CN1782115A - 马氏体系不锈钢管及其制造方法 - Google Patents
马氏体系不锈钢管及其制造方法 Download PDFInfo
- Publication number
- CN1782115A CN1782115A CNA2005101271995A CN200510127199A CN1782115A CN 1782115 A CN1782115 A CN 1782115A CN A2005101271995 A CNA2005101271995 A CN A2005101271995A CN 200510127199 A CN200510127199 A CN 200510127199A CN 1782115 A CN1782115 A CN 1782115A
- Authority
- CN
- China
- Prior art keywords
- temperature
- stainless steel
- cooling
- steel pipe
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
钢 | 化学组成(质量%) 剩余部分:Fe和杂质 | ||||||||||||||||
C | Si | Mn | P | S | Cr | Ni | Al | N | Cu | Ti | V | Mo | Nb | B | Ca | Fn的值 | |
1234567891011121314151617 | 0.200.190180.190.170.180.200.190.220.210.190.200.210.190.190.200.18 | 0.240.240.220.210.240.250.220.210.240.220.210.240.240.230.230.260.24 | *1.110.880.840.860.920.900.880.890.830.860.880.840.670.630.550.500.42 | 0.0140.0140.0120.0140.0160.0170.0140.0160.0150.0120.0160.0180.0110.0150.0130.0150.018 | 0.0010.0030.0020.0020.0010.0010.0020.0010.0010.0020.0010.0030.0010.0010.0010.0020.003 | 12.612.612.312.612.612.712.412.612.512.712.412.912.212.512.312.412.6 | 0.070.070.060.090.110.080.070.090.120.070.140.110.090.060.080.070.09 | 0.002*0.012*0.007*0.0040.0010.0020.0020.0020.0010.0030.0010.0020.0010.0010.0010.0020.001 | 0.0340.0340.0370.0340.0390.0370.0340.0310.0290.0240.0180.0120.0320.0280.0230.0170.013 | 0.020.020.010.010.030.020.030.020.030.020.010.020.030.010.030.020.02 | 0.010.010.020.010.030.020.030.010.020.010.010.030.020.010.020.010.01 | 0.040.030.050.040.040.070.050.090.080.110.140.180.060.050.050.080.12 | -----0.01-0.01-0.01------- | -0.001--0.0010.0010.0020.0010.0010.0010.0020.0010.0020.0040.0030.0050.008 | 0.00030.00010.00020.00030.00020.00030.00020.00020.00010.00020.00020.00010.00010.00010.00010.00010.0001 | 0.00030.00030.00040.00040.00050.00040.00030.00050.00030.00020.00040.00070.00030.00060.00030.00030.0003 | 0050520.51530.52540.560752025204580 |
fn=50Mo+500(V-0.04)+5000Nb*表示在(1)的发明的化学成分之外 |
试验编号 | 钢 | 加热条件 | 冷却条件 | 回火温度(℃) | 矫直机的出口温度(℃) | |||||
温度T1(℃) | 时间(分) | 温度T2(℃) | 从温度T1到温度T2的冷却速度(℃/秒) | 温度T3(℃) | 从温度T2到温度T3的冷却速度(℃/秒) | 从低于温度T3的温度区域冷却到常温的冷却速度(℃/秒) | ||||
12345678910111213141516171819202122232425262728293031323334 | *1*2*3*4567891011121314151617*1*2*3*4567891011121314151617 | 960970980960970960970960970970960950970970960980960960970980960970960970960970970960950970970960980960 | 109109111011912101111129101011109109111011912101111129101011 | 512553496505491488572561506511529483502515487535522512553496505491488572561506511529483502515487535522 | 16~2126~3219~289~1614~1922~2913~1929~356~1119~2615~195~1211~1718~2211~1822~3318~2516~2126~3219~289~1614~1922~2913~1929~356~1119~2615~195~1211~1718~2211~1822~3318~25 | 282213220297196265184168197228276219240188166287233282213220297196265184168197228276219240188166287233 | 0.60.50.70.60.40.60.70.50.40.40.30.30.70.40.50.30.50.60.50.70.60.40.60.70.50.40.40.30.30.70.40.50.30.5 | 128119131920157132522311681418128119131920157132522311681418 | 660660665660660685665695680705710730655685675705740615615620615615640620650635660665685625640635660695 | 540552554548560574555578568592596614544576564590623502505512501508524508543521543550567512534523549581 |
*表示在(1)的发明的化学成分之外的钢。 |
试验编号 | 钢 | 抗拉特性 | 冲击特性 | ||
屈服强度[YS](MPa) | 抗拉强度[TS](MPa) | 屈服比[YS/TS](MPa) | 0℃的摆锤冲击值[V型槽口试验片](J/cm2) | ||
12345678910111213141516171819202122232425262728293031323334 | *1*2*3*4567891011121314151617*1*2*3*4567891011121314151617 | 691692698689702701693708699702708712693703697694707789798803793802811796786793797808812806803811794787 | 887885883892878878864874876871862857889902883867875976984980976966981958944957962976972997991994965954 | 78787977808080818081828378787980818181828183838383838383848181828282 | 373243647482908990738493102981041151232419233539424845484344475863728287 |
*表示在(1)的发明的化学成分之外的钢。 |
Claims (4)