CN1853887A - 稻壳板配料 - Google Patents

稻壳板配料 Download PDF

Info

Publication number
CN1853887A
CN1853887A CN 200610066037 CN200610066037A CN1853887A CN 1853887 A CN1853887 A CN 1853887A CN 200610066037 CN200610066037 CN 200610066037 CN 200610066037 A CN200610066037 A CN 200610066037A CN 1853887 A CN1853887 A CN 1853887A
Authority
CN
China
Prior art keywords
silica
rice husk
rice
wood
filler
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200610066037
Other languages
English (en)
Other versions
CN100398281C (zh
Inventor
巴鲁巴亚拉夫·弗拉基米尔·阿列克桑德罗维奇
卡拉塔耶娃·卓娅·阿列克谢夫娜
拉亚霍夫·尼卡拉伊·扎哈拉维奇
高宏
李千育
姜华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dalian Coastal Solchem Materials Co ltd
Institute Of Solid State Chemistry And Mechanochemistry Siberia Branch Russian Academy Of Sciences
Original Assignee
Dalian Coastal Solchem Materials Co ltd
Institute Of Solid State Chemistry And Mechanochemistry Siberia Branch Russian Academy Of Sciences
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dalian Coastal Solchem Materials Co ltd, Institute Of Solid State Chemistry And Mechanochemistry Siberia Branch Russian Academy Of Sciences filed Critical Dalian Coastal Solchem Materials Co ltd
Publication of CN1853887A publication Critical patent/CN1853887A/zh
Application granted granted Critical
Publication of CN100398281C publication Critical patent/CN100398281C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于制作木质板的合成填料配方。其稻壳板的配料包括木质填充料，钠质液体玻璃，硅的二氧化物和六氟乙烷硅酸钠。稻壳或稻壳与木屑按任意比混合物作为木质填充料，而二氧化硅包含了人造二氧化硅或者是SiO2含量不低于80％硅石粉状的各种冶金生产废料，配料成份按照以下比例(重量比)：稻壳：100，根据干燥物质加入的钠质液体玻璃：25－50，二氧化硅：10－70。该木质刨屑板具有耐水性和高强度的性能(静曲强度＝8－15.0Mpa)，此外这种方法还可以充分消化利用农业(稻壳)、木材加工(锯末)和工业(硅石粉)的生产废料。

Description

稻壳板配料
技术领域
该发明属于制作木质板的合成填料，特别是使用农业废料(稻壳)、木材加工废料(木屑)和工业生产废料(硅石粉)合成的稻壳板配料。
背景技术
利用无机、环保粘合物制作板材的配料有很多种。在这些配料中使用木屑、刨屑、粉尘作为木质填充料，使用液体硅酸钠作为粘合物。
已有木质刨屑板配料包括(重量比)：木质刨屑100；钠质液体玻璃80-20，干燥物40-60；含水量80-20；除此之外，在该技术方案中使用六氟乙烷硅酸钠作为改良剂(变性剂)1.2-4.2；(俄罗斯联邦2057773号专利，C08L97/02，10.04.1996)。该技术方案的不足之处是由这些混合物制作的木质刨屑板，其强度和耐水性低。
与本申请最接近的现有技术方案中木质刨屑板配料包括：
木质刨屑                            ---100
根据干燥物质加入的钠质玻璃          ---10-60
硅石粉状废料                        ---3-25
水                                  ---30-80
(俄罗斯2150376B27N3/04，C08L97/02，2000.06.10)。
在此技术方案中使用生产硅铁时产生的硅石粉状废料，含有一种型号的SiO2，其含量要求不低于90％。
发明内容
本发明的目的旨在提供一种扩大综合利用废料的范围、增强板的强度和耐水性的稻壳板配料。
本发明的技术解决方案是：稻壳板配料包括木质填充料、钠质水玻璃、二氧化硅，其特征在于使用稻壳或稻壳与木屑混合物作为木质填充料，二氧化硅包含了人造二氧化硅或是二氧化硅含量不低于80％的硅石粉状的各种生产废料，配料成分按照以下比例(重量比)配制：
稻壳(或者稻壳与木屑按任意比例混合而成的混合物)      ---100
根据干燥物质加入的钠质液体玻璃                      ---25-50
二氧化硅                                            ---10-70
本方案中建议使用人造的、比面超过50m2/k的硅的二氧化物和二氧化硅(SiO2含量为80％或更多的各种生产废料)。这些废料中含有大量的破坏硅酸钠的氯和铁，通过加入钠质液体玻璃进行中和。同时废料中的铬、铝、锆和其它一些成分可以起到增加强度的作用，并且能提高产品的耐水性。在某些情况下为了加快固化反应可以使用少量的六氟乙烷硅酸钠添加剂，加入比例不超过1(重量比)。
本方案中使用了钠质液体玻璃水溶液，模数为2.4-3.6，密度为1.4-1.6g/cm3，并且基本物质(干燥残余物)的含量为33-40％(重量比)。使用人造的、比面超过50m2/k的硅的二氧化物或者各种冶金生产中的微硅石粉末废料(非晶形硅石含量不低于80％)作为新的变性添加剂，起到固化作用。
具体实施方式
稻壳板样品按照以下程序制作：
开始准备粘合剂。模数为2.4-3.6、密度为1.4-1.6g/cm3的钠质液体水玻璃(25-50重量比)与硅的二氧化物或硅石粉(10-70重量比)混合后进行搅拌。将稻壳或者稻壳与锯末混合物放进所得到的粘合物种再次搅拌，可以视情况少量添加(100重量比)。
将搅拌后的配料均匀地铺到模具中，在1.0-4.0Mpa的压力下进行冷压并将炉温调至150-200℃，之后慢慢冷却至水分完全蒸发。制成板的密度为850-1400kg/cm3。
将制作好的板坯按照规格进行切割并按照“木质刨屑板”10632-89国标进行检测。
本申请的板材配料及样品见表1。其物理机械性能指标见表2。
从表中可见，本申请使用稻壳或稻壳与锯末混合物作为木质填充料，可以生产出强度大、耐水性好的板材。这种方法可以充分消化利用各种农业、木材加工和冶金生产中的废料。
表1
  样品                                              配料
  木质填充料(重量比)   钠质液体玻璃(重量比)   硅的二氧化物(重量比)
  稻壳   锯末
  1   100   40   16
  2   木质标准刨屑
  3   100   25   10
  4   100   33   30
  5   100   50   70
  6   50   33   30
  7   80   30   30
  8   100   40   70
表2
  产品及性能   某种方法   用酚醛树脂制作的板材               木质刨屑板配料与表1相符
  1   2   3   4   5   6   7   8
  密度，kg/cm3   850   850   850   1400   1000   1200   1000
  静曲强度，Mpa   11.1   17.6   8.0   11.3   15.0   13.5   14.7   13.0
  24小时内吸水厚度膨胀率，％   5.2                                        膨胀率低于3％

Claims (1)

1、一种稻壳板配料，包括木质填充料，钠质水玻璃，二氧化硅，其特征在于：使用稻壳或稻壳与木屑混合物作为木质填充料，二氧化硅包含了人造二氧化硅或者是二氧化硅含量不低于80％硅石粉状的各种冶金生产废料，配料成分按照以下比例配制：
稻壳                                           ---100
根据干燥物质加入的钠质液体玻璃                 ---25-50
二氧化硅                                       ---10-70。
CNB200610066037XA 2005-04-20 2006-03-27 稻壳板配料 Expired - Fee Related CN100398281C (zh)