofing, underground works, toilet or kitchen etc. are located; it has good provide protection to body of wall, can realize the purpose of waterproof, fire prevention, protection against the tide, anti-cracking, slip-off preventing.The decoration composite plate of making can be used as the floor tile on ground or the material of partition, the thermal insulating composite panel of making is when exterior wall uses, has advantage anti-aging, good weatherability, with the same life-span of fabric structure, be a kind of long and nontoxic, the tasteless environment-friendly and green of easy to use, lower production cost, life-span, energy-conservation novel product taken into account.
Description of drawings
Fig. 1 is the structural representation of a kind of decorative sheet among the present invention;
Fig. 2 is the structural representation of another kind of decorative sheet among the present invention;
Fig. 3 is the structural representation of thermal insulating composite panel among the present invention;
Fig. 4 is the structural representation of decoration composite plate among the present invention.
Embodiment
The invention will be further described below by specific embodiment, and following examples are descriptive, is not determinate, can not limit protection scope of the present invention with this.
A kind of cement based finishing material comprises cement flour, latex and Mierocrystalline cellulose.The quality proportion relation of each component is in the cement based finishing material: when latex was emulsion class latex, cement flour: latex is 100: 40~100, cement flour: Mierocrystalline cellulose was 100: 0.1~0.5; When latex was redispersable latex powder, the quality proportion relation of each component was in the cement based finishing material: cement flour: latex is 100: 1.5~2.4, cement flour: Mierocrystalline cellulose is 100: 0.1~0.5.Also comprise quartz sand or river sand, the ratio of itself and cement flour is 10~150: 100.Also comprise polyvinyl alcohol (molecular weight 20000~45000) or 107 glue, the ratio of itself and cement flour is 10~30: 100.Also comprise softening agent, the ratio of itself and cement flour is 0.1~0.5: 100.Also comprise gypsum, the ratio of itself and cement flour is 10~30: 100.
Wherein, cement flour can be the cement of various labels, such as: gray 32.5 #Cement, 42.5 #42.5 of cement or white #Cement etc.Latex is any one in emulsion class latex or the redispersable latex powder, and emulsion class latex is any one or two or more mixing in benzene emulsion, ACRYLIC EMULSION, organosilicon crylic acid latex, elastic emulsion, flexible emulsion, EVA emulsion or the VAE emulsion.Wherein, benzene emulsion is that the Nantong life reaches the S-01 benzene emulsion that chemical industry company limited produces, ACRYLIC EMULSION is the A-106 polyacrylic water-proof emulsion that Nantong federal chemical industry company limited produces, organosilicon crylic acid latex is that the Nantong life reaches the SD-528 organosilicon crylic acid latex that chemical industry company limited produces, elastic emulsion is that the Nantong life reaches the S-07 cross-linking elasticity emulsion that chemical industry company limited produces, and flexible emulsion is the flexible emulsion of XG-6158 that the new photoinitiator chemical in Hengshui, Hebei is produced.Redispersable latex powder can use the sky, Henan to contain HW-5115, the HW-5116 of chemical industry company limited, also can use the SWF-04 of Shanxi Sanwei Group Co., Ltd., SWF-05, also can use Tianjin Ke Yuan chemical building material company limited 0510 type, 0520 type or VAE latex powder etc., above-mentioned various redispersable latex powder can use separately, also can two or more mix use.
Mierocrystalline cellulose is lignocellulose, Vltra tears (HPMC), Polyanionic Cellulose (PAC), hydroxyethyl ether cellulose (HEC) etc.
Softening agent is dioctyl phthalate (DOP), dibutyl phthalate, diheptyl phthalate, Di Iso Decyl Phthalate, dimixo-octyl phthalate etc.
Each component is not limited to above-described content, and other like product that can buy on market all can use.
Above-mentioned cement based finishing material is mixed with water after measuring mixing again, and the quality proportion relation of water and cement based finishing material is:
When latex was emulsion class latex, water: the latex in the cement based finishing material was 4~7: 7~4; When latex was redispersable latex powder, water: the cement based finishing material was 4~7: 7~4.
