CN1847413A - 20Cr2Ni4钢材的正火热处理工艺 - Google Patents

20Cr2Ni4钢材的正火热处理工艺 Download PDF

Info

Publication number
CN1847413A
CN1847413A CN 200510050228 CN200510050228A CN1847413A CN 1847413 A CN1847413 A CN 1847413A CN 200510050228 CN200510050228 CN 200510050228 CN 200510050228 A CN200510050228 A CN 200510050228A CN 1847413 A CN1847413 A CN 1847413A
Authority
CN
China
Prior art keywords
20cr2ni4
steel
normalizing
heat treatment
stove
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200510050228
Other languages
English (en)
Other versions
CN100434542C (zh
Inventor
王晓华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wanxiang Qianchao Co Ltd
Original Assignee
Wanxiang Qianchao Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wanxiang Qianchao Co Ltd filed Critical Wanxiang Qianchao Co Ltd
Priority to CNB2005100502282A priority Critical patent/CN100434542C/zh
Publication of CN1847413A publication Critical patent/CN1847413A/zh
Application granted granted Critical
Publication of CN100434542C publication Critical patent/CN100434542C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种钢材的热处理，特别是涉及一种20Cr2Ni4钢材的正火工艺。工艺步骤如下：(1)将钢材放入炉温度850℃－930℃的炉内加热到850℃－930℃后保温4－11小时，(2)通过7－12小时的降温时间降温至540℃－650℃后保温0.5－5小时，(3)出炉整筐空冷。它工艺较为简单，成本较低，20Cr2Ni4钢材一次正火后硬度就能达到180HBS－227HBS，解决了现有技术所存在的正火加二到三次高温回火热处理工艺存在着工艺较为复杂和成本较高等问题。

