CN1847444A - Carburizing process with pre-vacuumizing, protecting nitrogen-base atmosphere and no inner oxidation - Google Patents
Carburizing process with pre-vacuumizing, protecting nitrogen-base atmosphere and no inner oxidation Download PDFInfo
- Publication number
- CN1847444A CN1847444A CN 200610026435 CN200610026435A CN1847444A CN 1847444 A CN1847444 A CN 1847444A CN 200610026435 CN200610026435 CN 200610026435 CN 200610026435 A CN200610026435 A CN 200610026435A CN 1847444 A CN1847444 A CN 1847444A
- Authority
- CN
- China
- Prior art keywords
- nitrogen
- carburizing
- acetylene
- forvacuum
- protecting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The carburizing process with pre-vacuumizing, protecting nitrogen-base atmosphere and no inner oxidation belongs to the field of heat treatment technology of metal material. The present invention has the hot treating furnace pre-vacuumized to 10-100 Pa, introduced with high purity nitrogen and heated to 900-1050 deg.c, before maintaining and introducing acetylene gas to carburize at nitrogen pressure of 0.1-0.11 MPa and acetylene gas pressure of 5000-20000 Pa. The present invention has no carbon black production, environment friendship, less oxidation of workpiece, low cost and high safety.
Description
Technical field
A kind of method for carburizing that the present invention relates to, particularly a kind of method for carburizing of forvacuum protecting nitrogen-base atmosphere and no inner oxidation belongs to metallic substance thermal treatment field.
Background technology
For improving the thermo-chemical treatment quality, reduce defectives such as the interior oxidation of carburizing, adopt the low-pressure carburization method usually.Low-pressure carburization is a kind of novel carburizing tech that grows up on gas cementation and vacuum hardening technical foundation, workpiece placed under the vacuum environment heat, the hydrocarbon polymer that feeds certain pressure carries out carburizing, hydrocarbons decompose is the carbon and the hydrogen of free state under the hot metal surface catalysis, the carbon of high density is adsorbed by the pyritous workpiece surface, thereby reaches the carburizing purpose of no inner oxidation.The shortcoming of this technology is: 1) carbon concentration can't detect and control at present under the vacuum environment; 2) can't utilize existing pit carburizing furnace and mult-purpose chamber furnace, the early investment of equipment is very big.And the conventional gas carburizing is that a certain proportion of carrier gas (as nitrogen or methyl alcohol) and enriched gas (kerosene or acetone etc.) are fed realization carburizing in the burner hearth, and the shortcoming of this technology is that oxidation is more serious in the workpiece.In order to improve workpiece quality, reduce cost, reduce pollution to environment, the investigator is just attempting adopting and is carrying out carburizing under the different nitrogen-based atmospheres both at home and abroad.
Find through literature search prior art, " the nitrogen base atmosp-here heat treatment progress " of Wu Guangzhi, external metal heat treatmet, 1999 (6), introduced: adopt N
2+ C
3H
8, N
2+ CH
4+ CO
2Deng protecting carburizing.Use N
2+ C
3H
8Protect carburizing to be easy to generate carbon black; Use N
2+ CH
4+ CO
2Protect its speed of carburizing slow, and have interior oxidation to take place.These factors have restricted popularization and the application of above-mentioned technology in industry.
Summary of the invention
The present invention is directed to and carry out two kinds of methods of carburizing deficiency and defective separately under low-pressure carburization and the existing nitrogen-based atmosphere; a kind of method for carburizing of forvacuum protecting nitrogen-base atmosphere and no inner oxidation has been proposed; advantage to two kinds of methods integrates; make it to realize the no inner oxidation carburizing; can reduce cost again, also have advantages such as security is good, environmental protection simultaneously.
The present invention is achieved by the following technical solutions, by carrying out forvacuum to 10-100Pa to the heat treatment furnace that is provided with stove internal recycle blower fan, feeds high-purity nitrogen, furnace temperature risen to 900-1050 ℃ again, feeds acetylene gas after the insulation again and carry out carburizing.In the heat treatment furnace, under the driving of stove internal recycle blower fan be that carrier gas, acetylene are that the mixed gas of enriched gas flows in stove with the high pure nitrogen, be the carbon atom that acetylene decomposites free state under 900-1050 ℃ the katalysis of workpiece surface in temperature, carbon atom is adsorbed by workpiece surface and carries out carburizing.Nitrogen gas pressure is 1 * 10 in the burner hearth
5-1.1 * 10
5Between the Pa, the acetylene dividing potential drop that charges into is between the 5000-20000Pa, and the pressure of nitrogen, acetylene can be regulated by the inlet and outlet under meter continuously according to the signal that the furnace pressure table feeds back.Wherein, the purity of nitrogen is greater than 99.9%.
