CN1904139A - 一种清除航空管表面油污用脱脂剂 - Google Patents

一种清除航空管表面油污用脱脂剂 Download PDF

Info

Publication number
CN1904139A
CN1904139A CN 200610095007 CN200610095007A CN1904139A CN 1904139 A CN1904139 A CN 1904139A CN 200610095007 CN200610095007 CN 200610095007 CN 200610095007 A CN200610095007 A CN 200610095007A CN 1904139 A CN1904139 A CN 1904139A
Authority
CN
China
Prior art keywords
aviation pipe
sodium
pipe surface
surface oil
inhibiter
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200610095007
Other languages
English (en)
Other versions
CN100402704C (zh
Inventor
严明英
王周树
杨军和
张全新
陈红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chongqing Iron and Steel Group Co Ltd
Original Assignee
Chongqing Iron and Steel Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chongqing Iron and Steel Group Co Ltd filed Critical Chongqing Iron and Steel Group Co Ltd
Priority to CNB2006100950071A priority Critical patent/CN100402704C/zh
Publication of CN1904139A publication Critical patent/CN1904139A/zh
Application granted granted Critical
Publication of CN100402704C publication Critical patent/CN100402704C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种清除航空管表面油污用脱脂剂，它由氢氧化钠、碳酸钠、十二水磷酸钠、硅酸钠、洗涤剂、缓蚀剂和溶剂水均匀混合而成，上述成分在整个溶液中的浓度为，氢氧化钠50－100g/L；碳酸钠20－50g/L；十二水磷酸钠10－40g/L；硅酸钠10－30g/L；洗涤剂1－5g/L；缓蚀剂1－5g/L。所述洗涤剂为十二烷基苯磺酸钠，缓蚀剂为硫脲。本脱脂剂原料易得，成本低，保存时间长，性能稳定，对环境不产生污染，去除航空管油污能力更彻底，能有效防止航空管产生晶间腐蚀，提高航空管的质量及成材率，从而提高经济效益。

