CN1633480A - Compositions for forming photocatalytic film and substrate provided with photocatalytic film - Google Patents
Compositions for forming photocatalytic film and substrate provided with photocatalytic film Download PDFInfo
- Publication number
- CN1633480A CN1633480A CN 03803822 CN03803822A CN1633480A CN 1633480 A CN1633480 A CN 1633480A CN 03803822 CN03803822 CN 03803822 CN 03803822 A CN03803822 A CN 03803822A CN 1633480 A CN1633480 A CN 1633480A
- Authority
- CN
- China
- Prior art keywords
- photocatalyst film
- photocatalyst
- mentioned
- composition
- base material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
It is intended to provide compositions for forming a photocatalytic film whereby an excellent hydrophilic nature can be imparted to the surface of a substrate, in particular, compositions for forming a photocatalytic film whereby a photocatalytic film having an excellent effect of decomposing stains and a highly hydrophilic durability can be formed. It is also intended to provide a substrate provided with a photocatalytic film having an excellent hydrophilic nature. These compositions for forming a photocatalytic film comprise as the essential components a photocatalyst (titanium oxide, etc), a specific silica precursor (a silicic acid compound containing from 0.001 to 1 part by mass of an alkali metal ion per 100 parts by mass of silicic acid, for example, sodium silicate wherein the sodium ion content has been lowered with the use of an ionic exchange resin) and a vehicle.
Description
Technical field
The photocatalyst film that the present invention relates to can to form photocatalyst film on the surface of various base materials forms with composition, by formed photocatalyst film of said composition and the base material that has photocatalyst film with this photocatalyst film.
Background technology
People are well known that: when photocatalyst is carried out optical excitation, decompose attached to meetings such as the organic dirts on the photocatalyst surface, its result can form hydrophilic surface with photocatalyst surface.As the method that forms photocatalyst film, people know all the time is a kind of in the drying process, i.e. thermal decomposition method etc. (for example, the public table of Japan's special permission communique is flat 11-512337 number).But relatively there are the relatively poor problem of hydrophilic persistence in aforesaid method and damp process.
In addition, the method for using the coating composition that contains photocatalyst and silicon-dioxide to form photocatalyst film also is people's known (for example, No. 2756474, Japan's special permission).But the film of the employing silicon-dioxide of aforesaid method also exists hydrophilic persistence and the relatively poor problem of dirt decomposability.
In order to address the above problem, the object of the present invention is to provide a kind of photocatalyst film that can on the surface of base material, form photocatalyst film to form with composition, have the base material of photocatalyst film by the formed photocatalyst film of said composition and this with excellent wetting ability and dirt decomposability extra-heavy.In addition, the present invention also aims to provide the photocatalyst film of the also good photocatalyst film of a kind of wearability that can form hydrophilic longer duration, surface to form with composition, by formed photocatalyst film of said composition and the base material that has this photocatalyst film.
Summary of the invention
The invention provides a kind of photocatalyst film with photocatalyst semiconductive particles, following silica precursor and medium forms and uses composition.
Silica precursor is the silicic acid with respect to 100 mass parts, contains the silicate compound of the alkalimetal ion of 0.001-1 mass parts.
The present invention also provides a kind of formation by photocatalyst film to be formed on the lip-deep photocatalyst film of base material with composition, and the base material that has photocatalyst film with this photocatalyst film.
Description of drawings
Fig. 1 is the schematic cross-section that shows an embodiment of the base material that has a photocatalyst film of the present invention.
The explanation of symbol
10: the base material that has photocatalyst film
20: base material
30: photocatalyst film
Embodiment
When photocatalyst semiconductive particles of the present invention is meant the rayed that has with the energy bigger than the energy difference between the valence band of this photocatalyst and the conduction subband, can generate the material of the character in conduction and hole by exciting electronics in the valence band.As such photocatalyst semiconductive particles, more handy anatase titanium dioxide, rutile titanium dioxide, stannic oxide, zinc oxide, tungstic oxide, three oxidation iron, strontium titanate etc.
The median size of photocatalyst semiconductive particles of the present invention be utilize scattering of light, use microtrackUPA size-grade distribution meter (manufacturings of HONEYWELL company) measure the particulate in the composition the aggegation particle diameter and must.Be preferably 5-90nm, particularly preferably 40-70.Median size too hour because of the particulate of photocatalyst is buried in formed photocatalyst film, is difficult to find the various effects of photocatalyst.If median size is too big, the physical strength of formed photocatalyst film is not enough, also can not guarantee the transparency in addition.
