CN203594124U - Reinforced phenolic foam color steel laminboard - Google Patents
Reinforced phenolic foam color steel laminboard Download PDFInfo
- Publication number
- CN203594124U CN203594124U CN201320697469.6U CN201320697469U CN203594124U CN 203594124 U CN203594124 U CN 203594124U CN 201320697469 U CN201320697469 U CN 201320697469U CN 203594124 U CN203594124 U CN 203594124U
- Authority
- CN
- China
- Prior art keywords
- plate
- phenol formaldehyde
- steel
- formaldehyde foam
- color steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
A reinforced phenolic foam color steel laminboard is characterized by comprising an upper color steel contour plate, a lower color steel flat plate and an insulation interlaid layer; the lower surface of the upper color steel contour plate and the upper surface of the lower color steel flat plate are coated with binders and form an upper binder layer and a lower binder layer respectively after being dried; the insulation interlaid layer is composed of phenolic foam, a rectangular phenolic insulation plate block and two steel wire gauze layers, and the phenolic foam and the phenolic insulation plate block are located between the two steel wire gauze layers. The reinforced phenolic foam color steel laminboard has the advantages of being high in strength, good in toughness, environmentally friendly, high in combustion performance level, attractive in appearance, long in service life and capable of resisting corrosion by strong acid and weak base, insulating sound and lowering noise.
Description
Technical field
The utility model relates to building board structure field, particularly a kind of reinforced phenol formaldehyde foam chromatic steel sandwich plate.
Background technology
So far, the chromatic steel sandwich plate that domestic construction field is generally used, its laminboard layer is take inorganic heat insulation materials such as organic foam heat insulating material or rock-wool heat insulation plate, glass wool thermal insulation board such as expanded polystyrene foams, extruded polystyrene foam, polyurethane foams as main.Wherein, aforementioned three kinds of organic foam heat insulating materials belong to combustible material together, and when burning, flame propagation velocity is exceedingly fast and produces a large amount of hypertoxic flue gases, has caused grave danger to people's safety of life and property.Domestic chromatic steel sandwich plate fire cases can be found everywhere, and has beaten alarm bell to compatriots.Although can reaching, the combustibility rank of three kinds of inorganic heat insulation materials that chromatic steel sandwich plate is conventional do not fire A level, the defects such as poor, the easy water suction of ubiquity heat insulation effect, unit weight are large, construction inconvenience, easily breed bacteria, fiber fines be harmful.
For addressing the above problem, people actively seek a kind of heat insulating material of excellent combination property, and thus, phenolic aldehyde foam thermal insulation material enters people's the visual field.Phenol formaldehyde foam belongs to organic obturator-type thermosetting rigid foam, have both that environmental protection, light weight are high-strength, adiabatic heat-insulation, the burn into of resistance to strong acid weak base good stability of the dimension, low-smoke low-toxicity, flame resistant penetrate, meet fire difficultly fire, shrink, without drippage, without the feature such as melting, indeformable, be the best one of combination property in all heat insulating materials.
In recent years, phenol formaldehyde foam industry has obtained tremendous development, product category is abundant gradually, be widely used in the industries such as building, pipe insulation, household electrical appliances, communications and transportation, indoor decorating, formed the series of products such as phenolic foam heat insulation plate, phenol formaldehyde foam insulating tube, phenolic foam composite insulation board, phenol formaldehyde foam aluminium foil filled board, phenol formaldehyde foam insulation and decoration integrated plate, phenol formaldehyde foam chromatic steel sandwich plate.But phenol formaldehyde foam is also non-perfect in every way, its fragility is large, bend resistance ability is poor.In addition, there are a large amount of leftover bits in phenolic foam products, if things go on like this, will damage natural environment in production and use procedure.
Utility model content
The purpose of this utility model is in order to overcome the deficiencies in the prior art, and spy provides a kind of reinforced phenol formaldehyde foam chromatic steel sandwich plate.
