CN1903960A - Thin layer multi coloured sand wall shaped paint - Google Patents
Thin layer multi coloured sand wall shaped paint Download PDFInfo
- Publication number
- CN1903960A CN1903960A CN 200610115857 CN200610115857A CN1903960A CN 1903960 A CN1903960 A CN 1903960A CN 200610115857 CN200610115857 CN 200610115857 CN 200610115857 A CN200610115857 A CN 200610115857A CN 1903960 A CN1903960 A CN 1903960A
- Authority
- CN
- China
- Prior art keywords
- coating
- water
- film
- paint
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a thin-layer multicolour sand textured architectural coating. Its formula composition includes the following components: (by wt%) 20-60% of various colour stone powders, 2-6% of polyvinyl alcohol hydrosol, 5-20% of hydroxyethyl cellulose hydrosol, 15-65% of film-forming resin emulsion, 0-10% of colour coating film, 0.5-1.5% of film-forming adjuvant, 0.5-10% of covering filling material, 2-5% of bentonite suspension, 0-5% of water-base various colour pastes and the rest is water.
Description
Technical field
What the present invention relates to is a kind of coating for wall surface, especially a kind of thin layer multi coloured sand wall shaped paint with emulsion paint color characteristics.
Background technology
Sandy paint is a kind of coating of thick-layer, be commonly called as stone coating and be called colored stone lacquer, true mineral varnish or stone similar paint again, it is to have mixed a kind of thick coating with imitative stone effect that stone flour and stone particulate filler are prepared from by the resin emulsion film forming matter, the paint thickness that this thick coating is coated with when decorating wall is bigger, general consumption be the 1.5-5 kilogram/square metre, otherwise opacifying power does not reach requirement, and coating color is not plentiful, yet just not imitative stone effect.The shown color effect that comes out of this coating is all by natural stone-powder or will stone flour dyeing back produce painted to coating and produces, so just apparent stone flour color of all kinds but can't reach the performance requirement of emulsion paint color; Good structure properties is arranged after the characteristics of this coating are to construct, the performance of unique texture is arranged.Yet, its existing deficiency also is conspicuous, that is exactly a not resistant of coarse surface, the opacifying power of filming is not strong, large usage quantity, the use cost height, higher use cost has restricted promoting the use of of sandy paint, make sandy paint can only be used in high-grade wall body decoration, can not enter common people house.Because existing sandy paint generally can not be lower than 1.5 kilograms of every square meters when using, do not merge the problem that the demonstration of texture effect is not come out otherwise will produce the surface.At present, in the art, each producer is all at the effective ways of seeking to reduce the sandy paint use cost, yet, yet there are no the Bi Lu of correlation technique so far.And emulsion paint is a kind of book matter wall decorative material, though have coloury advantage, what lack only is splitting resistance, the weather resistance that has more the decorative effect and the thick material of texture.What sandy paint lacked exactly is exactly the advantage of emulsion paint, also exactly is exactly the advantage of sandy paint and emulsion paint lacked.If both advantage complementations, both strong points are integrated together, obtain the net effect that the rich color of the texture of sandy paint and emulsion paint has concurrently, make sandy paint keep stone coloured silk and texture, the color effect that has emulsion paint again, and consumption is reduced to every square meter below 1.5 kilograms when using, even be reduced to every square meter below 1 kilogram, cost will reduce greatly, construction is simplified simple as the round brush emulsion paint, the difficult problem that Here it is at present will make great efforts to solve in the present technique field, yet, yet there are no relevant report so far.
Summary of the invention
Purpose of the present invention just provides a kind of thin layer multi coloured sand wall shaped paint with emulsion paint color characteristics, with a little less than overcoming present employed sandy paint color and being confined to stone color, opacifying power, consumption is big, cost is high deficiency.Improve the performance of sandy paint, make the present invention have the net effect of emulsion paint and sandy paint, and consumption is reduced to 1.5 kilograms of every square meters even reduced to below 1 kilogram.
