CN1810704A - 砼承重保温砖及其制造方法 - Google Patents

砼承重保温砖及其制造方法 Download PDF

Info

Publication number
CN1810704A
CN1810704A CN 200610008406 CN200610008406A CN1810704A CN 1810704 A CN1810704 A CN 1810704A CN 200610008406 CN200610008406 CN 200610008406 CN 200610008406 A CN200610008406 A CN 200610008406A CN 1810704 A CN1810704 A CN 1810704A
Authority
CN
China
Prior art keywords
weight part
foam
concrete
foam grain
cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200610008406
Other languages
English (en)
Other versions
CN1328204C (zh
Inventor
周智民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from CN 200510050806 external-priority patent/CN1736938A/zh
Application filed by Individual filed Critical Individual
Priority to CNB200610008406XA priority Critical patent/CN1328204C/zh
Publication of CN1810704A publication Critical patent/CN1810704A/zh
Application granted granted Critical
Publication of CN1328204C publication Critical patent/CN1328204C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种砼承重保温砖,由水泥、水、砂和石屑组成的砼混合料加入泡沫塑料颗粒及减水剂混合组成,其重量配比如下:水泥1重量份、水0.16-0.55重量份、砂0-1.5重量份、石屑1.5-6重量份、泡沫塑料颗粒0.002-0.06重量份、减水剂0-0.03重量份。本发明还公开了其制造方法,是将水泥、砂、石屑、0.5-8mm粒径的泡沫塑料、减水剂等按配比加入水搅拌成混合料后用制砖设备加工成型,脱模堆放进行养护,达到强度后即可使用。本发明产品在保持原有砌体作用的基础上又增加了保温节能效果;利用废泡沫塑料,有利环境保护;制作成本低、效率高、工艺简单;大大节省了为达到节能效果的工程费用。

Description

砼承重保温砖及其制造方法
技术领域
本发明涉及一种兼备承重、分隔围护和保温作用的砌体用砖,具体来说是一种在砼混合料内加入了一定量泡沬塑料颗粒制成的保温砖。
背景技术
现有的保温砌体产品多为加气砼块材,产品主要以磨细石英砂、石灰、水泥和石膏为原料,以铝粉为发气剂,经配料、搅拌、预养、切割,在高温高压下养护10~14小时而制成的细密多孔状轻质加气混凝土制品。该生产工艺复杂,发气所产生的气泡并不十分稳定,且需要进行蒸养,相对成本较高,由于配料中必须掺有较多量的石灰,用于与铝粉的作用进行发气,决定了该产品的抗压远远低于砼的抗压强度;且在该砌体表面进行粉刷经常引起空鼓,是目前建筑施工中的一大通病。为了达到节能目的,现在有采用在外墙面粘贴泡沬板再进行粉刷的做法,也有在外粉刷时采用保温砂浆的做法,前者显然要提高较多的成本,而且施工工艺复杂,且极易造成粉刷起壳;后者存在掺量是否正确的问题,且效果不太明显。
砼具有很好的抗压强度,泡沬塑料有很好的保温效果,在砼混合料内加入了一定量泡沬塑料颗粒制成的保温砖,在具备原有的承重作用的基础上又增加了保温节能效果,且其导热系数低λ=0.26-0.43(W/(m.K)),是普通砼砖1/4-1/2左右,强度可达Mu5-Mu15,符合国家现行政策和节能要求。
发明内容
本发明提供了一种在砼混合料内加入了一定量泡沬塑料颗粒制成的保温砖,该保温砖具有良好的抗压强度,而且具有更好的保温节能效果。
一种砼承重保温砖,其特征是主要由水泥、砂和石屑、水组成的砼混合料加入泡沬塑料颗粒及减水剂组成,其重量配比如下:
水泥1重量份、水0.16-0.55重量份、砂0-1.5重量份、石屑1.5-6重量份、泡沫塑料颗粒0.002-0.06重量份。
上述组成中还可加入:粉煤灰0-0.25重量份、早强剂0-0.02重量份减水剂0-0.03重量份。
所述的泡沬塑料颗粒为粒径为0.5-8mm的泡沬塑料颗粒或由废泡沬塑料加工成的0.5-8mm的泡沬塑料颗粒。
上述砼承重保温的砖制造方法的步骤如下:
a、选取0.5-8mm的泡沬塑料颗粒或按将废泡沬塑料块用粉碎机制成粒径为0.5-8mm的泡沬塑料颗粒;
b、按配比计量称取水泥、水、砂、石屑、泡沬塑料颗粒、粉煤灰、减水剂和早强剂,各项材料的计量误差不超过2.5%;
c、配料后将石屑、砂、润湿后的泡沬塑料颗粒、粉煤灰、水泥依次倒入搅拌机料斗,加水搅拌成均匀的混合料,泡沬塑料颗粒可在砼搅拌均匀后再投入并搅拌至均匀;
d、混合料用小车或输送装置送至制砖设备,入模后铺平进行振捣成型后脱模,运至堆放处,堆成砖垛,也可在胎座上用钢模制作;
e、成型后砼砖可进行自然养护或堆垛进行自然养护或蒸养,达到强度即成产品。
本发明同样采用传统的砌体装饰施工工艺,但与现有的砼加气块材相比,本发明具有加工工艺简单、质量稳定、兼备承重、分隔围护与保温作用、成本相对较低等优点;解决了泡沬塑料的回收利用问题,变废为宝,能有效地防止环境污染,简化了为达到建筑节能所采取的相应技术措施;导热系数低λ=0.26-0.43(W/(m.K)),是普通砼砖1/4-1/2左右,符合国家现行政策和环保要求;且粉刷时不易引起空鼓,大大节省了为达到节能效果的工程费用。本发明适用范围广泛。
具体实施方式
实施例1:
a、将回收的聚苯乙烯泡沬塑料块用粉碎机制成粒径为0.5-8mm的泡沬塑料颗粒;
b、按配比计量称取各物料:水泥1重量份、水0.3重量份、砂1.5重量份、石屑1.5重量份、泡沬塑料颗粒0.0035重量份、粉煤灰0.25重量份、减水剂0.03重量份、早强剂0.02重量份;
c、将配好后的石屑、砂、加少量水润湿后的泡沬塑料颗粒、粉煤灰、水泥依次倒入搅拌机料斗,加其余的水和减水剂、早强剂搅拌成均匀的混合料,泡沬塑料颗粒可在砼搅拌均匀后再投入并搅拌至均匀;
d、混合料用小车或输送装置送至制砖设备,入模后铺平进行振捣成型后脱模,运至堆放处,堆成砖垛,也可在胎座上用钢模制作;
e、成型后砼砖可进行自然养护或堆垛进行自然养护(可用塑料薄膜进行履盖)或蒸养,达到强度即成产品。
本配比主要用于冬季制砖。
实施例2:
生产步骤同实施例1,各物料的配比为:水泥1重量份、水0.4重量份、石屑4重量份、泡沬塑料颗粒0.005重量份。
实施例3:
a、选取粒径为0.5mm-8mm的聚乙烯泡沬塑料颗粒;
b、按配比计量称取各物料:水泥1重量份、水0.5重量份、砂1重量份、石屑3.2重量份、泡沬塑料颗粒0.002重量份、其余步骤同实施例1。
实施例4:
生产步骤同实施例1,各物料的配比为:水泥1重量份、水0.2重量份、石屑3重量份、泡沬塑料颗粒0.008重量份、减水剂0.02重量份。
实施例5:
生产步骤同实施例1,各物料的配比为:水泥1重量份、水0.25重量份、砂1.2重量份、石屑5重量份、泡沬塑料颗粒0.02重量份。
实施例6:
生产步骤同实施例1,各物料的配比为:水泥1重量份、水0.55重量份、砂0.5重量份、石屑6重量份、泡沬塑料颗粒0.06重量份。
实施例7:
生产步骤同实施例1,各物料的配比为:水泥1重量份、水0.16重量份、砂0.8重量份、石屑2重量份、泡沬塑料颗粒0.04重量份。
实施例8:
生产步骤同实施例1,各物料的配比为:水泥1重量份、水0.35重量份、砂1.5重量份、石屑2.5重量份、泡沬塑料颗粒0.05重量份。
实施例9:
生产步骤同实施例1,各物料的配比为:水泥1重量份、水0.45重量份、砂0.6重量份、石屑4.5重量份、泡沬塑料颗粒0.01重量份。
本发明在砼的混合料中掺入一定比例的泡沬塑料颗粒,既可利用新的泡沫塑料原料,也可利用废旧泡沫塑料原料,材料来源广泛,使砼砖在具备原有的承重作用的基础上增加了保温效果;所生产的砼承重保温砖导热系数低,λ=0.26-0.43(W/(m.K))是普通砼砖1/4-1/2左右,符合国家现行政策和节能要求,制造方法简单,便于操作,综合效率高;产品表面粗糙,便于使用传统的方法操作,适用范围广泛。
本发明的砼承重保温砖与普通(砼及普通粘土)砖相似。可设计成现有砖的任何尺寸,具体规格有:240*115*53、240*115*90、240*180*90、365*190*240、365*190*180、190*190*90、600*125*250等。并可根据承重要求,设计成Mu5-15且可制成实心砖与空心砖。

