CN1807121A - Production process for printing whole-cotton transfer printing paper using copper-plate press - Google Patents
Production process for printing whole-cotton transfer printing paper using copper-plate press Download PDFInfo
- Publication number
- CN1807121A CN1807121A CN 200510026661 CN200510026661A CN1807121A CN 1807121 A CN1807121 A CN 1807121A CN 200510026661 CN200510026661 CN 200510026661 CN 200510026661 A CN200510026661 A CN 200510026661A CN 1807121 A CN1807121 A CN 1807121A
- Authority
- CN
- China
- Prior art keywords
- printing
- paper
- halftone etching
- transfer printing
- cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates the manufacturing technique of all-cotton transfer printing paper. The technology comprises the following steps: treating roller, engraving activation according to image processing system signal, checking image, raw-paper halftone etching basecoat technology, drying with hot wind, starching the halftone etching to catalyze isolated layer, drying with double-layer hot wind, screen printing color register color printing, and all-cotton bat printing. The raw-paper halftone etching basecoat technology, starching the halftone etching to catalyze isolated layer, drying with double-layer hot wind, and screen printing color register color printing are new additional procedure. The all-cotton transfer printing paper made with the method has better bat printing effect. The method has the advantages of easy operation, high standard-piece rate, low cost, environmental protection and saving energy.
Description
Technical field
The present invention relates to textile printing and dyeing industry, specifically be meant the production technology of a kind of intaglio press printing cotton transfer printing Paper
Background technology
On textile, carry out transfer printing and release in the whole world in nineteen sixty-eight, just produced 2,000,000 square metres then by plucked instrument Boli this generation Supreme Being gram (Sublistatic) company.Because this product and production technology meet energy-conservation and environmental requirement, operate simple again, so on market, started a stamp revolution already very soon.But this transfer printing is confined to synthetic fabrics such as polyester fiber, and is applied to cotton, on the natural fabrics such as hair and silk, remains in many shortcomings and problem.Though transfer printing is improved in recent years, when on all-cotton fabric, using, not that printing quality is undesirable, be exactly the all-cotton fabric feel variation behind the stamp, be not received by the market.The cotton transfer printing is the dyestuff that originally was imprinted on the cotton will to be imprinted on earlier on the transfer paper, uses machinery or chemical method transfer printing again on cotton.In April, 2004, a kind of catalysis transfer printing paper with separation layer has been invented by Shanghai Difang Textile Science ﹠ Technology Co., Ltd, and granted utility model patent, number of patent application are 200420022026.8.This catalysis transfer printing paper with separation layer can be applicable on the all-cotton fabric, and not only printing quality is better, and simple to operation.At present, the transfer printing Paper that produces prints with printing process both at home and abroad, and be to acquire a certain degree of difficulty producing this catalysis transfer printing paper with separation layer, can not print with original printing process, need a kind of distinctive production technology and equipment.
Summary of the invention
Can not produce the difficult problem of catalysis transfer printing paper in order to solve traditional embossing plate printing machine with separation layer, patent of the present invention provides a kind of production technology of printing cotton transfer printing Paper with intaglio press, can produce this cotton transfer printing Paper, and simple and easy to use.
The described production technology of printing cotton transfer printing Paper with intaglio press of patent of the present invention, the technological process of production that it is characterized in that cotton transfer printing Paper is: roller is handled, pressing image processing system signal engraving drives, the video verification, body paper halftone etching primary coat technology waterproof strengthens, hot-air seasoning, halftone etching starching catalysis separation layer, double-deck hot-air seasoning, the colour printing of printing gum cover, all cotton fabric bat printing.Wherein body paper halftone etching primary coat technology waterproof strengthens, halftone etching starching catalysis separation layer, and double-deck hot-air seasoning and each operation of printing gum cover colour printing are different with traditional intaglio press production transfer printing paper technology, or do not have.
