CN1799692A - 具有可见光诱导高催化活性掺锡纳米二氧化钛光触媒的制备方法 - Google Patents
具有可见光诱导高催化活性掺锡纳米二氧化钛光触媒的制备方法 Download PDFInfo
- Publication number
- CN1799692A CN1799692A CN 200610011238 CN200610011238A CN1799692A CN 1799692 A CN1799692 A CN 1799692A CN 200610011238 CN200610011238 CN 200610011238 CN 200610011238 A CN200610011238 A CN 200610011238A CN 1799692 A CN1799692 A CN 1799692A
- Authority
- CN
- China
- Prior art keywords
- film
- photo
- tio
- catalyst
- doping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种具有可见光诱导高催化活性掺锡纳米二氧化钛光触媒的制备方法,属于光触媒材料技术领域。工艺步骤为:首先制备掺锡TiO2溶胶,然后,制备掺锡TiO2薄膜。本发明的优点在于:所制备的掺杂Sn4+的纳米TiO2薄膜具有锐钛矿和金红石相的混晶结构,平均晶粒尺寸为25~30nm,经分析确定金红石相是Sn4+固溶到TiO2晶格中形成的(Ti,Sn)O2固溶体;透明薄膜表面平整,有粗糙度;掺杂Sn4+使得TiO2光触媒薄膜对入射光的吸收带边红移至可见光区,产生可见光诱导光催化效应;光催化活性以甲基橙的光催化降解率来表示,适量掺杂Sn4+能够显著提高TiO2薄膜的光催化活性,相较纯纳米TiO2薄膜,对甲基橙的光催化降解率提高了34%以上。
Description
技术领域
本发明属于光触媒材料技术领域,特别是提供了一种具有可见光诱导高催化活性掺锡纳米二氧化钛光触媒的制备方法。
背景技术
纳米级二氧化钛属于环保领域的无机新材料,也是最具有开发前途的绿色环保型光触媒材料。通过光催化氧化还原效应降解有害污染物,且无二次污染,具有废水处理、空气净化、杀灭病毒和癌细胞、抗菌、除臭、自清洁等功能。
制约TiO2光触媒实际应用的瓶颈:一是激发波长的限制,由于TiO2的禁带宽度为3.2eV,对应的激发波长在387nm,属于紫外光区,而紫外光在大阳能中占不足5%,最经济实用的光触媒材料应该能利用太阳光中丰富的可见光部分,来替代昂贵的人工紫外光源;二是TiO2半导体光生电子与光生空穴的快速复合几率高,以及产生的光生载流的界面转移率低,限制了TiO2光触媒的光催化活性。解决上述问题的关键技术就是对TiO2光触媒进行改性,其中最引人注目的改性方法之一就是过渡金属离子的掺杂。过渡金属离子的掺入可在TiO2晶格中引入缺陷位置或改变TiO2结晶度等,可充当光生电子或光生空穴的捕获者,有效的阻止电荷在转移过程中的复合,提高量子产率,从而影响TiO2光触媒的催化活性;或在TiO2能带中引入新能级,减小带隙,诱导电子跃迁,使得光响应波长扩展到可见光区。
悬浮相TiO2微粒在水溶液中易于凝聚,难以回收,活性成分损失大,也严重限制了光催化技术的实用化。因而纳米TiO2光触媒薄膜作为具有反应与分离双功能的新材料成为催化新材料的热点,又由于其具有纳米效应和高活性,而具有理论研究和实际应用价值。
发明内容
本发明的目的在于提供一种具有可见光诱导高催化活性掺锡纳米二氧化钛光触媒的制备方法,利用掺入的锡离子促进TiO2晶型转变,抑制TiO2晶粒长大,提高光量子产率,扩展光响应范围,从而明显改善纳米晶TiO2光触媒的催化活性。
本发明的工艺步骤为:
a.掺锡TiO2溶胶的制备
