CN1595613A - A method for making metal induced polysilicon film having diffuse layer above metal - Google Patents
A method for making metal induced polysilicon film having diffuse layer above metal Download PDFInfo
- Publication number
- CN1595613A CN1595613A CN 200410010970 CN200410010970A CN1595613A CN 1595613 A CN1595613 A CN 1595613A CN 200410010970 CN200410010970 CN 200410010970 CN 200410010970 A CN200410010970 A CN 200410010970A CN 1595613 A CN1595613 A CN 1595613A
- Authority
- CN
- China
- Prior art keywords
- metal
- layer
- amorphous silicon
- annealing
- induced
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a manufacture method for metal induced polysilicon film with diffusion layer, comprising sediment of amorphous silicon film (11) on isolated substrate (10) , sediment of metal isolation layer (12) on amorphous silicon film (11) , a layer of induced metal layer (13), a layer of sediment on induced metal layer (13) as diffusion dielectric layer (14) on metal, using low temperature(<600 deg.C) annealing to realize crystallization of amorphous silicon to polysilicon, using corrasion technique to clear away metal diffusion dielectric layer (14) , induced metal layer (13) and metal isolation layer (12) . Using the method of the invention, can adjust the quality of metal atom which enters amorphous silicon layer to acquire polysilicon film with large crystal grain, at the same time, avoid pollution of remained metal since metal and silicon layer not touch each other, in addition, increase width of induced metal layer (13) to raise operability and repeatability of technique.
Description
Technical field
The present invention relates to a kind of manufacture method of low-temperature polysilicon film, particularly a kind of improved metal inducement that utilizes makes the amorphous silicon crystallization, thereby obtains the manufacture method of high-quality polysilicon, and it also is the semiconductor processing technology of carrying out under a kind of low temperature.
Background technology
As everyone knows, polysilicon membrane has been widely used in the making of semiconductor device now, as show the polycrystalline SiTFT (TFT that uses in the industry, Thin Film Transistor), microelectromechanical systems, aspects such as integrated circuit and alternative SOI (Silicon on Insulator) material.Wherein in showing industry, especially at AMOLED (Active Matrix Organic Light-emitting Device, active organic luminescent device), in TFT-LCD (TFT liquid crystal display device) product, in order to improve the performance of display screen, usually adopt TFT to form pixel drive circuit and peripheral driving circuit thereof, these TFT adopt polysilicon membrane as its active layer mostly, and drive circuit and display element are produced on the transparent glass substrate with low cost together, this all requires the better performances of polysilicon membrane, and requires to make under cryogenic conditions.
The method that several formation low-temperature polysilicon films have been arranged now, wherein a class is the direct growth method, such as in the following document report: 1., " Comparison of poly-Si films deposited by UHVCVD andLPCVD and its application for thin film transistors ", D.Z.Peng, et a1., Vacuum, (2002), vol.67, pp641; 2., " Low temperature polycrystallinesilicon thin film transistors ", Jin Jang, Jai Il Ryu, Soo Young Yoon andKyung Ha Lee, Vacuum, (1998), Vol.51, pp769.This method generally is to utilize ultra high vacuum CVD (UHVCVD) or equipment such as RPCVD, PECVD directly to grow polysilicon membrane on substrate, its advantage is to need not to use annealing crystallization again, thereby shortened the time of preparation, but shortcoming is also fairly obvious, that is exactly that the surface roughness of film is big, has had a strong impact on the mobility of device and the stability of device; Other class methods are to prepare the a-Si film earlier, method by annealing makes a-Si film crystallization formation polysilicon membrane more again, as document 1., " Advanced excimer laser crystallization technique; L.Mariucci, A.Pecora, et.al.; Thin Solid Films; 2001, Vol.383, pp39 "; 2., the employing excimer laser heating a-Si film of being reported in " Effect ofexcimer laser annealing on the structural and electrical properties ofpolycrystalline silicon thin-film transistors; C.T.Angelis and C.A.Dimitriadis; J.APPL.PHYS.; (1999); Vol.86; pp4600 ", annealing crystallization then; And as document 1., " Polycrystalline siliconprepared by metal induced crystallization; Jong Hyun Choi; Do Young Kim; Seung Soo Kim, Seong Jin Park, Jin Jang; Thin Solid Films; (2003), Vol.440, pp.1 "; 2., " Low-temperature crystallization of hydrogenatedamorphous silicon induced by Nickel silicide formation; Yunosuke KAWAZU; et al.; Jpn.J.Appl.Phys.; (1990); Vol.29, pp.2698 " described in metal inducement (MIC; Metal Induced Crystallization) technology; wherein utilize metal material and silicon to form metal silicide; and with this as media, impel polysilicon can form (being lower than 600 ℃) at a lower temperature.