Claims (4)

1.一种砼承重保温砖,其特征是主要由水泥、水、砂和石屑组成的砼混合料加入泡沫塑料颗粒组成,其重量配比如下:
水泥1重量份、水0.16-0.55重量份、砂0-1.5重量份、石屑1.5-6重量份、泡沫塑料颗粒0.002-0.06重量份。
2.根据权利要求1所述的砼承重保温砖,其特征是:上述组成中还可加入:粉煤灰0-0.25重量份、早强剂0-0.02重量份、减水剂0-0.03重量份。
3.根据权利要求1所述的砼承重保温砖,其特征是:所述的泡沫塑料颗粒为粒径为0.5-8mm的泡沫塑料颗粒或由废泡沫塑料加工成的0.5-8mm的泡沫塑料颗粒。
4.根据权利要求1所述的一种砼承重保温砖的制造方法,包括如下步骤:
a、选取0.5-8mm的泡沫塑料颗粒或将废泡沫塑料块用粉碎机制成粒径为0.5-8mm的泡沫塑料颗粒;
b、按配比计量称取水泥、水、砂、石屑、泡沫塑料颗粒、粉煤灰、减水剂和早强剂,各项材料的计量误差不超过2.5%;
c、配料先将石屑、砂、润湿后的泡沫塑料颗粒、粉煤灰、水泥依次倒入搅拌机料斗,材料进入搅拌筒时加入水及粉煤灰、减水剂和早强剂,搅拌成均匀的混合料,泡沫塑料颗粒可在砼搅拌均匀后再投入并搅拌至均匀;
d、混合料送至制砖设备,入模后铺平进行振捣成型后脱模,运至堆放处,堆成砖垛,也可在胎座上用钢模制作;
e、成型后砼砖可进行自然养护或堆垛进行自然养护或蒸养,达到强度即成产品。
CNB200610008406XA 2005-07-19 2006-01-20 砼承重保温砖及其制造方法 Expired - Fee Related CN1328204C (zh)