CN205637406U - Take heat retaining nanometer mud base artificial dull and stereotyped stone material that excels in - Google Patents
Take heat retaining nanometer mud base artificial dull and stereotyped stone material that excels in Download PDFInfo
- Publication number
- CN205637406U CN205637406U CN201620351230.7U CN201620351230U CN205637406U CN 205637406 U CN205637406 U CN 205637406U CN 201620351230 U CN201620351230 U CN 201620351230U CN 205637406 U CN205637406 U CN 205637406U
- Authority
- CN
- China
- Prior art keywords
- plate
- screw rod
- nut block
- stone
- decorative board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model provides a take heat retaining nanometer mud base artificial dull and stereotyped stone material that excels in, includes veneer panel, heated board, and characterized by veneer panel splices together with the heated board, has buried the nut piece in the veneer panel underground, and the position that the heated board corresponds the nut piece is equipped with the perforation of screw rod connecting piece, and nut piece one end is connected with the screw rod connecting piece, and the screw rod connecting piece other end is connected with hanging strip. The utility model discloses the principle is peeled off on application lithotome surface, forms the plain noodles, burns surperficial decorative effect such as face, litchi face with stone machinery and overcome technical problem such as a lacquer type finish coat easily fades, delaminating. Utilize the characteristic of cement -based materials from liquid to the solid, in the panel production process, pre -buried can interconnect the nut piece, combine screw rod, hanging strip, the expansion bolts that implants with the wall body locks each other, forms the whole of an interconnection, even the adhesive with paste mortar viscidity and reduce completely and also can guarantee its security to overcome current heat preservation intergral template's various drawbacks.
Description
Technical field
This utility model relates to building decoration field, and it is high-strength that a kind of nano cement sill makes
The production of the heat insulation decoration integrated plate that artificial flat-plate stone is combined with all kinds of warming plates and installation method.
Background technology
Existing heat insulation decoration integrated plate, mainly has:
1. using the sheet materials such as metallic plate, aluminium-plastic panel, calcium silicate board with microporous to be bonded with all kinds of warming plates by adhesive, plate surface sprays
It is coated with all kinds of coating or mineral varnish forms integrated plate for heat insulation；
2. use natural veneer stone material, porcelain silicon etc. to form integrated plate for heat insulation by adhesive with the bonding of all kinds of warming plates；
3. use and paste network cloth formation surface layer with mortar on all kinds of warming plate faces, then directly each in surface layer spraying
Class coating or mineral varnish form decorative integrated plate.
Installation all uses mortar to paste, and part adds between surface layer plate and warming plate adhesion or is directly clamped among
Middle suspension member.Suspension member is fixed at body of wall expandable implant bolt during installation.
Above-mentioned technique has the disadvantage in that
1. weatherability is poor: existing all kinds of coating and mineral varnish are combined by various industrial chemicals, at long-time acid rain, ash
Being easy to oxidation decoloration occur under the environment such as dirt, the temperature difference, radiation, ftracture skin effect phenomenon, i.e. there will be above-mentioned asking some one or two years
Topic, makes house become the most shabby.
2. poor stability: various sheet materials are all bonded with warming plate by adhesive, is also that all kinds of sticking mortar glues during installation
Even, owing to the material character between decoration panel, warming plate, body of wall three is different, shrinkage rates liquid is different, and empty for a long time
Under the environment such as gas, rainwater, blast, the temperature difference, Binder Materials viscosity reduces, the deadweight of sheet material in addition, it is easy to cause delamination, drop
Phenomenon.Although have adds suspension member, but owing to all kinds of sheet materials have been solid state.Stainless steel can only stick in the sheet material back of the body
Portion, or directly card is placed between surface layer plate and warming plate, and the natural drawback of adhesive cannot overcome equally.
Summary of the invention
For the problems referred to above, this utility model provides the life of the high-strength artificial flat-plate stone of nano cement base of a kind of band insulation
Produce and installation method solves above-mentioned technical problem.
This utility model concrete scheme is as follows: the high-strength artificial flat-plate stone of nano cement base of a kind of band insulation, including decorations
Panel material, warming plate, is characterized in that decorative board is glued together with warming plate, is embedded with nut block in decorative board, insulation
The position of plate correspondence nut block is provided with bolt jointing part perforation, and nut block one end is connected with bolt jointing part, and bolt jointing part is another
One end is connected with hanging strip.
As preferably, described nut block longitudinal section is convex shape, and its nut block center is provided with screw, surrounding bottom nut block
Being provided with wing plate, described wing plate is embedded in decorative board, and nut block top maintains an equal level with the decorative board back side.
