CN1775856A - Method for preparing composite biodegradable master batch - Google Patents
Method for preparing composite biodegradable master batch Download PDFInfo
- Publication number
- CN1775856A CN1775856A CNA2005101112429A CN200510111242A CN1775856A CN 1775856 A CN1775856 A CN 1775856A CN A2005101112429 A CNA2005101112429 A CN A2005101112429A CN 200510111242 A CN200510111242 A CN 200510111242A CN 1775856 A CN1775856 A CN 1775856A
- Authority
- CN
- China
- Prior art keywords
- master batch
- biodegradable master
- composite biodegradable
- kilograms
- premix
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a method to make compounding biodegradation master batchg. It is made up of poly-caprolactone, poly-lactic acid and polyethylene glycol after taking the process of whisking twin-screw extruding. It is a degrading material that has no pollution to the environment and could be used in medical, agriculture and consumer goods package fields.
Description
Technical field
The present invention relates to the preparation method of composite biodegradable master batch.
Background technology
Along with rapid development of economy, non-returnable container goods, medical treatment product, industrial or agricultural film etc., the widespread use in industrial or agricultural, daily life causes white pollution to become the social effects of pollution of human survival and development.Particularly mass production and use nondegradable material not only causes the huge waste of resource, and serious pollution of ecological environment.Light, biodegradable material that prior art is produced, mostly be with polypropylene, polyethylene add starch or lime carbonate or talcum powder, olefin lubricant makes, but this technology belongs to disintegration-type, is not complete biodegradable.
Summary of the invention
The purpose of this invention is to provide a kind of pollution-free, the preparation method of composite biodegradable master batch completely degrades.
The object of the present invention is achieved like this: composite biodegradable master batch is characterized in that comprising following each component (in weight part): 10～45 parts of polycaprolactones, 10～45 parts of poly(lactic acid), 5～40 parts of weighting agents, 1～6 part of lubricant, 1～6 part of polyoxyethylene glycol.Described weighting agent is one or both in diatomite or the wilkinite.Described lubricant is a kind of in stearic acid or the stearates or several.
Its preparation method is the material of said ratio to be added stir in the mixing roll, during whipping temp to 100 ℃-120 ℃, becomes premix, and premix is added tie rod pelletizing packing in the parallel dual-screw extruding granulator, makes composite biodegradable master batch.
The technical progress that the present invention obtains is: the microbiological deterioration material is a poly(lactic acid) in the component of the present invention, is to be polymerized by corn fermentation.The biodegradable material of synthetic is a polycaprolactone in the component of the present invention, and is the unique material that can be degraded by water.The more important thing is biodegradable master batch, can be degraded into carbonic acid gas and water, concerning animals and plants, also do not constitute harm.Preferred diatomite and wilkinite belong to nontoxic, innoxious substance in the component of the present invention, and diatomite and wilkinite do not constitute soil, waters, animals and plants harm after the biodegradable master batch degraded yet.Polyoxyethylene glycol, stearic acid and stearates are lubricant and dispersion agent, are again the biological degradation auxiliary agents.The organic compound blend of material can make mixture performance function to greatest extent, changes original component character, well can regulate and control material character on request, can effectively improve Mechanical Properties of Materials by compound blend.The more important thing is biodegradable master batch after compound can be in soil, water pool or under the anaerobic condition complete biodegradable, can also recycle simultaneously, can not cause environmental pollution.The present invention adopts the mixing reaction of parallel dual-screw to extrude tie rod pelletizing packaging disposable and finishes.
Embodiment:
Embodiment one:
(1) gets 35 kilograms of poly(lactic acid), 25 kilograms of polycaprolactones, 2 kilograms of polyoxyethylene glycol, 3 kilograms of stearic acid, 35 kilograms in diatomite
(2) material of said ratio is added stir in the mixing roll, during whipping temp to 100 ℃-120 ℃, become premix, premix is added tie rod pelletizing packing in the parallel dual-screw extruding granulator, make composite biodegradable master batch.
Embodiment two:
(1) gets 40 kilograms of poly(lactic acid), 45 kilograms of polycaprolactones, 3 kilograms of polyoxyethylene glycol, 2 kilograms of Zinic stearass, 10 kilograms in diatomite
(2) material of said ratio is added stir in the mixing roll, during whipping temp to 100 ℃-120 ℃, become premix, premix is added tie rod pelletizing packing in the parallel dual-screw extruding granulator, make composite biodegradable master batch.
Embodiment three:
(1) gets 30 kilograms of poly(lactic acid), 40 kilograms of polycaprolactones, 5 kilograms of polyoxyethylene glycol, 5 kilograms of stearic acid, 20 kilograms of wilkinites
(2) material of said ratio is added stir in the mixing roll, during whipping temp to 100 ℃-120 ℃, become premix, premix is added tie rod pelletizing packing in the parallel dual-screw extruding granulator, make composite biodegradable master batch.
Embodiment four:
(1) gets 30 kilograms of poly(lactic acid), 30 kilograms of polycaprolactones, 5 kilograms of polyoxyethylene glycol, 5 kilograms of calcium stearates, 30 kilograms of wilkinites
(2) material of said ratio is added stir in the mixing roll, during whipping temp to 100 ℃-120 ℃, become premix, premix is added tie rod pelletizing packing in the parallel dual-screw extruding granulator, make composite biodegradable master batch.
Claims (4)
1, composite biodegradable master batch is characterized in that comprising following each component (in weight part):
10～45 parts of polycaprolactones,
10～45 parts of poly(lactic acid),
5～40 parts of weighting agents,
1～6 part of lubricant,
1～6 part of polyoxyethylene glycol.
2, composite biodegradable master batch according to claim 1 is characterized in that: weighting agent is one or both in diatomite or the wilkinite.
3, composite biodegradable master batch according to claim 1 is characterized in that: lubricant is a kind of in stearic acid or the stearates or several.
4, by any preparation method of composite biodegradable master batch in the claim 1～3; it is characterized in that: the material of said ratio is added in the stirring mixing roll; during whipping temp to 100 ℃-120 ℃; become premix; premix is added tie rod pelletizing packing in the parallel dual-screw extruding granulator, make composite biodegradable master batch.