The technology that quasi-molecule laser annealing and metal inducement prepare polysilicon is two kinds of extremely important methods of preparation polysilicon membrane in the present industry.Utilize the method for quasi-molecule laser annealing can obtain the big and less polysilicon membrane of surface roughness of mobility, but its device costs an arm and a leg, the uniformity of the polysilicon membrane of making in addition is relatively poor; Utilize the metal inducement technology can obtain good uniformity, the mobility height, the polysilicon membrane that has an even surface, manufacture craft and equipment are also comparatively simple.But this method also exists some problems at present, and after for example crystallization was finished, metal remained polluted raceway groove at the raceway groove place, thereby influences the performance of device; In order to reduce the pollution of kish, and the polysilicon membrane that is beneficial to formation large-size crystal grain (improves mobility, reduce the intercrystalline defective), generally will induce very thin that metal level does, even arrive than a degree that atomic layer is also thin, make so again and the wayward and repetition of technology increased the difficulty that realizes on the technology.The metal side of development in recent years is to inductive technology (MILC, Metal Induced Lateral Crystallization), " Lowtemperature poly-Si thin film transistor fabrcation by metal-inducedlateral crystallization; Seok-Woon Lee and Seung-Ki Joo; IEEE ElectronDevice Letter; 1996; Vol17; pp160 " reports as document, although this technology can reach the problem that reduces residual metallic contamination, but it is also very complicated on the technology, and still can not avoid metal level to contact fully with the direct of semiconductor layer, also exist between MIC and the MILC and crystal boundary that the MILC of both direction stays when meeting in the centre, and the existence of crystal boundary has influenced the puncture voltage and the leakage current of device.
In sum, in this field, explore new method for manufacturing polycrystalline silicon, improve the quality of polysilicon membrane, simplify manufacturing process, the controllability that improves preparation is very significant.
Summary of the invention
The objective of the invention is to utilize improved metal inducement technology, at low temperatures with the a-Si film again crystallization form high-quality polysilicon membrane, for the use of element manufacturing.
Concrete scheme of the present invention is as follows:
At first deposit one deck amorphous silicon membrane 11 on dielectric substrate 10, its thickness is generally tens nanometers to the hundreds of nanometer, also can be thick in several microns.Using plasma strengthens the method growth of chemical vapor deposition (PECVD) or low-pressure chemical vapor deposition (LPCVD).Substrate 10 adopts insulating material, as with glass, quartz or be covered with SiO
2The silicon chip of insulating barrier (thickness is hundreds of nanometers).
Second step, regrowth one deck and silicon kinds of materials are as the separator 12 of inducing metal on amorphous silicon membrane 11, its thickness generally is between hundreds of nanometers in tens nanometers, make metal level avoid contacting with the direct of amorphous silicon layer, can guarantee again simultaneously near annealing temperature (about 500 ℃), metallic atom can spread in separator 12 and enter into amorphous silicon layer, reaches the purpose of revulsive crystallization.Metallic spacer 12 also can adopt the method growth of PECVD or LPCVD to form, and metallic spacer 12 materials can adopt the material different with silicon, specifically adopt material such as SiNx, SiO
2, SiON, SiCF.
In the 3rd step, evaporation induces metal level 13, its thickness to be generally a nanometer between the tens nanometer again on metallic spacer 12.The effect of this layer material is that feasible metallic atom wherein is by after diffusing into metallic spacer, enter into silicon layer again, form metal silicide with silicon atom, make crystallization can carry out (" Silicide formation and silicide-mediated crystallizationof nickel-implanted amorphous silicon thin films; C.Hayzelden and J.L.Batstone; J.Appl.Phys; (1993); Vol73 No.12, pp8279 " is described for the effect of metal such as document) at low temperatures.Induce metal level 13 can adopt metal Ni, Au, Cu, Al, Pd, Co, Ag, these metals can adopt the method preparation of sputter, thermal evaporation and electron beam evaporation.
The 4th step, inducing on the metal level 13 diffusion media layers 14 on the regrowth layer of metal, its thickness is generally tens nanometers to hundreds of nanometers.Diffusion media layers 14 can adopt the material identical or different with metallic spacer 12 on the metal, the also method growth by PECVD or LPCVD, as: SiNx, a-Si, SiO
2, SiON, SiCF.