As preferably, described bolt jointing part is tack or countersunk head screw rod, screw rod through the perforation of hanging strip hole and warming plate and
Nut block connects.
The high-strength artificial flat-plate stone of nano cement base of a kind of band insulation, is characterized in that this decorative board following component is by weight
Amount ratio is made: cement 100 parts, flyash 15-30 part, slag powders 10-20 part, SILICA FUME 5-10 part, nanosized SiO_2 3-7 part, 4-
8 mesh rice stone 150-200 parts, 10-20 mesh rice stone 100-150 part, 40-80 mesh stone powder 25-50 part, iron oxide pigment 0-5 part, hydrophobic
Rubber powder 1-3 part, extender 5-10 part, poly-third fiber 0.1-0.5 part, water reducer 0.5-1.5 part, water-cement ratio 0.18-0.25.
The manufacture method of the high-strength artificial flat-plate stone of nano cement base of a kind of band insulation, comprises the following steps:
One. decorative board makes:
Mold Making: according to the sheet material specification of required making, has certain degree of hardness with metal, plastics, composite, timber etc.
Material is fabricated to box-like mould, and coats remover.
1. artificial stone material is added water by water-cement ratio and stir into slurry.
2. the mould putting into slurry is put into and vibrate on four-column hydraulic press platform.
3. in the mould vibrated, put nut block by defined location, with the alignment mould inside casing pressurization of hydraulic press pressing plate
And simultaneously evacuation.
4. the mould by static pressure evacuation is layered stacked, and sends into fog room maintenance.
Two. decorative board surface processes:
1. the machineries such as sheet material stone polishing machine good for maintenance, baked wheaten cake face machine, bush-hammered face machine are carried out surface process.
2. the sheet material cleaning will handled well, and carry out hexahedro hydrophobic process.
Three. the high-strength artificial flat-plate stone of nano cement base of band insulation makes:
1. the warming plate of desirable type is cut out material, punching by specification；
2. by artificial slabstone back brush coating stick；
3. by the sheet material face down of brush coating, put on press bench, the warming plate of brush coating be directed at sheet material back,
Open forcing press compacting, obtain the high-strength artificial flat-plate stone of nano cement base of band insulation.
The installation method of the high-strength artificial flat-plate stone of nano cement base of a kind of band insulation, comprises the following steps:
1. hanging strip bolt jointing part is connected standby with decorative board back nut block；
2. cleaning base course wall, and unwrapping wire determines installation site；
3. add water stirring by sticking mortar, and is put on warming plate back, taps to standard thickness with skin hammer；
4. punch on the body of wall at the hanging strip hole of hanging strip, and expandable implant bolt, hanging strip is tightened solid with expansion bolt
It is scheduled on body of wall；
5. dividing joint gluing, stamps foamed glue bottom warming plate, with sponge stick on foamed glue, finally at decorative board with resistance to
Wait glue jointing complete；
6. clear up and spray hydrophober.
As preferably, described decorative board is more than C60 strength criterion.
As preferably, Nano-meter SiO_2 in described decorative board2Purity is not less than 99.5%, and particle diameter is 20-30nm.
As preferably, the water reducer in described decorative board is high-efficiency water-reducing agent of poly-carboxylic acid.
As preferably, described four-column hydraulic press, suppress (1000-for possessing high frequency vibrating (725-1450 beat/min)
2000KN) evacuation (below 0.06MPa) functions machine.
Beneficial effect
This utility model uses lithotome sur-face peeling principle, forms bright finish, baked wheaten cake face, bush-hammered face etc. with stone machining equipment
Surface decoration effect overcomes the technical problems such as paint class finish coat fugitive color, delamination.Utilize cement-based material from liquid to solid
Characteristic, in production process of plate, pre-buried can with interconnective nut block, combine screw rod, expansion that hanging strip and body of wall are implanted
Bolt mutually locks, and forms the entirety of an interconnection, even if adhesive and sticking mortar viscosity reduce completely also can guarantee that it is pacified
Quan Xing, thus overcome the various drawbacks of existing integrated plate for heat insulation.It is embodied in:
One, low cost
With cement, hardened fly ashes, slag powders as major gelled material, add a large amount of discarded aggregate chips, stone powder, thus be substantially reduced
Cost.
Two, good endurance
Use high-strength concrete formula, add nanometer adjuvant and anti-fiber of tearing open, use shake by force, suppress, evacuation process, make
The degree of compaction of sheet material, intensity are greatly improved, endosmosis hydrophobic rubber powder and outer painting hydrophober, make the water absorption rate of sheet material be preferably minimized, from
And exceed 50 year service life of concrete.
