CN1730224A - Ti－Al金属间化合物合金过渡液相扩散焊复合连接方法 - Google Patents

Ti－Al金属间化合物合金过渡液相扩散焊复合连接方法 Download PDF

Info

Publication number
CN1730224A
CN1730224A CN 200510098587 CN200510098587A CN1730224A CN 1730224 A CN1730224 A CN 1730224A CN 200510098587 CN200510098587 CN 200510098587 CN 200510098587 A CN200510098587 A CN 200510098587A CN 1730224 A CN1730224 A CN 1730224A
Authority
CN
China
Prior art keywords
alloy
joint
liquid phase
clean
insulation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200510098587
Other languages
English (en)
Inventor
宁立芹
梁德彬
李海刚
毛建英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NO 703 INSTITUTE OF CHINA ACADEMY OF LAUNCH VEHICLE TECHNOLOGY
Original Assignee
NO 703 INSTITUTE OF CHINA ACADEMY OF LAUNCH VEHICLE TECHNOLOGY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NO 703 INSTITUTE OF CHINA ACADEMY OF LAUNCH VEHICLE TECHNOLOGY filed Critical NO 703 INSTITUTE OF CHINA ACADEMY OF LAUNCH VEHICLE TECHNOLOGY
Priority to CN 200510098587 priority Critical patent/CN1730224A/zh
Priority to CNB2005101171183A priority patent/CN100434225C/zh
Publication of CN1730224A publication Critical patent/CN1730224A/zh
Pending legal-status Critical Current

Abstract

一种Ti－Al金属间化合物合金过渡液相扩散焊复合连接方法，利用该方法焊接Ti3Al合金，接头室温及高温强度均可达到母材强度的80％以上，室温下可获得与母材同等塑性，接头组织均匀与母材接近。