Description

20Cr2Ni4钢材的正火热处理工艺
技术领域
本发明涉及一种钢材的热处理，特别是涉及一种20Cr2Ni4钢材的正火工艺。
背景技术
20Cr2Ni4钢材硬度太高(大于227HBS)或太低(小于180HBS)一般会对机加工产生不利的影响，使钢材不能机加工成形。原工艺一次正火后20Cr2Ni4钢材硬度为621HBS，目前均认为：20Cr2Ni4钢材采用正火加二到三次高温回火，其硬度才能达到180HBS-227HBS。
如一种锻压件双重预热正火预先热处理工艺，它包括预热和正火工序，在正火前加了预热工序，工艺步骤为：第一次正火前，对锻压件进行预热加温至600-710℃之后，进行保温四小以上，之后再对锻压件进行加温至950-1000℃，保温后再空气冷却到室温，第二次正火前，对锻压件进行第二次预热加温至600-710℃，之后，进行保温四小时以上，之后再对锻件进行加温至870℃保温后再空气冷却到室温，冷却后再预热加温至600-710℃，保温小于四小时再转入调质工序。
发明内容
本发明主要目的在于提供一种工艺较为简单，成本较低，20Cr2Ni4钢材一次正火后硬度就能达到180HBS-227HBS的正火工艺，解决了现有技术所存在的正火加二到三次高温回火热处理工艺存在着工艺较为复杂和成本较高等问题。
本发明的上述技术目的是通过以下技术方案解决的：工艺步骤如下：
(1)、将钢材放入炉温度850℃-930℃的炉内加热到850℃-930℃后保温4-11小时，
(2)、通过7-12小时的降温时间降温至540℃-650℃后保温0.5-5小时，
(3)、出炉整筐空冷。
其中，炉温指工件放入炉体前的炉内温度；保温温度指工件受加热或冷却所达到的保温温度；降温时间指从较高的温度降到较低的温度所需的时间。以本发明技术方案提供的正火方法进行一次正火(不需回火)后20Cr2Ni4钢材硬度就能达到180HBS-227HBS，工艺较为简单，降低了加工成本。
作为优选，所述的炉温为860℃-910℃；所述(1)的保温温度为860℃-900℃；所述(1)的保温时间为5-9小时。
作为优选，所述(2)的降温时间为8-10小时；所述(2)的保温温度为550℃-600℃；所述(2)的保温时间为1-3小时。
因此，本发明具有进行一次正火(不需回火)后20Cr2Ni4钢材硬度就能达到180HBS-227HBS，工艺较为简单，降低了加工成本的特点。
附图说明
附图1是原正火后金相照片(1000×)；
附图2是本发明正火后金相照片(1000×)。
具体实施方式
下面通过具体实施例，并结合附图，对本发明的技术方案作进一步具体的说明。
实施例：实施例1：将20Cr2Ni4钢材制成的料坯放入炉内温度为890℃的井式炉，将料坯加热到890℃，在炉内保温9小时后，降温至650℃(降温时间为11小时)，在炉内保温0.5小时后，出炉整筐空冷，即可得到硬度为180HBS-227HBS(采用国标GB231-84规定的金属布氏硬度试验方法测定)，金相组织(如图2)为铁素体加片状珠光体的机加工用正火料。
实施例2：将20Cr2Ni4钢材制成的料坯放入炉内温度为910℃的井式炉，将料坯加热到910℃，在炉内保温11小时后，降温至580℃(降温时间为7小时)，在炉内保温5小时后，出炉整筐空冷，即可得到硬度为180HBS-227HBS(采用国标GB231-84规定的金属布氏硬度试验方法测定)，金相组织(如图2)为铁素体加片状珠光体的机加工用正火料。
实施例3：将20Cr2Ni4钢材制成的料坯放入炉内温度为850℃的井式炉，将料坯加热到850℃，在炉内保温4小时后，降温至550℃(降温时间为12小时)，在炉内保温3小时后，出炉整筐空冷，即可得到硬度为180HBS-227HBS(采用国标GB231-84规定的金属布氏硬度试验方法测定)，金相组织(如图2)为铁素体加片状珠光体的机加工用正火料。
实施例4：将20Cr2Ni4钢材制成的料坯放入炉内温度为930℃的井式炉，将料坯加热到930℃，在炉内保温5小时后，降温至610℃(降温时间为8小时)，在炉内保温1小时后，出炉整筐空冷，即可得到硬度为180HBS-227HBS(采用国标GB231-84规定的金属布氏硬度试验方法测定)，金相组织(如图2)为铁素体加片状珠光体的机加工用正火料。
实施例5：将20Cr2Ni4钢材制成的料坯放入炉内温度为860℃的井式炉，将料坯加热到860℃，在炉内保温8小时后，降温至600℃(降温时间为10小时)，在炉内保温3小时后，出炉整筐空冷，即可得到硬度为180HBS-227HBS(采用国标GB231-84规定的金属布氏硬度试验方法测定)，金相组织(如图2)为铁素体加片状珠光体的机加工用正火料。

Claims (7)

1.一种20Cr2Ni4钢材的正火热处理工艺，其特征在于工艺步骤为：
(1)、将钢材放入炉温度850℃-930℃的炉内加热到850℃-930℃后保温4-11小时，
(2)、通过7-12小时的降温时间降温至540℃-650℃后保温0.5-5小时，
(3)、出炉整筐空冷。
2.根据权利要求1所述的20Cr2Ni4钢材的正火热处理工艺，其特征在于所述的炉温为860℃-910℃。
3.根据权利要求1或2所述的20Cr2Ni4钢材的正火热处理工艺，其特征在于所述(1)的保温温度为860℃-900℃。
4.根据权利要求1或2所述的20Cr2Ni4钢材的正火热处理工艺，其特征在于所述(1)的保温时间为5-9小时。
5.根据权利要求1或2所述的20Cr2Ni4钢材的正火热处理工艺，其特征在于所述(2)的降温时间为8-10小时。
6.根据权利要求1或2所述的20Cr2Ni4钢材的正火热处理工艺，其特征在于所述(2)的保温温度为550℃-600℃。
7.根据权利要求1或2所述的20Cr2Ni4钢材的正火热处理工艺，其特征在于所述(2)的保温时间为1-3小时。
CNB2005100502282A 2005-04-12 2005-04-12 20Cr2Ni4钢材的正火热处理工艺 Expired - Fee Related CN100434542C (zh)