CN1858095A - 热塑性弹性体表面处理剂 - Google Patents

热塑性弹性体表面处理剂 Download PDF

Info

Publication number
CN1858095A
CN1858095A CN 200610035857 CN200610035857A CN1858095A CN 1858095 A CN1858095 A CN 1858095A CN 200610035857 CN200610035857 CN 200610035857 CN 200610035857 A CN200610035857 A CN 200610035857A CN 1858095 A CN1858095 A CN 1858095A
Authority
CN
China
Prior art keywords
thermoplastic elastomer
weight portions
treating agent
surface treating
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200610035857
Other languages
English (en)
Inventor
许玉良
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DUOZHENG CHEMICAL SCIENCE AND TECHNOLOGY Co Ltd GUANGDONG
Original Assignee
DUOZHENG CHEMICAL SCIENCE AND TECHNOLOGY Co Ltd GUANGDONG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DUOZHENG CHEMICAL SCIENCE AND TECHNOLOGY Co Ltd GUANGDONG filed Critical DUOZHENG CHEMICAL SCIENCE AND TECHNOLOGY Co Ltd GUANGDONG
Priority to CN 200610035857 priority Critical patent/CN1858095A/zh
Publication of CN1858095A publication Critical patent/CN1858095A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种热塑性弹性体(TPE)表面处理剂，其特征在于，它由如下组分配比构成(重量份)，甲苯(TOL)50－65份、丁酮(MEK)5－12份、醋酸乙酯(EAC)5－12份、天然橡胶6－9份、氯化聚丙烯1－2.5份、甲基丙烯酸甲酯(MMA)1－3份、醋酸乙烯酯(VAC)1－3份、过氧化苯甲酰(BPO)0.05－0.1份、抗氧化剂(BHP)0.05－0.1份。本发明具有实用，稳定性效果好、粘接力强等优点。

Description

热塑性弹性体表面处理剂
技术领域
本发明涉及一种处理剂，具体是涉及热塑性弹性体的表面处理剂。
背景技术
热塑弹性体总称是TPE，其还分有TPU是热塑性聚氨酯弹性体，TPV为硫化热塑性弹性体，TPR等，TPR在国内普遍用于鞋底料。据有关资料显示，2006年世界热塑性弹性体(TPE)消费将接近220万吨，总产值超过110亿美元，2001-2006年间世界消费将保持年均6.4份的增长率，高速的增长将带动各行各业对TPE的使用，我国是鞋类生产集散地，对鞋底料TPR的需求量更是与日俱增。现有的TPE处理剂通常所用SBS(丁苯热塑弹性体)为主体基料，这种主体基料制作的处理剂存在稳定性较差，加工成本高，对TPR鞋材表面的粘接力不够强等缺点。如申请号为95107916，申请日为1995年8月4日，发明名称为丁苯嵌段共聚物热塑弹性体及制法的专利申请，它由苯乙烯均聚嵌段、丁二烯均聚嵌段及苯乙烯与丁二烯共聚嵌段组成，其特征在于所说的丁苯嵌段共聚物热塑弹性体为如下二种结构嵌段共聚物的混合物：S1-B-S2/B-S2(I)B-S2/B-S2(II)其中S1为第一批加入的苯乙烯所形成的苯乙烯均聚嵌段、S2为第二批加入的苯乙烯所形成的苯乙烯均聚嵌段、B为丁二烯所形成的丁二烯均聚嵌段、S2/B为第二批加入的苯乙烯与丁二烯所形成的丁苯共聚嵌段，且苯乙烯与丁二烯的总量比S总/B总为10/90～60/40(重量比)，两批苯乙烯的加料比S1/S2为1/1.0～1/1.5(重量比)，两种结构的嵌段共聚物的比例II/I为0.01～0.30(摩尔比)。此专利以苯乙烯、丁二烯为单体合成的SBS为主基料，它同样存在上述缺点。
发明内容
本发明的目的是为了解决上述之不足，而提供一种具有的稳定性好，粘接力强的热塑性弹性体(TPE)表面处理剂。
本发明为了达到上述效果而采用的技术解决方案如下：
本热塑性弹性体(TPE)表面处理剂，其特征在于，它由如下组分配比构成(重量份)，甲苯(TOL)50-65份、丁酮(MEK)5-12份、醋酸乙酯(EAC)、5-12份、天然橡胶6-9份、氯化聚丙烯1-2.5份、甲基丙烯酸甲酯(MMA)1-3份、醋酸乙烯酯(VAC)1-3份、过氧化苯甲酰(BPO)0.05-0.1份、抗氧化剂(BHP)0.05-0.1份。
本发明采用上述技术解决方案所能达到的有益效果是：
本发明没有采用SBS为主体基料，而采用天然橡胶、氯化聚丙烯为主体基料，加强了对TPR鞋材表面的处理功能，对TPU、TPV等材质同样具有良好的处理效果。鞋材先使用本处理剂打底后再配合PU胶(聚氨酯胶粘剂)使用，粘合效果明显增强。
具体实施方式
本热塑性弹性体(TPE)表面处理剂，由如下组分配比构成，甲苯TOL63.8重量份、丁酮MEK10重量份、醋酸乙酯EAC-10重量份、天然橡胶-8重量份、氯化聚丙烯-2.5重量份、甲基丙烯酸甲酯MMA-3重量份、醋酸乙烯酯VAC-3重量份、过氧化苯甲酰BPO-0.1重量份、抗氧化剂BHP-0.1重量份。
鞋材先使用本处理剂打底后再配合PU胶(聚氨酯胶粘剂)使用，粘合效果明显增强，稳定性好。

Claims (1)

1、一种热塑性弹性体表面处理剂，其特征在于，它由如下组分配比构成(重量份)，甲苯(TOL)50-65份、丁酮(MEK)5-12份、醋酸乙酯(EAC)、5-12份、天然橡胶6-9份、氯化聚丙烯1-2.5份、甲基丙烯酸甲酯(MMA)1-3份、醋酸乙烯酯(VAC)1-3份、过氧化苯甲酰(BPO)0.05-0.1份、抗氧化剂(BHP)0.05-0.1份。
CN 200610035857 2006-06-09 2006-06-09 热塑性弹性体表面处理剂 Pending CN1858095A (zh)