CN205800415U - A kind of leather of reversible color - Google Patents
A kind of leather of reversible color Download PDFInfo
- Publication number
- CN205800415U CN205800415U CN201620740198.1U CN201620740198U CN205800415U CN 205800415 U CN205800415 U CN 205800415U CN 201620740198 U CN201620740198 U CN 201620740198U CN 205800415 U CN205800415 U CN 205800415U
- Authority
- CN
- China
- Prior art keywords
- layer
- leather
- temperature
- color
- variable pigments
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses the leather of a kind of reversible color, including the fiber fabric layer set gradually from bottom to top, leather layer, temperature variable pigments coating and waterproof layer, it is connected by glue between upper surface and the bottom surface of leather layer of fiber fabric layer, temperature become be coated with by veneer, root between bottom surface and the upper surface of leather layer of dope layer, print, wheel table or spraying method are connected, being interval with the reflective projection of several tapers on the upper surface of temperature change dope layer, waterproof layer is coated in the upper surface of temperature variable pigments coating.This utility model, temperature variable pigments coating can change color along with the change of temperature, make this leather can ambient temperature less than design temperature time, various pattern and color can be manifested, when ambient temperature is higher than design temperature, picture on surface and color disappear immediately, and have reversibility, colour temp and color can arbitrarily regulate, the most colorful.
Description
Technical field
This utility model relates to leather technology field, is specifically related to the leather of a kind of reversible color.
Background technology
Leather is seen everywhere as the product that household, consumer goods industries are longer, along with improving constantly of people's life,
Also being more and more higher to material degree of viewing and admiring, the single color of leather or pattern can not meet people's need to quality of the life
Want, so the leather of changeable colour arises at the historic moment on existing market, but the most not ideal enough there are problems, as variable color is the most equal
After even, variable color, the problem such as irreversible exists.
Therefore, the leather in existing household, the articles for daily use exist variable color not uniformly, irreversible problem after variable color.
Utility model content
It is inadequate that technical problem to be solved in the utility model is that the leather in existing household, the articles for daily use exists variable color
Uniformly, irreversible problem after variable color.
In order to solve above-mentioned technical problem, this utility model be employed technical scheme comprise that the skin providing a kind of reversible color
Leather, including the fiber fabric layer set gradually from bottom to top, leather layer, temperature variable pigments coating and waterproof layer, described fabric
Being connected by glue between upper surface and the bottom surface of described leather layer of layer, described temperature becomes the bottom surface of dope layer and described leather layer
Upper surface between is coated with by veneer, root, prints, wheel table or spraying method connect, on the upper surface of described temperature change dope layer
Being interval with the reflective projection of several tapers, described waterproof layer is coated in the upper surface of described temperature variable pigments coating.
In such scheme, described waterproof layer uses transparent reflective material.
In such scheme, described leather layer uses PVC, half PU or PU material.
In such scheme, described fiber fabric layer is hollow mesh structure.
This utility model, temperature variable pigments coating can change color along with the change of temperature so that this leather can be
When ambient temperature is less than design temperature, various pattern and color can be manifested, when ambient temperature is higher than design temperature, picture on surface
And color disappears immediately, and having reversibility, colour temp and color can arbitrarily regulate, the most colorful.
Accompanying drawing explanation
Fig. 1 is structural representation of the present utility model.
Detailed description of the invention
Below in conjunction with Figure of description, this utility model is described in detail.
As it is shown in figure 1, this utility model provides the leather of a kind of reversible color, including the fibre set gradually from bottom to top
Dimensional fabric layer 4, leather layer 3, temperature variable pigments coating 2 and waterproof layer 1, the bottom surface of the upper surface of fiber fabric layer 4 and leather layer 3 it
Between connected by glue, fiber fabric layer 4 is for being wrapped in the outer surface of furniture, seamless applying with furniture, plays protection furniture
The effect that outer surface is without damage, fiber fabric layer 4 is hollow mesh structure, good permeability.
Temperature become be coated with by veneer, root between bottom surface and the upper surface of leather layer 3 of dope layer 2, print, wheel table or spraying
Mode connects, and leather layer 3 plays the supporting role of entirety, it is preferred that leather layer 3 uses PVC, half PU or PU material, low cost,
Sound construction.
