CN202891384U - Tea tray - Google Patents

Tea tray Download PDF

Info

Publication number
CN202891384U
CN202891384U CN 201220189197 CN201220189197U CN202891384U CN 202891384 U CN202891384 U CN 202891384U CN 201220189197 CN201220189197 CN 201220189197 CN 201220189197 U CN201220189197 U CN 201220189197U CN 202891384 U CN202891384 U CN 202891384U
Authority
CN
China
Prior art keywords
tray body
tea
aggregates
particles
filter
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 201220189197
Other languages
Chinese (zh)
Inventor
秦升益
马志坤
王振邦
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Rechsand Science and Technology Group Co Ltd
Original Assignee
Beijing Rechsand Science and Technology Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing Rechsand Science and Technology Group Co Ltd filed Critical Beijing Rechsand Science and Technology Group Co Ltd
Priority to CN 201220189197 priority Critical patent/CN202891384U/en
Application granted granted Critical
Publication of CN202891384U publication Critical patent/CN202891384U/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

The utility model discloses a tea tray and belongs to the field of tea drinking tools. The tea tray comprises a tray body (1) with a cavity and a filtering plate (2) placed on the tray body (1). An upper surface of the filtering plate (2) is flat. The filtering plate (2) comprises particles of aggregates and a hydrophilic binder covering the particles of the aggregates. According to the tea tray, the technical problems that a prior tea tray with railings is difficult to clean and forming process is complex are solved and the tea tray is a product which is energy-saving and environmental friendly.

