CN1821135A - Jade color glass material and its use in producing glass products - Google Patents
Jade color glass material and its use in producing glass products Download PDFInfo
- Publication number
- CN1821135A CN1821135A CN 200610044492 CN200610044492A CN1821135A CN 1821135 A CN1821135 A CN 1821135A CN 200610044492 CN200610044492 CN 200610044492 CN 200610044492 A CN200610044492 A CN 200610044492A CN 1821135 A CN1821135 A CN 1821135A
- Authority
- CN
- China
- Prior art keywords
- jade
- glass
- jade color
- bottle
- jar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
One kind of jade color glass material consists of quartzite 53.6-63 wt%, aluminum hydroxide 7.6-14 wt%, sodium carbonate 20.3-29 wt%, sodium fluorosilicate 1.7-5.1 wt%, barite 2.4-6.4 wt% and cobalt powder 0.012-0.024 wt%. Using the jade color glass material can match produce glass bottle, jar and other utensils. The jade color glass has fine texture, foggy translucent effect, smooth surface, lubricating and tender look and beautiful appearance as well as low cost.
Description
Art
The present invention relates to a kind of jade green frit and the application in producing glass bottle and jar and glassware thereof.
Background technology
Along with improving constantly of people's living standard and quality of life, also more and more high to the service requirements of glass bottle and jar or glassware.People, and select as a kind of artwork of beautifying the environment, decorating culture life it with not only being confined on its functions of use its need, are a kind of class of pursuing when daily life is consumed of people and to the demand of the enjoyment of U.S..For constantly satisfying people's demand, frosting the decoration to glass bottle and jar or glassware appearred in recent years:.Mat glass Bottle ﹠ Can or mat glass vessel from outside to watch them be translucent, have indistinct dim aesthetic feeling; But they carry out secondary processing to glass and just make, and its dim, fuzzy sense is often inhomogeneous, and it is bright to occur local full impregnated sometimes, and the rough situation of surface irregularity.Harmful soup very easily remains in the goods inwall in the frosting process in addition, therefore also the goods of producing thoroughly must be cleaned with water clean could the use afterwards, the manufacturing cost of product is significantly improved, thereby reduced the competitiveness of product in market.Simultaneously, the waste liquid that produces in the above-mentioned frosting process can cause environmental pollution to a certain degree, thereby has limited further developing of this series products.Existing jade green glassy product removes has general fine and smooth quality of jade and the tender outward appearance of oil, the dim aesthetic feeling that also has mat glass, be that a kind of class is high, the glassy product that the market demand potential is huge, and it is produced employing crucible oven production technique, belongs to batch production at present, not only yields poorly, and expect matter and expect that look very unstable, of poor quality, the products production limitation is big, no matter thereby be that output or quality all can not be met the need of market far away.
Summary of the invention
The purpose of this invention is to provide a kind of jade green frit and the application in producing glass bottle and jar and glassware thereof, it can overcome the above-mentioned shortcoming of existing frosting product and crucible oven production jade green glassy product.
A kind of jade green frit, it is characterized in that admixtion is made up of quartz sand, aluminium hydroxide, soda ash, Sodium Silicofluoride, barite and cobalt powder, their weight percentage scope is respectively 53.6-63,7.6-14,20.3-29,1.7-5.1,2.4-6.4 and 0.012-0.024.
The application of above-mentioned jade green frit in tank furnace production glass bottle and jar or glassware.
The glass bottle and jar and the glassware that adopt jade green frit of the present invention to produce, its quality exquisiteness not only has indistinct translucent effect uniformly; Also have smooth surface, color and luster moistens characteristics such as tender no porcelain, need not to carry out deep processing, just can obtain the dim aesthetic effect of uniformity.The present invention can carry out extensive continuous production in enormous quantities on tank furnace; Greatly reduce product cost, effectively guaranteed quality product, stopped bad environment pollution; But the various glass bottle and jars of widespread production, glassware, Glass tubing, glass stick, piece, glass decoration lamp sheet etc., widened product applications, have good market development space, have high economic benefit and social benefit, filled up the blank that domestic tank furnace is produced the jade green glasswork.
Embodiment
During batching, take by weighing quartz sand 62.5kg (SiO wherein
2Content is 99%), aluminium hydroxide 8.9kg (AL wherein
2O
3Content is 65%), soda ash 23.5kg (Na wherein
2O content is 57%), Sodium Silicofluoride 2.586kg (Na wherein
2SiF
6Content is 98%), barite 2.5kg (wherein BaO content is 52%) and cobalt powder 0.014kg (wherein CoO content is 70%), through being mixed and made into admixtion.When making jade green glass bottle and jar or glassware, the compound of making is joined in the tank furnace through charging machine, carrying out high temperature (1400-1530 ℃) founds, then the glass metal that melts is continuously supplied with molding device by feed and carry out moulding, the glasswork of moulding is annealed in annealing furnace, then through the packing warehouse-in that is up to the standards.
Described glass bottle and jar comprises Beer Bottle, White Spirit Bottle, beverage bottle, burgundy bottle, food packaging bottle, saline bottle, bottle for cosmetics, school supply and stationery bottle etc., and described glassware comprises glass cylinder, glass bowl, tallboy, microwave plate, frying pan, enamelware pot, coffee pot, ashtray etc.
Adopt above technology, use jade green frit of the present invention to add micro-discoloring agent and tinting material, can also produce versicolor jade green glassy products such as white jade look, ruby, palm fibre, Huang.At present, sample is produced and is succeedd.
Claims (2)
1, a kind of jade green frit, it is characterized in that admixtion is made up of quartz sand, aluminium hydroxide, soda ash, Sodium Silicofluoride, barite and cobalt powder, their weight percentage scope is respectively 53.6-63,7.6-14,20.3-29,1.7-5.1,2.4-6.4 and 0.012-0.024.
2, the application of the described jade green frit of claim 1 in tank furnace production glass bottle and jar or glassware.