The utility model provides a kind of reinforced phenol formaldehyde foam chromatic steel sandwich plate, it is characterized in that: described reinforced phenol formaldehyde foam chromatic steel sandwich plate, top color corrugated sheet steel, the color steel surface plate in bottom and thermal insulation clamp sandwich layer, the upper surface coated with adhesive of the color steel surface plate in the soffit of top color corrugated sheet steel and bottom, after drying, form respectively upper adhesive layer and lower adhesive layer, thermal insulation clamp sandwich layer is made up of phenol formaldehyde foam, rectangle phenolic aldehyde heat preserving plate and two-layer gauze wire cloth, and phenol formaldehyde foam and phenolic aldehyde heat preserving plate are between two-layer gauze wire cloth.
Described top color corrugated sheet steel, the thickness of the color steel surface plate in bottom are 0.2~4.0mm, and top color corrugated sheet steel is trapezoidal rib shape bulge-structure with cross section, and bulge-structure spacing is 20~100mm.
After described phenol formaldehyde foam is all mixed by phenolic resins, curing compound, surfactant, blowing agent, modifier etc., through heating, foaming, curing making.
The structure of phenolic aldehyde heat preserving plate is that rectangular structure, triangular prism structure or six ribs are lived structure.
Described thermal insulation clamp sandwich layer density is 30~100kg/m3.
In described thermal insulation clamp sandwich layer, the ratio of the volume of phenol formaldehyde foam and the volume of phenolic aldehyde heat preserving plate is 0.01~10000.
Advantage of the present utility model:
Reinforced phenol formaldehyde foam chromatic steel sandwich plate described in the utility model, intensity is high, good toughness, environmental protection, combustibility rank are high, good looking appearance, long service life, the burn into of resistance to strong acid weak base sound insulation and noise reduction.
Accompanying drawing explanation
Below in conjunction with drawings and the embodiments, the utility model is described in further detail:
Fig. 1 is reinforced phenol formaldehyde foam chromatic steel sandwich plate structural representation;
In figure, 1 is top color corrugated sheet steel, and 2 is the color steel surface plate in bottom, and 3 is phenol formaldehyde foam, and 4 is gauze wire cloth, and 5 is phenolic aldehyde heat preserving plate.
The specific embodiment
The present embodiment provides a kind of reinforced phenol formaldehyde foam chromatic steel sandwich plate, it is characterized in that: described reinforced phenol formaldehyde foam chromatic steel sandwich plate, top color corrugated sheet steel, the color steel surface plate in bottom and thermal insulation clamp sandwich layer, the upper surface coated with adhesive of the color steel surface plate in the soffit of top color corrugated sheet steel and bottom, after drying, form respectively upper adhesive layer and lower adhesive layer, thermal insulation clamp sandwich layer is made up of phenol formaldehyde foam, rectangle phenolic aldehyde heat preserving plate and two-layer gauze wire cloth, and phenol formaldehyde foam and phenolic aldehyde heat preserving plate are between two-layer gauze wire cloth.
Described top color corrugated sheet steel, the thickness of the color steel surface plate in bottom are 0.2mm, and top color corrugated sheet steel is trapezoidal rib shape bulge-structure with cross section, and bulge-structure spacing is 20mm.
After described phenol formaldehyde foam is all mixed by phenolic resins, curing compound, surfactant, blowing agent, modifier etc., through heating, foaming, curing making.
The structure of phenolic aldehyde heat preserving plate is rectangular structure.
Described thermal insulation clamp sandwich layer density is 30kg/m3.
In described thermal insulation clamp sandwich layer, the ratio of the volume of phenol formaldehyde foam and the volume of phenolic aldehyde heat preserving plate is 0.01.
