CN201864665U - 一种特殊膜系的可钢化双银low-e玻璃 - Google Patents
一种特殊膜系的可钢化双银low-e玻璃 Download PDFInfo
- Publication number
- CN201864665U CN201864665U CN2010205798053U CN201020579805U CN201864665U CN 201864665 U CN201864665 U CN 201864665U CN 2010205798053 U CN2010205798053 U CN 2010205798053U CN 201020579805 U CN201020579805 U CN 201020579805U CN 201864665 U CN201864665 U CN 201864665U
- Authority
- CN
- China
- Prior art keywords
- layer
- glass
- low
- thickness
- silver
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本实用新型公开了一种特殊膜系的可钢化双银LOW-E玻璃,包括有玻璃基片,在玻璃基片的复合面上由内到外依次相邻地复合有十个膜层,其特征在于:其中第一膜层即最内层为Si3N4层,第二层为TiO2层,第三层为ZnO层,第四层为Ag层,第五层为NiCr层,第六层为TiO2层,第七层为ZnO层,第八层为Ag层,第九层为NiCr层,第十层即最外层为Si3N4层。本实用新型提供了一种透过率高、辐射率低的特殊膜系可钢化双银LOW-E玻璃。
Description
[技术领域]
本实用新型涉及一种镀膜玻璃,尤其是一种特殊膜系的可钢化双银LOW-E玻璃。
[背景技术]
玻璃是建筑物和汽车不可缺少的组成部分,承担着许多重要的功能,包括美化建筑物和汽车的外观,采光以及给室内带来开阔的视野。但是普通玻璃阳光透过率一般,红外反射率很低,大部分太阳光透过玻璃而进入室内,从而加热物体,而这些室内物体的能量又会以辐射形式通过玻璃散失掉。
为此,本发明人设计出了本专利,以克服上述问题。
[实用新型内容]
本实用新型克服了上述技术的不足,提供了一种透过率高、辐射率低的特殊膜系可钢化双银LOW-E玻璃。
为实现上述目的,本实用新型采用了下列技术方案:
一种特殊膜系的可钢化双银LOW-E玻璃,包括有玻璃基片,在玻璃基片的复合面上由内到外依次相邻地复合有十个膜层,其特征在于:其中第一膜层即最内层为Si3N4层,第二层为TiO2层,第三层为ZnO层,第四层为Ag层,第五层为NiCr层,第六层为TiO2层,第七层为ZnO层,第八层为Ag层,第九层为NiCr层,第十层即最外层为Si3N4层;
所述第一膜层的Si3N4层的厚度是15~20nm;所述第二层的TiO2层的厚度是20~25nm;第六层的TiO2层的厚度是20~25nm;所述第三层的ZnO层的厚度是5~8nm;所述第四层的Ag层的厚度是8~12nm;第八层的Ag层的厚度是8~12nm;所述第五层的NiCr层的厚度是5~8nm;第九层的NiCr层的厚度是5~8nm;所述第七层的ZnO层的厚度是5~10nm;所述第十层的Si3N4层的厚度是40~50nm。
与现有技术相比,本实用新型有如下优点:
1、本玻璃的镀膜层具有对可见光高透过及对中远红外线高反射的特性。冬季,它对室内暖气及室内物体散发的热辐射,可以像一面热反射镜一样,将绝大部分反射回室内,保证室内热量不向室外散失。夏季,它可以阻止室外地面、建筑物发出的热辐射进入室内。用LOW-E玻璃制造建筑物门窗,可大大降低因辐射而造成的室内热能向室外的传递,达到理想的节能效果。
2、本玻璃透光率T(透过透明或半透明体的光通量与其入射光通量的百分率)≥75%;本玻璃辐射率≤0.045(辐射率是某物体的单位面积辐射的热量同单位面积黑体在相同温度、相同条件下辐射热量之比。辐射率定义是某物体吸收或反射热量的能力。玻璃的辐射率越接近于零,其绝热性能就越好)。
