CN1695752A - 新型森林灭火剂配方及工艺 - Google Patents
新型森林灭火剂配方及工艺 Download PDFInfo
- Publication number
- CN1695752A CN1695752A CN 200410037879 CN200410037879A CN1695752A CN 1695752 A CN1695752 A CN 1695752A CN 200410037879 CN200410037879 CN 200410037879 CN 200410037879 A CN200410037879 A CN 200410037879A CN 1695752 A CN1695752 A CN 1695752A
- Authority
- CN
- China
- Prior art keywords
- fire
- forest
- ammonium
- extinguishing agent
- catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种新型森林灭火剂配方,包括硅酸钾、柠檬酸铵、硫酸和磷酸的钾盐和/或铵盐、表面活性剂、增稠剂、催化剂;以重量百分比计,各组分的配比为:硅酸钾为5-25%,柠檬酸铵为5-25%,硫酸钾为0-30%,硫酸铵为10-30%,磷酸铵为0-30%,磷酸二氢铵为0-28%,表面活性剂聚5-乙烯基-1,2-二甲基吡啶甲基硫酸酯0.5-1.5%,增稠剂羧甲基纤维素0-2%,催化剂0-0.5%,所说的催化剂是硫酸铜和二茂铁的1∶1混合物;所述配方所采用的制造工艺为将其高速搅拌球磨,然后用气流分离制成粒径<10μm的灭火剂微粒;该灭火剂灭火速度快,该发明灭火速度快、灭火效率高。可在燃烧表面形成不透氧膜,不易复燃。使用水溶液时,灭火剂溶解速度快,利于灭火。
Description
技术领域:
本发明是一种新型森林灭火剂。
背景技术:
森林火灾每年造成大量的损失,森林火灾的扑救十分困难,其中一个主要原因是复燃问题。
许多国家都在开展对森林灭火剂的研究。如JP62,02,973所述的配方羟乙基纤维素作为增稠剂1、(NH4)2HPO4 12、水100,可用于灭森林火。su 1,544,450森林火灭火剂含尿素31-32、硫醇2-3、酸性红0.5-1、氯化铝13-15、磷酸二铵等。但这些灭火剂对抑制扑救森林火灾后出现的复燃现象效果不理想,这一问题使森林火灾难于彻底扑灭。
发明内容:
本发明的目的正是为了避免上述已有技术的不足,而设计的一种新型灭火剂配方。
该配方由硅酸钾、柠檬酸铵和硫酸、磷酸的钾盐和/或铵盐,表面活性剂,增稠剂和催化剂组成;以重量百分比计,各组分的配比为:硅酸钾为5-25%,柠檬酸铵为5-25%,硫酸钾为0-30%,硫酸铵为10-30%,磷酸铵为0-30%,磷酸二氢铵为0-28%,表面活性剂聚5-乙烯基-1,2-二甲基吡啶甲基硫酸酯0.5-1.5%,增稠剂羧甲基纤维素0-2%,催化剂0-0.5%,催化剂是硫酸铜和二茂铁的1∶1混合物。该配方先通过高速搅拌球磨,然后用气流分离出粒径<10μm的颗粒。该粉剂可配制成浓度为5-35%的水溶液灭森林火,也可直接用于灭A类火。
本发明的主要特点是可抑制森林火的复燃。灭火速度快、灭火效率高。可在燃烧表面形成不透氧膜,不易复燃。使用溶液时,灭火剂溶解速度快,利于灭火。
具体实施方式:
例一、将硅酸钾5份、柠檬酸铵21份、硫酸钾30份、硫酸铵10份,磷酸铵30份、表面活性剂聚5-乙烯基-1,2-二甲基吡啶甲基硫酸酯1.5份、增稠剂羧甲基纤维素2份及催化剂(催化剂是硫酸铜和二茂铁的1∶1混合物)0.5份,均匀混合后通过高速搅拌球磨,然后用气流分离出粒径<10μm的颗粒。即制得灭火剂。
该粉剂可配制成浓度为5-35%的水溶液灭森林火,也可直接用于灭A类火。
另实施例如下:
表1、配方举例
其中表面活性剂为聚5-乙烯基-1,2-二甲基吡啶甲基硫酸酯,增稠剂为羧甲基纤维素,催化剂是硫酸铜和二茂铁的1∶1混合物。
Claims (5)
1、一种新型森林灭火剂配方,其特征在于:所述灭火剂包括硅酸钾、柠檬酸铵、硫酸和磷酸的钾盐和/或铵盐、表面活性剂、增稠剂、催化剂;以重量百分比计,各组分的配比为:硅酸钾为5-25%,柠檬酸铵为5-25%,硫酸钾为0-30%,硫酸铵为10-30%,磷酸铵为0-30%,磷酸二氢铵为0-28%,表面活性剂0.5-1.5%,增稠剂0-2%,催化剂0-0.5%。
2、根据权利要求1所说的森林灭火剂,其特征在于:所说的表面活性剂是聚5-乙烯基-1,2-二甲基吡啶甲基硫酸酯。
3、根据权利要求1所说的森林灭火剂,其特征在于:所说的增稠剂是羧甲基纤维素。
4、根据权利要求1所说的森林灭火剂,其特征在于:所说的催化剂是硫酸铜和二茂铁的1∶1混合物。
5、如权利要求1所说的森林灭火剂配方,其特征在于所述配方所采用的制造工艺为将其高速搅拌球磨,然后用气流分离制成粒径<10μm的灭火剂微粒。