CN1632017A - 预涂卷材用聚氨酯底漆 - Google Patents
预涂卷材用聚氨酯底漆 Download PDFInfo
- Publication number
- CN1632017A CN1632017A CN 200410065242 CN200410065242A CN1632017A CN 1632017 A CN1632017 A CN 1632017A CN 200410065242 CN200410065242 CN 200410065242 CN 200410065242 A CN200410065242 A CN 200410065242A CN 1632017 A CN1632017 A CN 1632017A
- Authority
- CN
- China
- Prior art keywords
- epoxy
- resin
- priming paint
- paint according
- alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
原料名称 | 规格 | 用量(重量份) | |
PE-1 | PE-2 | ||
甲基丙二醇 | 工业级,含量≥95% | 253.6 | 229.6 |
间苯二甲酸 | 工业级,含量≥99.5% | 267.8 | 286.4 |
己二酸 | 工业级,含量≥99.5% | 78.5 | 84.0 |
溶剂 | 反应溶剂二甲苯 | 工业级 | 80.0 | 80.0 |
兑稀溶剂 | 工业级 | 130.0 | 278.5 | |
二丁基氧化锡 | 工业级 | 0.2 | 0.2 |
组分 | 原料名称 | 用量(重量份) | ||||
PU-1 | PU-2 | PU-3 | PU-4 | PU-5 | ||
多元醇 | PE-1 | 157.1 | 145.2 | - | - | - |
PE-2 | - | - | 167.9 | - | - | |
Uralac SN833 | - | - | - | 446.0 | 486.2 | |
DEA | - | - | - | 82.0 | 81.6 | |
含羧基二元醇 | DMPA | 10.2 | 9.4 | 3.6 | 5.7 | 6.0 |
二异氰酸酯 | IPDI | 48.1 | - | - | 53.8 | - |
TDI | - | 34.8 | 11.7 | - | 38.8 | |
环氧化合物 | CARDURA E-10 | 18.0 | 17.5 | 6.6 | - | - |
E-44(80%二甲苯溶液) | - | - | - | 18.2 | 18.8 | |
催化剂 | 二月桂酸二丁基锡 | 0.05 | 0.05 | 0.05 | 0.4 | 0.4 |
溶剂 | 混合溶剂 | 146.9 | 125.0 | 146.9 | 287.9 | 287.4 |
环己酮 | - | - | - | 73.9 | 71.8 | |
总-OH/-NCO,摩尔比 | 1.25/1 | 1.24/1 | 1.51/1 | 1.4/1 | 1.54/1 | |
多元醇-OH/含羧基二元醇的-OH,摩尔比 | 71.9/28.1 | 71.9/28.1 | 73.5/26.5 | 87.5/12.5 | 86.9/13.1 | |
环氧官能团/-COOH,摩尔比 | 0.95/1 | 1/1 | 0.98/1 | 1.6/1 | 1.53/1 |
树脂特性 | PU-1 | PU-2 | PU-3 | PU-4 | PU-5 |
固含量,% | 53.1 | 53.6 | 38.9 | 40.0 | 40.0 |
羟值(固体树脂),mgKOH/g | 26.6 | 28.0 | 18.2 | 28.2 | 34.6 |
酸值(固体树脂),mgKOH/g | 3.0 | 2.9 | 3.3 | ≈0 | ≈0 |
数均分子量(理论) | 18412.3 | 17449.2 | 16178.8 | 9365.0 | 8975 |
组分 | 原料名称 | 用量(重量份) | |
底漆-1~5 | 底漆-6 | ||
环氧改性的带羟基的聚氨酯树脂 | PU-1~PU-5 | 160.1(PU-1~PU-5) | 218.5(PU-3) |
环氧树脂 | E-20(60%环己酮溶液) | 16.7 | 16.7 |
交联树脂 | Cymel303 | 5.1 | 5.1 |
防腐蚀颜料 | 锌铬黄 | 20.0 | - |
锶铬黄 | 40.0 | - | |
磷酸锌 | 20.0 | 20.0 | |
氧化锌 | 5.0 | 5.0 | |
Shieldex 303 | - | 50.0 | |
着色颜料 | R-706 | 10.0 | 20.0 |
填料 | 沉淀硫酸钡 | 5.0 | 5.0 |
助剂 | 分散剂Byk-P-104S | 2.0 | 2.0 |
催化剂Byk-450 | 2.0 | 2.0 | |
流平剂EFKA-3777 | 2.0 | 2.0 | |
溶剂 | S-150#∶DME∶乙二醇乙醚醋酸酯=3∶1∶1 | 117.6 | 59.7 |
检测项目 | 样板-1 | 样板-2 | 样板-3 | 样板-4 | 样板-5 | 样板-6 | 对比例样板-1 | 对比例样板-2 | 对比例样板-3 | 对比例样板-4 | ||||||||||
白灰 | 海蓝 | 白灰 | 海蓝 | 白灰 | 海蓝 | 白灰 | 海蓝 | 白灰 | 海蓝 | 闪光 | 白灰 | 白灰 | 海蓝 | 白灰 | 海蓝 | 闪光 | 白灰 | 闪光 | 白灰 | |
T弯 | 1T | 2T | 2T | 2T | 2T | 1T | 2T | 1T | 2T | 2T | 0T | 1T | 3T | 2T | 3T | 3T | 1T | 2T | 1T | 2T |
MEK擦拭来回,次 | >100 | >100 | >100 | >100 | >100 | >100 | >100 | >100 | >100 | >100 | >100 | >100 | >100 | >100 | >100 | >100 | >100 | >100 | >100 | >100 |
杯突,mm | 8.5 | 8.5 | 8.0 | 8.5 | 8.0 | 8.5 | 8.0 | 8.5 | 8.0 | 8.5 | 9.0 | 8.5 | 8 | 8 | 8 | 8 | 8 | 8 | 8 | 8 |
耐盐雾,h | >500 | >500 | >500 | >500 | >500 | >500 | >500 | >500 | >500 | >500 | >200 | >200 | >500 | >500 | >500 | >500 | >200 | >200 | >150 | >150 |
Claims (10)