CN1873032A - 一种用于真空罐真空脱碳精炼的钢包顶渣 - Google Patents
一种用于真空罐真空脱碳精炼的钢包顶渣 Download PDFInfo
- Publication number
- CN1873032A CN1873032A CNA2005100263239A CN200510026323A CN1873032A CN 1873032 A CN1873032 A CN 1873032A CN A2005100263239 A CNA2005100263239 A CN A2005100263239A CN 200510026323 A CN200510026323 A CN 200510026323A CN 1873032 A CN1873032 A CN 1873032A
- Authority
- CN
- China
- Prior art keywords
- slag
- vacuum
- ladle
- ladle top
- decarburization
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种用于真空罐真空脱碳精炼的钢包顶渣,其包含占钢包顶渣总重量30~45%的CaO,12~18%的SiO2,25~35%的Al2O3,5~15%的FeO,3~8%的MgO和不大于0.2%的H2O;该钢包顶渣为颗粒状混合料,其粒度组成为3-10mm。本发明提供的用于真空罐真空脱碳精炼的钢包顶渣,在无气体供氧条件下,能使渣中氧向钢水传递,促进真空脱碳反应;同时可有效抑制真空脱碳过程的溢渣;有利于对真空脱碳后的钢水中的夹杂物进行吸附,也有利于钢水脱硫、脱氧反应的进行等。
Description
技术领域
本发明涉及一种用于真空罐真空脱碳精炼的钢包顶渣。
背景技术
真空罐真空精炼装置(VD装置)是一种应用广泛的真空罐精炼设备,具有良好的脱氢、脱氧、脱碳、脱氮和脱硫等功能,同时也能去除钢中的夹杂物,并对钢中夹杂物的形态进行控制。由于VD不具备顶吹氧功能,故不能进行强制脱碳,因此,目前在国内外生产低碳钢和超低碳钢时,基本都是采用RH(真空循环脱气)装置或VOD(真空吹氧脱碳)装置对钢水进行脱碳处理,但是上述相应的脱碳装置成本相当高,对于一些不具有这些设备装置的厂家,会造成生产上的限制,同时提高生产成本。
目前,在国外所存在的VD真空脱碳工艺,从初炼炉,即电炉或转炉出钢后,对钢包顶渣基本不进行任何处理,钢水就直接进入VD真空罐进行真空脱碳,钢包顶渣基本就是转炉终点或电炉终点渣在出钢过程中带入钢包,真空脱碳过程顶渣的有利作用不能得到发挥,VD精炼过程极好的渣-金反应条件没有得到充分利用,有时甚至造成真空处理过程的溢渣,影响了工艺的顺行,对设备也造成损坏。
发明内容
本发明的目的在于提供一种用于真空罐真空脱碳精炼的钢包顶渣,在无气体供氧条件下,能使渣中氧向钢水传递,促进真空脱碳反应;同时可有效抑制真空脱碳过程的溢渣;有利于对真空脱碳后的钢水中的夹杂物进行吸附,也有利于钢水脱硫、脱氧反应的进行等。
为达到上述目的,本发明提供一种用于真空罐真空脱碳精炼的钢包顶渣,其包含占钢包顶渣总重量30~45%的CaO,12~18%的SiO2,25~35%的Al2O3,5~15%的FeO,3~8%的MgO和不大于0.2%的H2O;
所述的钢包顶渣为颗粒状混合料,其粒度组成为3-10mm。
本发明提供的用于真空罐真空脱碳精炼的钢包顶渣,是由高活性的冶金石灰、铝酸钙预熔渣、白云石等工业原料经过破碎、筛分、充分混匀制成的,在加工和运输过程中需要严格防止吸潮,以保证钢包顶渣的使用效果。
本发明提供的用于真空罐真空脱碳精炼的钢包顶渣,在电炉/转炉出钢过程中随出钢钢流加入到钢包中,其CaO和SiO2的含量保持在CaO/SiO2=2左右,用以提高并使钢包顶渣中FeO的活度为最大,从而使钢包顶渣中的氧具备向钢水传递的良好热力学条件,在无气体供氧条件下,利用来自钢包顶渣中的氧补充钢水脱碳所需要的氧量,以促进钢水在真空下的脱碳反应。
本发明提供的用于真空罐真空脱碳精炼的钢包顶渣,其具有良好的流动性以及很弱的储泡能力,既可以保持良好的渣金反应动力学,也可以使穿过渣层的气体和渣-金反应的气体能尽快离开渣层,避免溢渣情况的发生。
本发明提供的用于真空罐真空脱碳精炼的钢包顶渣,其具有合适的碱度,有利于对真空脱碳后的钢水中的夹杂物进行吸附,同时也有利于钢水脱硫、脱氧反应的进行等。
本发明提供的用于真空罐真空脱碳精炼的钢包顶渣,由于不含CaF2,不会损伤钢包耐火材料,也不会对环境造成污染。
具体实施方式
以下通过表1中列出的本发明的三个实施例A、B和C的具体组成成分,说明本发明的使用效果。
实施例A | 实施例B | 实施例C | ||
化学组成% | CaO | 33.0 | 38.4 | 43.9 |
SiO2 | 13.5 | 15.7 | 17.6 | |
Al2O3 | 31.7 | 27.9 | 26.3 | |
FeO | 12.6 | 9.3 | 5.2 | |
MgO | 7.6 | 6.5 | 5.1 | |
H2O | 0.10 | 0.11 | 0.10 | |
其它 | 余量 | 余量 | 余量 | |
钢包渣加入量,kg/t.s | 3.5 | 2.9 | 2.3 | |
钢包渣的流动性 | 良好 | 良好 | 良好 |
VD处理前钢水的碳含量,% | 0.07 | 0.06 | 0.04 |
VD脱碳后钢水的碳含量,% | 0.0020 | 0.0045 | 0.0040 |
VD脱碳过程渣的起泡情况 | 无起泡现象 | 无起泡现象 | 无起泡现象 |
VD脱碳过程渣的溢渣情况 | 无溢渣现象 | 无溢渣现象 | 无溢渣现象 |
表1、实施例A、B和C的组成及使用效果
由表1可得到,本发明提供的用于真空罐真空脱碳精炼的钢包顶渣,在无气体供氧的条件下,能有效的促进脱碳反应,使经过真空脱碳处理后的钢水中的碳含量大大降低;同时该钢包顶渣具有良好的流动性,能有效地抑制钢包溢渣;还对真空脱碳后的钢中夹杂物的吸附、脱硫、脱氧等有利;消除了真空罐脱气过程生产低碳钢和超低碳钢系列产品的限制,在不大幅度增加成本的基础上,大大提高其生产能力。
Claims (2)
1.一种用于真空罐真空脱碳精炼的钢包顶渣,特征在于,其包含占钢包顶渣总重量30~45%的CaO,12~18%的SiO2,25~35%的Al2O3,5~15%的FeO,3~8%的MgO和不大于0.2%的H2O。
2.如权利要求1所述的用于真空罐真空脱碳精炼的钢包顶渣,其特征在于,所述的钢包顶渣为颗粒状混合料,其粒度组成为3-10mm。