For achieving the above object, the present invention has taked such measure, a kind of thin layer multi coloured sand wall shaped paint has comprised coating industry thickening material, sanitas, defoamer, dispersion, wetting agent commonly used, has comprised that also following raw materials in percentage by weight also is prepared from according to a conventional method:
Shades of colour stone flour 20-60% polyvinyl alcohol water-sol 2-6%
Film-forming resin emulsion 15-65% Natvosol water-sol 5-20%
Colo(u)r coating diaphragm 0-10% film coalescence aid 0.5-1.5%
Hide filler 0.5-10% bentonite suspension 2-5%
Water-based mill base 0-5% of all kinds surplus is a water;
Described shades of colour stone flour is meant 30-300 purpose natural colorful or artificially colored stone flour or carpolite;
Described film-forming resin emulsion is meant arbitrary combination of any or they of acrylic acid aqueous resin, ACRYLIC EMULSION, acid-organosilicon crylic acid graft emulsion, vinyl acetate between to for plastic, ethylene copolymerization emulsions or polyaminoester emulsion;
Described covering filler refers to a class material that plays the covering effect in coating, comprises any of the titanium dioxide slurry of 70% titanium white solid content or 150-3000 order silica ashes or calcined kaolin powder or mica powder or aluminium silicate powder;
Described colo(u)r coating diaphragm is meant with 0.05-1.5 kilogram/square metre colo(u)r coating film forming pulverizes the 10-150 purpose colo(u)r coating sheet that obtains;
Described film coalescence aid be meant coating industry commonly used have a film forming raw material of help, especially refer to alcohol ester-12;
Described bentonite suspension is meant receives the suspension of base bentonite 5%.
The described polyvinyl alcohol water-sol contains 15% admittedly;
The described Natvosol water-sol contains 2% admittedly;
Water-based mill base of all kinds is the finished product slurry of market sale;
Thickening material commonly used in the coating industry has " associative thickener-1306, alkaline swelling type thickening material HAS663 ", and usual amounts is 0.05-0.5% (weight percentage);
Sanitas commonly used in the coating industry has " Hua Ke-98, heterocycle bactericide PT, extra large river F-251 ", usual amounts 1-2% (weight percentage);
Defoamer commonly used in the coating industry has " NXZ, extra large river 127, KNP315, NOPCD306-A ", usual amounts 0.1-0.5% (weight percentage);
Dispersion, wetting agent commonly used in the coating industry have " SN5040,5050, amino methyl propyl alcohol AMP-95 ", usual amounts 0.5-1% (weight percentage).
Preparation method of the present invention is lithotomy powder in above-mentioned raw materials (or adding the colo(u)r coating diaphragm), water, mixes with resin emulsion, add film coalescence aid, dispersion, wilkinite aqeous suspension, wetting agent, defoamer, sanitas, add stablizer or other mill bases again and mix stirring, adding entry accent viscosity is 20000P, and packing can make the present invention.
Take the present invention of above-mentioned measure, have such characteristics: 1, usually sandy paint all is to rely on bigger coat-thickness being used for producing to the covering of bottom and reaching the effect of color even with stone flour.And the present invention introduces an amount of functional covering filler, and the opacifying power that improves coating shows the characteristics of sandy paint colored stone seed again, thereby has reached the purpose that reduces the coating consumption.2, the following filler fine powder of 80 orders of present sandy paint all is natural white, and it is that multiple colour stone powder is formed that the present invention adds the following filler fine powder of 80 orders, can rely on this fine powder to reach the effect of performance emulsion paint look.3, sandy paint all relies on the specific side oil on surface to reach effect bright and clean, fine and close, resistant usually.And the present invention has improved the content of film-forming resin in the sandy paint, during use above oil, coating surface is still bright and clean, densification and resistant.4, after the present invention adds the colo(u)r coating diaphragm, make this thin coating surface show rough texture.Therefore, the present invention is a kind of book matter sandy paint of having very much texture, is used for wall body decoration and can makes the coating consumption reduce to 0.35 to 1.0 kilogram/square metre, and satisfy the opacifying power requirement; The present invention is fuller, even than the sandy paint color of not doing above-mentioned adjustment; The present invention has manifested the emulsion paint tone, and that can satisfy the emulsion paint look selects the look requirement.The present invention has obtained the net effect of sandy paint and emulsion paint, and cost the has been reduced to approaching low cost of emulsion paint, having enriched the performance of the emulsion paint color of self again, improved crack resistance, is that new market orientation has been found in the combination of two kinds of traditional product advantages.By improving the film-forming resin ratio of lining of the present invention, thereby changed sandy paint and relied on the traditional method that the cover agent produces resistant, water-fast effect, reduced applying operation, improved the fullness ratio and the gloss uniformity coefficient of coating surface layer, and reduced production cost.