In the 5th step, annealing (being lower than 600 ℃) under cryogenic conditions realizes the crystallization of amorphous silicon to polysilicon.Annealing is carried out in quick anneal oven, and adopts protective gas (as nitrogen) that sample is protected in the annealing process, and the time of annealing is generally a few hours to tens hour.
The 6th step, after crystallization is finished, the method that adopts dry method or wet etching separately or together with diffusion media layers on the metal 14, induce metal level 13 and separator 12 to remove, guarantee that simultaneously polysilicon layer and dielectric substrate are not damaged in the etching process, thereby staying polysilicon layer and dielectric substrate uses for element manufacturing
In the scheme of the present invention, induce metallic atom both can diffuse into amorphous silicon layer downwards by metallic spacer 12, simultaneously also can upwards diffuse into diffusion media layers 14 on the metal, making like this induces the part metals atom in the metal level 13 to obtain shunting, and can be by changing this two layers of material thickness and material category separately, metallic atom quantity to diffusion is up and down regulated and control, when guaranteeing to induce effect preferably, can increase and induce metal layer thickness, improve the operability and the repeatability of technology; Again because the quality of polysilicon membrane such as the size of crystal grain be and the quantity of metallic atom, promptly the formed nucleus quantity of metal silicide is relevant, the quantity that reduces nucleus helps improving the size of polysilicon grain.Therefore, adopt the method among the present invention, can prepare high-quality polysilicon membrane, as less grain boundary defective, bigger crystallite dimension (lateral dimension of single crystal grain is greater than 8 microns); Simultaneously, induce bigger that the thickness of metal level 13 can do, reach nanoscale so that bigger thickness, thereby improve the repeatability of technology, the controllability of technology is strengthened; Moreover the existence of metallic spacer 12 has avoided inducing metal level to contact with the direct of semiconductor layer, reduced crystallization finish after kish to the pollution of semiconductor layer, also reduced influence to device (as TFT); By selection, make diffusion layer medium on the etching metal, the residual process of metal level and metallic spacer of inducing to semiconductor layer and not influence of substrate to diffusion layer medium on the metal and metallic spacer material.
Description of drawings
Fig. 1: polysilicon membrane of the present invention prepares schematic diagram.
Wherein dielectric substrate 10, amorphous silicon membrane 11 (crystallization becomes polysilicon layer after finishing), and metallic spacer 12 is induced diffusion media layers 14 on metal level 13 and the metal.
Embodiment
Embodiment 1:
Process program in this example as shown in Figure 1.
The first step at first adopts PECVD method deposition a-Si film 11 on plate glass substrate 10, its thickness is 60nm, with SiH
4Decomposition obtains a-Si as source of the gas.Underlayer temperature is 200 ℃ during deposition, and base vacuum is 2 * 10
-4Pa, chamber pressure 80Pa.Plate glass substrate 10 is used organic solvent such as toluene, acetone, ethanol ultrasonic cleaning respectively before using;
Second step was the SiNx layer of 50nm at a-Si film 11 depositions one layer thickness, and as metallic spacer 12, the growth of this layer film utilizes PECVD at SiH equally
4And NH
3Down growth of mixed atmosphere, underlayer temperature remains on 270 ℃, chamber pressure is 30Pa;
The 3rd step, then sample to be put into magnetic control platform growth one deck and induced metal 13, the thickness of this layer is 1nm, uses metal Ni as inducing metal, and underlayer temperature is 130 ℃ during growth, and base vacuum is 2 * 10
-4Pa, chamber pressure is 0.1Pa during sputter;
The 4th step, adopt the process conditions identical with second step then the layer thickness of growing on the sample be the SiNx layer of 50nm as metal on diffusion layer 14;
The 5th step, utilize quick anneal oven annealing in process 10 hours under 520 ℃ temperature, pass to N therebetween
2As protective gas;
In the 6th step, annealing utilizes plasma etch process (dry etching) at CF after finishing
4Carve diffusion layer 14 (SiNx) on the metal under the atmosphere, then erode remaining metal Ni with watery hydrochloric acid, last using plasma etching technics is at CF
4Carve metallic spacer 12 (SiNx) under the atmosphere, polysilicon layer that stays and substrate just can use for element manufacturing.
Embodiment 2:
Process program in this example as shown in Figure 1.