The cement based finishing material is with after water mixes, can be made into decorative sheet with material such as non-woven fabrics after through the extruding of transmission rolling equipment and drying again, the thickness of this decorative sheet can be determined according to client's needs, decorative sheet thinner thickness such as following structure, the decoration that can be used for interior wall, alternative wallpaper, its structure as shown in Figure 1, comprise non-woven fabrics top layer 3, bottom layer of non-woven fabrics 2 and cement based decorative material layer 1, upper surface, the bottom layer of non-woven fabrics that the non-woven fabrics top layer is packed in cement based decorative material layer upper strata is packed in the lower surface of cement based decorative material layer lower floor.Also can make structure as shown in Figure 2, glazing fibrous mesh cloth layer 4 can remove the non-woven fabrics top layer in the structure shown in Figure 2 in the cement based decorative material layer, and particular case will be determined according to client's needs.The decorative sheet of structure illustrated in figures 1 and 2 can have thin thickness, such as adopt in the structure shown in Figure 2 50 grams/square metre fiberglass gridding cloth can to make the integral thickness of decorative sheet be 1.2~1.5 millimeters, adopt thin cement based decorative material layer in the structure shown in Figure 1, at this moment, the decorative sheet of making can roll up, its good toughness, fire prevention, waterproof, anticracking, anti-aging, apply different colours on its top layer, the metallic paint of pattern, true stone type coating, behind the dissimilar coating such as flexible paint, can realize different visual effects, can be used on the top layer of exterior wall, also can be used in interior wall and use as wallpaper.
When the client needs thicker thickness, in order to keep its tension, anti crack performance, can increase the thickness of the fiberglass gridding cloth layer in the structure shown in Figure 2, as use 600 grams/square metre fiberglass gridding cloth can to make the integral thickness of decorative sheet be 4~6 millimeters, adopt thicker cement based decorative material layer in the structure shown in Figure 1, at this moment, the rigidity of decorative sheet strengthens, both can use, also can be used as the finishing material on interior wall, ground at exterior wall.
When exterior wall uses, between upper strata decorative sheet 5 and lower floor's decorative sheet 7, clamp one deck insulation laminate and can be made into thermal insulating composite panel 6, can adopt tamanori to fix between the three ply board.
The insulation laminate can be any one in hard polyurethane foam board, EPS polystyrene board, XEPS polystyrene board or the glass microballon warming plate, and common other organic heat-insulating plate or the inorganic heat preservation plate in market all can use certainly.
Can adopt decoration composite plate when cutting off in interior wall or making room, its structure is: clamp one deck inorganic board between upper strata decorative sheet and lower floor's decorative sheet, this inorganic board is any one in calcium-plastic board, plasterboard or the fiber cement board.(inorganic board is seen the label 8 among Fig. 3).
Embodiment 1
In the present embodiment, the component of cement based finishing material is as follows:
Cement flour (label: 42.5 #) 100 kilograms
40 kilograms of ACRYLIC EMULSION (A-106)
0.1 kilogram of Vltra tears (HPMC)
Make decorative sheet with said components, may further comprise the steps:
(1) will mix with 40 kg of water behind the abundant mixing of said components, the cement slurry of making is standby.
(2) fiberglass gridding cloth and bottom non-woven fabrics are placed in the transmission rolling equipment, the two is advanced forward under the traction of transmission rolling equipment, the cement slurry that step (1) is obtained is poured on fiberglass gridding cloth and the bottom non-woven fabrics simultaneously, and upper and lower pressure roller evenly makes work in-process after the extruding.
(3) work in-process that step (2) is obtained are delivered to oven dry in the baking box, drying condition is: temperature is by 300 ℃ of 150 ℃ of reducing to the exit gradually of drying baker ingress, the conveying belt motor speed is 2200 rev/mins, and the transmitting ratio of the wheel casing that motor output shaft connects is 1: 25, and drying time is; 15 minutes;
(4) after the oven dry, cut typing, then material is rebuild the decorative sheet coiled material finished product that promptly obtains 1.5 mm thick (specification of fiberglass gridding cloth is: 50 grams/square metre) by the physical size and the shape need of customer requirement.
Between two-layer decorative sheet coiled material finished product, make thermal insulating composite panel, can be used for interior wall or exterior wall with the bonding EPS polystyrene board of tackiness agent.
Embodiment 2
In the present embodiment, the component of cement based finishing material is as follows:
Cement flour (label: 32.5 #) 100 kilograms
Elastic emulsion (S-07) and benzene emulsion (S-01) (1: 100 kilogram of weight ratio
0.3)
0.5 kilogram of Polyanionic Cellulose (PAC)
Polyvinyl alcohol (molecular weight: 25000) 30 kilograms
150 kilograms of quartz sands
Make decorative sheet with said components, may further comprise the steps:
(1) will mix with 175 kg of water behind the abundant mixing of said components, the cement slurry of making is standby.
