CN1857916A - Color combined composite rubber floor and its preparing process - Google Patents
Color combined composite rubber floor and its preparing process Download PDFInfo
- Publication number
- CN1857916A CN1857916A CN 200510039242 CN200510039242A CN1857916A CN 1857916 A CN1857916 A CN 1857916A CN 200510039242 CN200510039242 CN 200510039242 CN 200510039242 A CN200510039242 A CN 200510039242A CN 1857916 A CN1857916 A CN 1857916A
- Authority
- CN
- China
- Prior art keywords
- rubber floor
- semi
- cure
- 3mpa
- cut
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to color composite floor board for cab floor of engineering machines and agricultural machines and indoor and outdoor floor. The color composite floor board consists of a facing layer, a middle layer and a base layer. The facing layer consists of combined wear resistant color or patterned rubber sheets; the middle layer includes upper microporous structure and lower sucker disc structures; and the base layer is double-sided flat rubber sheet. The color composite floor board may be prepared through a cold adhering process, a hot sulfurizing process or a semi-sulfurizing process.
Description
Technical field
The present invention relates to a kind of color combined composite rubber floor, the laying that is mainly used in engineering machinery, shop, agricultural machinery driver's cabin ground decorations and indoor and outdoor place is decorated.
Background technology
Common rubber floor covering majority is the individual layer floor at present, the one, and the floor is harder, and elasticity is lower, and style and tone are single, be laid on driver's cabin especially, in the process of moving, in case brake, because of the rubber floor covering skin-friction force is little, be easy to generate relative slip, there is potential safety hazard.
Summary of the invention
The purpose of this invention is to provide a kind of color combined composite rubber floor and preparation technology thereof, can effectively overcome the weak point of above-mentioned rubber floor covering.
Technical scheme of the present invention is achieved in that described color composite rubber floor is made up of surface layer, intermediate layer and bottom, wherein surface layer is that wear-resisting colour of square or pattern rubber plate form through assembling combination, the intermediate layer is an obturator foramen micro-hole structural, be the sucker structure of being made up of equally distributed some semicircle orifices below it, bottom is two-sided smooth rubber slab.
The preparation technology on described color composite rubber floor, can use cold bonding method, heat curing system, the preparation of semi-cure method, described cold bonding method is with sizing material → calendering → cut-parts → sulfuration → surface treatment coating adhesive → bonding → cutting → finished product, wherein curing temperature is at 140-170 ℃, and sulfide stress is 0.5-3Mpa.
Described semi-cure method is that wherein curing temperature is 140-170 ℃ with sizing material → calendering → cut-parts → surface layer semi-cure → applying → sulfuration → finished product, and sulfide stress is 0.5-3Mpa.
Good effect of the present invention is, the assembly unit capable of being combined of the colored many patterns of described composite rubber floor, and the sucker structure in intermediate layer makes its good springiness, and wear-resisting, anti-skidding, fire-retardant, antistatic, described preparation technology, work simplification can alleviate labor strength.
Description of drawings
Below in conjunction with preparation technology's flow chart and embodiment the present invention is further described.
Fig. 1 is that the cold bonding legal system is equipped with process chart;
Fig. 2 is a heat curing system preparation technology flow chart;
Fig. 3 is that the semi-cure legal system is equipped with process chart.
The specific embodiment
As shown in Figure 1: the cold bonding method dissolves the sizing material of intermediate layer and bottom calender rolling out film come with vulcanizing press mold pressing overall sulfur again, and conditions of vulcanization is that curing temperature is 0.5-3Mpa at 140-170 ℃ of sulfide stress.Cure time is decided according to sizing compound formula and temperature etc., and also available vulcanizing tank of bottom or drum vulcanizer vulcanize and film; The sizing material of surface layer is also used the calender rolling out film earlier, by the size side's of being cut into sheet earlier, vulcanize out with vulcanizing press mold pressing burst, conditions of vulcanization is the same, three kinds of adhering components faces after the sulfuration through surface treatment (clean with water with solvent or polish after solvent clean with water), coated with adhesive (with neoprene adhesive etc.), treat a period of time (5-20 branch), brush second time, press pattern and pattern applying that product is installed and designed, can paste intermediate layer and bottom earlier, overlay coating again, bottom is pasted in perhaps first overlay coating and intermediate layer again, stops (more than time 8-24 hour) through the certain hour pressing at normal temperatures, carries out cutting by product size at last.
Heat curing system: the preparatory process of sizing material is identical with the front, roll into earlier film separately, surface layer is by the dimensional requirement side of being cut into sheet, intermediate layer, bottom are cut into sheet by product size, pattern of installing and designing by new product and pattern requirement are directly fitted on mould again, place the last hot-press vulcanization moulding of vulcanizing press, conditions of vulcanization is that curing temperature is that the 0.5-3Mpa cure time is decided according to sizing compound formula and temperature etc. at 140-170 ℃ of sulfide stress.
The semi-cure method: the preparatory process of sizing material is identical with the front, sheet mold pressing semi-cure side of one-tenth sheet (bottom also can) on vulcanizing press in the side's of being cut into behind the surface layer rolling out film, to be curing temperature vulcanize the sulphur point at 140-170 ℃ of sulfide stress for the 0.8-3Mpa cure time surpasses to conditions of vulcanization, about big half about normal cure time.Intermediate layer and bottom rolling out film are cut into sheet by product size, fit in mould by pattern and pattern requirement that product is installed and designed, place hot-press vulcanization moulding on the vulcanizing press.Conditions of vulcanization is that curing temperature is that the 0.5-3Mpa cure time is decided according to sizing compound formula and temperature etc. at 140-170 ℃ of sulfide stress.
Claims (4)
1, a kind of color combined composite rubber floor, it is characterized in that described color combined composite rubber floor is made up of surface layer, intermediate layer and bottom, wherein surface layer is that wear-resisting colour of square or pattern rubber plate form through assembling combination, the intermediate layer is an obturator foramen micro-hole structural, the sucker structure of being made up of equally distributed some semicircle orifices in its lower section, bottom is two-sided smooth rubber slab.
2, the preparation technology of the described color combinations rubber floor covering of a kind of claim 1, can use cold bonding method, heat curing system and the preparation of semi-cure method, it is characterized in that described cold bonding technology is with sizing material → calendering → cut-parts → sulfuration → surface treatment coating adhesive → bonding → cutting → finished product, wherein curing temperature is at 140-170 ℃, and sulfide stress is 0.5-3Mpa.
3, the preparation technology of the described color combinations rubber floor covering of a kind of claim 1 is characterized in that described hot vulcanization process is that wherein curing temperature is at 140-170 ℃ with sizing material → calendering → cut-parts → applying → sulfuration → finished product, and sulfide stress is 0.5-3Mpa.
4, the preparation technology of the described color combinations rubber floor covering of a kind of claim 1, it is characterized in that described semi-cure technology is with sizing material → calendering → cut-parts → surface layer semi-cure → applying → sulfuration → finished product, wherein curing temperature is 140-170 ℃, and sulfide stress is 0.5-3Mpa.