Description

A kind of tea saucer
Technical field
The utility model belongs to the apparatus field of drinking tea, particularly a kind of tea saucer.
Background technology
Along with tea culture is constantly carried out, tea saucer becomes some people's that sample tea indispensable tea set.Tea saucer is divided into two-layer, and water flows in lower floor's disk body from upper strata drainage pallet, the unlikely table top of making dirty.The quality of traditional tea saucer differs, and commonly used have woodenware and articles made of bamboo.This tea saucer generally is to offer fence or treatment hole at the woodenware on upper strata or articles made of bamboo; Fluid-tight structure is made by lower floor.But, there is following problem in this tea saucer: 1. the fence on the drainage pallet or treatment hole size arrange when unreasonable, can cause that tealeaves is blocked in fence or treatment hole place when pouring, perhaps fence or the treatment hole from tea saucer flow to lower floor, causes tea saucer to be difficult to clean; 2. making the woodenware of tea saucer or the junction of articles made of bamboo all is to adopt joinery and its construction, and moulding process is comparatively complicated, and under the environment of long-term immersion, the connection reliability of Tenon junction can descend.3. existing tea saucer is used precious timber and is made the very high and inadequate energy-conserving and environment-protective of cost.
The utility model content
For this reason, technical problem to be solved in the utility model is to provide a kind of and is easy to clean, moulding process is simple and the tea saucer of energy-conserving and environment-protective.
For solving the problems of the technologies described above, tea saucer of the present utility model, it comprises the tray body with cavity and places filter on the described tray body that described filter has smooth upper surface; Described filter includes particles of aggregates and coats the hydrophilic adhesive of particles of aggregates.
In the above-mentioned tea saucer, form shoulder on the described tray body inwall, described filter is arranged on the described shoulder.
In the above-mentioned tea saucer, the bilateral symmetry of described filter forms breach, and the degree of depth of described breach is less than the width of described shoulder.
In the above-mentioned tea saucer, the particle diameter of the particles of aggregates of described filter is 1.8-4mm.
In the above-mentioned tea saucer, described particles of aggregates is a kind of in quartz sand, slag, haydite or the glass microballoon or several mixture wherein.
In the above-mentioned tea saucer, described hydrophilic agglomerant is the hydrophilic resin binding agent; Described hydrophilic resin binding agent is one or more in the cruel and acrylic resin of epoxy resin, poly-ammonia; Described epoxy resin, poly-ammonia is cruel and acrylic resin in molecular side chain contain hydrophilic shuttle hydrochlorate, sulfonate, contain the non-ionic hydrophilic segment by salt, light base or main chain.
In the above-mentioned tea saucer, described tray body includes the silica sand particle and coats the hydrophobic binding agent of silica sand particle, and forming gas molecule between the adjacent described silica sand particle can pass through and the impervious hole of liquid water molecules.
Described hydrophobic binding agent is a kind of in fluorine-containing epoxy resin binding agent, siliceous epoxy adhesive, organosilicon binding agent, polyurethane, alkyd resin and the phenolic resins or several mixture wherein.
In the above-mentioned tea saucer, the particle diameter of the silica sand particle of described tray body is 0.65-1.1mm
In the above-mentioned tea saucer, be coated with the hydrophobic resin film on the silica sand particle of described tray body.Described hydrophobic resin film is the 1-8wt% of particles of aggregates.
Described hydrophobic resin film is by one or more films that form in hydrophobicity epoxy resin, phenolic resins, polyurethane resin and the silicones.
Technique scheme of the present utility model has the following advantages compared to existing technology:
(1) tea saucer of the present utility model, its filter include particles of aggregates and coat the hydrophilic adhesive of particles of aggregates; Can play the effect of fast permeable speed, and filter there is not filter opening, the difficult obstruction of tealeaves;
(2) simultaneously, particles of aggregates of the present utility model is a kind of in quartz sand, slag, haydite or the glass microballoon or several mixture wherein; Than the existing tea saucer of using the precious timber making, raw material sources are extensive, and moulding process is simple, compare existing tea saucer cost and greatly reduce.
(3) tea saucer of the present utility model has the filter realization tea filtration of surperficial continuous formation, and whole tea saucer outward appearance is neat, good integrity.
Description of drawings
For content of the present utility model is more likely to be clearly understood, the below is described in further detail the utility model, wherein according to specific embodiment of the utility model also by reference to the accompanying drawings
Fig. 1 is the profile of this tea saucer;
Fig. 2 is the top view of this tea saucer.
Reference numeral is expressed as among the figure: 1-tray body, 2-water filter plate, 11-shoulder, 21-breach.
The specific embodiment
Below with reference to accompanying drawing, use following examples that the utility model is further set forth.
Embodiment 1
Fig. 1, Fig. 2 are tea saucer of the present utility model, and it comprises the tray body 1 with cavity and places filter 2 on the described tray body 1; Wherein, form shoulder 11 on the described tray body 1, described filter is positioned on the described shoulder 11.For convenient described filter 2 and the described tray body 1 of separating, in the present embodiment, the both sides of described filter 2 form respectively the breach 21 of being convenient to move filter 2, and the degree of depth of described breach 21 is less than the width of described shoulder 11.
The hydrophilic adhesive that includes particles of aggregates and coating particles of aggregates in the described filter 2; Hydrophilic agglomerant in the present embodiment is the hydrophily epoxy adhesive.
The particles of aggregates of described filter 2 be slag and glass microballoon with the mixture of weight ratio 4:1, the particle diameter of described glass microballoon is 1.8-3mm, the particle diameter of slag is 2.5-4mm.
Described filter 2 is to make by following method:
A. pouring mixer into after 10:1 mixes by weight with hydrophily epoxy resin with above-mentioned particles of aggregates stirs;
The particles of aggregates that b. will be bonded with described hydrophilic adhesive is poured in the mould;