The present embodiment provides a kind of reinforced phenol formaldehyde foam chromatic steel sandwich plate, it is characterized in that: described reinforced phenol formaldehyde foam chromatic steel sandwich plate, top color corrugated sheet steel, the color steel surface plate in bottom and thermal insulation clamp sandwich layer, the upper surface coated with adhesive of the color steel surface plate in the soffit of top color corrugated sheet steel and bottom, after drying, form respectively upper adhesive layer and lower adhesive layer, thermal insulation clamp sandwich layer is made up of phenol formaldehyde foam, rectangle phenolic aldehyde heat preserving plate and two-layer gauze wire cloth, and phenol formaldehyde foam and phenolic aldehyde heat preserving plate are between two-layer gauze wire cloth.
Described top color corrugated sheet steel, the thickness of the color steel surface plate in bottom are 3.0mm, and top color corrugated sheet steel is trapezoidal rib shape bulge-structure with cross section, and bulge-structure spacing is 60mm.
After described phenol formaldehyde foam is all mixed by phenolic resins, curing compound, surfactant, blowing agent, modifier etc., through heating, foaming, curing making.
The structure of phenolic aldehyde heat preserving plate is triangular prism structure.
Described thermal insulation clamp sandwich layer density is 65kg/m3.
In described thermal insulation clamp sandwich layer, the ratio of the volume of phenol formaldehyde foam and the volume of phenolic aldehyde heat preserving plate is 500.
The present embodiment provides a kind of reinforced phenol formaldehyde foam chromatic steel sandwich plate, it is characterized in that: described reinforced phenol formaldehyde foam chromatic steel sandwich plate, top color corrugated sheet steel, the color steel surface plate in bottom and thermal insulation clamp sandwich layer, the upper surface coated with adhesive of the color steel surface plate in the soffit of top color corrugated sheet steel and bottom, after drying, form respectively upper adhesive layer and lower adhesive layer, thermal insulation clamp sandwich layer is made up of phenol formaldehyde foam, rectangle phenolic aldehyde heat preserving plate and two-layer gauze wire cloth, and phenol formaldehyde foam and phenolic aldehyde heat preserving plate are between two-layer gauze wire cloth.
Described top color corrugated sheet steel, the thickness of the color steel surface plate in bottom are 4.0mm, and top color corrugated sheet steel is trapezoidal rib shape bulge-structure with cross section, and bulge-structure spacing is 100mm.
After described phenol formaldehyde foam is all mixed by phenolic resins, curing compound, surfactant, blowing agent, modifier etc., through heating, foaming, curing making.
The structure of phenolic aldehyde heat preserving plate is that six ribs are lived structure.
Described thermal insulation clamp sandwich layer density is 100kg/m3.
In described thermal insulation clamp sandwich layer, the ratio of the volume of phenol formaldehyde foam and the volume of phenolic aldehyde heat preserving plate is 10000.
Claims (3)
1. a reinforced phenol formaldehyde foam chromatic steel sandwich plate, it is characterized in that: described reinforced phenol formaldehyde foam chromatic steel sandwich plate, top color corrugated sheet steel, the color steel surface plate in bottom and thermal insulation clamp sandwich layer, the upper surface coated with adhesive of the color steel surface plate in the soffit of top color corrugated sheet steel and bottom, after drying, form respectively upper adhesive layer and lower adhesive layer, thermal insulation clamp sandwich layer is made up of phenol formaldehyde foam, rectangle phenolic aldehyde heat preserving plate and two-layer gauze wire cloth, and phenol formaldehyde foam and phenolic aldehyde heat preserving plate are between two-layer gauze wire cloth.
2. according to reinforced phenol formaldehyde foam chromatic steel sandwich plate claimed in claim 1, it is characterized in that: described top color corrugated sheet steel, the thickness of the color steel surface plate in bottom are 0.2~4.0mm, top color corrugated sheet steel is trapezoidal rib shape bulge-structure with cross section, and bulge-structure spacing is 20~100mm.
3. reinforced phenol formaldehyde foam chromatic steel sandwich plate according to claim 1, is characterized in that: the structure of phenolic aldehyde heat preserving plate is rectangular structure, triangular prism structure or six prism structures.