CN206913828U - More metal composite steel plates - Google Patents
More metal composite steel plates Download PDFInfo
- Publication number
- CN206913828U CN206913828U CN201720676637.1U CN201720676637U CN206913828U CN 206913828 U CN206913828 U CN 206913828U CN 201720676637 U CN201720676637 U CN 201720676637U CN 206913828 U CN206913828 U CN 206913828U
- Authority
- CN
- China
- Prior art keywords
- composite bed
- steel plate
- metal
- thickness
- composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a kind of more metal composite steel plates, including:First composite bed, include a base material, base material is steel plate, and two surface recombinations up and down of base material have alumin(i)um zinc alloy layer;Second composite bed, including a metal ceramic composite bed, metal ceramic composite bed are formed on two surfaces up and down of the first composite bed;Protective layer, formed and be passivated the inoranic membrane of film outer surface on two surfaces up and down of the second composite bed, including passivating film and formation.Through the above way; the more metal composite steel plates of the utility model can prevent surface of steel plate rust corrosion; with higher impact resistance, pliability, chemical stability and wearability; excellent protective effect can be also played to surface of steel plate; it can ensure that surface of steel plate has anti-finger printing energy, ensure that the brilliance of surface of steel plate is smooth.
Description
Technical field
Composite metal plate technical field is the utility model is related to, more particularly to a kind of more metal composite steel plates.
Background technology
Application of the steel plate in industry, daily life is than wide, the household electrical appliances such as automobile, refrigerator, washing machine, furniture and kitchen
Equipment, decoration, building etc. is all a large amount of to be used.
In conventional art, steel plate corrosion resistance is improved mainly by the galvanizing by dipping on shaping surface of steel plate.This heat
The decay resistance of zinc immersion is limited, is also easy to scratch abrasion, service life is also restrained.
In addition, conventional art light plate surface is in use for some time, the markings such as fingerprint are easily stained with, influence steel plate table
Face it is smooth and attractive in appearance, have influence on the cleaning subsequently used.
Utility model content
The utility model can prevent surface of steel plate mainly solving the technical problems that a kind of more metal composite steel plates of offer
Rust corrosion, has higher impact resistance, pliability, chemical stability and wearability, also surface of steel plate can be played excellent
Protective effect, it is ensured that surface of steel plate has anti-finger printing energy, ensures that the brilliance of surface of steel plate is smooth.
In order to solve the above technical problems, the technical scheme that the utility model uses is:A kind of more metal composites are provided
Steel plate, including:
First composite bed, include a base material, base material is steel plate, and two surface recombinations up and down of base material have alumin(i)um zinc alloy
Layer,
Second composite bed, including a metal ceramic composite bed, metal ceramic composite bed are formed above and below the first composite bed
Two surfaces,
Protective layer, formed on two surfaces up and down of the second composite bed, including passivating film and formation are in passivating film appearance
The inoranic membrane in face.
In one preferred embodiment of the utility model, the thickness of the first composite bed is 4 ~ 26mm, the thickness of the second composite bed
Spend for 0.05 ~ 16mm, the thickness of protective layer is 1.50 ~ 5.25 μm.
In one preferred embodiment of the utility model, the thickness of base material is at least 8mm, and the thickness of alumin(i)um zinc alloy layer is
0.5~3mm。
In one preferred embodiment of the utility model, alumin(i)um zinc alloy layer is compounded in the upper of steel plate by continuously dip coat mode
Lower two surfaces.
In one preferred embodiment of the utility model, metal ceramic composite bed is aluminium oxide ceramics composite bed, zirconium oxide
Ceramic thin film or silicon carbide ceramics composite bed.
In one preferred embodiment of the utility model, metal ceramic composite bed is formed by collosol and gel coating method
Two surfaces up and down of first composite bed.
In one preferred embodiment of the utility model, passivating film is formed in metal ceramic composite bed after chromic acid salt treatment
Outer surface, the thickness of passivating film is 10 ~ 35nm.
In one preferred embodiment of the utility model, inoranic membrane is silicate films, the thickness of silicate films for 1.0 ~
5.20μm。
The beneficial effects of the utility model are:The more metal composite steel plates of the utility model can prevent surface of steel plate corrosion life
Rust, has excellent decay resistance, has higher impact resistance, pliability, chemical stability, corrosion resistance and wearability;
Excellent protective effect can be also played to surface of steel plate, it is ensured that surface of steel plate has anti-finger printing energy, ensures surface of steel plate
Brilliance it is smooth.
Brief description of the drawings
, below will be to needed for embodiment description in order to illustrate more clearly of the technical scheme in the embodiment of the utility model
The accompanying drawing to be used is briefly described, it should be apparent that, drawings in the following description are only some realities of the present utility model
Example is applied, for those of ordinary skill in the art, on the premise of not paying creative work, can also be according to these accompanying drawings
Other accompanying drawings are obtained, wherein:
Fig. 1 is the structural representation of the preferred embodiment of more metal composite steel plates one of the present utility model;
The mark of each part is as follows in accompanying drawing:100th, the first composite bed, 101, base material, 102, alumin(i)um zinc alloy layer, 200,
Two composite beds, 201, metal ceramic composite bed, 300, protective layer, 301, passivating film, 302, inoranic membrane.
