CN206011892U - Unify pearlescent effect PCM panels in a kind of bottom surface - Google Patents
Unify pearlescent effect PCM panels in a kind of bottom surface Download PDFInfo
- Publication number
- CN206011892U CN206011892U CN201620986749.2U CN201620986749U CN206011892U CN 206011892 U CN206011892 U CN 206011892U CN 201620986749 U CN201620986749 U CN 201620986749U CN 206011892 U CN206011892 U CN 206011892U
- Authority
- CN
- China
- Prior art keywords
- upside
- layer
- downside
- paint
- chemical treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
This utility model provides a kind of bottom surface and unifies pearlescent effect PCM panels, including：Substrate, the first chemical treatment layer is provided with the upside of substrate, the second chemical treatment layer is provided with the downside of substrate, back of the body enamelled coating is provided with the downside of second chemical treatment layer, paint for priming paint and top lacquer layer is provided with the upside of first chemical treatment layer, layer of varnish is provided with the upside of paint for priming paint and top lacquer layer, pearl layer is provided with the upside of layer of varnish, covers PE film layers on the upside of pearl layer.The substrate includes corrosion resistant plate, is provided with titanium steel plate on the downside of corrosion resistant plate, is provided with the upside of downside zinc coat, corrosion resistant plate and is provided with upside zinc coat, be provided with downside aluminium foil clad on the downside of the zinc coat of downside on the downside of titanium steel plate.This utility model is using common priming paint before the replacement of paint for priming paint and top lacquer layer, finish paint bilayer roller coat, be able to can be completed with roller coat one time, substantially increase production efficiency, production cost is reduced, can keep by force color and luster novel for a long time while having reached excellent dicoration, mouldability, resistance and fingerprint resistance, coating adhesion.
Description
Technical field
This utility model is related to technical field of novel materials, and pearlescent effect PCM panels are unified in specially a kind of bottom surface.
Background technology
Than wide, automobile, refrigerator, washing machine, top-grade furniture, kitchen set for application of the clad steel plate in industry and life
Standby, industrial and civil buildings etc. are required for using, and the environment that clad steel plate is used is also more and more special and more and more extensive,
Under certain special environment, clad steel plate can occur the phenomenon of molecular migration with other parts Long contact time, for
Under the traction of this molecular migration phenomenon, the space that the development of clad steel plate industry will have very wide development.
In current PCM panels, paint for priming paint and top lacquer layer and layer of varnish are to separate roller coat respectively, and manufacturing process is cumbersome, raw
Produce cost higher.
Content of the invention
The technical problem solved by this utility model is to provide a kind of bottom surface unification pearlescent effect PCM panels, to solve
Problem in above-mentioned background technology.
The technical problem solved by this utility model employs the following technical solutions to realize：Unify pearlescent effect in a kind of bottom surface
PCM panels, including：Substrate, is provided with the first chemical treatment layer on the upside of substrate, be provided with the second chemical treatment layer on the downside of substrate, and second
Back of the body enamelled coating is provided with the downside of chemical treatment layer, is provided with paint for priming paint and top lacquer layer, on the upside of paint for priming paint and top lacquer layer on the upside of the first chemical treatment layer
Layer of varnish is provided with, pearl layer on the upside of layer of varnish, is provided with, PE film layers on the upside of pearl layer, are coated with.
The substrate includes corrosion resistant plate, is provided with titanium steel plate on the downside of corrosion resistant plate, be provided with the downside of titanium steel plate downside zinc coat,
Upside zinc coat is provided with the upside of corrosion resistant plate, is provided with downside aluminium foil clad, sets on the upside of the zinc coat of upside on the downside of the zinc coat of downside
There is upside aluminium foil clad.
Further, first chemical treatment layer, the thickness of the second chemical treatment layer are 2 μm -3 μm.
Further, the thickness of the substrate is 0.02-0.25mm.
Further, the thickness of the paint for priming paint and top lacquer layer is 10 μm -15 μm.
Further, the thickness of the layer of varnish is 4 μm -8 μm.
Compared with disclosed technology, there is advantages below in this utility model：This utility model uses paint for priming paint and top lacquer layer generation
For priming paint common before, finish paint bilayer roller coat, can be completed with roller coat one time, substantially increase production efficiency, reduce
Production cost, meanwhile, reach excellent dicoration, mouldability, resistance and fingerprint resistance, coating adhesion by force, can keep color and luster new for a long time
Grain husk.
Description of the drawings
Fig. 1 is structural representation of the present utility model.
Fig. 2 is board structure schematic diagram of the present utility model.
Specific embodiment
In order that technological means of the present utility model, creation characteristic, workflow, using method reached purpose and effect are easy
In understand understanding, below in conjunction with this utility model embodiment, the technical scheme in this utility model embodiment is carried out clear,
It is fully described by, it is clear that described embodiment is only a part of embodiment of this utility model, rather than whole enforcement
Example.Embodiment in based on this utility model, those of ordinary skill in the art are obtained under the premise of creative work is not made
The every other embodiment for obtaining, belongs to the scope of this utility model protection.