Silica precursor of the present invention is meant the silicic acid with respect to 100 mass parts, contains the silicate compound of the alkalimetal ion of 0.001-1 mass parts.Especially better the silicate compound that contains 0.001-0.2 mass parts alkalimetal ion particularly preferably contains the silicate compound of the alkalimetal ion of 0.001-0.15 mass parts.Alkalimetal ion concentration is to utilize SPS4000 that セ イ コ one イ Application ス Star Le メ Application Star company makes etc., adopts the ICP luminescence analysis to record.Do not have special restriction for alkalimetal ion, can use a kind of alkalimetal ion, can also use the alkalimetal ion more than 2 kinds.As alkalimetal ion, more handy sodium ion or lithium ion.Silicate compound be meant by after the aftertreatment chatted can form the compound of silicon dioxide film.
Silica precursor better is to remove the resultant that a part of alkalimetal ion forms from an alkali metal salt of silicic acid.This resultant can make by the method for utilizing Zeo-karb to reduce alkalimetal ion from an alkali metal salt of silicic acid.Can control the amount of the alkalimetal ion of minimizing by amount, duration of contact and the contact method etc. of controlling used Zeo-karb.
As Zeo-karb, available storng-acid cation exchange resin (RSO
3The H type), weakly acidic cation-exchange resin (RCOOH type) etc.From speed of response, more handy storng-acid cation exchange resin.
Form with in the composition at photocatalyst film of the present invention, the concentration of alkalimetal ion is used composition with respect to photocatalyst film formation, in mass, is preferably 1-80ppm, particularly preferably 1-40ppm, more preferably 1-20ppm.If the concentration of alkalimetal ion is low excessively, the stability of said composition and wetting ability reduce, if when excessive, the stability of said composition obviously descends.
As an alkali metal salt of silicic acid, available be selected from water glass, lithium silicate and the potassium silicate etc. more than a kind, the spy is well water glass and/or lithium silicate.
As water glass, available SiO
2/ Na
2The material that the ratio of components of O is different is unrestricted to this.Especially Na
2O's contains than little material.The water glass of selling on the market has No. 1 (SiO of silicic acid soda
2/ Na
2The mol ratio of O is 2.0-2.3) (silicic acid soda is for No. 1 trade(brand)name that Japanese chemical industrial company makes, and following 2-4 number is too), No. 2 (SiO of silicic acid soda
2/ Na
2The mol ratio of O is 2.4-2.7), No. 3 (SiO of silicic acid soda
2/ Na
2The mol ratio of O is 3.0-3.3), No. 4 (SiO of silicic acid soda
2/ Na
2The mol ratio of O is 3.7-3.9).Special handy Na
2O contains than little silicic acid soda No. 3 and No. 4.
As lithium silicate, known have a SiO
2/ Li
2The material that the ratio of components of O is different is unrestricted to this.Especially Li
2O's contains than little material.The lithium silicate of selling on the market has: lithium silicate 35 (SiO
2/ Li
2The mol ratio of O is 3.5) (lithium silicate 35 is trade(brand)names that Japanese chemical industrial company makes, and following 45 and 75 is the same), lithium silicate 45 (SiO
2/ Li
2The mol ratio of O is 4.5), lithium silicate 75 (SiO
2/ Li
2The mol ratio of O is 7.5).The spy is Li well
2O's contains than little lithium silicate 75.
In forming with composition, photocatalyst film of the present invention preferably contains tensio-active agent.This tensio-active agent mainly contains 2 functions: the 1st can guarantee the wettability of composition to base material, and the 2nd more increases the wetting ability of the formed photocatalyst film of employing said composition.The kind of tensio-active agent there is not special restriction, from the solution dispersion stabilization, more handy nonionic surfactant.Special handy hydrophilic portion is that polyoxy alkylidene, hydrophobic portion are compound (for example, the C of fluorine-containing organic radical
8F
17CH
2CH
2CH (CH
3) O (CH
2CH
2O)
x(CH
2CH (CH
3) O)
yCompound shown in the H (x: y=70: 30, x+y=5.72, molecular-weight average are 800) (below be designated as tensio-active agent Q) etc.).Also available hydrophilic portion is that polyoxy alkylidene, hydrophobic portion are the compound (for example, Japanese ユ ニ カ one company makes, commodity " L-77 " by name etc.) of methyl polysiloxane.