Temperature becomes dope layer 2 can change the color of himself according to the change of temperature, promotes appreciation effect.Temperature variable pigments is coated with
Layer 2 is made up of the material of following mass percent: pigment Supporting Media, and 78%；Water, 20%；Dispersant, 0.2%；Anti-settling agent,
0.1%；Titanium dioxide, 2.3%；Colour developing pigment, 3.9%.Wherein, pigment Supporting Media is liquid elastomer polyurethane resin, oil
Property acrylic resin, waterborne polyurethane resin or water-borne acrylic resin.Above resin has higher strong as Supporting Media
Degree, hardness, resistance to water, solvent resistance.
Colour developing pigment can select temperature colour developing powder blue or other pigment as required.As a example by temperature colour developing powder orchid, temperature becomes
The colour temp scope of pigment coated 2 is-10～25 degrees Celsius, less than-10 degrees Celsius or more than 25 degrees Celsius this temperature model
Enclosing, temperature variable pigments coating 2 does not develops the color, and in this temperature range, along with the changes colour of temperature, along with the increase of temperature, temperature becomes
Pigment coated 2 gradually change, and become flower green, red, blueness successively.
Being interval with several tapers reflective protruding 21 on the upper surface of temperature change dope layer 2, taper reflective protruding 21 can
Temperature becomes the color after dope layer 2 changes well reflect and display, increase third dimension and aesthetic property.
Waterproof layer 1 is coated in temperature variable pigments coating 2 upper surface.Waterproof layer 1 uses transparent reflective material, is coated with temperature variable pigments
Layer 2 plays the effect of protection, and temperature variable pigments coating 2 will not be caused damage, transparent reflective material not shadow by general domestic water
Ring pattern texture and the displaying of color in temperature variable pigments coating 2.
This utility model additionally provides the manufacture method of the leather of a kind of reversible color, comprises the following steps:
Make temperature variable pigments, weigh the material of following mass percent: pigment Supporting Media, 78%；Water, 20%；Dispersion
Agent, 0.2%；Anti-settling agent, 0.1%；Titanium dioxide, 2.3%；Colour developing pigment, 3.9%；By above-mentioned material mix homogeneously, and heat
Melted, obtain allochroic paint.
Preferably, during making temperature variable pigments, the material of each component is put into agitator, mixed by blender
Close uniformly, obtain mixed material；Mixed material is heated, is heated to 50～60 degrees Celsius, cooling, obtain the Wen Bianyan after variable color
Material.
Carry out base at the bottom of leather cutting, grinding process so that upper and lower smooth surface, obtain leather layer 3；
Fiber fabric layer 4 is pasted onto on the bottom surface of leather layer 3 by glue；
Temperature variable pigments is covered with paint, lacquer, colour wash, etc. the upper surface at leather layer 3, during temperature variable pigments is covered with paint, lacquer, colour wash, etc., employing veneer,
Root is coated with, prints, wheel table or the mode of spraying, and the upper surface of temperature variable pigments is carried out extrusion process, obtains taper reflective convex
Play 21, be placed on ventilation and be dried, obtain temperature variable pigments coating 2；
Waterproof layer 1 is coated in the upper surface of temperature variable pigments coating 2, i.e. can get finished product.
This utility model, temperature variable pigments coating can change color along with the change of temperature so that this leather can be
When ambient temperature is less than design temperature, various pattern and color can be manifested, when ambient temperature is higher than design temperature, exterior view
Case and color disappear immediately, and have reversibility, and colour temp and color can arbitrarily regulate, the most colorful.
This utility model is not limited to above-mentioned preferred forms, and anyone should learn under enlightenment of the present utility model
The structure change made, every have same or like technical scheme with this utility model, each falls within guarantor of the present utility model
Within the scope of protecting.
Claims (4)
1. the leather of a reversible color, it is characterised in that the fiber fabric layer that includes setting gradually from bottom to top, leather layer,
Temperature variable pigments coating and waterproof layer, between upper surface and the bottom surface of described leather layer of described fiber fabric layer by glue even
Connect, described temperature become be coated with by veneer, root between bottom surface and the upper surface of described leather layer of dope layer, print, wheel table or spray
Painting mode connects, and the upper surface of described temperature change dope layer is interval with the reflective projection of several tapers, and described waterproof layer coats
Upper surface in described temperature variable pigments coating.
The leather of a kind of reversible color the most as claimed in claim 1, it is characterised in that described waterproof layer uses transparent reflective material
Matter.
The leather of a kind of reversible color the most as claimed in claim 1, it is characterised in that described leather layer use PVC, half PU or
PU material.
The leather of a kind of reversible color the most as claimed in claim 1, it is characterised in that described fiber fabric layer is hollow mesh
Structure.