Described halftone etching primary coat technology, it is characterized in that: halftone etching primary coat mechanism is rubber rollers by a stock tank, a pair roller, on it, it is down the halftone etching steel rider, steel rider halftone etching line number is 30～180 lines/in, upward the rubber rollers top is a slim stainless steel elastic scraper, and blade thickness is that 0.3～0.7mm and two deflector rolls constitute.Printed former Paper behind two deflector rolls, between a pair roller, carry out waterproof and strengthen coating, halftone etching steel rider immerses in the stock tank under it, slurry is by the polyvinyl acetate alcohol resin in the stock tank, butadiene and styrol copolymer solution constitute, wherein polyvinyl acetate alcohol accounts for 20%～45% (weight ratio), and butadiene and styrol copolymer account for 25%～45% (weight ratio), and all the other are water and auxiliary agent.This pulp solution ph value is 6.5～8, and halftone etching primary coat starching amount is at 4～5 gram/m
2, the running speed of a motor vehicle is at 40m/min～90m/min.
Described halftone etching starching catalysis separation layer, it is characterized in that: the halftone etching starching mechanism is rubber rollers by deflector roll, a pair roller, on it, be down the halftone etching steel rider, steel rider halftone etching line number is that the other slim stainless steel elastic scraper for thickness 0.3～0.7mm of 30～180 lines/in, halftone etching steel rider constitutes.Printed former Paper behind deflector roll, between a pair roller, carry out the catalysis barrier coat, its down halftone etching steel rider immerse in stock tank, slurry is made of butadiene and styrol copolymer and the aqueous solution in the stock tank, wherein butadiene and styrol copolymer account for 0.8%～7% (weight ratio).
Described double-deck hot-air seasoning is characterized in that: double-deck air flow dryer is by the levels baking oven, and heating wire, exothermal infrared device and blower fan constitute.In the dryer air channel, carried out up and down two-sided non-contact type oven dry by the former Paper behind the catalysis barrier coat.The temperature in double-deck air flow dryer baking oven air channel is controlled at 80 ℃～120 ℃.
The colour printing of described printing gum cover, it is characterized in that: described thickener is made of sex change potato starch ethers.Printing gum earlier accounts for 6%～10% (weight ratio) and water and auxiliary agent by thickener and accounts for 94%～90% (weight ratio) formation thickener solution, accounts for 10%～30% (weight ratio) and thickener solution by dyestuff again and accounts for 90%～70% (weight ratio) and constitute printing gum solution together.Wherein the viscosity of thickener is 0.7 (mpa.s), and armful water-based 0.2cm of thickener and viscosity rate of change are within 7%.
The production technology principle of printing cotton transfer printing Paper with intaglio press is such: because of the hot transfer printing Paper of conventional gravure technology can't be printed cotton bat printing Paper, and cotton bat printing Paper technology be different from chemical ﹠ blended fabric by up to 190 ℃～shifting process of 210 ℃ of high temperature sublimation dye, it does not need temperature, only just can finish transfer printing at ambient temperature.Therefore when printing cotton bat printing Paper, must in the bat printing process, be subjected to another compound reaction and play the polymer that the catalysis dyestuff shifts at precoating layer on the former Paper earlier, and, in bat printing, make dyestuff that the separation layer of affinity interaction does not take place with Paper with another kind of high molecular polymer.In addition, cold bat printing cotton figured cloth adopts electronic engraving usually in order to embody the meticulous of photoengraving and pattern and to divide chromatic effect, calculates by standard intaglio plate ink cell form 150 lines/in, and ink cell adds up to 22500/in in the unit are
2The degree of depth only has 30 microns, and content is 1/10th～15 of conventional garden net.In order to reach the due dark concentration of stamp, traditional natural paste and synthetic thickener all can't bear the excess electrolyte and the heavy metal of high concentration dyestuff, and thickener weakens, the viscosity forfeiture, so that can't use.In order to adapt to the cold bat printing Paper of intaglio printing, developed a water-soluble thickener, pH value belongs to sex change potato starch ethers thickener between 7～7.5, solved the key technology of the cold bat printing cotton of intaglio printing stamp Paper.