As shown in Figure 1 and Figure 2, pearlescent effect PCM panels are unified in a kind of bottom surface, including：Substrate 1, is provided with the upside of substrate 1
One chemical treatment layer 2, is provided with the second chemical treatment layer 3 on the downside of substrate 1, be provided with back of the body enamelled coating 8 on the downside of the second chemical treatment layer 3, the
Paint for priming paint and top lacquer layer 4 is provided with the upside of one chemical treatment layer 2, is provided with layer of varnish 5, sets on the upside of layer of varnish 5 on the upside of paint for priming paint and top lacquer layer 4
There is pearl layer 6, on the upside of pearl layer 6, be coated with PE film layers 7.
The substrate 1 includes corrosion resistant plate 11, is provided with titanium steel plate 12, is provided with down on the downside of titanium steel plate 12 on the downside of corrosion resistant plate 11
Upside zinc coat 14 is provided with the upside of side zinc coat 13, corrosion resistant plate 11, is provided with downside aluminium foil clad on the downside of downside zinc coat 13
15, upside aluminium foil clad 16 is provided with the upside of upside zinc coat 14.
Embodiment 1
The manufacture method of pearlescent effect PCM panels is unified in a kind of bottom surface, comprises the following steps：
(1) titanium steel plate will be combined on the downside of corrosion resistant plate, is electroplated on the upside of plating downside zinc coat, corrosion resistant plate on the downside of titanium steel plate
Upside zinc coat, aluminium foil clad on the downside of overlay film on the downside of the zinc coat of downside, aluminium foil clad on the upside of overlay film on the upside of the zinc coat of upside,
Substrate is formed, the thickness of substrate is 0.02-0.25mm.；
(2) by substrate after pre- defat, defat and washing, to each roller coat potassium bichromate solution of substrate front side and the back side,
I.e. substrate positive and negative has been respectively formed chemical treatment layer, i.e. the first chemical treatment layer and the second chemical treatment layer；First chemical treatment
Layer, the thickness of the second chemical treatment layer are 2 μm -3 μm.；
On the downside of (3) second chemical treatment layers, the solidification of roller coat epoxy coating is dried；At first chemistry
Roller coat paint for priming paint and top lacquer layer on the upside of reason layer, the thickness of paint for priming paint and top lacquer layer is 10 μm -15 μm；
(4) roller coat layer of varnish on the upside of paint for priming paint and top lacquer layer, the thickness of layer of varnish is 4 μm -8 μm, and on the upside of layer of varnish, roller coat is precious
The white Polyester resin lacquer solidification of pearl is dried, shape after backsize polyurethane binder solidification of PE electron membrane
Into first adhesive phase, that is, PE films are obtained, on the upside of pearl layer, are coated with PE film layers.
This utility model is rational in infrastructure, novel, and product with stable quality is easy to process, can improve processing effect during use
Rate, in addition this utility model appearance looks elegant, sense of touch are good, can be widely used in various home appliance panels.
Ultimate principle of the present utility model, principal character and advantage of the present utility model has been shown and described above.One's own profession
The technical staff of industry it should be appreciated that this utility model is not restricted to the described embodiments, described in above-described embodiment and description
Principle of the present utility model is described simply, on the premise of without departing from this utility model spirit and scope, this utility model is also
Various changes and modifications are had, these changes and improvements are both fallen within the range of claimed this utility model.This utility model
Claimed scope by appending claims and its equivalent thereof.
Claims (6)
1. pearlescent effect PCM panels are unified in a kind of bottom surface, including：Substrate, it is characterised in that：It is provided with the upside of substrate at the first chemistry
Reason layer, is provided with the second chemical treatment layer, is provided with back of the body enamelled coating, on the first chemical treatment layer on the downside of the second chemical treatment layer on the downside of substrate
Side is provided with paint for priming paint and top lacquer layer, is provided with layer of varnish on the upside of paint for priming paint and top lacquer layer, is provided with pearl layer, on the upside of pearl layer on the upside of layer of varnish
It is coated with PE film layers.
2. pearlescent effect PCM panels are unified in a kind of bottom surface according to claim 1, it is characterised in that：The substrate includes
Corrosion resistant plate, is provided with titanium steel plate on the downside of corrosion resistant plate, be provided with the upside of downside zinc coat, corrosion resistant plate and be provided with upside on the downside of titanium steel plate
Zinc coat, is provided with downside aluminium foil clad on the downside of the zinc coat of downside, be provided with upside aluminium foil clad on the upside of the zinc coat of upside.
3. pearlescent effect PCM panels are unified in a kind of bottom surface according to claim 1, it is characterised in that：First chemistry
Process layer, the thickness of the second chemical treatment layer are 2 μm -3 μm.
4. pearlescent effect PCM panels are unified in a kind of bottom surface according to claim 1, it is characterised in that：The thickness of the substrate
Spend for 0.02-0.25mm.
5. pearlescent effect PCM panels are unified in a kind of bottom surface according to claim 1, it is characterised in that：The bottom surface unification
The thickness of enamelled coating is 10 μm -15 μm.
6. pearlescent effect PCM panels are unified in a kind of bottom surface according to claim 1, it is characterised in that：The layer of varnish
Thickness is 4 μm -8 μm.