Form with in the composition at photocatalyst film of the present invention, silica precursor better with respect to the photocatalyst semiconductive particles of 100 mass parts, contains the 25-900 mass parts.The spy is contained the 50-400 mass parts well.When containing tensio-active agent, the content of tensio-active agent is preferably the photocatalyst semiconductive particles with respect to 100 mass parts, is the 0.1-10 mass parts.
When if the concentration of silica precursor is excessive, the hydrophilic weather resistance of the photocatalyst film of gained descends, and crosses when hanging down, and the photocatalyst film of gained is possess hydrophilic property not.When if the ratio of tensio-active agent is excessive, the appearance damage of the photocatalyst film of gained, hydrophilic weather resistance descends, if when too small, the coating of composition is bad, the wetting ability of photocatalyst film descends.
Photocatalyst film of the present invention forms and contains medium with composition.As medium, there is not restriction especially, preferably aqueous medium also can contain solvent.Solvent is mainly dilution and uses, and said composition is the form of solution preferably.As this solvent, the polar solvent of more handy lower alcohol, nitrogenous kind solvent, sulfur-bearing kind solvent etc.Special handy lower alcohol.Solvent is also available more than 2 kinds.As medium, special good water.
Photocatalyst film of the present invention forms can be according to the thickness decision of the photocatalyst film of coating process, target with the total amount of the photocatalyst semiconductive particles of composition and silica precursor.Consider the stability of said composition and economy etc., above-mentioned total amount better is that the photocatalyst film with respect to 100 mass parts forms and uses composition, contains the 0.5-50 mass parts.0.5-15 mass parts particularly preferably, especially good is the 0.5-5 mass parts.
In forming with composition, photocatalyst film of the present invention can also contain functional additives.As this functional additive, more handy painted dyestuff, pigment, UV light absorber, antioxidant, the photocatalyst semiconductive particles of the present invention oxide fine particle (Vanadium Pentoxide in FLAKES, magnesium oxide etc., median size 200nm more fortunately are following) in addition etc. of using.
Utilize photocatalyst film of the present invention to form and use composition, on the surface of base material, be coated with said composition, form photocatalyst film, make the base material that has photocatalyst film.In above-mentioned photocatalyst film, silica precursor is transformed to silicon-dioxide, also can the part residual silanol groups.
Silica precursor can think to have silanol group in compound, promptly has SiO
s(OH)
t(s, t are the integers more than 0, the s+t=4) structure shown in (in this structure, not being that the Sauerstoffatom of hydroxyl and other Siliciumatom carry out Chemical bond), and silicon-dioxide can form by dehydration condensation from this silica precursor.
In the present invention, adopt known damp process that photocatalyst film is formed and be coated on the surface of base material, as shown in Figure 1, can form the base material that has photocatalyst film 10 that is formed with photocatalyst film 30 on the base material 20 with composition.As damp process, better with for example spraying method, spread coating, hand are coated with method, revolve tumbling barrel process, dipping is coated with method, various mode of printings coating, the curtain formula coating processes such as coating method, mould coating method (diecoat), the coating method that flows that flow.
Photocatalyst film is formed with after the composition coating,, preferably carry out aftertreatment in order to improve the hardness with photocatalyst film of removing of medium.Above-mentioned aftertreatment is: the dry or heating under the room temperature, the electromagnetic irradiation of ultraviolet ray, electron rays etc., heating etc.Consider the thermotolerance of base material, heating more fortunately 50-700 ℃ was carried out 5-60 minute in special 100-350 ℃ the scope fortunately.When particularly base material is the low material of the thermotolerance of organic resin etc. or the low molecular compound in the base material when heating can be diffused into outside the base material, above-mentioned aftertreatment better is the electromagnetic irradiation of carrying out ultraviolet ray, electron rays etc.