Three, good weatherability
Plate surface uses and lithotome surface identical stripping technology principle, and
The various decorative effects formed, due to without spraying any coating or mineral varnish, thus it is weather-proof to there is not paint class facing
Fade produced by property difference, the drawback such as come off.
Four, safety is good
Utilizing cement-based material characteristic from liquid to solid pre-buried trapezoidal nut block, melting completely after sheet material solidifies is one
Body, in conjunction with screw rod, hanging strip and the expansion bolt implanting body of wall are interconnected to form an entirety, drop completely in adhesion slurry viscosity
After low, do not have obscission yet.
Five, rich color, no color differnece
Utilize the rubble of nature shades of colour, various pigment can be added in right amount, use unified mark
Quasi-metrology recipe, and industrial equipment spice, make product color abundant unified.
Six, environmental protection
Add a large amount of discarded Herba Epigeneii fargesii, without firing, without chemical reaction, without garbage generation,
Avoid welding of cutting into a mountain for quarrying.
Accompanying drawing explanation
Fig. 1 is a kind of structural representation of the present utility model；
Fig. 2 is decorative board cross-sectional view of the present utility model；
Fig. 3 is decorative board perspective structure schematic diagram of the present utility model；
Fig. 4 is perspective structure schematic diagram of the present utility model；
Fig. 5 is mounting structure schematic diagram of the present utility model；
Fig. 6 is this utility model mounting structure sectional view.
Detailed description of the invention
Make to comment further to technical solutions of the utility model below in conjunction with embodiment:
Embodiment one:
One. raw material configures: the high-strength artificial flat-plate stone of nano cement base of band insulation is made up of following material with weight portion
Number calculates: cement 100 parts, flyash 15-30 part, slag powders 10-20 part, SILICA FUME 5-10 part, Nano-meter SiO_223-7 part, 4-8 mesh
Rice stone 150-200 part, 10-20 mesh rice stone 100-150 part, 40-80 mesh stone powder 25-50 part, iron oxide pigment 0-5 part, hydrophobic glue
Powder 1-3 part, extender 5-10 part, poly-third fiber 0.05-0.1 part, water reducer 0.5-1.5 part, water-cement ratio 0.18-0.25.Described
Cement is white portland cement or the Portland cement of more than 425 strength grades；Described flyash is more than II grade powder
Coal ash；Described slag powders is the above slag powders of S95 level；Described SILICA FUME is purity 92% SILICA FUME；Described Nano-meter SiO_22For SiO2
Content is not less than 99.5, the Nano-meter SiO_2 of particle diameter 20-30nm2；Described Herba Epigeneii fargesii, stone powder are the various face for hardness more than 5 grades of rubbing
Granule that the stone of color is made and powder body；Described hydrophobic rubber powder is water soluble, has the latex of good redispersible performance
Dry powder；Described poly-third fiber is the polypropylene short merit fiber of specification 6-12mm；Described extender is the expanding cement of aluminium sulfate；
Described water reducer is high-efficiency water-reducing agent of poly-carboxylic acid, liquid powdery.
Mixed powder material is formulated as follows: 1. choose Herba Epigeneii fargesii and stone powder according to the sheet material color of required preparation；2. with forcing
Formula blender presses cement, coal ash, breeze, SILICA FUME, Nano-meter SiO_22, rubber powder, iron oxide pigment, stone powder, Herba Epigeneii fargesii, fiber step by
Step is thrown in stirring and is packed standby to the most uniformly.
Sheet material specification: 600mm × 800m thickness: 10mm color: imitative Giallo Cecilia smooth effect
Warming plate kind: extrusion molding polystyrene polyfoam (being called for short XPS) thickness 30mm
Two. the high-strength artificial flat-plate stone of nano cement base produces and installation method:
1. Mold Making metallic plate or wood composite board or plastic plate are as base plate and frame, in punching locking is fabricated to
Frame is the square diaphragm capsule of 600 × 800mm, and is coated with that to touch releasing agent standby；
2. the imitative Giallo Cecilia dry powder of preparation is added water by water-cement ratio 0.2 and water reducer stirs into slurry；
3. slurry is thrown in mould, mould is put into open on four-column hydraulic press platform vibrator vibration 30s(institute
State four-column hydraulic press, for possess dither (725-1450 beat/min) suppress (1000-2000KN) evacuation (0.06MPa with
Under) functions machine)；
4., by specifying position to put nut block 3 in mould, nut block 3 longitudinal section is convex shape, and its nut block 3 center sets
There is screw 6, bottom nut block 3, be formed around wing plate 31.