(2) the bottom non-woven fabrics is placed in the bottom traction wheel of transmission rolling equipment, the top layer non-woven fabrics is placed in the top traction wheel of transmission rolling equipment, two layers of cloth is advanced forward under the traction of transmission rolling equipment, the cement slurry that step (1) is obtained is poured on the bottom non-woven fabrics simultaneously, and upper and lower pressure roller evenly makes work in-process after the extruding.
(3) work in-process that step (2) is obtained are delivered to oven dry in the baking box, drying condition is: temperature is by 40 ℃ of 250 ℃ of reducing to the exit gradually of drying baker ingress, the conveying belt motor speed is 2200 rev/mins, and the transmitting ratio of the wheel casing that motor output shaft connects is 1: 25, and drying time is; 25 minutes;
(4) after the oven dry, cut typing, then material is rebuild the decorative sheet finished product that promptly obtains 5 mm thick by the physical size and the shape need of customer requirement.
This decorative sheet can be directly used in interior wall and ground.
Embodiment 3
In the present embodiment, the component of cement based finishing material is as follows:
Cement flour (label: 42.5 #) 300 kilograms
6 kilograms of HW-5115
1.2 kilograms of hydroxyethyl ether celluloses (HEC)
Polyvinyl alcohol (molecular weight: 45000) 60 kilograms
150 kilograms in river sand
1.2 kilograms of dimixo-octyl phthalates
Make decorative sheet with said components, may further comprise the steps:
(1) will mix with 512.4 kg of water behind the abundant mixing of said components, the cement slurry of making is standby.
(2) fiberglass gridding cloth and bottom non-woven fabrics are placed in the bottom traction wheel of transmission rolling equipment, the top layer non-woven fabrics is placed in the top traction wheel of transmission rolling equipment, three layers of cloth are advanced forward under the traction of transmission rolling equipment, the cement slurry that step (1) is obtained is poured on fiberglass gridding cloth and the bottom non-woven fabrics simultaneously, and upper and lower pressure roller evenly makes work in-process after the extruding.
(3) work in-process that step (2) is obtained are delivered to oven dry in the baking box, drying condition is: temperature is by 300 ℃ of 25 ℃ of reducing to the exit gradually of drying baker ingress, the conveying belt motor speed is 2200 rev/mins, and the transmitting ratio of the wheel casing that motor output shaft connects is 1: 25, and drying time is; 8 minutes;
(4) after the oven dry, cut typing, then material is rebuild the decorative sheet finished product that promptly obtains 2.2 mm thick (specification of fiberglass gridding cloth is: 150 grams/square metre) by the physical size and the shape need of customer requirement.
Between two-layer decorative sheet coiled material finished product, make thermal insulating composite panel, can be used for exterior wall with the bonding hard polyurethane foam board of tackiness agent.
Embodiment 4
In the present embodiment, the component of cement based finishing material is as follows:
Cement flour (label: 32.5 #) 150 kilograms
2.25 kilograms on SWF-04 and 0510 type (weight ratio 1: 1)
6 kilograms of lignocelluloses
30 kilograms in 107 glue
90 kilograms in river sand
4.5 kilograms of dibutyl phthalates
22.5 kilograms in gypsum
To mix with 381.6 kg of water behind the abundant mixing of said components.The process of making decorative sheet is identical with embodiment 1.
Between two-layer decorative sheet coiled material finished product, make decoration composite plate, can be used for interior wall with the bonding calcium-plastic board of tackiness agent.
Embodiment 5
In the present embodiment, the component of cement based finishing material is as follows:
Cement flour (label: 42.5 #) 50 kilograms
20 kilograms of flexible emulsion (XG-6158) and VAE emulsion and organosilicon crylic acid latexs
(SD-528) (weight ratio 1: 1: 1)
0.2 kilogram of Vltra tears (HPMC)
Polyvinyl alcohol (molecular weight: 30000) 5 kilograms
50 kilograms of quartz sands
0.25 kilogram of dioctyl phthalate (DOP)
To mix with 35 kg of water behind the abundant mixing of said components.The process of making decorative sheet is identical with embodiment 2.
Between two-layer decorative sheet coiled material finished product, make thermal insulating composite panel, can be used for interior wall or ground with tackiness agent adhering glass micro-sphere thermal insulation plate.