Embodiment
Embodiment 1
Composition of raw materials:
7 kilograms of 15 kilograms of titanium dioxide slurries of ACRYLIC EMULSION
20 kilograms of 2 kilograms of Natvosol water-sols of the polyvinyl alcohol water-sol
0.5 kilogram of alcohol ester-12 0.5 kilogram SN5040
0.1 kilogram of Hua Ke-981 1.5 of NXZ kilogram
25 kilograms of 0.15 kilogram of 120-200 order of thickening material-1306 and HAS663 stone flours of all kinds
20 kilograms of 0.5 kilogram of 200-300 order of 100-150 order colo(u)r coating diaphragm stone flours of all kinds
5 kilograms of 2 kilograms of bentonite suspensions of water-based mill base of all kinds
Water is an amount of
Preparation method: lithotomy powder, colo(u)r coating diaphragm, water, mix with ACRYLIC EMULSION, add alcohol ester-12, SN5040, bentonite suspension, NXZ, Hua Ke-981, add titanium dioxide slurry and water-based mill base of all kinds again and mix stirring, adding entry accent viscosity is 20000P, and packing gets final product.
Embodiment 2
Composition of raw materials:
0.5 kilogram of 65 kilograms of titanium dioxide slurry of ACRYLIC EMULSION
5 kilograms of 3 kilograms of Natvosol water-sols of the polyvinyl alcohol water-sol
0.1 kilogram of alcohol ester-12 1 kilogram SN5040
0.1 kilogram of Hua Ke-981 1 of NXZ kilogram
18 kilograms of 0.3 kilogram of 60-200 order of thickening material-1306 and HAS663 stone flours of all kinds
7 kilograms of 1 kilogram of 200-300 order of 60-120 order colo(u)r coating diaphragm stone flours of all kinds
Bentonite suspension 2 kg of water are an amount of
The preparation method is identical with embodiment 1.
Embodiment 3
Composition of raw materials:
3 kilograms of 22 kilograms of titanium dioxide slurries of ACRYLIC EMULSION
15 kilograms of 6 kilograms of Natvosol water-sols of the polyvinyl alcohol water-sol
1 kilogram of alcohol ester-12 1.5 kilogram SN5040
0.5 kilogram of Hua Ke-981 2 of NXZ kilogram
20 kilograms of 0.5 kilogram of 120-200 order of thickening material-1306 and HAS663 stone flours of all kinds
20 kilograms of 0.5 kilogram of 200-300 order of 100-120 order colo(u)r coating diaphragm stone flours of all kinds
3 kilograms of 3 kilograms of bentonite suspensions of water-based name look mill base
Water is an amount of
The preparation method is identical with embodiment 1.
Embodiment 4
Composition of raw materials:
3 kilograms of 22 kilograms of wollastonite powder of ACRYLIC EMULSION
15 kilograms of 6 kilograms of Natvosol water-sols of the polyvinyl alcohol water-sol
1 kilogram of alcohol ester-12 1.5 kilogram SN5040
0.5 kilogram of Hua Ke-981 2 of NXZ kilogram
20 kilograms of 0.5 kilogram of 120-200 order of thickening material-1306 and HAS663 stone flours of all kinds
3 kilograms of 20 kilograms of water-baseds of 200-300 order stone flour of all kinds mill bases of all kinds
3 kilograms of bentonite suspensions
Water is an amount of
The preparation method is identical with embodiment 1.
Claims (1)
1, a kind of thin layer multi coloured sand wall shaped paint, comprised coating industry thickening material, sanitas, defoamer, dispersion, wetting agent commonly used, it is characterized in that described sandy paint has comprised that also following raw materials in percentage by weight also is prepared from according to a conventional method:
Shades of colour stone flour 20-60% polyvinyl alcohol water-sol 2-6%
Film-forming resin emulsion 15-65% Natvosol water-sol 5-20%
Colo(u)r coating diaphragm 0-10% film coalescence aid 0.5-1.5%
Hide filler 0.5-10% bentonite suspension 2-5%
Water-based mill base 0-5% of all kinds surplus is a water;
Described shades of colour stone flour is meant 30-300 purpose natural colorful or artificially colored stone flour or carpolite;
Described film-forming resin emulsion is meant arbitrary combination of any or they of acrylic acid aqueous resin, ACRYLIC EMULSION, acid-organosilicon crylic acid graft emulsion, vinyl acetate between to for plastic, ethylene copolymerization emulsions or polyaminoester emulsion;
Described covering filler refers to a class material that plays the covering effect in coating, comprises any of the titanium dioxide slurry of 70% titanium white solid content or 150-3000 order silica ashes or calcined kaolin powder or mica powder or aluminium silicate powder;
Described colo(u)r coating diaphragm is meant with 0.05-1.5 kilogram/square metre colo(u)r coating film forming pulverizes the 10-150 purpose colo(u)r coating sheet that obtains;
Described film coalescence aid be meant coating industry commonly used have a film forming raw material of help, especially refer to alcohol ester-12;
Described bentonite suspension is meant receives the suspension of base bentonite 5%.