5. static pressure machine top hold-down being directed at mould inside casing, comparison is accurate, opens hydraulic press and suppresses with 200 tons of pressure, and
Open evacuator simultaneously, be evacuated to 0.08MPa time 60s；
6. by die layout on smooth removable supporting plate；
7. carry out continuing operation by above-mentioned steps；
8. mould is sent into steam-curing chamber, about 50 DEG C curing times of curing temperature 24 hours；
9. the mold releasability that will solidify, and send into fog room continuation maintenance, 3-5 days time；
10., by the sheet material of maintenance to normal intensity, polish with continuous polishing machine；
The stone glue that surface is had the place of gap to mix colours by 11. cleanings is repaired, and is polished to phase with manual polishing machine
Same standard, obtains decorative board 1；
12. carry out hexahedro hydrophobic process with colourless hydrophober to decorative board 1；
Decorative board 1 face down is placed on forcing press platform by 13., by polyurethane adhesive 9 scraper plate, scrapes on sheet material,
Smear uniformly；
14. will be cut out by decorative board 1 specification and smear poly-according to the XPS warming plate scraper plate of sheet material nut location punching
Urethane glue；
Warming plate 2 is aligned by 15. with decorative board 1 ratio, opens the forcing press press time 6 hours；
16. by hanging strip 4 with bolt jointing part 5 be directed at nut block 3 tighten obtain band insulation nano cement base high-strength artificial
Flat-plate stone, this artificial flat-plate stone structure is mainly made up of decorative board 1, warming plate 2, wherein decorative board 1 and warming plate 2
Being glued together, be embedded with nut block 3 in decorative board 1, nut block wing plate 31 is embedded in decorative board 1, nut block 3 top
Maintaining an equal level with decorative board 1 back side, the position of the corresponding nut block 3 of warming plate 2 is provided with bolt jointing part 5 and bores a hole, nut block 3 one end with
Bolt jointing part 5 connects, and bolt jointing part 5 other end is connected with hanging strip 4.Bolt jointing part 5 is tack or countersunk head screw rod 52, spiral shell
Bar 52 is connected through hanging strip hole 41 with warming plate 2 perforation and nut block 3.
17. cleaning metopes, and unwrapping wire confirmation installation site；
Sticking mortar 13 is added water modulation slurry by 18.；
19. use point type mounting method, and mortar is put on insulation back, and alignment installation site skin hammer taps to standard high gently
Degree；
Punch on 20. bodies of wall 7 at the hanging strip hole 41 of hanging strip 4, and expandable implant bolt 8, will hang with expansion bolt 50
Bar 4 is tightened on body of wall 7, and carries out the installation of lower block of plate；
Polyurethane foam glue 12 is injected in sheet material partitioning slot by 21., to be advisable less than 2/3, will accomplish fluently foamed glue 12
Dividing joint sponge stick 10 continues to fill up, and finally fills tight with fluid sealant 11；
22. cleaning surface irregularities, after checking that dividing joint is the most closely knit, surface all sprays hydrophober.
Embodiment two
Specification: 500 × 500mm thickness: 10mm color: imitative Indian red bush-hammered face effect
Warming plate kind: polyurethane heat-insulation plate thickness 40mm, except being formed at bush-hammered face with bush-hammered face of stone material machine, other are same
Embodiment 1 makes and installation method.
Embodiment three
Specification: 1200 × 900mm thickness: 12mm color: imitative Sesame White burns face effect
Warming plate kind: cement foamed plate thickness 50mm, is formed at baked wheaten cake face except burning face machine with stone material, and other are with real
Execute example 1 to make and installation method.
Claims (3)
1. the high-strength artificial flat-plate stone of nano cement base of band insulation, including decorative board, warming plate, is characterized in that facing
Sheet material is glued together with warming plate, is embedded with nut block in decorative board, and the position of warming plate correspondence nut block is provided with screw rod
Connector is bored a hole, and nut block one end is connected with bolt jointing part, and the bolt jointing part other end is connected with hanging strip.
The high-strength artificial flat-plate stone of nano cement base of band the most according to claim 1 insulation, is characterized in that described nut
Block center is provided with screw, is formed around wing plate bottom nut block, and described wing plate is embedded in decorative board, nut block top and decorations
Face plate back maintains an equal level.
The high-strength artificial flat-plate stone of nano cement base of band the most according to claim 1 insulation, is characterized in that described screw rod
Connector is tack or countersunk head screw rod, and screw rod is connected through hanging strip hole with warming plate perforation and nut block.