C. 15 ℃ place 12 hours curing moldings after the demoulding can obtain described filter 2.
In the present embodiment, described tray body 1 is to be formed by silica sand particle and hydrophobic binding agent bonding, and the particle diameter of the silica sand particle of described tray body 1 is 0.65-1.1mm.Described tray body 1 can realize permeable watertight.Described hydrophobic binding agent is mylar (bisphenol A-type saturated polyester resin).
Described tray body 1 is to make by following method:
A. pouring mixer into after 99:1 mixes by weight with mylar bisphenol A-type saturated polyester resin with the silica sand particle stirs;
The silica sand particle that b. will be bonded with described hydrophobic binding agent is poured the tray body mould into;
C. 5 ℃ place 48 hours curing moldings after the demoulding can obtain described tray body 1.
Embodiment 2
Tea saucer among the tea saucer of present embodiment and the embodiment 1 is basically identical, and its distinctive points is:
The silica sand particle of the described tray body 1 in the present embodiment is coated with the hydrophobic resin film.Described hydrophobicity epoxy resin is the 8wt% of particles of aggregates.Described hydrophobicity epoxy resin is to be made by phthalic anhydride and methyl vinyl ether copolymerization.
Described hydrophobic binding agent is organosilicon binding agent (methyl phenyl silicone resin), and hydrophobic binding agent and particles of aggregates use by weight 3:97.
The method that described epoxy resin is coated on the described particles of aggregates is:
1) epoxy resin is heated to molten condition;
When 2) the silica sand particle being heated to 200 ℃, add described epoxy resin, stirred and evenly mixed in 20 seconds, make described epoxy resin be dispersed in described silica sand particle surface;
3) paraformaldehyde curing agent (accounting for the 0.05wt% of particles of aggregates) is added in the above-mentioned mixture for preparing, stir and evenly mix, solidified 20 seconds;
4) Tissuemat E lubricant (accounting for the 0.0025wt% of particles of aggregates) is added in the mixture that is cured, stir, cooling is sieved, and be get final product.
Described tray body 1 is to make by following steps:
The silica sand particle that a. will be coated with hydrophobicity epoxy resin with pour mixer into after the hydrophobic binding agent mixes and stir;
The silica sand particle that b. will be bonded with the hydrophobic binding agent is poured described tray body mould into;
C. 20 ℃ place 12 hours curing moldings after the demoulding can obtain described tray body.
Embodiment 3
Tea saucer among the tea saucer of present embodiment and the embodiment 1 is basically identical, and its distinctive points is:
Described tray body 1 is to be made by common pottery or glass.
Described filter 2 particless of aggregates be quartz sand and haydite with weight ratio 3:1 mixture, the particle diameter of described quartz sand is 2-3mm, the particle diameter of haydite is 3-4mm.
The hydrophilic adhesive that coats particles of aggregates in the described filter 2 is the acrylic resin of hydroxyl.
Described filter 2 is to make by following method:
A. the acrylic resin of above-mentioned particles of aggregates and hydroxyl is stirred by weight pouring mixer into after 12:1 mixes;
The particles of aggregates that b. will be bonded with described hydrophilic adhesive is poured in the mould;
C. 10 ℃ place 18 hours curing moldings after the demoulding can obtain described filter 2.
Obviously, above-described embodiment only is for example clearly is described, and is not the restriction to embodiment.Wherein, described hydrophilic agglomerant can also be the poly-cruel resin of ammonia, epoxy resin described in the utility model, poly-ammonia is cruel and acrylic resin in molecular side chain contain hydrophilic shuttle hydrochlorate, sulfonate, contain the non-ionic hydrophilic segment by salt, light base or main chain.
Described hydrophobicity binding agent can also be a kind of in fluorine-containing epoxy resin binding agent, siliceous epoxy adhesive, polyurethane and the phenolic resins or several mixture wherein.
The film that described hydrophobic resin film can also be formed by one or more resins in phenolic resins, polyurethane resin and the silicones, described hydrophobic resin film can be 1wt%, 4 wt% etc. of particles of aggregates according to different situations, but the highest can not superelevation 8 wt%.
The size of particles of aggregates described in the utility model can't and needn't be unified a grain size when screening; Therefore; as long as the particle diameter such as the particles of aggregates of described filter within above-mentioned particle size range is 2.5mm, 3mm, 3.5mm, 4mm, the particle diameter of the silica sand particle of described tray body is that 0.65mm, 0.7mm, 0.8mm, 1.1mm etc. all belong to protection domain of the present utility model.
For those of ordinary skill in the field, above-mentioned hydrophilic agglomerant, hydrophobicity binding agent and hydrophobic resin film can be chosen in the process of the making of filter 2 and tray body 1 according to specific circumstances; Can also make other changes in different forms on the basis of the above description.Here need not also can't give all embodiments exhaustive.And the apparent variation of being extended out thus or change still are among the protection domain of the utility model creation.

Claims (6)

1. tea saucer is characterized in that: it comprises the tray body (1) with cavity and places filter (2) on the described tray body (1) that described filter (2) has smooth upper surface; Described filter (2) includes particles of aggregates and coats the hydrophilic adhesive of particles of aggregates.
2. tea saucer according to claim 1 is characterized in that:
Form shoulder (11) on described tray body (1) inwall, described filter (2) is arranged on the described shoulder (11).
3. tea saucer according to claim 1 and 2 is characterized in that:
The bilateral symmetry of described filter (2) forms breach (21), and the degree of depth of described breach (21) is less than the width of described shoulder (11).
4. tea saucer according to claim 3 is characterized in that:
The particle diameter of the aggregate of described filter (2) is 1.8-4mm.
5. tea saucer according to claim 1 is characterized in that:
Described tray body (1) includes the silica sand particle and coats the hydrophobic binding agent of silica sand particle, and forming gas molecule between the adjacent described silica sand particle can pass through and the impervious hole of liquid water molecules.
6. tea saucer according to claim 5 is characterized in that:
The particle diameter of the silica sand particle of described tray body (1) is 0.65-1.1mm.
CN 201220189197 2012-04-28 2012-04-28 Tea tray Expired - Fee Related CN202891384U (en)