将体积百分含量为15%~20%钛酸四丁酯、22%~24%无水乙醇和10%~12%乙酰丙酮配制成均匀溶液A,根据摩尔百分比MSn∶MTi=0.57%~17.11%分别计算称量五水四氯化锡,将所需掺量的SnCl4·5H2O溶解于43%~49%无水乙醇和2%~3%蒸馏水配制的溶液B中,滴加浓硝酸调节溶液B的pH为3.15~4.20,再将溶液B缓慢滴加到溶液A中进行水解反应,控制反应温度为30~40℃。将形成的Sn4+离子掺杂的TiO2溶胶在10~35℃密封陈化4~10天;
b.掺锡TiO2薄膜的制备
在镀膜前预处理玻璃基体:玻璃基体在箱式电阻炉中500~550℃下热处理120~130min后用酸洗液浸泡,然后用蒸馏水和无水乙醇超声清洗,最后放入烘箱中烘干备用;将洁净的玻璃基体以2~4cm/min的速度浸入到制备的溶胶液中静置2~5min,待液面稳定后以同样的提拉速度垂直向上提拉,湿膜在室温下放置5~15min,再在真空干燥箱中60~100℃下干燥10~20min而成为凝胶膜,取出在10~35℃冷却5~10min后继续镀制下一层膜;重复上述镀膜过程循环制备1~10层薄膜,镀完最后一层膜后,放入60~80℃的真空干燥箱中干燥;然后在箱式电阻炉中以1~2℃/min的速率升温到500~550℃保温热处理120~180min,在炉内自然冷却至室温,得到不同掺锡量的Sn4+离子掺杂的TiO2光触媒薄膜。
掺锡纳米TiO2光触媒薄膜光催化活性测试方法:
选择染料甲基橙作为降解对象,偶氮结构的甲基橙是一种较难降解的有机化合物,以成品甲基橙染料配制的模拟废水作为评价纳米TiO2薄膜光催化活性的反应模型具有一定的代表性。使用200ml锥形瓶作为简易反应器,以125W荧光高压汞灯为激发光源,以玻璃管负载的纯TiO2薄膜或Sn4+离子掺杂的TiO2薄膜作为光催化剂。光催化活性测试试验过程为:在200ml锥形瓶中放入玻璃管负载的TiO2光触媒薄膜和100ml不同浓度、不同pH的甲基橙水溶液,一个125W自镇流荧光高压汞灯距离锥形瓶反应器5~10cm。先用空气泵向甲基橙溶液中通入空气,数分钟后开启光源照射不同时间。用紫外-可见分光光度计测定甲基橙溶液在最大吸收波长处的吸光度,根据甲基橙溶液的吸光度变化来计算甲基橙的光催化降解率。计算公式为
式中A0为甲基橙染料溶液的初始吸光度,A为甲基橙染料溶液光催化氧化降解反应后的吸光度。
利用X射线衍射、原子力显微镜、紫外-可见分光光度计研究了TiO2光触媒薄膜的表面形貌、相结构及其光催化活性。本发明的优点在于:制备的掺杂Sn4+的纳米TiO2薄膜具有锐钛矿和金红石相的混晶结构,平均晶粒尺寸为25~30nm,经分析确定金红石相是Sn4+固溶到TiO2晶格中形成的(Ti,Sn)O2固溶体;透明薄膜表面平整,有粗糙度;掺杂Sn4+使得TiO2光触媒薄膜对入射光的吸收带边红移至可见光区,产生可见光诱导光催化效应;光催化活性以甲基橙的光催化降解率来表示,适量掺杂Sn4+能够显著提高TiO2薄膜的光催化活性,相较纯纳米TiO2薄膜,对甲基橙的光催化降解率提高了34%以上。
附图说明
图1为500℃热处理的11.41%Sn4+掺杂的TiO2粉体的XRD图谱。该图说明经过500℃热处理2h获得的Sn4+掺杂的TiO2粉体具有锐钛矿型和金红石型的混合晶型,且TiO2晶粒尺寸明显变小。金红石晶相是Sn4+固溶到TiO2晶格中形成的(Ti,Sn)O2固溶体。
图2为在玻璃基体上镀制的11.41%Sn4+掺杂的TiO2薄膜的AFM照片。该图说明镀制的掺杂Sn4+的TiO2薄膜均匀平整,薄膜表面比较光滑,平均晶粒尺寸在27nm左右,有孔隙。
图3为掺杂不同浓度Sn4+的TiO2薄膜光催化剂的可见光吸收曲线图谱。该图说明掺杂Sn4+使得TiO2薄膜的光吸收边红移,光响应范围扩展到可见光区。掺杂11.41%Sn4+的TiO2薄膜在整个可见光波长范围400nm~800nm内都有较强的光吸收。
