CN106079774A - A kind of preparation method of high intensity titanium aluminium foil clad steel plate - Google Patents
A kind of preparation method of high intensity titanium aluminium foil clad steel plate Download PDFInfo
- Publication number
- CN106079774A CN106079774A CN201610504887.7A CN201610504887A CN106079774A CN 106079774 A CN106079774 A CN 106079774A CN 201610504887 A CN201610504887 A CN 201610504887A CN 106079774 A CN106079774 A CN 106079774A
- Authority
- CN
- China
- Prior art keywords
- upside
- downside
- aluminium foil
- layer
- steel plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides the preparation method of a kind of high intensity titanium aluminium foil clad steel plate, including: substrate, the first chemical treatment layer it is provided with on the upside of substrate, it is provided with the second chemical treatment layer on the downside of substrate, is provided with back of the body enamelled coating on the downside of the second chemical treatment layer, on the upside of the first chemical treatment layer, is provided with prime coat, adhesive layer it is provided with on the upside of prime coat, it is provided with aluminium foil layer on the upside of adhesive layer, is coated with PET film layer on the upside of aluminium foil layer, on the upside of PET film layer, is coated with PE film.Described substrate includes corrosion resistant plate, titanium steel plate it is provided with on the downside of corrosion resistant plate, it is provided with on the downside of titanium steel plate on the upside of downside zinc coat, corrosion resistant plate and is provided with upside zinc coat, on the downside of the zinc coat of downside, be provided with downside Aluminium Foil Package coating, on the upside of the zinc coat of upside, be provided with upside Aluminium Foil Package coating.Present configuration is reasonable, novel, and product with stable quality is easy to process, can improve working (machining) efficiency during use, and appearance looks elegant the most of the present invention, sense of touch are good, can be widely used in various home appliance panel.
Description
Technical field
The present invention relates to technical field of novel materials, the preparation side of a kind of high intensity titanium aluminium foil clad steel plate
Method.
Background technology
Clad steel plate Application comparison in industry and life is extensive, and automobile, refrigerator, washing machine, top-grade furniture, kitchen set
Standby, industrial and civil buildings etc. is required for using, and the environment that clad steel plate uses is more and more special and more and more extensive,
Under certain special environment, clad steel plate and other parts Long contact time can occur the phenomenon of molecular migration, for
Under the traction of this molecular migration phenomenon, the development of clad steel plate industry will have the space of the most wide development.
The primary structure of aluminium foil film is divided into PET+ aluminium foil, and because aluminium foil surface glossiness is high, surfacing light is clean, uses glue
Paste with baseplate-laminating after, cupping adhesive force only has 3mm, and industry standard is 8mm, and adhesion performance is defective, actual production
Client's forming requirements cannot be met.
Summary of the invention
Technical problem solved by the invention is to provide the preparation method of a kind of high intensity titanium aluminium foil clad steel plate, with
The problem solving to propose in above-mentioned background technology.
Technical problem solved by the invention realizes by the following technical solutions: a kind of high intensity titanium aluminium foil clad steel
Plate, including: substrate, it is provided with the first chemical treatment layer on the upside of substrate, is provided with the second chemical treatment layer on the downside of substrate, at the second chemistry
It is provided with back of the body enamelled coating on the downside of reason layer, is provided with prime coat on the upside of the first chemical treatment layer, on the upside of prime coat, is provided with adhesive layer, binding agent
It is provided with aluminium foil layer on the upside of Ceng, is coated with PET film layer on the upside of aluminium foil layer, on the upside of PET film layer, is coated with PE film.
Described substrate includes corrosion resistant plate, is provided with titanium steel plate on the downside of corrosion resistant plate, be provided with on the downside of titanium steel plate downside zinc coat,
It is provided with upside zinc coat on the upside of corrosion resistant plate, is provided with downside Aluminium Foil Package coating on the downside of the zinc coat of downside, sets on the upside of the zinc coat of upside
There is upside Aluminium Foil Package coating.
