CN1609245A - High-copper silverless contact for low voltage apparatus material and processing method thereof - Google Patents

High-copper silverless contact for low voltage apparatus material and processing method thereof Download PDF

Info

Publication number
CN1609245A
CN1609245A CN 200410155250 CN200410155250A CN1609245A CN 1609245 A CN1609245 A CN 1609245A CN 200410155250 CN200410155250 CN 200410155250 CN 200410155250 A CN200410155250 A CN 200410155250A CN 1609245 A CN1609245 A CN 1609245A
Authority
CN
China
Prior art keywords
copper
lanthanum
yttrium
aluminium
diamond
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200410155250
Other languages
Chinese (zh)
Other versions
CN1328401C (en
Inventor
吴康楼
刘本义
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xianju NANDA Alloy Technology Co., Ltd.
Original Assignee
QUEQING NANDA ALLOY TECHNOLOGY DEVELOPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QUEQING NANDA ALLOY TECHNOLOGY DEVELOPMENT Co Ltd filed Critical QUEQING NANDA ALLOY TECHNOLOGY DEVELOPMENT Co Ltd
Priority to CNB2004101552509A priority Critical patent/CN1328401C/en
Publication of CN1609245A publication Critical patent/CN1609245A/en
Application granted granted Critical
Publication of CN1328401C publication Critical patent/CN1328401C/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to electric contact material for low voltage electric appliance and household electric appliance and its production process. The electric contact material has copper as base component and may have the combination of Al, Cd, La, Y and diamond; the combination of Al, Y, Zr, La and diamond; or the combination of Al, Y, La, Zr and chromium carbide. The alloy of the present invention has high electric conductivity, high heat conductivity, high arc ablation resistance, high fusion welding resistance, high temperature oxidation resistance, low contact resistance, low cost and other advantages.

Description

High-copper silverless contact for low voltage apparatus material and working method thereof
Technical field: the present invention is about the electric contact material and the manufacture method thereof of a kind of low voltage electrical apparatus industry and household electrical appliance industry.
Background technology: at present, in electrical apparatus industry, use ag-based contact material to become traditional technology.As: series such as Ag-MeO, Ag-c, Ag-Ni.These materials in use all have effect preferably, but these materials all are matrix with silver.And the price of at present domestic and international silver is all rising steadily, and silver-colored resource is more and more in short supply.For this reason, everybody attention is all at Xiang Jieyin, for silver-colored directional steering, the technology trends in this field has been catered in the exploitation of copper base low voltage electric contact material, disclosed already ZL.94102452.0 and ZL.98120087.7 have done a little technological development highly significant in this respect, but all there is alloy theory cost problem of higher, do not meet the circulation of the disclosed proportioning component of above-mentioned document alloy material more in the market.Quality of materials to its specific components proportioning can't be affirmed and deny absolutely.
Summary of the invention: the present invention seeks to propose one group also is that the low-voltage apparatus of specific component and proportioning does not have the silver contact material with high-copper, still has performances such as favorable conductive heat conductivility and anti-electrical arc erosion.Another object of the present invention is to provide a kind of alloy complete processing of uniqueness to make its alloy reach good performance and good cost performance.
The invention technical scheme is: a kind of high-copper silverless contact for low voltage apparatus material, with copper is base-material, its feature also includes combination a kind of of following element, or aluminium, cadmium, lanthanum, yttrium, diamond, its composition proportion (weight percentage) is an aluminium 0.1~2, cadmium 0.05~2, lanthanum 0.01~1.5, yttrium 0.01~0.15, diamond 0.05~2, all the other are copper and unavoidable impurities; Or aluminium, yttrium, zirconium, lanthanum, diamond, its composition proportion (weight percentage) is an aluminium 0.1~2, yttrium 0.01~1.5, zirconium 0.01~2, lanthanum 0.05~1.5, diamond 0.05~2, all the other are copper and unavoidable impurities; Or aluminium, yttrium, lanthanum, zirconium and chromium carbide, its proportioning components (weight percentage) is aluminium 0.1~2, yttrium 0.01~1.5, lanthanum 0.01~1.5, zirconium 0.01~2, chromium carbide 0.5~10, all the other are copper and unavoidable impurities.
The technique processing method of uniqueness of the present invention is: all prepares by the element that above-mentioned alloy component proportioning is formed with powder, and repressed, sintering, extruding or forging, rolling punching gets finished product.
The adding of each element-specific is played good effect to the good electrical and thermal conductivity performance of improving contact material and needing among the present invention, and the adding of aluminium has improved the high-temperature oxidation resistance of copper, and the existence of small amounts aluminium also plays dispersion-strengthened action, reduces the diamond consumption.Zirconium can improve anti-melting welding ability after adding, and improves hot strength.Zirconium white under the high temperature can improve the electroconductibility thermal diffusivity of contact.The adding of lanthanum, yttrium can make the material structure grain refining, has strengthened the resistance of oxidation under the high temperature of copper matrix at the sedimentary lanthanum of copper crystal boundary, yttrium particle.Diamond has high hardness, and it adds with the micro mist state, and good dispersity has dispersion-strengthened action to matrix.At high temperature, the reducing gas that produces with not change process of stone is alleviated the oxidation of inner base.It is better that wherein the adding of cadmium makes the arc extinguishing effect, and under the effect of moment high-temperature electric arc, cadmium is gasificated into Cadmium oxide, and the steam of this Cadmium oxide has stoped the burning and the expansion of electric arc, thereby reach the purpose of arc extinguishing.Chromium carbide is lower slightly than diamond hardness, but the effect of desirable cash equivalent hard rock reduces cost etc., and the reasonable adding of each element makes that alloy zoarium of the present invention has that good, the anti-electrical arc erosion of electrical and thermal conductivity, anti-melting welding, high temperature oxidation resisting, contact resistance are low, low price etc.
Working method technology uniqueness of the present invention, after in prior powder metallurgy technology, having added extruding or/and forging, density, the hardness of its material are obviously improved, resistivity, temperature rise descend, high-temperature mechanical property has improvement greatly, make alloy of the present invention become the material that ideal substitutes money base, can be widely used in the various low-voltage apparatuses.
Contact material is the heart component of electric product innovation.Good electrical and thermal conductivity performance at first must be arranged, want anti-electrical arc erosion, reliable break-make and stability will be arranged, also low resistivity and favorable mechanical performance etc. will be arranged.Single component can not satisfy above-mentioned requirements simultaneously.Only choose different constituent elements, bring into play different constituent elements advantage separately, effect is preferably just arranged.
Further set forth the present invention below in conjunction with embodiment, wherein the per-cent number average is with the weight percent number.
Embodiment 1:
Cadmium 0.5% yttrium 0.05% lanthanum 0.01%
Aluminium 1.5% diamond 0.05% copper surplus
Embodiment 2:
Cadmium 1.0% yttrium 0.08% lanthanum 0.05%
Aluminium 0.5% diamond 0.08% copper surplus
Embodiment 3:
Cadmium 1.5% yttrium 0.1% lanthanum 0.15%
Aluminium 0.4% diamond 1.0% copper surplus
Embodiment 4:
Cadmium 2.0% yttrium 0.25% lanthanum 0.05%
Aluminium 1.0% diamond 0.8% copper surplus
Product innovation, the performance of making by above-mentioned (example 1-4) batching are as follows:
Density 〉=8.6g/cm3
Hardness HB 800-1200Mpa
Resistivity≤2.3 μ Ω cm
Embodiment 5
Yttrium 0.02% zirconium 1.5% lanthanum 0.5%
Aluminium 1.0% diamond 0.5% copper surplus
Embodiment 6:
Yttrium 0.08% zirconium 0.5% lanthanum 0.1%
Aluminium 1.0% diamond 0.5% copper surplus
Embodiment 7:
Yttrium 0.2% zirconium 0.1% lanthanum 0.5%
Aluminium 1.0% diamond 0.5% copper surplus
Embodiment 8:
Yttrium 1.5% zirconium 0.05% lanthanum 0.1%
Aluminium 1.0% diamond 0.5% copper surplus
The product innovation performance of making by above-mentioned (example 5-8) batching is as follows:
Density 〉=8.6g/cm3
Hardness HB 800-1200Mpa
Resistivity≤2.2 μ Ω cm
Embodiment 9:
Yttrium 0.02% zirconium 1.5% lanthanum 0.1%
Aluminium 2.0% chromium carbide 0.5% copper surplus
Embodiment 10:
Yttrium 0.2% zirconium 1.0% lanthanum 0.1%
Aluminium 1.5% chromium carbide 2.0% copper surplus
Embodiment 11:
Yttrium 0.08% zirconium 1.0% lanthanum 0.1%
Aluminium 1.5% chromium carbide 6.0% copper surplus
Embodiment 12:
Yttrium 1.5% zirconium 0.5% lanthanum 0.1%
Aluminium 1.5% chromium carbide 10% copper surplus
The product innovation performance of making by above-mentioned (example 9-12) batching is as follows:
Density 〉=8.4g/cm3
Hardness HB 800-1200Mpa
Resistivity≤2.6 μ Ω cm
The alloy material of the foregoing description all adopts in the conventional powder metallurgical technology and to add extruding or/and unique working method of forging process particularly, the excellent processing conditions of making be component element powder granularity below 74 microns, pressing conditions is 3~8T/CM 2, sintering condition is 800~980 ℃, 2~5 hours time under the gas shield, the condition of extruding is 80~300KG/MM 2With forged condition be 30~100KG/MM 2