Description

一种清除航空管表面油污用脱脂剂
技术领域
本发明涉及一种脱脂剂，具体涉及一种清除航空管表面油污用的脱脂剂。
背景技术
航空管(主要包括高温合金GH163航空管及1Cr18Ni9Ti不锈钢管)是航空、航天发动机的专用制造材料，主要应用于航天、航空和核能等尖端领域中。航空管属于高技术及生命周期较长的产品，对其质量要求非常高，因此对其生产过程的控制就显得特别重要。由于航空管的生产工艺较复杂，从熔炼到管材，其生产工序繁多，在这些生产过程中，航空管内外壁上容易附着油污，油污中含有较多的氯化石蜡，去除起来比较困难。而油污的存在会导致航空管在高温热处理过程中产生晶间腐蚀，晶间腐蚀不合格将直接影响航空管产品的质量。因此，去除油污是航空管不可缺少的处理步骤。而传统的去除油污的方法是将航空管浸泡在保持一定温度的脱脂剂中，过一段时间待油脂完全溶解后将航空管取出，用清水加压冲洗即可，因此，脱脂剂对油污去除的最终效果将产生直接影响。目前使用的脱脂剂主要有LT-83清洗剂、BCS-943水基脱脂剂、BH-7多功能碱性除油剂等，其存在的主要缺点有脱脂不彻底、需要的温度高、能耗大、产生污染、废水处理费用高等，最终使油污去除成本高。
发明内容
针对现有脱脂剂存在的上述不足，本发明的目的是提供一种低成本、无污染、去除航空管油污能力更彻底的脱脂剂。
本发明的目的是这样实现的：一种清除航空管表面油污用脱脂剂，它由氢氧化钠、碳酸钠、十二水磷酸钠、硅酸钠、洗涤剂、缓蚀剂和溶剂水均匀混合而成，上述成分在整个溶液中的浓度为，氢氧化钠50-100g/L；碳酸钠20-50g/L；十二水磷酸钠10-40g/L；硅酸钠10-30g/L；洗涤剂1-5g/L；缓蚀剂1-5g/L。
所述洗涤剂为十二烷基苯磺酸钠，缓蚀剂为硫脲。
上述成分在整个溶液中的浓度优选方案为：氢氧化钠80g/L；碳酸钠40g/L；十二水磷酸钠30g/L；硅酸钠15g/L；洗涤剂3.5g/L；缓蚀剂3.5g/L。
相比现有技术，本发明的脱脂剂原料易得，处理时需要的温度不高，成本低，保存时间长，性能稳定，对环境不产生污染，去除航空管油污能力更彻底，能有效防止航空管产生晶间腐蚀，提高航空管的质量及成材率，从而提高经济效益。
具体实施方式
以下结合实施例对本发明的脱脂剂进行详细说明。
本发明的主要成分为氢氧化钠、碳酸钠、十二水磷酸钠、硅酸钠、洗涤剂和缓蚀剂，上述六种成分与作为溶剂用的水均匀混合而成。混合后，六种成分在整个溶液中的浓度有一个范围要求，分别为：氢氧化钠50-100g/L；碳酸钠20-50g/L；十二水磷酸钠10-40g/L；硅酸钠10-30g/L；洗涤剂1-5g/L；缓蚀剂1-5g/L。
其中氢氧化钠、碳酸钠主要是同油脂发生皂化作用，生成可溶于水的脂肪酸钠和脂肪酸醇。硅酸钠有较强的乳化作用和一定的皂化能力。由于氢氧化钠和硅酸钠粘度大，难以冲洗干净，加入十二水磷酸钠(Na3PO412H2O)的目的是改善其冲洗性。本实施例中洗涤剂为十二烷基苯磺酸钠，缓蚀剂为硫脲。除了十二烷基苯磺酸钠还可以选用海鸥洗涤剂等作洗涤剂，而缓蚀剂除了硫脲外，还可以选用硫脲的衍生物、硫醚及其衍生物、吡啶及其衍生物作缓蚀剂。
本发明通过对碱、洗涤剂和缓蚀剂等组分的合理选择和组合，达到最佳的协同效应，来提高脱脂溶液对金属表面油污的润湿、渗透、卷离和扩散作用，提高脱脂效果，并使脱脂液稳定，延长使用寿命，降低航空管的加工成本。
以下以表格的形式列出7个脱脂剂各组分浓度的实施例。
  实施例   氢氧化钠   碳酸钠   十二水磷酸钠   硅酸钠   洗涤剂   缓蚀剂
  1   90g/L   40g/L   30g/L   15g/L   1.5g/L   3g/L
  2   80g/L   45g/L   30g/L   30g/L   2g/L   1g/L
  3   80g/L   40g/L   40g/L   20g/L   3g/L   1g/L
  4   50g/L   30g/L   20g/L   20g/L   2g/L   1.5g/L
  5   65g/L   50g/L   35g/L   25g/L   4g/L   3.5g/L
  6   100g/L   25g/L   20g/L   10g/L   5g/L   5g/L
  7   75g/L   20g/L   10g/L   30g/L   1g/L   4g/L
实验表明，随着脱脂剂各成分浓度的增大，脱脂效果提高，脱脂时间缩短。

Claims (4)

1、一种清除航空管表面油污用脱脂剂，其特征在于：它由氢氧化钠、碳酸钠、十二水磷酸钠、硅酸钠、洗涤剂、缓蚀剂和溶剂水均匀混合而成，上述成分在整个溶液中的浓度为，氢氧化钠50-100g/L；碳酸钠20-50g/L；十二水磷酸钠10-40g/L；硅酸钠10-30g/L；洗涤剂1-5g/L；缓蚀剂1-5g/L。
2、根据权利要求1所述的清除航空管表面油污用脱脂剂，其特征在于：所述洗涤剂为十二烷基苯磺酸钠。
3、根据权利要求1所述的清除航空管表面油污用脱脂剂，其特征在于：所述缓蚀剂为硫脲。
4、根据权利要求1所述的清除航空管表面油污用脱脂剂，其特征在于：所述成分在整个溶液中的浓度为，氢氧化钠80g/L；碳酸钠40g/L；十二水磷酸钠30g/L；硅酸钠15g/L；洗涤剂3.5g/L；缓蚀剂3.5g/L。
CNB2006100950071A 2006-07-31 2006-07-31 一种清除航空管表面油污用脱脂剂 Expired - Fee Related CN100402704C (zh)