Adopt the described production technology of patent of the present invention, can print cotton transfer printing Paper with intaglio press, this cotton transfer printing Paper opens the Paper that reactive dye are printed on through specially treated, passes through the cold type bat printing then to all-cotton fabric.The bat printing effect of this cotton transfer printing Paper is: no matter ganoid cotton plain cloth, coarse fabric, khaki cotton, denim or thin elastic fabric, reappear the pattern of transfer printing Paper on the precision truly, can print very fine colored type, the printing effect ratio is generally anti-, discharge printing is good; Especially the knitted fabric that suitable shrinkage is bigger and the stamp of stockinette.Because cold type bat printing stamp mode is simple, easy to operate, the percentage of A-class goods height of finished product, the equipment investment expense only is advantages such as original printing equipment 1/5, is a kind of new technology of environmental protection and energy saving.
Description of drawings
Below in conjunction with drawings and Examples patent of the present invention is described further.
Fig. 1 is the technological process of production figure that intaglio press is printed cotton transfer printing Paper.
Fig. 2 is a halftone etching primary coat schematic diagram.
Fig. 3 is halftone etching starching catalysis separation layer and double-deck hot-air seasoning schematic diagram.
Fig. 4 is a cotton transfer printing Paper schematic diagram.
Code name explanation among the figure:
1-scraper 2-goes up rubber rollers
Halftone etching steel rider 4-stock tank under the 3-
5-is printed body paper 6-deflector roll
7-upper strata baking oven 8-lower floor baking oven
Halftone etching steel rider 10-stock tank under the 9-
The last rubber rollers 12-of 11-is printed body paper
13-scraper 14-deflector roll
15-blank sheet of paper base 16-primary coat waterproof enhancement layer
17-catalysis separation layer, 18-shifts the coloured dye layer
The specific embodiment
Embodiment 1
A kind of intaglio press of printing cotton transfer printing Paper
The technological process of production of cotton transfer printing Paper as shown in Figure 1, form by many parts, to handle through roller, press image processing system signal engraving and drive the video verification, body paper halftone etching primary coat technology waterproof strengthens, hot-air seasoning, halftone etching starching catalysis separation layer, double-deck hot-air seasoning, the colour printing of printing gum cover, all cotton fabric bat printing paper.Wherein body paper halftone etching primary coat technology waterproof strengthens, halftone etching starching catalysis separation layer, double-deck hot-air seasoning and each operation of printing gum cover colour printing, be that traditional intaglio press is produced in the thermal transfer printing marble paper technology and do not had, therefore need to increase halftone etching primary coat equipment, halftone etching starching catalysis separation layer device, double-deck air flow dryer and thickener.The existing halftone etching primary coat equipment of Zeng Jiaing, halftone etching starching catalysis separation layer device, double-deck air flow dryer three device parts are as follows:
The halftone etching primary coat: halftone etching primary coat mechanism as shown in Figure 2, by a stock tank 4, a pair roller 2 and 3, on it is rubber rollers 2, it is down halftone etching steel rider 3, steel rider 3 halftone etching line numbers are 30～180 lines/in, upward rubber rollers 2 tops are a slim stainless steel elastic scraper 1, and blade thickness is that 0.3～0.7mm and deflector roll 6 constitute.Can between a pair roller, be carried out waterproof and strengthen coating through two deflector rolls by the former Paper 5 of seal.