In the present invention, can form the thickness that waits the photocatalyst film of controlling gained with concentration, solvent types, coating condition, the post-treatment condition of composition by adjusting photocatalyst film.If the thickness of photocatalyst film is blocked up, exist the crack arranged in the film, produce interference fringe, this damage significant disadvantages when damage occurring; If thin excessively, may not bring into play needed photocatalyst performance.The thickness of photocatalyst film is also considered economy, is preferably 10-300nm, particularly preferably 10-150nm.
For being used for base material of the present invention, do not have restriction especially, for the shape of base material, also be not limited to flat board, can integral body or a part have curvature.Be used for the transparent base material that base material of the present invention is preferably glass, organic resin etc.As above-mentioned glass, for example available soda-lime glass that is mainly used in plate glass or automotive glass, as above-mentioned organic resin, available for example polycarbonate, the resin of vinylformic acid, polyethylene, polypropylene, polyethylene terephthalate etc. etc.In order to improve the intensity of above-mentioned organic resin, can on the surface of resin, be coated with the organosilicon hard coat.During as base material, from its visual angle, the visible light transmissivity (JIS R3106 (1998 years)) that has the base material of photocatalyst film is better more than or equal to 70% at the transparent base material that uses glass, organic resin etc.
Also can carry out pre-treatment for base material, pre-treatment comprises the physical treatment of the discharge process of Cement Composite Treated by Plasma, corona discharge, UV processing, ozonize etc., the chemical treatment of using acid or alkali etc., employing abrasive substance etc.By carrying out pre-treatment, can improve the wettability of composition on base material, coating composition improves the adhesivity of composition on the base material of formed photocatalyst film equably.When particularly base material is organic resin, preferably carry out pre-treatment.It is effective especially that pre-treatment is carried out in the uviolizing of low pressure mercury lamp of the modification by being generally used for plastics etc.
Above-mentioned pre-treatment and aftertreatment because of about to a great extent the performance of film of gained, so must be respectively with its treatment condition optimization.For example carry out the aftertreatment polycondensation of not only dewatering and make film sclerosis, but also improved the adhesivity of substrate surface and composition by ultraviolet irradiation.Make carrying out aftertreatment like this under the situation that the adhesivity with base material improves, do not need pre-treatment.If the pre-treatment beyond needing, can make the base material deterioration on the contrary and with its performance reduction.
The base material that has photocatalyst film of the present invention because of its surface has excellent wetting ability, and has the good transparency, so can perform well in transportation equipment article, article for building etc.The transportation equipment article are that the body, window glass, speculum, various display element of electric car, automobile, boats and ships, aircraft etc. is with cover plate etc.Article for building comprise the structure in exterior wall, sealing ply, window glass, bridge and tunnel etc. etc.As other purposes, can be used for illumination cover glass, soundproof wall etc.
The base material that has a photocatalyst film of the present invention has excellent wetting ability because of its surface, thus can turbid profit expansion attached to lip-deep water droplet, and the surface can not be blured and be had an antifog property.In addition, Biao Mian organic dirt also can decompose.By toward surface irradiation light, can improve the decomposability of organic dirt more.Moreover, when rain descends along surface current, dirt also can pour off simultaneously (self-cleaning effect).The base material that has photocatalyst film of the present invention also can be realized the effect of the guaranteeing of the visual field, protection attractive in appearance or reduction of maintenance cost etc.
Form the photocatalyst film that forms with composition by photocatalyst film of the present invention, with compare by the formed mulch film of composition that has adopted resultant to form with following structure, have excellent more hydrophilic persistence and dirt decomposability, described structure is to incite somebody to action organoalkoxysilane in the past, i.e. Si (OR)
4The SiO that (R is an alkyl) hydrolysis forms
p(OH)
q(OR)
r(p, q are the integers more than 0, and r is the integer more than 1, p+q+r=4) structure shown in (in this structure, not being that the Sauerstoffatom of hydroxyl and other Siliciumatom carry out Chemical bond).
The base material that has photocatalyst film of the present invention can also be the base material that has photocatalyst film that other film is set between base material and photocatalyst film.Above-mentioned other film comprises for example alkali barrier layer (when base material is the glass of alkali metal containing, in order to prevent the layer of basic metal toward the photocatalyst film diffusion).
Embodiment
By embodiment (routine 1-7,10-12), comparative example (example 8,9) the present invention is specifically described.Utilize following method that sample is estimated.Evaluation result is as shown in table 1.