Description

Ti-Al金属间化合物合金过渡液相扩散焊复合连接方法
技术领域
本发明涉及一种材料的连接方法，具体地说是Ti-Al金属间化合物合金过渡液相扩散焊复合连接方法。
背景技术
Ti3Al金属间化合物是一种新型金属基高温合金，与普通钛合金相比，其密度(3.8～4.2g/cm3)相当，而使用温度更高。普通钛合金的工作温度迄今仍限于600℃以下，Ti3Al金属间化合物工作温度在600～750℃，甚至更高，而且还具有高温比强度、比模量高、抗高温氧化及高温蠕变等优点，与镍基高温合金相比可减重40％左右。因此，近几年来得到了快速发展，并已进入工程化应用，广泛地用于制造航空航天飞行器中承受较高温度的结构件。
作为耐高温的轻质结构材料，Ti3Al基合金在应用过程中也会遇到与其同种或其它材料(如高强度结构钢、钛合金、镍基合金等)的连接，以获得实际使用中所需要的各种形状结构件，尤其是航空、航天、汽车、能源等领域，因其对Ti3Al基合金结构件的需要和特殊要求，更是需要新型复合连接技术，以获得高性能连接接头满足设计要求。
国外开展Ti3Al基合金连接研究的工作相对较早且较深入，所采用的连接方法主要有：
(1)熔化焊-主要包括电子束焊、激光焊、氩弧焊、闪光对焊和电容放电加热熔化电阻焊等；
(2)固态连接-包括摩擦焊、直接对接固态扩散连接、超塑成型与扩散连接(SPF/DB)组合工艺及电容放电加热固态扩散连接等。
根据已有的国内外文献可知，Ti3Al基合金不存在本质上不可连接的问题，其连接技术的关键是：(1)找到某种方法及其相应的工艺，使连接件室温下仍能保持一定的塑性，特别是对于结构复杂和尺寸大的构件确保连接后不出现裂纹，同时保证结构尺寸的稳定性；(2)接头室温强度，特别是高温抗拉强度和高温抗蠕变强度接近母材的强度。
熔化焊存在的主要问题是：焊缝和热影响区(特别是熔合线附近区域)容易出现脆性组织甚至出现裂纹，同时，非真空熔焊工艺都不可避免地在合金中引入间隙元素(如氧、氮和氢等)，这种元素一般具有有害作用。
电子束焊虽然焊接了涡轮壳体组件等结构件，但由于受真空室的限制，在焊接法兰环缝等不规则曲线焊缝时，难以自动进行轨迹行走，只能采用人工调节分段拟合，使得电子束焊在较复杂焊缝轨迹产品上的推广应用受到限制。
传统的钨极氩弧焊，采用焊前预热和焊后热处理的方法，接头塑性＜5％，即使调整冷却速度塑性相对有所改善，但实际中也难以控制，因此工艺上进一步改进提高塑性的余地不大。
固态扩散焊接是目前较理想的连接方法，但因需要施加大的连接压力，对于结构复杂特别是具有曲面和大尺寸的构件，操作困难，同时对连接面的预处理要求高，结构尺寸精度很难保证，工艺复杂。
相对而言，特种钎焊与扩散焊技术具有如下主要特点：通过设计钎料成分可控制钎焊温度、对待焊面预处理的要求不高、小尺寸构件可批量焊接，尤其适合于复杂曲面的焊接、不需要施加大的连接压力、构件变形和残余应力小等。
目前，国内外在Ti3Al基合金本身及其与其它材料的钎焊技术研究方面已进行一定的研究，并取得了较好的成果：我国的潘晖等人为提高Ti3Al基合金钎焊接头的性能，研究了成分为Ti-22.4Al-21.5Nb-2.1Mo的Ti3Al合金粉末对Ti-21.5Cu-21.5Ni钎料组织的影响，但未采用混合钎料实际钎焊Ti3Al基合金；1998年报导美国航空航天局Langley研究中心的R.K.Bird等人采用过渡液相扩散连接(TLPB)方法系统地研究了Ti-14Al-21Nb(wt％)合金与Ti-14Al-21Nb(wt％)合金、Ti-14Al-21Nb(wt％)合金与三种钛合金(包括α+β型钛合金Ti-3Al-2.5V和Ti-6Al-4V，β型钛合金Ti-15V-3Cr-3Sn-3Al)的连接，该文献并未介绍两者的具体成分和其相应的连接工艺；1997年报导美国橡树国家实验室的C.H.Cadden等人采用三种成分五种形式的Ti-Cu-Ni合金钎料扩散钎焊Ti-13.4Al-21.2Nb(wt％)合金，钎焊工艺为：982℃(加热升温速度为5℃/min)×60min×0.4MPa(W块加压)×真空(至少1×10-5Torr)×冷速40℃/min(982℃到800℃)。
所有的研究资料表明：到目前为止Ti3Al基合金的钎焊与扩散焊技术尚存在以下不足：(1)已有的研究都是针对较低Nb含量的Ti3Al基合金进行，对于具有更高力学性能的高Nb含量的Ti3Al基合金，以及O相为主的双相合金等缺乏研究；(2)接头的室温强度548MPa，高温强度485MPa(650℃)，塑性低于母材。
发明内容
本发明的目的在于提供一种Ti-Al金属间化合物合金过渡液相扩散焊连接的方法。
为了实现上述目的，本发明包括如下步骤：
(1)采用Ti-Cu-Ni或Ti-Zr-Cu-Ni合金作为连接材料，将合金制备成非晶态或以非晶态组织为主的快速凝固的箔带，剪成与接头相匹配的形式，用丙酮清洗干净；
(2)将Ti3Al合金待焊件除油酸洗，表面清洗干净；
(3)将非晶态或以非晶态组织为主的快速凝固的Ti-Cu-Ni或Ti-Zr-Cu-Ni合金箔带清洗干净置于待焊面，用储能点焊机点焊定位，表面无毛刺、无搭接，接头为对接形式，然后装入焊接夹具，夹紧后放入真空炉；
(4)在温度为1000±50℃条件下，保温30～90min，压块加压0.4～1MPa，随后在920±50℃保温90～360min，之后随炉冷却，加热过程中真空度不低于2×10-2MPa。
优选的工艺参数为：
在温度为980±10℃条件下，保温30min，后降至900℃保温90min。
采用本发明焊接Ti3Al合金，接头室温及高温强度均可达到母材强度的80％以上，室温下可获得与母材同等塑性，接头组织均匀与母材接近。
具体实施方式
下面结合具体实施例详细描述本发明，所述的实施例仅用于描述本发明，而不是限制本发明。
                         实施例1
将Ti3Al基合金TAC-1B加工成Φ16×30mm圆棒，表面经3％HF，10％HNO3酸洗液清洗后烘干，
将Ti-13Zr-21Cu-9Ni按重量百分比熔炼成铸锭，制备成非晶态或以非晶态组织为主的快速凝固箔带，剪成与接头相匹配的形式，用丙酮清洗干净。
用储能点焊机点焊定位，将合金箔带清洗干净置于待焊面点焊定位，焊点表面无毛刺、无搭接，接头为对接形式，然后装入焊接夹具，装配定位，用压快加压约0.4～1MPa，装入真空炉。
连接工艺为980℃保温30min，然后降至900℃保温6h，随炉冷却，加热过程中真空度不低于1×10-2MPa，焊后将试样加工成标准拉伸试样。采用上述连接工艺接头强度见表1(其中σb为抗拉强度，σ0.2为屈服强度，δ为延伸率，Ψ为断面收缩率)：
                           表1
  σb(MPa)   σ0.2(MPa)   δ(％)   Ψ(％)
  接头   842   800   1.5   1.7
  母材   880   840   3.5   5.0
                         实施例2
将Ti3Al基合金TAC-1B加工成Φ16×30mm圆棒，表面经3％HF，10％HNO3酸洗液清洗后烘干，
将Ti-23Cu-15Ni按重量百分比熔炼成铸锭，制备成非晶态或以非晶态组织为主的快速凝固箔带，剪成与接头相匹配的形式，用丙酮清洗干净。
用储能点焊机点焊定位，将合金箔带清洗干净置于待焊面点焊定位，焊点表面无毛刺、无搭接，接头为对接形式，然后装入焊接夹具，装配定位，用压快加压约0.4～1MPa，装入真空炉。
连接工艺为980℃保温30min，然后降至900℃保温3h，随炉冷却，加热过程中真空度不低于1×10-2MPa，焊后将试样加工成标准拉伸试样。采用上述连接工艺接头强度见表2(其中σb为抗拉强度，σ0.2为屈服强度，δ为延伸率，Ψ为断面收缩率)：
                           表2
  σb(MPa)   σ0.2(MPa)   δ(％)   Ψ(％)
  接头   846   717   3.6   4.5
  母材   880   840   3.5   5.0