Halftone etching starching catalysis separation layer: as shown in Figure 3, the halftone etching starching mechanism is a rubber rollers 11 by deflector roll 14, a pair roller 11 and 9, on it, be down halftone etching steel rider 9, steel rider halftone etching line number is that 30～180 lines/in, halftone etching steel rider 9 left sides are a slim stainless steel elastic scraper 13 and a stock tank 10 formations of thickness 0.3～0.7mm.Through deflector roll 6, between a pair roller, carried out the catalysis barrier coat by the former Paper of seal.
Double-deck hot-air seasoning: as shown in Figure 3, double-deck air flow dryer is by levels baking oven 7 and 8, and heating wire, exothermal infrared device and blower fan parts constitute.Carried out two-sided oven dry in the former Paper drying machine air channel behind the catalysis barrier coat.
Print coarse fabric, as the cotton transfer printing Paper of khaki cotton and denim.
The technological process of production and equipment are seen shown in Fig. 1 and the embodiment 1: roller is handled, pressing image processing system signal engraving drives, the video verification, body paper halftone etching primary coat technology waterproof strengthens, hot-air seasoning, halftone etching starching catalysis separation layer, double-deck hot-air seasoning, the colour printing of printing gum cover, all cotton fabric bat printing.
Processing parameter:
Halftone etching primary coat technology, several 50 lines of steel rider halftone etching line/in, slim stainless steel elastic scraper is 0.7mm; Slurry is by the polyvinyl acetate alcohol resin, and butadiene and styrol copolymer solution constitute, and wherein polyvinyl acetate alcohol accounts for 40% (weight ratio), and butadiene and styrol copolymer account for 35% (weight ratio), and all the other are water and auxiliary agent.Its ph value is 7, and halftone etching primary coat starching amount is at 5 gram/m
2, the running speed of a motor vehicle is at 45m/min.
Halftone etching starching catalysis spacer processes, steel rider halftone etching line number is 50 lines/in; Slim stainless steel elastic scraper is 0.7mm; Slurry is made of butadiene and styrol copolymer and the aqueous solution, and wherein butadiene and styrol copolymer account for 6% (weight ratio).
Double-deck hot-air seasoning technology, the temperature in double-deck air flow dryer baking oven air channel is controlled at 100 ℃.
Printing gum technology, thickener is made of sex change potato starch ethers.Printing gum accounts for 9% (weight ratio) and water and auxiliary agent by thickener earlier and accounts for 91% formation thickener solution, accounting for 30% (weight ratio) and thickener solution by dyestuff again accounts for 70% and constitutes printing gum solution, wherein the viscosity of thickener is 0.7 (mpa.s), and armful water-based 0.2cm of thickener and viscosity rate of change are within 7%.Wherein scraper is with 0.7mm slim stainless steel elastic scraper.
All cotton fabric bat printing technology, cotton transfer printing Paper is as shown in Figure 4: by shifting coloured dye layer 18, catalysis separation layer 17, primary coat technology waterproof enhancement layer 16 and paper substrate 15 constitute, and can use the pressure roller transfer printing down on cotton khaki cotton and denim at normal temperature (0 ℃～40 ℃).
Print the tabby cotton transfer printing of ganoid cotton Paper.
The technological process of production and equipment are seen shown in Fig. 1 and the embodiment 1: roller is handled, pressing image processing system signal engraving drives, the video verification, body paper halftone etching primary coat technology waterproof strengthens, hot-air seasoning, halftone etching starching catalysis separation layer, double-deck hot-air seasoning, the colour printing of printing gum cover, all cotton fabric bat printing.，
Processing parameter:
Halftone etching primary coat technology, steel rider halftone etching line number is 100 lines/in; Slim stainless steel elastic scraper is 0.6mm; Slurry is by the polyvinyl acetate alcohol resin, butadiene and and styrol copolymer solution constitute, wherein polyvinyl acetate alcohol accounts for 30% (weight ratio), butadiene and styrol copolymer account for 30%, all the other are water and auxiliary agent.This solution ph is 7.5, and halftone etching primary coat starching amount is at 4.5 gram/m
2, the running speed of a motor vehicle is at 70m/min.
