CN102888619A - 冷轧硅钢板专用清洗剂 - Google Patents
冷轧硅钢板专用清洗剂 Download PDFInfo
- Publication number
- CN102888619A CN102888619A CN2012103946618A CN201210394661A CN102888619A CN 102888619 A CN102888619 A CN 102888619A CN 2012103946618 A CN2012103946618 A CN 2012103946618A CN 201210394661 A CN201210394661 A CN 201210394661A CN 102888619 A CN102888619 A CN 102888619A
- Authority
- CN
- China
- Prior art keywords
- parts
- cold
- rolled silicon
- silicon iron
- tsa
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了冷轧硅钢板专用清洗剂，主要包括以下组分，以重量份数表示为：氢氧化钠：19~35份；硅酸钠：43-62份；三聚磷酸钠：10-28份；聚氧乙烯醚：1~6份；肥皂：1~3份；高效有机硅抑泡剂：0.1~0.2；通用有机硅消泡粉：0.1~0.2份；磷酸三丁酯：0.1~0.2份。本发明所述冷轧硅钢板专用清洗剂，可以克服现有技术中清洗效果差、能耗大、容易引起作业故障等缺陷，以实现清洗效果好、能耗小和不易引起作业故障的优点。
Description
技术领域
本发明涉及金属材料清洗技术领域，具体地，涉及冷轧硅钢板专用清洗剂。
背景技术
由于硅钢板在冷轧过程中要使用轧制油，使得冷轧硅钢板表面粘有一层油污，这层油污在退火之前必须清洗干净，以避免硅钢板在退火过程中油污碳化，对硅钢板表面造成污染，影响后续工序涂层质量。
一般地，冷轧硅钢板表面油污常用碱性清洗剂清洗。但是，这些清洗剂对冷轧硅钢板的清洗效果不好，清洗后的冷轧硅钢板表面常常还附着一层油污，致使退火后的冷轧硅钢板表面形成碳质污斑，严重地影响钢板表面的质量。并且，这些清洗剂的工作温度较高，清洗时能耗大，且容易造成设备和管道结垢而堵塞管道，影响正常生产。另外，这些清洗剂中均不含消泡剂，在对冷轧硅钢板的清洗过程中会产生大量的泡沫，这些泡沫轻则污染作业环境，重则使生产不能正常进行。
在实现本发明的过程中，发明人发现现有技术中至少存在清洗效果差、能耗大、容易引起作业故障等缺陷。
发明内容
本发明的目的在于，针对上述问题，提出冷轧硅钢板专用清洗剂，以实现清洗效果好、能耗小和不易引起作业故障的优点。
为实现上述目的，本发明采用的技术方案是：冷轧硅钢板专用清洗剂，主要包括以下组分，以重量份数表示为：
氢氧化钠：19~35份；
硅酸钠：43-61份；
三聚磷酸钠：10-28份；
聚氧乙烯醚：1~6份；
肥皂：1~3份；
高效有机硅抑泡剂：0.1~0.2；
通用有机硅消泡粉：0.1~0.2份；
磷酸三丁酯：0.1~0.2份。
进一步地，所述聚氧乙烯醚具体包括脂肪醇的EO/PO嵌段的聚氧乙烯醚。
进一步地，所述高效有机硅抑泡剂具体包括高效有机硅抑泡剂TSA-7133、TSA-672、TSA-10A、D-30X、TSA-630和TSA-5701中的任意一种。
进一步地，所述通用有机硅消泡粉具体包括通用有机硅消泡粉T-20GB。
由于冷轧硅钢板上的油污中，含有少量的动植物油（或合成脂）和大量的矿物油。采用本发明各实施例的冷轧硅钢板专用清洗剂，可以克服现有技术中清洗效果差、能耗大、容易引起作业故障的缺陷，以实现清洗效果好、能耗小和不易引起作业故障的优点；例如：
⑴可以利用氢氧化钠和冷轧硅钢板上少量得动植物油（或合成脂）发生皂化反应，生成聚氧乙烯醚和甘油，聚氧乙烯醚和甘油能很好地溶解在清洗液中，从而使冷轧硅钢板上的动植物油除去；
⑵可以利用硅酸钠的乳化作用，有效除去冷轧硅钢板上大量的矿物油；
⑶利用三聚磷酸钠和硬水中的钙离子和镁离子发生络合作用，并络合溶解在清洗液中的其它金属离子，同时洗掉冷轧硅钢板表面的二氧化硅膜，以提高清洗效果；