The present invention realizes the control of the distribution of cementation zone carbon concentration, carburizing speed and case depth by parameters such as acetylene dividing potential drops in control carburizing temperature, carburizing time and the burner hearth.At first be determined by experiment under different carburizing temperatures and different carburizing time: the relation of the relation of the relation of acetylene dividing potential drop and surface carbon concentration, acetylene dividing potential drop and case depth, acetylene dividing potential drop and carburizing speed.Utilize these 3 relations to calculate again: workpiece can obtain the case depth and the needed acetylene dividing potential drop of surface carbon concentration of expection.This method has overcome the expensive and conventional carburizing of low-pressure carburization stove can't avoid the shortcoming of interior oxidation, thereby realizes the purpose of workpiece no inner oxidation carburizing.
The present invention and low-pressure carburization with conventional gas carburizing compared following characteristics: 1) by heat treatment furnace is carried out forvacuum, feed nitrogen and acetylene again, avoid the interior oxidation of workpiece when heating and carburizing, overcome the defective of oxidation in the conventional gas carburizing takes place; 2) by can effectively control the generation of workpiece surface carbon black in case depth and the cementation process to the adjusting that feeds the acetylene dividing potential drop; 3) mixed gas of nitrogen and acetylene evenly motion in stove under the effect of stove internal recycle blower fan makes the homogeneous carburizing of workpiece surface energy, has overcome the shortcoming of conventional gas carburizing inequality; 4) can in mult-purpose chamber furnace or pit carburizing furnace, realize the no inner oxidation carburizing, reduce the cost of technological transformation greatly.
Embodiment
Content in conjunction with the inventive method provides following examples:
Embodiment 1
At first workpiece is put into pit carburizing furnace, carry out forvacuum, when furnace pressure arrived 100Pa, filling purity again in stove was 99.9%-99.9999% nitrogen, and adjusting pressure is 1.02 * 10
5Pa, heater starts stove internal recycle blower fan simultaneously, the speed of rotation of stove internal recycle blower fan is 1000rpm, charges into acetylene after temperature rises to 980 ℃ in burner hearth, and dividing potential drop is 10000Pa, speed of rotation with stove internal recycle blower fan is adjusted into 500rpm simultaneously, behind the 60min with the workpiece oil quenching.This example cementation zone is more even, the infiltration layer no inner oxidation.
Embodiment 2
At first workpiece is put into mult-purpose chamber furnace, carry out forvacuum, when furnace pressure arrived 10Pa, filling purity again in stove was 99.9%-99.9999% nitrogen, and adjusting pressure is 1.1 * 10
5Pa, heater, start stove internal recycle blower fan simultaneously, the speed of rotation of stove internal recycle blower fan is 1400rpm, after rising to 1000 ℃, temperature in burner hearth, charges into acetylene, dividing potential drop is 20000Pa, and the speed of rotation with stove internal recycle blower fan is adjusted into 700rpm simultaneously, behind the 60min workpiece transfer is quenched to cooling room.This example cementation zone is more even, and the surface does not have carbon black, the infiltration layer no inner oxidation.
Embodiment 3
At first workpiece is put into pit carburizing furnace, carry out forvacuum earlier, when furnace pressure arrived 10Pa, filling purity again in stove was 99.9%-99.9999% nitrogen, and adjusting pressure is 1.04 * 10
5Pa, heater, start stove internal recycle blower fan simultaneously, the speed of rotation of stove internal recycle blower fan is 700rpm, after rising to 1050 ℃, temperature in burner hearth, charges into acetylene, dividing potential drop is 20000Pa, and the speed of rotation with stove internal recycle blower fan is adjusted into 500rpm simultaneously, behind the 120min workpiece transfer is carried out air cooling to cooling room.This example cementation zone is more even, the infiltration layer no inner oxidation.
Claims (4)
1, a kind of method for carburizing of forvacuum protecting nitrogen-base atmosphere and no inner oxidation; it is characterized in that; by carrying out forvacuum to 10-100Pa to the heat treatment furnace that is provided with stove internal recycle blower fan; feed nitrogen; furnace temperature is risen to 900-1050 ℃ again; feed acetylene gas after the insulation again and carry out carburizing, nitrogen gas pressure is 1 * 10 in the burner hearth
5-1.1 * 10
5Between the Pa, the acetylene dividing potential drop that charges into is between the 5000-20000Pa.
2, the method for carburizing of forvacuum protecting nitrogen-base atmosphere and no inner oxidation according to claim 1; feature is; in the heat treatment furnace; under the driving of stove internal recycle blower fan be that carrier gas, acetylene are that the mixed gas of enriched gas flows in stove with nitrogen; be the carbon atom that acetylene decomposites free state under 900-1050 ℃ the katalysis of workpiece surface in temperature, carbon atom is adsorbed by workpiece surface and carries out carburizing.
3, according to the method for carburizing of claim 1 or 2 described forvacuum protecting nitrogen-base atmosphere and no inner oxidations, feature is that the pressure of nitrogen, acetylene is regulated by the inlet and outlet under meter continuously according to the signal that the furnace pressure table feeds back.
4, according to the method for carburizing of claim 1 or 2 described forvacuum protecting nitrogen-base atmosphere and no inner oxidations, feature is that the purity of nitrogen is greater than 99.9%.