Embodiment
The technical scheme in the embodiment of the utility model will be clearly and completely described below, it is clear that described
Embodiment is only part of the embodiment of the present utility model, rather than whole embodiments.Based on the implementation in the utility model
Example, all other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, is belonged to
The scope of the utility model protection.
Referring to Fig. 1, the utility model embodiment includes:
A kind of more metal composite steel plates, including:First composite bed 100, in the first composite bed, about 100 two surfaces for formation
The second composite bed 200 and formed two surfaces up and down of the second composite bed 200 protective layer 300.
The wherein thickness of the first composite bed 100 is 4 ~ 26mm, and the thickness of the second composite bed 200 is 0.05 ~ 16mm, protective layer
300 thickness is 1.50 ~ 5.25 μm.
First composite bed 100 includes a base material 101, and base material 101 is steel plate, two surface recombinations up and down of base material 101
There is alumin(i)um zinc alloy layer 102.Wherein, the thickness of base material 101 is at least 8mm, and the thickness of alumin(i)um zinc alloy layer 102 is 0.5 ~ 3mm.
Alumin(i)um zinc alloy layer 102 is compounded in two surfaces up and down of steel plate by continuously dip coat mode, can prevent surface of steel plate
Rust corrosion, there is excellent decay resistance, heat resistance is more excellent with acid resistance, and wear-resisting scratch resistance service life is grown.
Second composite bed 200 includes a metal ceramic composite bed 201, and metal ceramic composite bed 201 forms compound first
Two surfaces up and down of layer 100.
Metal ceramic composite bed 201 is that aluminium oxide ceramics composite bed, zirconia ceramics composite bed or silicon carbide ceramics are compound
Layer.
Metal ceramic composite bed 201 forms two tables up and down in the first composite bed 100 by collosol and gel coating method
Face.So, metal ceramic composite bed 201 can uniformly be stably formed the upper and lower surface in the first composite bed 100, and its with
First composite bed 100 has very high adhesion strength, has higher impact resistance, pliability, chemical stability, corrosion resistance and resistance to
Mill property.
Protective layer 300 is formed on two surfaces up and down of the second composite bed 200, including passivating film 301 and formation are blunt
Change the inoranic membrane 302 of the outer surface of film 301.
Passivating film 301 is formed in the outer surface of metal ceramic composite bed 201, the thickness of passivating film 301 after chromic acid salt treatment
Spend for 10 ~ 35nm, its forming technology is simple, cost is low, etch resistant properties are good.
Inoranic membrane 302 is silicate films, and the thickness of silicate films is 1.0 ~ 5.20 μm, it is ensured that surface of steel plate has resistance to
Fingerprint performance, ensure that the brilliance of surface of steel plate is smooth.
The beneficial effect of the more metal composite steel plates of the utility model is:
Surface of steel plate rust corrosion can be prevented, there is excellent decay resistance, there is higher impact resistance, flexible
Property, chemical stability, corrosion resistance and wearability;Excellent protective effect can be also played to surface of steel plate, it is ensured that steel plate table
Face has anti-finger printing energy, ensures that the brilliance of surface of steel plate is smooth.
Embodiment of the present utility model is the foregoing is only, not thereby limits the scope of the claims of the present utility model, it is every
The equivalent structure or equivalent flow conversion made using the utility model description, or directly or indirectly it is used in other phases
The technical field of pass, similarly it is included in scope of patent protection of the present utility model.
Claims (8)
- A kind of 1. more metal composite steel plates, it is characterised in that including:First composite bed, including a base material, base material is steel plate, and two surface recombinations up and down of base material have alumin(i)um zinc alloy layer,Second composite bed, including a metal ceramic composite bed, metal ceramic composite bed are formed at two up and down of the first composite bed Surface,Protective layer, formed on two surfaces up and down of the second composite bed, including passivating film and formation are in passivation film outer surface Inoranic membrane.
- 2. more metal composite steel plates according to claim 1, it is characterised in that the thickness of the first composite bed is 4 ~ 26mm, The thickness of second composite bed is 0.05 ~ 16mm, and the thickness of protective layer is 1.50 ~ 5.25 μm.
- 3. clad steel plate according to claim 2, it is characterised in that the thickness of base material is at least 8mm, alumin(i)um zinc alloy layer Thickness is 0.5 ~ 3mm.
- 4. clad steel plate according to claim 3, it is characterised in that alumin(i)um zinc alloy layer is compounded in by continuously dip coat mode Two surfaces up and down of steel plate.
- 5. more metal composite steel plates according to claim 1, it is characterised in that metal ceramic composite bed is aluminium oxide ceramics Composite bed, zirconia ceramics composite bed or silicon carbide ceramics composite bed.
- 6. more metal composite steel plates according to claim 5, it is characterised in that metal ceramic composite bed passes through collosol and gel Coating method is formed on two surfaces up and down of the first composite bed.
- 7. more metal composite steel plates according to claim 1, it is characterised in that passivating film is formed after chromic acid salt treatment The outer surface of metal ceramic composite bed, the thickness of passivating film is 10 ~ 35nm.
- 8. more metal composite steel plates according to claim 7, it is characterised in that inoranic membrane is silicate films, silicate films Thickness be 1.0 ~ 5.20 μm.