(wetting ability)
The contact angle of the water at the initial stage of irradiates light not after working sample has just been made.
(hydrophilic persistence)
After just having made sample, hold it in the environment of no directing light after 1 week, measure and the contact angle of water, from keeping hydrophilic angle, contact angle is more fortunately below 20 °, better below 10 °.
(dirt decomposability)
Make the sample of just having made adhere to oleic acid, the contact angle of making water is about 70 ° contaminated surface, with 0.5mW/cm
2Intensity with invisible light (black light) (centre wavelength is 365nm) to above-mentioned surface irradiation after 6 hours, measure the contact angle of water.From the angle of resistance to soiling, contact angle is more fortunately below 10 °, better below 6 °.
(film toughness)
Sample is carried out taper (taper) wear test (the abrasion number of times is 100 times, and loading is 4.9N).Measure the turbidity value (haze value) (the metering equipment name is called ス ガ trier company and makes ヘ one ズ コ Application ピ ユ one that directly reads) of wear test front and back, obtain its variable quantity.From the angle of wear resistant, variable quantity is more fortunately below 3%.
(resistance to soiling)
With the sample just made in outdoor exposure after 1 month, range estimation pollution level (zero: dirt is not obvious, △: dirt is obvious a little, *: dirt is clearly).
(antifog property)
Blow facing to the sample just made, visual observation have or not mist (zero: no mist, *: the generation mist).
(example 1)
Prepare soda-lime glass plate (100mm * 100mm, thickness are 3.5mm), this sample surfaces is ground, clean after drying, form the sheet glass of having finished pre-treatment with distilled water with cerium oxide.
In the water of 37.5g, add No. 4 (trade(brand)names: the manufacturing of Japanese chemical industrial company, SiO of silicic acid soda of 12.5g
2: 23.35 quality %, Na
2O:6.29 quality %.SiO
2/ Na
2The mol ratio of O: 3.83), add the storng-acid cation exchange resin (Mitsubishi Chemical Ind makes, trade(brand)name " SK1BH ") of 30g again, at room temperature stirred 10 minutes, preparation desalination silicic acid soda solution (with respect to the silicic acid of 100 mass parts, sodium ion is 0.12 mass parts).
In the 2-of 32.1g propyl alcohol, (median size is 56nm to the anatase titanium dioxide particulate of interpolation 9g, below be designated as photocatalyst A) aqueous dispersions (solid component concentration is 10 quality %) and the desalination silicic acid soda solution of 8.9g, add tensio-active agent " L-77 " (trade(brand)name: Japanese ユ ニ カ one company makes) again so that be 100ppm, make coating solution 1 (Na ion concentration is 12ppm) with respect to solution amount.
With the coating solution 1 of the gained of 2mL, drip on above-mentioned surface of having finished the sheet glass of handling, after the spin-coating method coating, in air atmosphere, 200 ℃ of roastings 60 minutes, make and have the sample that thickness is the photocatalyst film of 80nm.
(example 2)
In the water of 36.07g, add the lithium silicate 75 (trade(brand)name: the manufacturing of Japanese chemical industrial company, SiO of 13.93g
2: 21.54 quality %, Li
2O:1.43 quality %.SiO
2/ Li
2The mol ratio of O: 7.49), add " SK1BH " of 30g again, at room temperature stirred 10 minutes, preparation desalination lithium silicate solution (with respect to the silicic acid of 100 mass parts, lithium ion is 0.13 mass parts).
In the 2-of 32.1g propyl alcohol, add the photocatalyst A of 9g and the desalination lithium silicate solution of 8.9g, add " L-77 " again so that be 100ppm with respect to solution amount, make coating solution 2 (lithium concentration is 13ppm).Coating solution 2 with gained has the sample that thickness is the photocatalyst film of 83nm with example 1 the same making.
(example 3)
In the 2-of 32.1g propyl alcohol, add the photocatalyst A of 10.5g and the desalination silicic acid soda solution of 6.69g, add " L-77 " again so that be 100ppm with respect to solution amount, make coating solution 3 (Na ion concentration is 7ppm).Coating solution 3 with gained has the sample that thickness is the photocatalyst film of 82nm with example 1 the same making.
