CN204073649U - 一种耐高温、高阻燃性覆膜滤料 - Google Patents
一种耐高温、高阻燃性覆膜滤料 Download PDFInfo
- Publication number
- CN204073649U CN204073649U CN201420557837.1U CN201420557837U CN204073649U CN 204073649 U CN204073649 U CN 204073649U CN 201420557837 U CN201420557837 U CN 201420557837U CN 204073649 U CN204073649 U CN 204073649U
- Authority
- CN
- China
- Prior art keywords
- flame retardant
- filter material
- coated filter
- high temperature
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
本实用新型为一种耐高温、高阻燃性覆膜滤料，所述覆膜滤料包括三层结构，上层为膨体聚四氟乙烯膜层，作为表面过滤功能层；下层为透气性阻燃基材层，作为支撑层，所述聚四氟乙烯膜层与透气性阻燃基材层之间通过胶黏剂层粘合。本实用新型具有耐高温以及阻燃特性优良的优点。
Description
技术领域
本实用新型涉及覆膜滤料领域，具体涉及一种耐高温、高阻燃性覆膜滤料。
背景技术
聚四氟乙烯(PTFE)具有高化学稳定性、耐高低温性、高阻燃性、低表面能等优异性能，其通过挤出、压延、拉伸等工序制备得到的膨体PTFE膜具有优异的防水性和透气性，属于表面过滤，过滤效率高，易清灰，可重复使用，是一种理想的过滤材料。然而PTFE膜厚度一般很薄(<10um)，其力学性能不能满足实际使用要求，往往需要通过和支撑材料覆合后使用。目前，耐高温、高阻燃性覆膜滤料领域选用最多的阻燃支撑材料是玻璃纤维、芳纶纤维等透气性阻燃材料，其与PTFE膜覆合工艺都会涉及到高温处理工序。
实用新型内容
为了克服上述技术问题，本实用新型旨在提供一种具有耐高温且阻燃的覆膜滤料。
为了达到上述目的，本实用新型所设计的一种耐高温、高阻燃性覆膜滤料，所述覆膜滤料包括三层结构，上层为膨体聚四氟乙烯膜层，作为表面过滤功能层；下层为透气性阻燃基材层，作为支撑层，所述聚四氟乙烯膜层与透气性阻燃基材层之间通过胶黏剂层粘合。
作为优选，所述PTFE膜呈现纤维互穿网络结构，孔径范围在0.3-3.0um。
进一步地，所述透气性阻燃基材层可选用玻璃纤维、聚酰亚胺纤维、芳纶纤维、阻燃改性聚酯纤维、碳纤维、金属纤维或者硅石纤维。
进一步地，所述胶黏剂层为有机磷酸酯类阻燃剂与聚氨酯的混合物，有机磷酸酯类阻燃剂与聚氨酯按质量比为1:100—50:100。
与现有技术相比，本实用新型具有耐高温以及阻燃特性优良的优点。
附图说明
图1为本实用新型的的结构示意图；
图中：1、聚四氟乙烯膜层，2、粘合层，3、透气性阻燃基材层。
具体实施方式
下面通过实施例结合附图对本实用新型作进一步的描述。
如图1所示，本实用新型为一种耐高温、高阻燃性覆膜滤料，所述覆膜滤料包括三层结构，上层为膨体聚四氟乙烯膜层1，作为表面过滤功能层；下层为透气性阻燃基材层3，作为支撑层，所述聚四氟乙烯膜层与透气性阻燃基材层之间通过胶黏剂层2粘合。所述PTFE膜呈现纤维互穿网络结构，孔径范围在0.3-3.0um。所述透气性阻燃基材层可选用玻璃纤维、聚酰亚胺纤维、芳纶纤维、阻燃改性聚酯纤维、碳纤维、金属纤维或者硅石纤维。所述胶黏剂层为有机磷酸酯类阻燃剂与聚氨酯的混合物，有机磷酸酯类阻燃剂与聚氨酯按质量比为1:100—50:100。
以上对本实用新型的具体实施例进行了描述。需要理解的是，本实用新型并不局限于上述特定实施方式，本领域技术人员可以在权利要求的范围内做出各种变形或修改，这并不影响本实用新型的实质内容。
Claims (4)
1.一种耐高温、高阻燃性覆膜滤料，其特征在于，所述覆膜滤料包括三层结构，上层为膨体聚四氟乙烯膜层，作为表面过滤功能层；下层为透气性阻燃基材层，作为支撑层，所述聚四氟乙烯膜层与透气性阻燃基材层之间通过胶黏剂层粘合。
2.根据权利要求1所述的一种耐高温、高阻燃性覆膜滤料，其特征在于，所述PTFE膜呈现纤维互穿网络结构，孔径范围在0.3-3.0um。
3.据权利要求1所述的一种耐高温、高阻燃性覆膜滤料，其特征在于，所述透气性阻燃基材层可选用玻璃纤维、聚酰亚胺纤维、芳纶纤维、阻燃改性聚酯纤维、碳纤维、金属纤维或者硅石纤维。
4.据权利要求1所述的一种耐高温、高阻燃性覆膜滤料，其特征在于，所述胶黏剂层为有机磷酸酯类阻燃剂与聚氨酯的混合物，有机磷酸酯类阻燃剂与聚氨酯按质量比为1:100—50:100。