3、本玻璃可实现先镀膜后钢化,且膜层稳定耐高温能力强,经高温处理后膜层色变小,保存时间长。
[附图说明]
图1是本实用新型结构示意图。
[具体实施方式]
下面结合附图与本实用新型的实施方式作进一步详细的描述:
参见图1,一种特殊膜系的可钢化双银LOW-E玻璃,包括有玻璃基片1,在玻璃基片的复合面上由内到外依次相邻地复合有十个膜层,其特征在于:其中第一膜层即最内层为Si3N4层21,即氮化硅层;Si3N4是一种非常坚硬的材料,它确保了整个镀层具有良好的机械耐久性。Si3N4层的厚度是15~20nm(nm是纳米,1m=109nm)。
第二层为TiO2层22,即钛的氧化物——二氧化钛。采用高折射率n=2.5的TiO2是为了提高玻璃的透光率,而且玻璃呈中性颜色,TiO2膜表面非常光滑,因而改善了银膜的导电率。TiO2层的厚度是20~25nm。
第三层为ZnO层23,减反射的金属氧化物层,同时进一步提高银膜的导电率。氧化锌(ZnO)可用作助熔剂,降低玻璃的烧结温度,用作玻璃涂料,让可见光通过的同时反射红外线,以达到保温或隔热的效果。ZnO层的厚度是5~8nm。
第四层为Ag层24,金属银提供了较低的辐射率,起环保节能的作用;Ag层的厚度是8~12nm。
第五层为NiCr层25,镍铬层为了进一步保护银膜,以避免银膜在反应溅射过程受到浸蚀,还要在薄的银膜一侧或两侧增加所谓的“阻挡层”,这种NiCr对于镀层具有非常良好的抗化学和机械性能。NiCr层的厚度是5~8nm。
第六层为TiO2层26,二氧化钛层。TiO2层的厚度是20~25nm。
第七层为ZnO层27,减反射的金属氧化物层。ZnO层的厚度是5~10nm。
第八层为Ag层28,金属银,Ag层的厚度是8~12nm。
第九层为NiCr层29,NiCr层为了进一步保护银膜,即阻挡层。NiCr层的厚度是5~8nm。
第十层即最外层为Si3N4层20,即氮化硅层;它确保了整个镀层具有良好的机械耐久性。Si3N4膜是非常坚硬,而且抗划伤,它的硬度是玻璃的三倍,是TiO2的二倍;Si3N4的折射率为2.05,吸收率几乎为零,所以它作为Low-e镀层的顶层是非常适合的。Si3N4层的厚度是40~50nm。
双银LOW-E玻璃在阳光性能上有很大提高,两层银膜可以使发射率降到很低值,即传热系数降到低值;而且它在降低太阳能的同时,仍然能保持很高的可见光透过率,所以双银LOW-E镀层在阳光性能方面具有良好的选择性。
LOW-E玻璃也叫做低辐射镀膜玻璃。
Claims (8)
1.一种特殊膜系的可钢化双银LOW-E玻璃,包括有玻璃基片(1),在玻璃基片的复合面上由内到外依次相邻地复合有十个膜层,其特征在于:其中第一膜层即最内层为Si3N4层(21),第二层为TiO2层(22),第三层为ZnO层(23),第四层为Ag层(24),第五层为NiCr层(25),第六层为TiO2层(26),第七层为ZnO层(27),第八层为Ag层(28),第九层为NiCr层(29),第十层即最外层为Si3N4层(20)。
2.根据权利要求1所述的特殊膜系的可钢化双银LOW-E玻璃,其特征在于所述第一膜层的Si3N4层的厚度是15~20nm。
3.根据权利要求1所述的特殊膜系的可钢化双银LOW-E玻璃,其特征在于所述第二层的TiO2层的厚度是20~25nm;第六层的TiO2层的厚度是20~25nm。
4.根据权利要求1所述的特殊膜系的可钢化双银LOW-E玻璃,其特征在于所述第三层的ZnO层的厚度是5~8nm。
5.根据权利要求1所述的特殊膜系的可钢化双银LOW-E玻璃,其特征在于所述第四层的Ag层的厚度是8~12nm;第八层的Ag层的厚度是8~12nm。
6.根据权利要求1所述的特殊膜系的可钢化双银LOW-E玻璃,其特征在于所述第五层的NiCr层的厚度是5~8nm;第九层的NiCr层的厚度是5~8nm。
7.根据权利要求1所述的特殊膜系的可钢化双银LOW-E玻璃,其特征在于所述第七层的ZnO层的厚度是5~10nm。
8.根据权利要求1所述的特殊膜系的可钢化双银LOW-E玻璃,其特征在于所述第十层的Si3N4层的厚度是40~50nm。