CN206011891U - A kind of metal wiredrawing composite steel plate - Google Patents
A kind of metal wiredrawing composite steel plate Download PDFInfo
- Publication number
- CN206011891U CN206011891U CN201620975396.6U CN201620975396U CN206011891U CN 206011891 U CN206011891 U CN 206011891U CN 201620975396 U CN201620975396 U CN 201620975396U CN 206011891 U CN206011891 U CN 206011891U
- Authority
- CN
- China
- Prior art keywords
- upside
- downside
- steel plate
- layer
- coat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model provides a kind of metal wiredrawing composite steel plate, including：Substrate, the first chemical treatment layer is provided with the upside of substrate, the second chemical treatment layer is provided with the downside of substrate, back of the body enamelled coating is provided with the downside of second chemical treatment layer, prime coat is provided with the upside of first chemical treatment layer, top coat layer is provided with the upside of prime coat, metal drawbench film is provided with the upside of top coat layer, layer of varnish is coated with the upside of metal drawbench film, the substrate includes silicon carbon alloy steel plate, 16Mn steel plates are provided with the downside of silicon carbon alloy steel plate, downside zinc coat is provided with the downside of 16Mn steel plates, titanium steel plate is provided with the upside of corrosion resistant plate, upside zinc coat is provided with the upside of titanium steel plate, downside aluminium foil clad is provided with the downside of the zinc coat of downside, upside aluminium foil clad is provided with the upside of the zinc coat of upside.The utility model is provided with metal drawbench film on the upside of top coat layer, is coated with layer of varnish on the upside of metal drawbench film, can improve surface quality, covers surface shadow scratch, improves surface aesthetics.
Description
Technical field
The utility model is related to technical field of novel materials, specially a kind of metal wiredrawing composite steel plate.
Background technology
Than wide, automobile, refrigerator, washing machine, top-grade furniture, kitchen set for application of the clad steel plate in industry and life
Standby, industrial and civil buildings etc. are required for using, and the environment that clad steel plate is used is also more and more special and more and more extensive,
Under certain particular surroundings, clad steel plate contacts the phenomenon that molecular migration can occur with other parts long-times, for
Under the traction of this molecular migration phenomenon, the space that the development of clad steel plate industry will have very wide development.
But, the surface tidiness of current clad steel plate is not high, it is impossible to avoid surface shadow scratch completely, therefore can cause
Surface is unsightly.
Utility model content
The technical problem solved by the utility model is to provide a kind of metal wiredrawing composite steel plate, to solve above-mentioned background
The problem proposed in technology.
The technical problem solved by the utility model employs the following technical solutions to realize：A kind of metal wire-drawing clad steel
Plate, including：Substrate, is provided with the first chemical treatment layer on the upside of substrate, be provided with the second chemical treatment layer, at the second chemistry on the downside of substrate
Back of the body enamelled coating is provided with the downside of reason layer, and prime coat is provided with the upside of the first chemical treatment layer, top coat layer is provided with, on top coat layer on the upside of prime coat
Side is provided with metal drawbench film, is coated with layer of varnish on the upside of metal drawbench film.The substrate includes silicon carbon alloy steel plate, silicon carbon alloy
16Mn steel plates are provided with the downside of steel plate, be provided with the upside of downside zinc coat, corrosion resistant plate and be provided with titanium steel plate, titanium steel plate on the downside of 16Mn steel plates
Upside is provided with upside zinc coat, is provided with downside aluminium foil clad on the downside of the zinc coat of downside, is provided with upside aluminium on the upside of the zinc coat of upside
Paper tinsel clad.
Further, first chemical treatment layer, the thickness of the second chemical treatment layer are 2 μm -3 μm.
Further, the thickness of the substrate is 0.02-0.25mm.
Further, the thickness of the back of the body enamelled coating is 4 μm -8 μm.
Further, the thickness of the prime coat is 4 μm -8 μm.
Further, the thickness of the top coat layer is 4 μm -8 μm.
Compared with prior art, the beneficial effects of the utility model are：The utility model is provided with metal on the upside of top coat layer
Drawing film, is coated with layer of varnish on the upside of metal drawbench film, can improve surface quality, covers surface shadow scratch, improves surface
Aesthetics.
Description of the drawings
Fig. 1 is structural representation of the present utility model.
Fig. 2 is board structure schematic diagram of the present utility model.
Specific embodiment
In order that of the present utility model realize that technological means, creation characteristic, reached purpose and effect are easy to understand, under
Face combines and is specifically illustrating, and the utility model is expanded on further.
As shown in Figure 1 and Figure 2, the clad steel plate of resistance to deep draw is planted, including：Substrate 1, is provided with the upside of substrate 1 at first chemistry
Reason layer 2, is provided with the second chemical treatment layer 3 on the downside of substrate 1, be provided with back of the body enamelled coating 8, at the first chemistry on the downside of the second chemical treatment layer 3
Prime coat 4 is provided with the upside of reason layer 2, top coat layer 5 on the upside of prime coat 4, is provided with, metal drawbench film 6 on the upside of top coat layer 5, is provided with, metal draws
Layer of varnish 7 is coated with the upside of cortina 6.