Embodiment 6
In the present embodiment, the component of cement based finishing material is as follows:
Cement flour (label: 42.5 #) 220 kilograms
VAE latex powder and HW-5116 and 5.28 kilograms
0520 type
(weight ratio 1: 1: 1)
1.1 kilograms of Vltra tearss (HPMC)
22 kilograms in 107 glue
220 kilograms of quartz sands
1.1 kilograms of diheptyl phthalates
22 kilograms in gypsum
To mix with 267 kg of water behind the abundant mixing of said components.The process of making decorative sheet is identical with embodiment 3.
Between two-layer decorative sheet coiled material finished product, make thermal insulating composite panel, can be used for exterior wall with the bonding hard polyurethane foam board of tackiness agent.

Claims (14)

1. cement based finishing material, it is characterized in that: comprise cement flour, latex and Mierocrystalline cellulose, the quality proportion relation of each component is:
When latex is emulsion class latex: cement flour: latex is 100: 40~100, cement flour: Mierocrystalline cellulose is 100: 0.1~0.5;
When latex is redispersable latex powder: cement flour: latex is 100: 1.5~2.4, cement flour: Mierocrystalline cellulose is 100: 0.1~0.5.
2. cement based finishing material according to claim 1 is characterized in that: described emulsion class latex is any one or two or more mixing in benzene emulsion, ACRYLIC EMULSION, organosilicon crylic acid latex, elastic emulsion, flexible emulsion, EVA emulsion or the VAE emulsion.
3. a kind of cement based finishing material according to claim 2 is characterized in that: also comprise quartz sand or river sand, the ratio of itself and cement flour is 10~150: 100.
4. a kind of cement based finishing material according to claim 3 is characterized in that: also comprise polyvinyl alcohol or 107 glue, the ratio of itself and cement flour is 10~30: 100.
5. a kind of cement based finishing material according to claim 4 is characterized in that: also comprise softening agent, the ratio of itself and cement flour is 0.1~0.5: 100.
6. a kind of cement based finishing material according to claim 5 is characterized in that: also comprise gypsum, the ratio of itself and cement flour is 10~30: 100.
7. decorative sheet of making by claim 1 or 2 or 3 or 4 or 5 or 6 described cement based finishing material, it is characterized in that: comprise nonwoven layer and cement based decorative material layer, nonwoven layer is packed in the bottom surface of cement based decorative material layer, is embedded with the fiberglass gridding cloth layer in the cement based decorative material layer.
8. decorative sheet according to claim 7 is characterized in that: the upper surface at the cement based decorative material layer is fixed with the layer of non-woven fabric layer.
9. decorative sheet of being made by claim 1 or 2 or 3 or 4 or 5 or 6 described cement based finishing material, it is characterized in that: comprise nonwoven layer and cement based decorative material layer, nonwoven layer is packed in the upper surface and the bottom surface of cement based decorative material layer respectively.
10. according to the composite structure of the described decorative sheet of claim 7, it is characterized in that: between the adjacent two layers decorative sheet, clamp the insulation laminate, or between the adjacent two layers decorative sheet, clamp inorganic board.
11. the composite structure according to the described decorative sheet of claim 9 is characterized in that: between the adjacent two layers decorative sheet, clamp the insulation laminate, or between the adjacent two layers decorative sheet, clamp inorganic board.
12. according to claim 10 or 11 described composite structures, it is characterized in that: described insulation laminate is any one in hard polyurethane foam board, EPS polystyrene board, XEPS polystyrene board or the glass microballon warming plate.
13. a method of making the described decorative sheet of claim 7 is characterized in that: may further comprise the steps:
(1) the cement based finishing material is mixed with water;
(2) the fiberglass gridding cloth layer of overlapping placement and bottom layer of non-woven fabrics are advanced forward under the traction of transmission rolling equipment, the material that step (1) is obtained is poured on fiberglass gridding cloth layer and the bottom layer of non-woven fabrics simultaneously, is squeezed into work in-process through upper and lower pressure roller;
(3) work in-process that step (2) is obtained are delivered to oven dry in the baking box;
(4) after the oven dry, cut typing, material is rebuild promptly obtained the decorative sheet finished product then by physical size and shape need.
14. the manufacture method of decorative sheet according to claim 13 is characterized in that: the water in the described step (1) and the quality proportion relation of cement based finishing material are:
When latex was emulsion class latex, water: the latex in the cement based finishing material was 4~7: 7~4;
When latex was redispersable latex powder, water: the cement based finishing material was 4~7: 7~4.
CN2009100707810A 2009-10-13 2009-10-13 Cement-based decoration material, decoration plate and production method thereof Expired - Fee Related CN101693609B (en)