At first be covered with 400nmSiO
2Adopt PECVD method deposition a-Si film 11 on the silicon chip of insulating barrier, its thickness is 200nm, with SiH
4Decomposition obtains a-Si as source of the gas.Underlayer temperature is 200 ℃ during deposition, and base vacuum is 2 * 10
-4Pa, chamber pressure 80Pa.Before using, to being covered with 400nmSiO
2The silicon chip 10 of insulating barrier is used organic solvent such as toluene, acetone, ethanol ultrasonic cleaning respectively;
Second step was the SiNx layer of 100nm at a-Si film 11 depositions one layer thickness, and as metallic spacer 12, the growth of this layer film utilizes PECVD at SiH equally
4And NH
3Down growth of mixed atmosphere, underlayer temperature remains on 270 ℃, chamber pressure is 30Pa;
The 3rd step, then sample to be put into magnetic control platform growth one deck and induced metal 13, the thickness of this layer is 5nm, uses metal Ni as inducing metal, and underlayer temperature is 130 ℃ during growth, and base vacuum is 2 * 10
-4Pa, chamber pressure is 0.1Pa during sputter;
The 4th step, adopts the process conditions identical with the first step follow the layer thickness of growing on the sample be the 50nma-Si layer as metal on diffusion layer 14;
The 5th step, utilize quick anneal oven annealing in process 20 hours under the temperature of 520C, pass to N therebetween
2As protective gas;
In the 6th step, annealing utilizes plasma etch process (dry etching) at CF after finishing
4Carve diffusion layer 14 (a-Si) on the metal under the atmosphere, then erode remaining metal Ni with watery hydrochloric acid, last using plasma etching technics is at CF
4Carve metallic spacer 12 (SiNx) under the atmosphere, polysilicon layer that stays and substrate can use for element manufacturing.
Though the above form that the present invention's employing is given an example has been carried out concrete description, but one of ordinary skill in the art should be understood, these disclosed contents under the premise without departing from the spirit and scope of the present invention, can be done many changes just as an example on the details of each several part.
Claims (3)
1, a kind of metal inducement method for manufacturing polycrystalline silicon thin film with diffusion layer on the metal is characterized in that adopting improved metal inducement technology, and the amorphous silicon membrane crystallization is become polysilicon membrane, and its concrete method is:
At first go up deposition one deck amorphous silicon membrane (11) in dielectric substrate (10), its thickness is generally tens nanometers to several microns;
In second step, regrowth one deck and silicon kinds of materials are as the separator (12) of inducing metal on amorphous silicon membrane (11), and its thickness generally is to arrive between hundreds of nanometers in tens nanometers, and metallic spacer (12) material adopts SiNx, SiO
2, SiON or SiCF;
The 3rd step, metal level (13) is induced in evaporation again on metallic spacer (12), its thickness is generally a nanometer between the tens nanometer, induce metal level (13) can adopt metal Ni, Au, Cu, Al, Pd, Co or Ag, these metals can adopt the method preparation of sputter, thermal evaporation and electron beam evaporation;
The 4th step, inducing on the metal level (13) diffusion media layers (14) on the regrowth layer of metal, its thickness generally is that tens nanometers arrive hundreds of nanometers, and diffusion media layers on the metal (14) can adopt and the identical or different material of metallic spacer (12), as SiNx, a-Si, SiO
2, SiON or SiCF;
The 5th step, carry out crystallization being lower than under 600 ℃ the cryogenic conditions annealing, annealing is carried out in quick anneal oven, and adopts protective gas that sample is protected in the annealing process, and the time of annealing was generally several hours to tens hours;
The 6th step, after crystallization is finished, the method that adopts dry method or wet etching separately or together with diffusion media layers on the metal (14), induce metal level (13) and metallic spacer (12) to remove, on dielectric substrate, obtain polysilicon membrane.
2, the metal inducement method for manufacturing polycrystalline silicon thin film with diffusion layer on the metal according to claim 1 is characterized in that: dielectric substrate (10) is glass, quartz or the silicon chip that is covered with hundreds of nanometer SiO2 insulating barriers.
3, the metal inducement method for manufacturing polycrystalline silicon thin film with diffusion layer on the metal according to claim 1 and 2 is characterized in that: diffusion media layers (14) is to utilize the method for plasma-enhanced chemical vapor deposition or low-pressure chemical vapor deposition to make on amorphous silicon membrane (11), metallic spacer (12) and the metal.