The substrate 1 includes silicon carbon alloy steel plate 11, is provided with 16Mn steel plates 12,16Mn steel plates on the downside of silicon carbon alloy steel plate 11
It is provided with the downside of in the of 12 on the upside of downside zinc coat 13, corrosion resistant plate 11 and is provided with titanium steel plate 17, on the upside of titanium steel plate 17, is provided with upside zinc coat
14, downside aluminium foil clad 15 is provided with the downside of downside zinc coat 13, is provided with upside aluminium foil clad 16 on the upside of upside zinc coat 14.
Specifically, the carbon silicon mass fraction of the silicon carbon alloy steel plate 11 is C：0.03～0.05%, Si：0.035～
0.045%.
Manufacture method of the present utility model is：
(1) 16Mn steel plates will be combined on the downside of silicon carbon alloy steel plate, plating downside zinc coat, corrosion resistant plate on the downside of 16Mn steel plates
The compound titanium steel plate in upside, plating upside zinc coat on titanium steel plate, aluminium foil clad on the downside of overlay film on the downside of the zinc coat of downside, upside are plated
Aluminium foil clad on the upside of overlay film on the upside of zinc layers, forms substrate, and the thickness of substrate is 0.02-0.25mm；
(2) by substrate after pre- degreasing, degreasing and washing, to each roller coat potassium bichromate solution of substrate front side and the back side,
I.e. substrate positive and negative has been respectively formed chemical treatment layer, i.e. the first chemical treatment layer and the second chemical treatment layer, the first chemical treatment
Layer, the thickness of the second chemical treatment layer are 2 μm -3 μm；
On the downside of (3) second chemical treatment layers, the solidification of roller coat epoxy coating is dried, and carries on the back the thickness of enamelled coating
Spend for 4 μm -8 μm；On the upside of first chemical treatment layer, the solidification of roller coat Polyester resin lacquer is dried.The thickness of prime coat
Spend for 4 μm -8 μm；
(4) on the upside of prime coat, the solidification of roller coat pearl white Polyester resin lacquer is dried
For 4 μm -8 μm, move back and forth to form metal drawbench film by adopting the cloth of silk on top coat layer, gather in the backsize of PE electron membranes
First adhesive phase is formed after the solidification of urethane adhesive, that is, PE films is obtained, on the upside of metal drawbench film, is coated with layer of varnish.
Present configuration is reasonable, novel, and product with stable quality is easy to process, can improve working (machining) efficiency during use, separately
Outer appearance looks elegant of the present invention, sense of touch are good, can be widely used in various home appliance panels.
General principle of the present utility model and principal character and advantage of the present utility model has been shown and described above.One's own profession
The technical staff of industry it should be appreciated that the utility model is not restricted to the described embodiments, described in above-described embodiment and specification
Principle of the present utility model is described simply, on the premise of without departing from the utility model spirit and scope, the utility model is also
Various changes and modifications are had, these changes and improvements are both fallen within the range of claimed the utility model.The utility model
Claimed scope by appending claims and its equivalent thereof.
Claims (6)
1. a kind of metal wiredrawing composite steel plate, including：Substrate, it is characterised in that：The first chemical treatment layer, base is provided with the upside of substrate
The second chemical treatment layer is provided with the downside of plate, is provided with back of the body enamelled coating, is provided with the upside of the first chemical treatment layer on the downside of the second chemical treatment layer
Prime coat, is provided with top coat layer on the upside of prime coat, be provided with metal drawbench film on the upside of top coat layer, is coated with varnish on the upside of metal drawbench film
Layer, the substrate includes silicon carbon alloy steel plate, is provided with 16Mn steel plates on the downside of silicon carbon alloy steel plate, is provided with downside on the downside of 16Mn steel plates
Titanium steel plate is provided with the upside of zinc coat, corrosion resistant plate, is provided with upside zinc coat, is provided with downside on the downside of the zinc coat of downside on the upside of titanium steel plate
Aluminium foil clad, is provided with upside aluminium foil clad on the upside of the zinc coat of upside.
2. a kind of metal wiredrawing composite steel plate according to claim 1, it is characterised in that：First chemical treatment layer,
The thickness of the second chemical treatment layer is 2 μm -3 μm.
3. a kind of metal wiredrawing composite steel plate according to claim 1, it is characterised in that：The thickness of the substrate is
0.02-0.25mm.
4. a kind of metal wiredrawing composite steel plate according to claim 1, it is characterised in that：The thickness of the back of the body enamelled coating is 4 μ
m-8μm.
5. a kind of metal wiredrawing composite steel plate according to claim 1, it is characterised in that：The thickness of the prime coat is 4 μ
m-8μm.
6. a kind of metal wiredrawing composite steel plate according to claim 1, it is characterised in that：The thickness of the top coat layer is 4 μ
m-8μm.