The preparation method of a kind of high intensity titanium aluminium foil clad steel plate, comprises the following steps:
(1) by composite titanium steel plate on the downside of corrosion resistant plate, electroplate on the upside of zinc coat, corrosion resistant plate on the downside of plating on the downside of titanium steel plate
Upside zinc coat, Aluminium Foil Package coating on the downside of overlay film on the downside of the zinc coat of downside, Aluminium Foil Package coating on the upside of overlay film on the upside of the zinc coat of upside,
Form substrate;
(2) by substrate after pre-defat, defat and washing, roller coat potassium bichromate solution each to substrate front side and the back side,
I.e. substrate positive and negative has been respectively formed chemical treatment layer, the i.e. first chemical treatment layer and the second chemical treatment layer;
On the downside of (3) second chemical treatment layer, the solidification of roller coat epoxy coating is dried and is i.e. formed back of the body enamelled coating;At first chemistry
On the upside of reason layer, the solidification of roller coat Polyester resin lacquer is dried and is i.e. formed prime coat, is formed after the solidification of prime coat roller coat Polyester resin lacquer
Adhesive layer;
(4) clad aluminum layers of foil on the upside of adhesive layer, is coated with PET film layer, is coated with PE on the upside of PET film layer on the upside of aluminium foil layer
Film, forms PE film after backsize polyurethane binder of PE electron membrane solidifies.
Further, described first chemical treatment layer, the thickness of the second chemical treatment layer are 2 μm-3 μm.
Further, the thickness of described substrate is 0.02-0.25mm.
Further, the thickness of described prime coat is 4 μm-8 μm.
Further, the thickness of described back of the body enamelled coating is 4 μm-8 μm.
Compared with prior art, the invention has the beneficial effects as follows: present configuration is reasonable, novel, product with stable quality adds
Work is convenient, can improve working (machining) efficiency during use, and appearance looks elegant the most of the present invention, sense of touch are good, can be widely used in various
Home appliance panel.
Accompanying drawing explanation
Fig. 1 is the structural representation of the present invention.
Fig. 2 is the board structure schematic diagram of the present invention.
Detailed description of the invention
In order to make realizing technological means, creation characteristic, reaching purpose and be easy to understand with effect of the present invention, knot below
Conjunction is specifically illustrating, and the present invention is expanded on further.
As shown in Figure 1 and Figure 2, the preparation method of a kind of high intensity titanium aluminium foil clad steel plate, including: substrate 1, on substrate 1
Side is provided with the first chemical treatment layer 2, is provided with the second chemical treatment layer 3, is provided with the back of the body on the downside of the second chemical treatment layer 3 on the downside of substrate 1
Enamelled coating 8, is provided with prime coat 4 on the upside of the first chemical treatment layer 2, be provided with adhesive layer 5, set on the upside of adhesive layer 5 on the upside of prime coat 4
There is aluminium foil layer 6, be coated with PET film layer 7 on the upside of aluminium foil layer 6, on the upside of PET film layer 7, be coated with PE film 9.
Described substrate 1 includes corrosion resistant plate 11, is provided with titanium steel plate 12, is provided with down on the downside of titanium steel plate 12 on the downside of corrosion resistant plate 11
It is provided with upside zinc coat 14 on the upside of side zinc coat 13, corrosion resistant plate 11, on the downside of downside zinc coat 13, is provided with downside Aluminium Foil Package coating
15, it is provided with upside Aluminium Foil Package coating 16 on the upside of upside zinc coat 14.
The preparation method of a kind of high intensity titanium aluminium foil clad steel plate, comprises the following steps:
(1) by composite titanium steel plate on the downside of corrosion resistant plate, electroplate on the upside of zinc coat, corrosion resistant plate on the downside of plating on the downside of titanium steel plate
Upside zinc coat, Aluminium Foil Package coating on the downside of overlay film on the downside of the zinc coat of downside, Aluminium Foil Package coating on the upside of overlay film on the upside of the zinc coat of upside,
Form substrate;
(2) by substrate after pre-defat, defat and washing, roller coat potassium bichromate solution each to substrate front side and the back side,
I.e. substrate positive and negative has been respectively formed chemical treatment layer, the i.e. first chemical treatment layer and the second chemical treatment layer;
On the downside of (3) second chemical treatment layer, the solidification of roller coat epoxy coating is dried and is i.e. formed back of the body enamelled coating;At first chemistry
On the upside of reason layer, the solidification of roller coat Polyester resin lacquer is dried and is i.e. formed prime coat, is formed after the solidification of prime coat roller coat Polyester resin lacquer
Adhesive layer;
(4) clad aluminum layers of foil on the upside of adhesive layer, is coated with PET film layer, is coated with PE on the upside of PET film layer on the upside of aluminium foil layer
Film, forms PE film after backsize polyurethane binder of PE electron membrane solidifies.