(example 4)
In the 2-of 32.1g propyl alcohol, add the desalination silicic acid soda solution of the example 1 of the photocatalyst A of 4.5g and 15.6g, add " L-77 " again so that be 100ppm with respect to solution amount, make coating solution 4 (Na ion concentration is 23ppm).Coating solution 4 with gained has the sample that thickness is the photocatalyst film of 83nm with example 1 the same making.
(example 5)
Except adopting tensio-active agent Q to replace " L-77 " in the example 1, with the example 1 the same sample that makes.
(example 6)
In example 1, be not in air atmosphere in 200 ℃ of roastings 60 minutes, but in air atmosphere, made sample in 30 minutes in 300 ℃ of roastings.
(example 7)
In example 1, be not in air atmosphere in 200 ℃ of roastings 60 minutes, but in air atmosphere, made sample in 5 minutes in 650 ℃ of roastings.
(example 8) (comparative example)
In the ethanol of 90g, add the tetramethoxy-silicane of 5g, after the stirring in 10 minutes, slowly add the aqueous nitric acid (1 quality %) of 5g, make the hydrolysis resultant B of tetramethoxy-silicane.
In the 2-of 32.1g propyl alcohol, add the photocatalyst A of 9g and the said hydrolyzed resultant B of 8.9g, add " L-77 " again so that be 100ppm with respect to solution amount, make coating solution 8 (Na ion concentration is Oppm).
Coating solution 8 with gained has the sample that thickness is the photocatalyst film of 80nm with example 1 the same making.
(example 9) (comparative example)
In the 2-of 32.1g propyl alcohol, add the silicic acid soda No. 4 (with respect to the silicic acid of 100 mass parts, sodium ion is 26.9 mass parts) of the photocatalyst A of 9g and 8.9g after, produced throw out and can not make coating solution.
(example 10)
Preparation has the polycarbonate resin plate (100mm * 100mm, thickness are 5.0mm) of organosilicon hard coat, and after with distilled water this hard coating surface being cleaned, drying forms the polycarbonate plate of having finished pre-treatment.
Coating solution 1 with example 1 gained of 2mL, dropping is on above-mentioned surface of having finished the polycarbonate plate of handling, after the spin-coating method coating, with low pressure UV irradiating unit (PL7-200 that セ Application エ Application ジ ニ ア リ Application グ Co., Ltd. makes), distance between lamp and the above-mentioned resin board is decided to be 2cm, carry out uviolizing in 5 minutes, make and have the sample that thickness is the photocatalyst film of 80nm.What the ultraviolet ray here was meant that low pressure mercury lamp sends is the high-energy ultraviolet ray (hereinafter referred to as UV-C) of predominant wavelength with 253.7nm and 184.9nm.
(example 11)
In example 10, except clean, after drying has the polycarbonate resin plate of organosilicon hard coat, the UV-C that uses above-mentioned low pressure UV irradiating unit to carry out 2 minutes shines and makes beyond the polycarbonate plate of having finished pre-treatment, with the example 10 the same samples that make.
(example 12)
In example 10, do not carry out 5 minutes irradiation UV-C, and with metal halide lamp (metal halidelamp) (ア イ グ ラ Off イ Star Network ス Co., Ltd. make M03-L31), the distance of lamp and above-mentioned resin board is decided to be 10cm, irradiation ultraviolet radiation 5 minutes makes and has the sample that thickness is the photocatalyst film of 80nm.The metal halide lamp here is meant the wavelength with 300-450nm, has than the long superpower UV-lamp of the ripple of low pressure mercury lamp.
Table 1
Example | Wetting ability | Hydrophilic persistence | The dirt decomposability | Film toughness | Resistance to soiling | Antifog property |
??1 | ????3° | ????8° | ????5° | ????2.1 | ????○ | ????○ |
??2 | ????4° | ????6° | ????4° | ????2.1 | ????○ | ????○ |
??3 | ????4° | ????12° | ????3° | ????2.8 | ????○ | ????○ |
??4 | ????3° | ????7° | ????5° | ????1.8 | ????○ | ????○ |
??5 | ????1° | ????6° | ????5° | ????2.1 | ????○ | ????○ |
??6 | ????5° | ????11° | ????5° | ????1.2 | ????○ | ????○ |
??7 | ????5° | ????10° | ????5° | ????0.8 | ????○ | ????○ |
??8 | ????3° | ????23° | ????46° | ????4.6 | ????△ | ????○ |
??10 | ????3° | ????6° | ????5° | ????2.2 | ????○ | ????○ |
??11 | ????4° | ????8° | ????5° | ????2.0 | ????○ | ????○ |
??12 | ????3° | ????7° | ????4° | ????2.4 | ????○ | ????○ |
The possibility of utilizing on the industry
Can make substrate surface by the present invention and have excellent hydrophilic photocatalyst film formation composition. Use photocatalyst film of the present invention to form and use composition, can form at low temperatures the photocatalyst film of hydrophily excellence, this hydrophily with the surface of the base material of photocatalyst film is good. Adopt photocatalyst film of the present invention to form with the formed photocatalyst film of composition, the excellent especially and hydrophilic longer duration of dirt decomposability. For this reason, the surface usually keeps peace and quiet.
