CN1919773A - 一种混凝土复合外加剂 - Google Patents
一种混凝土复合外加剂 Download PDFInfo
- Publication number
- CN1919773A CN1919773A CN 200510036671 CN200510036671A CN1919773A CN 1919773 A CN1919773 A CN 1919773A CN 200510036671 CN200510036671 CN 200510036671 CN 200510036671 A CN200510036671 A CN 200510036671A CN 1919773 A CN1919773 A CN 1919773A
- Authority
- CN
- China
- Prior art keywords
- concrete
- composite additive
- admixture
- water
- additive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种混凝土复合外加剂，包含如下几种组分(质量百分数)：β－萘磺酸盐25～40％，白糖0.5～1.5％，硫酸铝5～15％，乙烯醋酸乙烯酯0.1～0.4％，其余为水。该混凝土复合外加剂的pH值为3～4，固含量为26～40，添加量为水泥重量的2～4％。经过对样品的严格测定，各项指标均符合JC474－1999中一等品的技术要求，可以广泛用于普通混凝土和高性能混凝土，能显著提高混凝土的微膨胀、减缩、减水、缓凝等性能。
Description
技术领域
本发明涉及一种建筑材料外加剂，尤其是一种用于混凝土的复合外加剂。
背景技术
在混凝土、砂浆和净浆的制备过程中，掺入少量的(不超水泥用量的5％)能对混凝土、砂浆或净浆改变性能的一种产品，称为混凝土外加剂。在混凝土中加入适量的外加剂，能提高混凝土质量，改善混凝土性能，减少混凝土用水量，节约水泥，降低成本，加快施工进度。随着技术的进步，外加剂已成为除水泥、粗细骨料、掺合料和水以外的第5种必备材料，掺外加剂是混凝土配合比优化设计和提高混凝土耐久性的一项重要措施。因此新修订的《水工混凝土施工规范》(DL/T5144-2001)强调，水工混凝土中必须掺加适量的外加剂。
混凝土外加剂的分类
混凝土外加剂按其主要功能可分为以下4类：
(1)改善混凝土拌和物流变性能的外加剂。包括普通减水剂和高效减水剂、引气剂和泵送剂等。
(2)调节混凝土凝结时间、硬化性能的外加剂。包括缓凝剂、早强剂和速凝剂等。
(3)改善混凝土耐久性的外加剂。包括引气剂、防水剂和阻锈剂等。
(4)改善混凝土其他性能的外加剂。包括膨胀剂、防冻剂、着色剂等。
复合外加剂是具有两种以上主要功能的外加剂，如缓凝减水剂同时具有缓凝和减水功能，引气减水剂同时具有引气和减水功能。许多水电工程，特别是三峡工程，将两种外加剂复合使用，如缓凝高效减水剂和引气剂复合，同时具有高效减水、引气、缓凝作用，取得了很好的效果，既满足了大仓面浇筑混凝土缓凝的要求，又达到了减水和提高耐久性的目的。一个工程使用什么样的外加剂应根据工程设计和施工技术要求在工程开工之前进行认真优选，并根据原材料进行严格的适应性试验论证确定。
传统的混凝土外加剂往往只有一种单一的功能，如防水剂，只能提高混凝土的防水功能，而要延长混凝土的凝固时间，还得再另外添加缓凝剂。起单一功能作用的混凝土外加剂已经越来越不适应高性能混凝土技术的发展，高性能混凝土是当前国内外混凝土领域中研究的热点，高性能混凝土是一种具有良好施工性能、强度较高、体积稳定性好及高耐久性混凝土，是混凝土进入高科技时代的产物，是21世纪的重要建筑材料。
本发明的目的就是针对单一功能混凝土外加剂的不足和缺陷，提供一种同时具有微膨胀、减缩、减水、缓凝作用的混凝土复合外加剂。
发明内容
本发明公开了一种混凝土复合外加剂，包含如下几种组分(质量百分数)：
β-萘磺酸盐25～40％ 白糖0.5～1.5％
硫酸铝5～15％ 乙烯醋酸乙烯脂0.1～0.4％
其余为水
本发明一种混凝土复合外加剂的PH值为3～4，固含量为26～40。添加量为水泥重量的2～4％，其添加方法和其他的混凝土外加剂相同。
本发明的有益效果在于，该混凝土复合外加剂添加于混凝土中，能显著改善混凝土的抗裂、减缩性，使混凝土同时具有微膨胀、减缩、减水、缓凝等性能，经过对混凝土样品(样品数量4Kg)的严格测定，得到了如下数据。
| 序号 | 检测项目 | 标准要求 | 实测结果 | 单项评定(一等品) | ||||
| 一等品 | 合格品 | |||||||
| 1 | 净浆安定性 | 合格 | 合格 | 完好 | 合格 | |||
| 2 | 泌水率比(％) | ≤50 | ≤70 | 35.0 | 合格 | |||
| 3 | 凝结时间差(min) | 初凝 | ≥-90 | +75 | 合格 | |||
| 终凝 | --- | +70 | ||||||
| 4 | 抗压强度比(100) | 3d | ≥100 | ≥90 | 184 | 合格 | ||
| 7d | ≥110 | ≥100 | 174 | 合格 | ||||
| 28d | ≥100 | ≥90 | 152 | 合格 | ||||
| 5 | 渗透高度比(％) | 7d | ≤30 | ≤40 | 12.2 | 合格 | ||
| 6 | 48h吸水量比(％) | 28d | ≤65 | ≤75 | 61.9 | 合格 | ||
| 7 | 收缩率比(％) | 28d | ≤125 | ≤135 | 80.8 | 合格 | ||
| 8 | 对钢筋腐蚀作用 | 对钢筋无锈蚀作用 | 无锈蚀危害 | 合格 | ||||
检测结论：上述样品检测结果均符合JC474-1999中一等品的技术要求。
具体实施方式
实施例1一种混凝土复合外加剂，由以下几种组分组成：
β-萘磺酸盐25％ 白糖0.5％
硫酸铝5％ 乙烯醋酸乙烯脂0.1％
其余为水。
添加方法和其他的混凝土外加剂相同，添加量为水泥重量的3％，测定PH值为3.5，固含量为35。
对该外加剂的部分性能指标进行了检测，其结果如下：
| 序号 | 检测项目 | 实测结果 |
| 1 | 固含量(％) | 35 |
| 2 | 密度(g/ml) | ----- |
| 3 | 总碱量(％) | 4.87 |
| 4 | 氯离子含量(％) | 0.18 |
| 5 | PH值 | 3.5 |
| 6 | 硫酸钠含量(％) | ----- |
| 7 | 净浆流动度(87g水)(mm) | ----- |
| 备注 | 另根据JC476-1998膨胀剂标准测得：水中7d限制膨胀率：0.021％，水中28d限制膨胀率：0.036％，干空28d限制膨胀率：-0.024％。 | |
Claims (4)
1、一种混凝土复合外加剂，包含如下几种组分：β-萘磺酸盐、白糖、硫酸铝、乙烯醋酸乙烯脂、水，其特征在于：各种组分所占的重量百分数如下：
β-萘磺酸盐25～40％ 白糖0.5～1.5％
硫酸铝5～15％ 乙烯醋酸乙烯脂0.1～0.4％
其余为水
2、根据权利要求1所述的一种混凝土复合外加剂，其特征在于：该复合外加剂的PH值是3～4。
3、根据权利要求1所述的一种混凝土复合外加剂，其特征在于：该复合外加剂的固含量是26～40。
4、根据权利要求1所述的一种混凝土复合外加剂，其特征在于：该复合外加剂的添加量是水泥重量的2～4％。