⑷利用聚氧乙烯醚和肥皂作为表面活性剂，能降低清洗液的表面张力，增加清洗液的表面活性和清洗效果；
⑸利用高效有机硅抑泡剂、通用有机硅消泡粉和磷酸三丁酯作为消泡剂，能有效地消除清洗过程中产生的泡沫，避免污染作业环境，也对生产的正常进行有所保障。
本发明的其它特征和优点将在随后的说明书中阐述，并且，部分地从说明书中变得显而易见，或者通过实施本发明而了解。
下面通过实施例，对本发明的技术方案做进一步的详细描述。
具体实施方式
以下结合本发明的优选实施例进行说明，应当理解，此处所描述的优选实施例仅用于说明和解释本发明，并不用于限定本发明。
实施例一
根据本发明实施例，提供了冷轧硅钢板专用清洗剂。该冷轧硅钢板专用清洗剂，主要包括以下组分，以重量份数表示为：
氢氧化钠：19份；
硅酸钠：61份；
三聚磷酸钠：19份；
聚氧乙烯醚：1份；
肥皂：3份；
高效有机硅抑泡剂：0.2份；
通用有机硅消泡粉：0.1份；
磷酸三丁酯：0.15份。
将上述原料均匀混合后，密封包装即可制成合格的冷轧硅钢板专用清洗剂。使用时，只需将该种固态的冷轧硅钢板专用清洗剂倒入自来水中，充分搅拌使其溶解，配置成浓度为3%、液温在61℃之间的清洗液，通过管道送入硅钢板生产厂得带钢清洗槽中，对冷轧硅钢板进行喷淋清洗，经验证，洗净率可达到98%以上，并且使用后设备和管道均未产生结垢。
实施例二
根据本发明实施例，提供了冷轧硅钢板专用清洗剂。该冷轧硅钢板专用清洗剂，主要包括以下组分，以重量份数表示为：
氢氧化钠：35份；
硅酸钠：43份；
三聚磷酸钠：10份；
聚氧乙烯醚：6份；
肥皂：1份；
高效有机硅抑泡剂：0.1份；
通用有机硅消泡粉：0.15份；
磷酸三丁酯：0.2份。
将上述原料均匀混合后，密封包装即可制成合格的冷轧硅钢板专用清洗剂。使用时，只需将该种固态的冷轧硅钢板专用清洗剂倒入自来水中，充分搅拌使其溶解，配置成浓度为4%、液温在65℃之间的清洗液，通过管道送入硅钢板生产厂得带钢清洗槽中，对冷轧硅钢板进行喷淋清洗，经验证，洗净率可达到99%以上，并且使用后设备和管道均未产生结垢。
实施例三
根据本发明实施例，提供了冷轧硅钢板专用清洗剂。该冷轧硅钢板专用清洗剂，主要包括以下组分，以重量份数表示为：
氢氧化钠：27份；
硅酸钠：52份；
三聚磷酸钠：28份；
聚氧乙烯醚：3.5份；
肥皂：2份；
高效有机硅抑泡剂：0.15份；
通用有机硅消泡粉：0.2份；
磷酸三丁酯：0.1份。
将上述原料均匀混合后，密封包装即可制成合格的冷轧硅钢板专用清洗剂。使用时，只需将该种固态的冷轧硅钢板专用清洗剂倒入自来水中，充分搅拌使其溶解，配置成浓度为3.5%、液温在60℃之间的清洗液，通过管道送入硅钢板生产厂得带钢清洗槽中，对冷轧硅钢板进行喷淋清洗，经验证，洗净率可达到97%以上，并且使用后设备和管道均未产生结垢。
在上述各实施例中，聚氧乙烯醚具体包括脂肪醇的EO/PO嵌段的聚氧乙烯醚，高效有机硅抑泡剂具体包括高效有机硅抑泡剂TSA-7133、TSA-672、TSA-10A、D-30X、TSA-630和TSA-5701中的任意一种，通用有机硅消泡粉具体包括通用有机硅消泡粉T-20GB。
本发明上述各实施例的冷轧硅钢板专用清洗剂，可以专用于清洗冷轧硅钢板，采用浸渍脱脂或喷淋脱脂方式均可；该冷轧硅钢板专用清洗剂，也适用于其它钢材的化学清洗。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (4)
1.冷轧硅钢板专用清洗剂，其特征在于，主要包括以下组分，以重量份数表示为：
氢氧化钠：19~35份；
硅酸钠：43-61份；
三聚磷酸钠：10-28份；
聚氧乙烯醚：1~6份；
肥皂：1~3份；
高效有机硅抑泡剂：0.1~0.2；
通用有机硅消泡粉：0.1~0.2份；
磷酸三丁酯：0.1~0.2份。
2.根据权利要求1所述的冷轧硅钢板专用清洗剂，其特征在于，所述聚氧乙烯醚具体包括脂肪醇的EO/PO嵌段的聚氧乙烯醚。
3.根据权利要求1所述的冷轧硅钢板专用清洗剂，其特征在于，所述高效有机硅抑泡剂具体包括高效有机硅抑泡剂TSA-7133、TSA-672、TSA-10A、D-30X、TSA-630和TSA-5701中的任意一种。
4.根据权利要求1所述的冷轧硅钢板专用清洗剂，其特征在于，所述通用有机硅消泡粉具体包括通用有机硅消泡粉T-20GB。