Concrete, described first chemical treatment layer, the thickness of the second chemical treatment layer are 2 μm-3 μm.
Concrete, the thickness of described substrate 1 is 0.02-0.25mm.
Concrete, the thickness of described prime coat is 4 μm-8 μm.
Concrete, the thickness of described back of the body enamelled coating is 4 μm-8 μm.
The preparation method of the present invention is:
Substrate is carried out defat and washing processes, carry out chromium-free deactivation process in substrate front side and the back side, process in front
Pad pasting base paint special coating, processes aluminium foil glue special again, pastes aluminium foil film, re-use strong after solidification in front after solidification cooling
Cold water cools down, then pastes PE film.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.The technology of the industry
Personnel, it should be appreciated that the present invention is not restricted to the described embodiments, simply illustrating this described in above-described embodiment and description
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these become
Change and improvement both falls within scope of the claimed invention.The claimed scope of the present invention by appending claims and
Its equivalent defines.
Claims (5)
1. a preparation method for high intensity titanium aluminium foil clad steel plate, its clad steel plate includes: substrate, it is characterised in that: base
It is provided with the first chemical treatment layer on the upside of plate, is provided with the second chemical treatment layer on the downside of substrate, on the downside of the second chemical treatment layer, is provided with the back of the body
Enamelled coating, is provided with prime coat on the upside of the first chemical treatment layer, be provided with adhesive layer on the upside of prime coat, is provided with aluminium foil on the upside of adhesive layer
Layer, is coated with PET film layer, is coated with PE film on the upside of PET film layer on the upside of aluminium foil layer;Described substrate includes corrosion resistant plate, rustless steel
Being provided with titanium steel plate on the downside of plate, be provided with on the upside of downside zinc coat, corrosion resistant plate and be provided with upside zinc coat on the downside of titanium steel plate, downside is zinc-plated
Be provided with on the downside of Ceng downside Aluminium Foil Package coating, be provided with on the upside of the zinc coat of upside upside Aluminium Foil Package coating, the preparation method of clad steel plate,
Comprise the following steps:
(1) by composite titanium steel plate on the downside of corrosion resistant plate, on the downside of titanium steel plate on the downside of plating on the upside of zinc coat, corrosion resistant plate on the upside of plating
Zinc coat, Aluminium Foil Package coating on the downside of overlay film on the downside of the zinc coat of downside, Aluminium Foil Package coating on the upside of overlay film on the upside of the zinc coat of upside, formed
Substrate;
(2) by substrate after pre-defat, defat and washing, roller coat potassium bichromate solution each to substrate front side and the back side, i.e. base
Plate positive and negative has been respectively formed chemical treatment layer, the i.e. first chemical treatment layer and the second chemical treatment layer;
On the downside of (3) second chemical treatment layer, the solidification of roller coat epoxy coating is dried and is i.e. formed back of the body enamelled coating;First chemical treatment layer
Upside roller coat Polyester resin lacquer solidification is dried and is i.e. formed prime coat, forms bonding after the solidification of prime coat roller coat Polyester resin lacquer
Oxidant layer;
(4) clad aluminum layers of foil on the upside of adhesive layer, is coated with PET film layer, is coated with PE film on the upside of PET film layer on the upside of aluminium foil layer,
PE film is formed after backsize polyurethane binder of PE electron membrane solidifies.
The preparation method of a kind of high intensity titanium aluminium foil clad steel plate the most according to claim 1, it is characterised in that: described
First chemical treatment layer, the thickness of the second chemical treatment layer are 2 μm-3 μm.
The preparation method of a kind of high intensity titanium aluminium foil clad steel plate the most according to claim 1, it is characterised in that: described
The thickness of substrate is 0.02-0.25mm.
The preparation method of a kind of high intensity titanium aluminium foil clad steel plate the most according to claim 1, it is characterised in that: described
The thickness of prime coat is 4 μm-8 μm.
The preparation method of a kind of high intensity titanium aluminium foil clad steel plate the most according to claim 1, it is characterised in that: described
The thickness of back of the body enamelled coating is 4 μm-8 μm.