Halftone etching starching catalysis spacer processes, steel rider halftone etching order number is 100 lines/in; Slim stainless steel elastic scraper is 0.6mm; Slurry is made of butadiene and styrol copolymer and the aqueous solution, and wherein butadiene and styrol copolymer account for 5% (weight ratio).
Double-deck hot-air seasoning technology, the temperature in double-deck air flow dryer baking oven air channel is controlled at 95 ℃.
Printing gum technology, thickener is made of sex change potato starch ethers.Printing gum accounts for 8% (weight ratio) and water and auxiliary agent by thickener earlier and accounts for 92% formation thickener solution, accounting for 25% (weight ratio) and thickener solution by dyestuff again accounts for 75% and constitutes printing gum solution, wherein the viscosity of thickener is 0.7 (mpa.s), and armful water-based 0.2cm of thickener and viscosity rate of change are within 7%.Wherein scraper is with 0.6mm slim stainless steel elastic scraper.
All cotton fabric bat printing technology, cotton transfer printing Paper as shown in Figure 4: by shifting the coloured dye layer, the catalysis separation layer, primary coat technology waterproof enhancement layer and paper substrate constitute, can be at normal temperature (0 °～35 °) down with the pressure roller transfer printing to cotton plain cloth cloth.
Print bigger knitted fabric and the stockinette of shrinkage.
The technological process of production and equipment are seen shown in Fig. 1 and the embodiment 1: roller is handled, pressing image processing system signal engraving drives, the video verification, body paper halftone etching primary coat technology waterproof strengthens, hot-air seasoning, halftone etching starching catalysis separation layer, double-deck hot-air seasoning, the colour printing of printing gum cover, all cotton fabric bat printing.，
Processing parameter:
Halftone etching primary coat technology, steel rider halftone etching line number is 150 lines/in; Slim stainless steel elastic scraper is 0.5mm; Slurry is by the polyvinyl acetate alcohol resin, butadiene and and styrol copolymer solution constitute, wherein polyvinyl acetate alcohol accounts for 20% (weight ratio), butadiene and styrol copolymer account for 25%, all the other are water and auxiliary agent.This solution ph is 6.8, and halftone etching primary coat starching amount is at 4 gram/m
2, the running speed of a motor vehicle is at 80m/min
Halftone etching starching catalysis spacer processes is because of this knitted fabric is a kind of light and thin type lining, so this operation can be merged into halftone etching primary coat technique process.
Double-deck hot-air seasoning technology, the temperature in double-deck air flow dryer baking oven air channel is controlled at 90 ℃.
Printing gum technology, thickener is made of sex change potato starch ethers.Printing gum earlier by thickener account for 6%～(weight ratio) and the water conservancy project preface account for 94% formation thickener solution, accounting for 15% (weight ratio) and thickener solution by dyestuff again accounts for 85% and constitutes printing gum solution, wherein the viscosity of thickener is 0.7 (mpa.s), and armful water-based 0.2cm of thickener and viscosity rate of change are within 7%.Wherein scraper is with 0.5mm slim stainless steel elastic scraper.
All cotton fabric bat printing technology, cotton transfer printing Paper is as shown in Figure 4: by shifting the coloured dye layer, the catalysis separation layer, primary coat technology waterproof enhancement layer and paper substrate constitute, and can use the pressure roller transfer printing down on complete cotton knitted fabric and stockinette cloth at normal temperature (0 °～35 °).
Claims (8)
1. print the production technology of cotton transfer printing Paper with intaglio press, the technological process of production that it is characterized in that cotton transfer printing Paper is: roller is handled, pressing image processing system signal engraving drives, the video verification, body paper halftone etching primary coat technology waterproof strengthens, hot-air seasoning, halftone etching starching catalysis separation layer, double-deck hot-air seasoning, the colour printing of printing gum cover, all cotton fabric bat printing.Wherein body paper halftone etching primary coat technology waterproof strengthens, halftone etching starching catalysis separation layer, and double-deck hot-air seasoning and each operation of printing gum cover colour printing are that to produce transfer printing paper technology different or do not have with traditional intaglio press.