Claims (4)

1.[document source] electronic application
2.[the message in-coming date] 2004-8-26
3.[application number]
4.[claim item]
[claim 1]
A kind of high-copper silverless contact for low voltage apparatus material, with copper is base-material, its feature also includes combination a kind of of following element, or aluminium, cadmium, lanthanum, yttrium, diamond, its composition proportion (weight percentage) is an aluminium 0.1~2, cadmium 0.05~2, lanthanum 0.01~1.5, yttrium 0.01~0.15, diamond 0.05~2, all the other are copper and unavoidable impurities; Or aluminium, yttrium, zirconium, lanthanum, diamond, its composition proportion (weight percentage) is an aluminium 0.1~2, yttrium 0.01~1.5, zirconium 0.01~2, lanthanum 0.05~1.5, diamond 0.05~2, all the other are copper and unavoidable impurities; Or aluminium, yttrium, lanthanum, zirconium and chromium carbide, its proportioning components (weight percentage) is aluminium 0.1~2, yttrium 0.01~1.5, lanthanum 0.01~1.5, zirconium 0.01~2, chromium carbide 0.5~10, all the other are copper and unavoidable impurities.
[claim 2]
High-copper silverless contact for low voltage apparatus material working method by claim 1 is distributed into is characterized in that: component all prepared with powder, and repressed, sintering, extruding or forging, rolling punching gets finished product.
[claim 3]
By the described high-copper silverless contact for low voltage apparatus material working method of claim 2; it is characterized in that component element powder granularity is below 74 microns; pressing conditions is 3~8T/CM2; sintering condition is 800~980 ℃, 2~5 hours time under the gas shield, and the condition of extruding is that 80~300KG/MM2 and forged condition are 30~100KG/MM2.
CNB2004101552509A 2004-08-26 2004-08-26 High-copper silverless contact for low voltage apparatus material and processing method thereof Expired - Fee Related CN1328401C (en)