Adopt photocatalyst film of the present invention to form with the formed surface with excellent hydrophilic base material of composition and have good anti-drop property, antifog property, resistance to soiling, abrasion performance. That is, can make by making substrate surface have hydrophily that the water droplet that is attached on the substrate surface is moistening to scatter, the surface does not produce mist. Moreover the irradiation of the light by sunshine etc. can promote the decomposition (the particularly decomposition of organic dirt) of dirt. When the water of the generations such as rainfall flows down toward the surface of article, the dirt of inorganic matter also thereupon pour off (self-cleaning effect).
Claims (15)
1. photocatalyst film forms and uses composition, it is characterized in that, comprise photocatalyst semiconductive particles, following silica precursor and medium, silica precursor is the silicic acid with respect to 100 mass parts, contains the silicate compound of the alkalimetal ion of 0.001-1 mass parts.
2. photocatalyst film according to claim 1 forms and uses composition, it is characterized in that the median size of above-mentioned photocatalyst semiconductive particles is 5-90nm.
3. photocatalyst film according to claim 1 and 2 forms and uses composition, it is characterized in that, above-mentioned photocatalyst film forms the concentration with the alkalimetal ion in the composition, forms with respect to photocatalyst film and uses composition, with mass conversion, is 1-80ppm.
4. form and use composition according to claim 1,2 or 3 described photocatalyst films, it is characterized in that above-mentioned silica precursor forms by the alkalimetal ion of removing a part from an alkali metal salt of silicic acid.
5. form and use composition according to claim 1,2 or 3 described photocatalyst films, it is characterized in that above-mentioned silica precursor forms by the alkalimetal ion that utilizes Zeo-karb to remove a part from an alkali metal salt of silicic acid.
6. use composition according to claim 4 or 5 described photocatalyst films formation, it is characterized in that an alkali metal salt of above-mentioned silicic acid is water glass and/or lithium silicate.
7. form according to each described photocatalyst film among the claim 1-6 and use composition, it is characterized in that,, contain the above-mentioned silica precursor of 25-900 mass parts with respect to the above-mentioned photocatalyst semiconductive particles of 100 mass parts.
8. form according to each described photocatalyst film among the claim 1-7 and use composition, it is characterized in that, using composition, the total content of above-mentioned photocatalyst semiconductive particles and above-mentioned silica precursor with respect to the above-mentioned photocatalyst film formation of 100 mass parts is the 0.5-50 mass parts.
9. photocatalyst film is characterized in that, on the surface of base material, is formed with composition by each described photocatalyst film among the claim 1-8 and to form.
10. photocatalyst film is characterized in that, pre-treatment is carried out on the surface of base material, after each described photocatalyst film formation is coated on the above-mentioned surface with composition among the claim 1-8, forms by aftertreatment.
11. photocatalyst film according to claim 10 is characterized in that, above-mentioned aftertreatment is electromagnetic irradiation.
12., it is characterized in that the thickness of above-mentioned photocatalyst film is 10-300nm according to claim 9,10 or 11 described photocatalyst films.
13. have the base material of photocatalyst film, it is characterized in that on the surface of base material, having each described photocatalyst film among the claim 9-12.
14. the base material that has photocatalyst film according to claim 13 is characterized in that, above-mentioned base material is glass or organic resin.
15., it is characterized in that the visible light transmissivity of the above-mentioned base material that has a photocatalyst film is more than 70% according to claim 13 or the 14 described base materials that have photocatalyst film.