2. the production technology of printing cotton transfer printing Paper with intaglio press according to claim 1, it is characterized in that: described body paper halftone etching primary coat technology waterproof strengthens mechanism by a stock tank, a pair roller, upward be rubber rollers, it is down the halftone etching steel rider, and in the immersion stock tank, steel rider halftone etching line number is 30～180 lines/in, upward the rubber rollers top is a slim stainless steel elastic scraper, and blade thickness is that 0.3～0.7mm and two deflector rolls constitute., behind two deflector rolls, between a pair roller, carried out waterproof and strengthen coating by the former Paper of seal.
3. the production technology of printing cotton transfer printing Paper with intaglio press according to claim 1 and 2, it is characterized in that: in the described body paper halftone etching primary coat technology, slurry in the stock tank is by the polyvinyl acetate alcohol resin, and butadiene and styrol copolymer solution constitute.Wherein polyvinyl acetate alcohol accounts for 20%～45% (weight ratio), and butadiene and styrol copolymer account for 25%～45% (weight ratio), and all the other are water and auxiliary agent.This pulp solution ph value is 6.5～8, and halftone etching primary coat starching amount is at 4～5 gram/m
2, the running speed of a motor vehicle is at 40m/min～90m/min.
4. the production technology of printing cotton transfer printing Paper with intaglio press according to claim 1, it is characterized in that: described halftone etching starching catalysis separation layer mechanism is by deflector roll, a pair roller, upward be rubber rollers, it is down the halftone etching steel rider, and in the immersion stock tank, steel rider halftone etching line number is that the other slim stainless steel elastic scraper for thickness 0.3～0.7mm of 30～180 lines/in, halftone etching steel rider constitutes.Behind deflector roll, between a pair roller, carried out the catalysis barrier coat by the former Paper of seal.
5. according to claim 1 or the 4 described production technologies of printing cotton transfer printing Paper with intaglio press, it is characterized in that: in the described halftone etching starching catalysis spacer processes, slurry in the stock tank is made of butadiene and styrol copolymer and water and compounding agent solution, and wherein butadiene and styrol copolymer account for 0.8%～7% (weight ratio).
6. according to claim 1ly print the production technology of cotton transfer printing Paper with intaglio press, it is characterized in that: described double-deck hot-air seasoning mechanism is by the levels baking oven, and heating wire, exothermal infrared device and blower fan constitute.In the dryer air channel, carried out up and down two-sided non-contact type oven dry by the former Paper behind the catalysis barrier coat.The temperature in double-deck air flow dryer baking oven air channel is controlled at 80 ℃～120 ℃.
7. the production technology of printing cotton transfer printing Paper with intaglio press according to claim 1, it is characterized in that: the colour printing of described printing gum cover, its thickener is made of sex change potato starch ethers, printing gum earlier accounts for 6%～10% (weight ratio) and water and auxiliary agent by thickener and accounts for 94%～90% (weight ratio) formation thickener solution, accounts for 10%～30% (weight ratio) and thickener solution by dyestuff again and accounts for 90%～70% (weight ratio) and constitute printing gum solution together.Wherein the viscosity of thickener is 0.7 (mpa.s), and armful water-based 0.2cm of thickener and viscosity rate of change are within 7%.
8. the production technology of printing cotton transfer printing Paper with intaglio press according to claim 1, it is characterized in that: the cotton transfer printing Paper that is produced is by shifting the coloured dye layer, the catalysis separation layer, primary coat technology waterproof enhancement layer and paper substrate constitute, and can use the pressure roller transfer printing down to all cotton fabric at normal temperature (0 ℃～40 ℃).