Claims (2)

1.Ti-Al金属间化合物合金过渡液相扩散焊复合连接方法，其特征在于包括如下步骤：
(1)采用Ti-Cu-Ni或Ti-Zr-Cu-Ni合金作为连接材料，将合金制备成非晶态或以非晶态组织为主的快速凝固的箔带，剪成与接头相匹配的形式，用丙酮清洗干净；
(2)将Ti3Al合金待焊件除油酸洗，表面清洗干净；
(3)将非晶态或以非晶态组织为主的快速凝固的Ti-Cu-Ni或Ti-Zr-Cu-Ni合金箔带清洗干净置于待焊面，用储能点焊机点焊定位，表面无毛刺、无搭接，接头为对接形式，然后装入焊接夹具，夹紧后放入真空炉；
(4)在温度为1000±50℃条件下，保温30～90min，压块加压0.4～1MPa，随后在920±50℃保温90～360min，之后随炉冷却，加热过程中真空度不低于2×10-2MPa。
2.根据权利要求1所述的Ti-Al金属间化合物合金过渡液相扩散焊复合连接方法，其特征在于：在温度为980±10℃条件下，保温30min，后降至900℃保温90min。
CN 200510098587 2005-09-06 2005-09-06 Ti－Al金属间化合物合金过渡液相扩散焊复合连接方法 Pending CN1730224A (zh)