图4为光催化实验测得的甲基橙降解率与Sn4+的掺杂浓度关系曲线图。该图说明掺杂Sn4+使得TiO2薄膜对甲基橙的光催化降解作用显著增强,明显改善了TiO2薄膜的光催化活性。
具体实施方式
实施例1
先滴加17ml钛酸四丁酯到23ml无水乙醇中,持续磁力搅拌,后缓慢滴加11ml乙酰丙酮作为络合剂,充分反应后得到均匀溶液a;将2.00gSnCl4·5H2O溶于47ml无水乙醇中,再滴加2ml蒸馏水和0.4ml硝酸,磁力搅拌得到均匀溶液b。控制反应温度为30℃,缓慢滴加溶液b到溶液a中进行水解反应。最后将形成的Sn4+离子掺杂的TiO2溶胶在室温密封陈化。
将预处理过的洁净的玻璃管(1cm×2.5cm)以4cm/min的速度浸入到制备的溶胶液中静置2min,待液面稳定后以同样的提拉速度垂直向上提拉,湿膜在室温下放置5min,再在真空干燥箱中60℃下干燥至少10min而成为凝胶膜,取出在室温冷却5min后继续镀制下一层膜。重复上述镀膜过程循环制备5层薄膜,镀完最后一层膜后,放入80℃的真空干燥箱中干燥。然后在箱式电阻炉中以2℃/min的速率升温到500℃保温热处理120min,在炉内自然冷却至室温,即可得到11.41%Sn4+掺杂的TiO2光触媒薄膜。
光催化活性测试试验:在200ml锥形瓶中放入玻璃管负载的Sn4+离子掺杂TiO2光触媒薄膜和100ml浓度为0.76×10-5mol/L、pH=3.15的甲基橙水溶液,以一个125W自镇流荧光高压汞灯为光源,灯距离锥形瓶反应器5cm。先用空气泵向甲基橙溶液通入空气,数分钟后开启光源照射30min。本实施例中的11.41%Sn4+共掺杂TiO2光触媒薄膜对甲基橙溶液的光催化降解率为78.76%。
实施例2
本实施例的工艺步骤与实施例1基本相同,所不同的是SnCl4·5H2O的掺杂量为1.30g。光催化活性测试试验表明本实施例的7.42%Sn4+掺杂的TiO2光触媒薄膜对甲基橙溶液的光催化降解率为74.63%。
实施例3
本实施例的工艺步骤与实施例1基本相同,所不同的是SnCl4·5H2O的掺杂量为0.70g。光催化活性测试试验表明本实施例的3.99%Sn4+掺杂的TiO2光触媒薄膜对甲基橙溶液的光催化降解率为67.72%。
Claims (1)
1.一种具有可见光诱导高催化活性掺锡纳米二氧化钛光触媒的制备方法,其特征在于:工艺步骤为:
a.掺锡TiO2溶胶的制备
将体积百分含量为15%~20%钛酸四丁酯、22%~24%无水乙醇和10%~12%乙酰丙酮配制成均匀溶液A,根据摩尔百分比MSn∶MTi=0.57%~17.11%分别计算称量五水四氯化锡,将所需掺量的SnCl4·5H2O溶解于43%~49%无水乙醇和2%~3%蒸馏水配制的溶液B中,滴加浓硝酸调节溶液B的pH为3.15~4.20,再将溶液B缓慢滴加到溶液A中进行水解反应,控制反应温度为30~40℃;将形成的Sn4+离子掺杂的TiO2溶胶在10~35℃密封陈化4~10天;
b.掺锡TiO2薄膜的制备
在镀膜前预处理玻璃基体:玻璃基体在箱式电阻炉中500~550℃下热处理120~130min后用酸洗液浸泡,然后用蒸馏水和无水乙醇超声清洗,最后放入烘箱中烘干备用;将洁净的玻璃基体以2~4cm/min的速度浸入到制备的溶胶液中静置2~5min,待液面稳定后以同样的提拉速度垂直向上提拉,湿膜在室温下放置5~15min,再在真空干燥箱中60~100℃下干燥10~20min而成为凝胶膜,取出在10~35℃冷却5~10min后继续镀制下一层膜;重复上述镀膜过程循环制备1~10层薄膜,镀完最后一层膜后,放入60~80℃的真空干燥箱中干燥;然后在箱式电阻炉中以1~2℃/min的速率升温到500~550℃保温热处理120~180min,在炉内自然冷却至室温,得到不同掺锡量的Sn4+离子掺杂TiO2光触媒薄膜。