CN201751797U - 复合涂层及带该涂层的过热器管 - Google Patents
复合涂层及带该涂层的过热器管 Download PDFInfo
- Publication number
- CN201751797U CN201751797U CN2010202953358U CN201020295335U CN201751797U CN 201751797 U CN201751797 U CN 201751797U CN 2010202953358 U CN2010202953358 U CN 2010202953358U CN 201020295335 U CN201020295335 U CN 201020295335U CN 201751797 U CN201751797 U CN 201751797U
- Authority
- CN
- China
- Prior art keywords
- composite coating
- superheater
- utility
- model
- millimeters
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
本实用新型公开了一种复合涂层及带该涂层的过热器管，所述复合涂层由一层底层和一层表面保护层组成，所述底层为复合镍铬铝合金，厚度为0.01mm～0.1mm，所述表面保护层为陶瓷材料或高分子材料，厚度为0.02mm～0.04mm。本实用新型提供的复合涂层及带该涂层的过热器管，提高防热防腐蚀能力，从而保护了过热器管道，减少爆管，降低成本。
Description
技术领域
本实用新型涉及一种涂层及过热器管，尤其涉及一种复合涂层及带该涂层的过热器管。
背景技术
电站锅炉管道承受的压力大、温度高，容易爆裂，影响电厂安全、稳定发电并造成巨大经济损失，而处于高温高压段的过热器管是爆管的多发区。为了减少过热器爆管，以往的大量研究工作多认为是管材的短期超温和长期过热运行所致，因而多从提高钢管耐热等级，改进抗高温氧化能力和提高管材组织稳定性出发，建议更换更高等级的耐热钢管。但是，当使用温度高达620°C以上后，再进一步提高管材的热强度是十分有限的，而成本会大大增加。
发明内容
本实用新型所要解决的技术问题是提供一种复合涂层及带该涂层的过热器管，提高防热防腐蚀能力，从而保护了过热器管道，减少爆管，降低成本。
本实用新型为解决上述技术问题而采用的技术方案是提供一种复合涂层，所述复合涂层由一层底层和一层表面保护层组成，所述底层为复合镍铬铝合金，厚度为0.01mm～0.1mm，所述表面保护层为陶瓷材料或高分子材料，厚度为0.02mm～0.04mm。
上述的复合涂层，其中，所述复合镍铬铝合金底层中Cr含量30%～42%，Al含量5%～15%，其余为Ni。
本实用新型为解决上述技术问题还提供一种过热器管，所述热器管表面涂覆有上述复合涂层。
本实用新型对比现有技术有如下的有益效果：本实用新型提供的复合涂层及带该涂层的过热器管，通过提供复合涂层以及带该涂层的过热器管，提高防热防腐蚀能力，从而保护了过热器管道，减少爆管，降低成本。
附图说明
图1为本实用新型的复合涂层及带该涂层的结构示意图；
图2为本实用新型带复合涂层的过热器管结构示意图。
图中：
1表面保护层 2 底层 3 过热器管
具体实施方式
下面结合附图和实施例对本实用新型作进一步的描述。
图1为本实用新型的复合涂层及带该涂层的结构示意图；图2为本实用新型带复合涂层的过热器管结构示意图。
请参见图1，本实用新型提供的复合涂层由一层底层2和一层表面保护层1组成，所述底层2为复合镍铬铝合金，厚度为0.01mm～0.1mm，所述表面保护层1为陶瓷材料或高分子材料，厚度为0.02mm～0.04mm。
上述的复合涂层，所述复合镍铬铝合金底层中Cr含量30%～42%，Al含量5%～15%，其余为Ni。所述表面保护层1可以保护底层2免受外界物体摩擦损害。
请继续参见图2，上述的复合涂层可以直接涂在过热器管3表面，从而形成带上述复合涂层的过热器管。具体涂覆过程如下：
1. 清洁炉管表面，用金刚砂对炉管表面进行喷砂直至露出银灰色的金属本色；
2. 紧接着喷涂Ni-Cr-Al底层2；
3. 然后用表面保护层1刷涂在底层2上。
综上所述，本实用新型提供的复合涂层采用两层结构，具有持久的防热防腐蚀能力，从而保护了过热器管道，减少爆管，减小经济损失。在满足防热防腐蚀要求的条件下，可以选用低等级的耐热钢管，从而可以降低成本。
虽然本实用新型已以较佳实施例揭示如上，然其并非用以限定本实用新型，任何本领域技术人员，在不脱离本实用新型的精神和范围内，当可作些许的修改和完善，因此本实用新型的保护范围当以权利要求书所界定的为准。
Claims (2)
1.一种复合涂层，其特征在于，所述复合涂层由一层底层（2）和一层表面保护层（1）组成，所述底层（2）为复合镍铬铝合金，厚度为0.01mm～0.1mm，所述表面保护层（1）为陶瓷材料或高分子材料，厚度为0.02mm～0.04mm。
2.一种过热器管，其特征在于，所述热器管表面涂覆有如权利要求1所述的复合涂层。